CN109494268A - A kind of photovoltaic module and preparation method - Google Patents
A kind of photovoltaic module and preparation method Download PDFInfo
- Publication number
- CN109494268A CN109494268A CN201811363785.3A CN201811363785A CN109494268A CN 109494268 A CN109494268 A CN 109494268A CN 201811363785 A CN201811363785 A CN 201811363785A CN 109494268 A CN109494268 A CN 109494268A
- Authority
- CN
- China
- Prior art keywords
- photovoltaic module
- glass layer
- glass
- panel
- adhesive film
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of photovoltaic module and preparation methods, include successively from top to bottom transparent panel, cell piece and backboard, further include the first glass layer, and first glass layer is the glass fabric of the glass fibre composition containing fatty acid amide acetate.It include the glass fibre that fatty acid amide acetate is added in raw material in the glass layer of photovoltaic module of the present invention, in post-production, in the laminating process of solar panel, 105-165 DEG C can be warming up to, packaging adhesive film interpenetrates with glass layer, glass fabric can be converted into transparent by milky under this processing environment, it applies the strength that not only can increase solar panel in flexible solar panel, make solar panel that there is toughness and flexibility, and the translucency of solar panel is not influenced, does not influence the Generation Rate of solar panel.
Description
Technical field
The present invention relates to photovoltaic solar cell field more particularly to a kind of photovoltaic module and preparation methods.
Background technique
Existing solar panel is that at least one in backboard or panel is hard material, such as glass, such ability
It ensures the intensity of solar panel, but prevents solar panel from change shape, flexibility is lost, in many environment
Under cannot use, and hard material stress cracky is not readily transportable.
Increase strength and toughness does not lose flexibility again, the use of glass fibre is best selection, still, because of glass fibre primary colors
For milky, thus it is existing in the market, if wanting to change the color of glass fibre, exactly deepen the color of glass fibre.It uses in this way
Shi Ze will affect penetrating for light, reduce light transmittance, to reduce generating efficiency.
Summary of the invention
Technical problem to be solved by the present invention lies in the deficiency for overcoming the above-mentioned prior art, provide a kind of light transmittance it is high and
With toughness and a kind of photovoltaic module flexible and preparation method.
A kind of photovoltaic module provided by the invention includes successively from top to bottom transparent panel, cell piece and backboard, further includes
First glass layer, first glass layer are the glass fibers of the glass fibre composition containing fatty acid amide acetate
Wei Bu.
Wherein, first glass layer is arranged between the panel and the cell piece by packaging adhesive film.
It include the glass that fatty acid amide acetate is added in raw material in the glass layer of photovoltaic module in the present embodiment
Fiber in the laminating process of solar panel, can be warming up to 105-165 DEG C in post-production, packaging adhesive film and glass fibers
Dimension layer interpenetrates, and glass fabric can be converted into transparent by milky under this processing environment, be applied in flexible solar
It not only can increase the strength of solar panel in solar panel, make solar panel that there is toughness and flexibility, and do not influence solar energy
The translucency of solar panel does not influence the Generation Rate of solar panel.
And product weight is light, the only 30-40% weight of conventional crystalline silicon product, about 6-7kg；It is readily transported, number of casing
Measure the quantity of extra conventional products about 40%.It is suitble to a variety of occasion installations such as roof, bicycle shed, non-specification region.
Wherein, the first packaging adhesive film, first glass are provided between the panel and first glass layer
The second packaging adhesive film is provided between fibrous layer and the cell piece.
Wherein, first glass layer outer surface is also wrapped on acrylic acid.
Wherein, further include the second glass layer, second glass layer be pasted onto the backboard lower surface and/or
Between the backboard and the cell piece.
Wherein, second glass layer outer surface is also wrapped on acrylic acid.
Wherein, the panel is flexible glue film, and the backboard is white double-side fluorine flexibility glue film.
Wherein, the panel is the film made of ethylene and tetrafluoroethene copolymerization.
A kind of preparation method of photovoltaic module provided by the invention, comprising steps of
S1: successively lay panel, the first packaging adhesive film, the first glass layer, the second packaging adhesive film, solar panel and back
Just photovoltaic module is made in plate；
S2: sending first photovoltaic module into one chamber of laminating machine, and set temperature is 105~145 DEG C, vacuumizes and is pressurised into -11kpa
~-9kpa, 350~450s of pressure maintaining；
S3: being re-fed into two chamber of laminating machine, and set temperature is 125~165 DEG C, vacuumizes and is pressurised into -11kpa~-9kpa, protects
730~880s is pressed, photovoltaic module is made.
Wherein, first glass layer is the glass fibre of the glass fibre composition containing fatty acid amide acetate
Cloth.
Wherein, third packaging adhesive film, the second glass layer are also successively equipped in step S1 between solar panel and backboard
With the 4th packaging adhesive film.
Detailed description of the invention
Fig. 1 is the structure chart of the photovoltaic module of the embodiment of the present invention.
Panel 1, cell piece 2, backboard 3, the first glass layer 41, the second glass layer 42, the first packaging adhesive film 51,
Second packaging adhesive film 52, third packaging adhesive film 53, the 4th packaging adhesive film 54.
Specific embodiment
The present invention is described in detail below in conjunction with embodiment and attached drawing, it should be pointed out that described reality
It applies example and is intended merely to facilitate the understanding of the present invention, and do not play any restriction effect to it.In the case where there is no specified otherwