CN109503015A - A kind of high activity construction material auxiliary material and preparation method thereof - Google Patents
A kind of high activity construction material auxiliary material and preparation method thereof Download PDFInfo
- Publication number
- CN109503015A CN109503015A CN201811629547.2A CN201811629547A CN109503015A CN 109503015 A CN109503015 A CN 109503015A CN 201811629547 A CN201811629547 A CN 201811629547A CN 109503015 A CN109503015 A CN 109503015A
- Authority
- CN
- China
- Prior art keywords
- parts
- high activity
- modifying agent
- raw material
- auxiliary material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses kind of high activity construction material auxiliary materials and preparation method thereof; a kind of high activity construction material auxiliary material, it is made of the raw material that following weight parts match: cinder and/or 20~40 parts of 50~70 parts of flyash, steel slag and/or granulated blast-furnace slag, 4~9 parts of lime stone, 3~8 parts of desulfurized gypsum, 0.8~1.8 part of modifying agent;The modifying agent is made of the raw material that following weight parts match: 45~52 parts of sodium sulphate, 7~10 parts of calcium chloride, 0.2-0.8 parts of naphthalene water reducer, 0.5~1.5 part of triethanolamine, 0.5~1.5 part of lauryl sodium sulfate.Preparation method is to mix raw material in proportion, smash and grind as 400~500m2The powder of/kg.It can be used for the modified material of cement, be also used as Mine ventilator gel rubber material, and that it has that there are also raw material sources is abundant, production and application cost is cheap, resource border benefit and obvious economic advantage.
Description
Technical field
The invention belongs to building material technical field, especially a kind of high activity construction material auxiliary material and its preparation side
Method.
Background technique
The waste of industrial residue is stored up for a long time does not only take up a large amount of soils, and will cause to the serious of water system and atmosphere
Pollution and harm.The accumulation of mass breaking barren rock as a result, having damaged large stretch of farmland and backwoods.The long-term heap of industrial nocuousness slag
It deposits, by sleet leaching, soluble ingredient permeates downwards with water from earth's surface, converts to soil mobility, and enrichment harmful substance makes stockyard
Neighbouring soil property acidification, alkalization, hardening, or even the pollution of huge sum of money genotype occurs.
Industrial residue is comprehensively utilized, is turned waste into wealth, can to the maximum extent turn trade waste with Dai Zhi
Available commodity are turned to, not only expand resource, but also also reduce product cost.Reflection first is input and output rate
It improves, under conditions of showing the same raw material of consumption, by comprehensive utilization, more more valuable products can be produced, because
And relatively reduce the cost of unit product.Followed by by comprehensive utilization, blowdown object reduces, thus also just reduces useless
The occupied area of slag reduces remote transport, while also instead of the consumption of natural resources.Low freight charges, low cost, low price
Lattice had both improved the economic benefit of enterprise, and had also improved social benefit.
Summary of the invention
It is an object of the invention to using Industry Waste waste residue as primary raw material, provide a kind of high activity construction material auxiliary material,
Cement grade can be improved in addition in cement, also blends insulation effect with antifreeze, anti-;As Mine ventilator gel rubber material, with
Mine ventilator framework material has good fluidity, meets construction requirement with the use of filling mine, meanwhile, it has, and there are also raw materials
Abundance, production and application cost be cheap, resource border benefit and obvious economic advantage.
Another object of the present invention is to provide a kind of preparation methods of high activity construction material auxiliary material.
In order to achieve the above objectives, the present invention adopts the following technical scheme: a kind of high activity construction material auxiliary material, it be by
The raw material of following weight parts proportion is made: cinder and/or 50~70 parts of flyash, steel slag and/or granulated blast-furnace slag 20~40
Part, 4~9 parts of lime stone, 3~8 parts of desulfurized gypsum, 0.8~1.8 part of modifying agent;The modifying agent is matched by following weight parts
Raw material be made: 45~52 parts of sodium sulphate, 7~10 parts of calcium chloride, 0.2-0.8 parts of naphthalene water reducer, triethanolamine 0.5~1.5
Part, 0.5~1.5 part of lauryl sodium sulfate.
Preferably, the high activity construction material auxiliary material, it is made of the raw material that following weight parts match: cinder
25~35 parts of 25~35 parts, 25~35 parts of flyash, steel slag and/or granulated blast-furnace slag, 5~8 parts of lime stone, desulfurized gypsum 4
~7 parts, 1.0~1.5 parts of modifying agent.
Preferably, the modifying agent is made of the raw material that following weight parts match: 47~50 parts of sodium sulphate, calcium chloride
7.5~9.5 parts, 0.4-0.6 parts of naphthalene water reducer, 0.8~1.2 part of triethanolamine, 0.8~1.2 part of lauryl sodium sulfate.
Preferably, the high activity construction material auxiliary material, it is made of the raw material that following weight parts match: cinder
30 parts of 30 parts, 30 parts of flyash, steel slag and/or granulated blast-furnace slag, 5.5 parts of lime stone, 5 parts of desulfurized gypsum, modifying agent 1.3
Part.
Preferably, the modifying agent is made of the raw material that following weight parts match: 48.5 parts of sodium sulphate, calcium chloride 8.5
Part, 0.5 part of naphthalene water reducer, 1 part of triethanolamine, 1 part of lauryl sodium sulfate.
A kind of preparation method of above-mentioned high activity construction material auxiliary material, it includes the following steps:
1) cinder and/or flyash, steel slag and/or granulated blast-furnace slag, lime stone and modifying agent are proportionally added into
First of powder-grinding process, it is 350~380m that smashing and grinding, which obtains specific surface area,2The mixed powder of/kg;
2) mixed powder of step 1) preparation and desulfurized gypsum are proportionally added into second powder-grinding process, smashed and ground
Obtaining specific surface area is 400~500m2The high activity construction material auxiliary material of/kg.
Preferably, above-mentioned steps 2) in, the mixed powder of step 1) preparation and desulfurized gypsum are proportionally added into second
Road powder-grinding process, it is 430~460m that smashing and grinding, which obtains specific surface area,2The high activity construction material auxiliary material of/kg.
Primary raw material used in the present invention is all industrial residue, and the lower various industrial residues of face handle are illustrated:
The cinder is the waste residue in thermal power plant, industrial civil boiler and its discharge of equipment fire coal;Main component is:
SiO2、Al2O3、Fe2O、CaO、MnO2。
The flyash is the fine ash that catching is got off in flue gas after coal combustion, and flyash is the master of coal-burning power plant's discharge
Want solid waste;The main component of flyash is: SiO2、Al2O3、FeO、Fe2O3、CaO、TiO2、MgO、K2O、Na2O、SO3、
MnO2。
The steel slag is the waste residue of steel-making discharge, it is one of vessel slag, open hearth slag, electroslag or a variety of;It
Main component be: CaO, Fe2O3、SiO2、Al2O3、MgO、MnO、TiO2、SO3。
The granulated blast-furnace slag when being the blast furnace process pig iron be able to silicate and alumino-silicate it is as main component
Fusant, after quenching granulating, as granulated blast-furnace slag;Its main component is: SiO2、CaO、Al2O3、MgO。
The desulfurized gypsum is also known as flue gas desulfurization gypsum, sulphur gypsum or FGD gypsum, it is coal-fired or oil industrial enterprise
Industry by-product gypsum obtained from after the sulfur dioxide administered in flue gas, main component are calcium sulphate dihydrate CaSO4·2H2O。
The beneficial effects of the present invention are:
1) in the raw material that the present invention uses, cinder, flyash, steel slag, granulated blast-furnace slag, desulfurized gypsum are all industrial lifes
The solid waste of production prepares high activity construction material auxiliary material with these raw materials, and the utilization for not only solving these solid wastes is asked
Topic reduces stockpiling land occupation, reduces the destruction of ecological environment, while cost is relatively low, is conducive to large-scale promotion application.
2) core of the invention technology is the preparation of modifying agent, according to the characteristic of primary raw material, targetedly selects
Formula of modifier raw material is as exciting agent, to effectively excite primary raw material potential activity, shows under modifying agent excitation
Activity and gelling property well.
3) specific surface area of high activity construction material auxiliary material product of the invention is 400~500m2/ kg, it is demonstrated experimentally that
The high activity construction material auxiliary material of this fineness adds in cement, it is possible to reduce clinker dosage reduces cost, improves and lives
Property, in construction, increase the toughness of cement and stick together performance, construction efficiency is high;Pressure-proof and snap-resistent as Mine ventilator
Intensity is best.
4) in the raw material that the present invention uses, cinder, flyash, steel slag, granulated blast-furnace slag are all the items in high-temp combustion
The waste residue produced under part contains a large amount of porous particle, large specific surface area, added with conducive to raising concrete in concrete
Label improves the antiseepage, antifreeze, heat preservation and thermal insulation property of concrete.
5) high activity construction material auxiliary material of the invention can be used cooperatively with various Mine ventilator framework materials, can root
Usage ratio is adjusted according to transportation range, means of transportation, pumping technology, mine filling material is made to keep good mobility, it can
It is carried out under normal pressure and lower temperature, required low energy consumption, thus greatly reduces mine filling material production cost, has good
Popularization and application foreground.
6) raw material sources used by the preparation method of high activity construction material auxiliary material of the present invention are extensive, low in cost,
The preparation method simple process, easily operated, nothing " three wastes " discharge, resource border benefit and obvious economic.
Specific embodiment
To keep technical solution of the present invention clearer, embodiment of the present invention is made into one below by specific embodiment
Step describes in detail.
Embodiment 1: a kind of high activity construction material auxiliary material, it is made of the raw material that following weight parts match: cinder
30 parts, 30 parts of flyash, 30 parts of granulated blast-furnace slag, 5.5 parts of lime stone, 5 parts of desulfurized gypsum, 1.3 parts of modifying agent;Described changes
Property agent is made of the raw material that following weight parts match: 48.5 parts of sodium sulphate, 8.5 parts of calcium chloride, 0.5 part of naphthalene water reducer, three second
1 part of hydramine, 1 part of lauryl sodium sulfate.
The preparation method of the embodiment high activity construction material auxiliary material, it includes the following steps:
1) cinder, flyash, granulated blast-furnace slag, lime stone and modifying agent are proportionally added into first of grinding work
Sequence, it is 360m that smashing and grinding, which obtains specific surface area,2The mixed powder of/kg;
2) mixed powder of step 1) preparation and desulfurized gypsum are proportionally added into second powder-grinding process, smashed and ground
Obtaining specific surface area is 420m2The high activity construction material auxiliary material of/kg.
High activity construction material auxiliary material prepared by the embodiment is according to cement: high activity construction material auxiliary material=1:
1 ratio is added in cement, and the Cement Concrete block activity of detection in 28 days for adding high activity construction material auxiliary material improves 5%.
High activity construction material auxiliary material prepared by the embodiment is used for Mine ventilator, the recipe ratio of Mine ventilator material
Example are as follows: crude tailings: high activity construction material auxiliary material: water=48: 12: 23.Laboratory test results are as follows: pre-hardening 886min, eventually
Solidifying 3210min, 7 days intensity 2.9MPa, 14 days intensity 4.2MPa, 28 days intensity 5.6MPa.It is complete as Mine ventilator cementitious material
It meets the requirements entirely.
Embodiment 2: a kind of high activity construction material auxiliary material, it is made of the raw material that following weight parts match: cinder
35 parts, 25 parts of flyash, 30 parts of steel slag, 5 parts of lime stone, 6 parts of desulfurized gypsum, 1 part of modifying agent;The modifying agent is by following heavy
The raw material of amount part proportion is made: 52 parts of sodium sulphate, 7 parts of calcium chloride, 0.4 part of naphthalene water reducer, 0.8 part of triethanolamine, dodecane
1.2 parts of base sodium sulphate.
The preparation method of the embodiment high activity construction material auxiliary material, it includes the following steps:
1) cinder, flyash, steel slag, lime stone and modifying agent are proportionally added into first of powder-grinding process, crushing is ground
It is 370m that mill, which obtains specific surface area,2The mixed powder of/kg;
2) mixed powder of step 1) preparation and desulfurized gypsum are proportionally added into second powder-grinding process, smashed and ground
Obtaining specific surface area is 430m2The high activity construction material auxiliary material of/kg.
Embodiment 3: a kind of high activity construction material auxiliary material, it is made of the raw material that following weight parts match: cinder
20 parts, 40 parts of flyash, 12 parts of steel slag, 18 parts of granulated blast-furnace slag, 7 parts of lime stone, 4 parts of desulfurized gypsum, 1.6 parts of modifying agent;
The modifying agent is made of the raw material that following weight parts match: 45 parts of sodium sulphate, 9 parts of calcium chloride, 0.6 part of naphthalene water reducer,
1.2 parts of triethanolamine, 0.9 part of lauryl sodium sulfate.
The preparation method of the embodiment high activity construction material auxiliary material, it includes the following steps:
1) cinder, flyash, steel slag, granulated blast-furnace slag, lime stone and modifying agent are proportionally added into first of powder
Grinder sequence, it is 380m that smashing and grinding, which obtains specific surface area,2The mixed powder of/kg;
2) mixed powder of step 1) preparation and desulfurized gypsum are proportionally added into second powder-grinding process, smashed and ground
Obtaining specific surface area is 440m2The high activity construction material auxiliary material of/kg.
Embodiment 4: a kind of high activity construction material auxiliary material, it is made of the raw material that following weight parts match: fine coal
Grey 65 parts, 25 parts of granulated blast-furnace slag, 6 parts of lime stone, 7 parts of desulfurized gypsum, 1.5 parts of modifying agent;The modifying agent is by following
The raw material of weight is made: 49 parts of sodium sulphate, 8 parts of calcium chloride, 0.7 part of naphthalene water reducer, 0.9 part of triethanolamine, 12
1.3 parts of sodium alkyl sulfate.
The preparation method of the embodiment high activity construction material auxiliary material, it includes the following steps:
1) flyash, granulated blast-furnace slag, lime stone and modifying agent are proportionally added into first of powder-grinding process, are crushed
It is 390m that grinding, which obtains specific surface area,2The mixed powder of/kg;
2) mixed powder of step 1) preparation and desulfurized gypsum are proportionally added into second powder-grinding process, smashed and ground
Obtaining specific surface area is 450m2The high activity construction material auxiliary material of/kg.
Finally, it should be noted that the foregoing is only a preferred embodiment of the present invention, it is not intended to restrict the invention,
Although the present invention is described in detail referring to the foregoing embodiments, for those skilled in the art, still may be used
To modify the technical solutions described in the foregoing embodiments or equivalent replacement of some of the technical features,
All within the spirits and principles of the present invention, any modification, equivalent replacement, improvement and so on should be included in of the invention
Within protection scope.
Claims (7)
1. a kind of high activity construction material auxiliary material, it is made of the raw material that following weight parts match: cinder and/or flyash
20~40 parts of 50~70 parts, steel slag and/or granulated blast-furnace slag, 4~9 parts of lime stone, 3~8 parts of desulfurized gypsum, modifying agent 0.8
~1.8 parts;The modifying agent is made of the raw material that following weight parts match: 45~52 parts of sodium sulphate, 7~10 parts of calcium chloride,
0.2-0.8 parts of naphthalene water reducer, 0.5~1.5 part of triethanolamine, 0.5~1.5 part of lauryl sodium sulfate.
2. high activity construction material auxiliary material according to claim 1, it is characterised in that: it is matched by following weight parts
Raw material be made: 25~35 parts of cinder, 25~35 parts of flyash, steel slag and/or 25~35 parts of granulated blast-furnace slag, lime stone 5
~8 parts, 4~7 parts of desulfurized gypsum, 1.0~1.5 parts of modifying agent.
3. high activity construction material auxiliary material according to claim 2, it is characterised in that: the modifying agent is by following heavy
The raw material of amount part proportion is made: 47~50 parts of sodium sulphate, 7.5~9.5 parts of calcium chloride, 0.4-0.6 parts of naphthalene water reducer, three ethyl alcohol
0.8~1.2 part of amine, 0.8~1.2 part of lauryl sodium sulfate.
4. high activity construction material auxiliary material according to claim 3, it is characterised in that: it is matched by following weight parts
Raw material be made: 30 parts of 30 parts of cinder, 30 parts of flyash, steel slag and/or granulated blast-furnace slag, 5.5 parts of lime stone, desulfurized gypsum
5 parts, 1.3 parts of modifying agent.
5. high activity construction material auxiliary material according to claim 4, it is characterised in that: the modifying agent is by following heavy
The raw material of amount part proportion is made: 48.5 parts of sodium sulphate, 8.5 parts of calcium chloride, 0.5 part of naphthalene water reducer, 1 part of triethanolamine, 12
1 part of sodium alkyl sulfate.
6. the preparation method of high activity construction material auxiliary material described in claim 1 to 5 any one, it includes following step
It is rapid:
1) cinder and/or flyash, steel slag and/or granulated blast-furnace slag, lime stone and modifying agent are proportionally added into first
Road powder-grinding process, it is 350~380m that smashing and grinding, which obtains specific surface area,2The mixed powder of/kg;
2) mixed powder of step 1) preparation and desulfurized gypsum are proportionally added into second powder-grinding process, smashing and grinding obtains
Specific surface area is 400~500m2The high activity construction material auxiliary material of/kg.
7. the preparation method of high activity construction material auxiliary material according to claim 6, it is characterised in that: above-mentioned steps 2)
In, the mixed powder of step 1) preparation and desulfurized gypsum are proportionally added into second powder-grinding process, smashing and grinding is compared
Surface area is 430~460m2The high activity construction material auxiliary material of/kg.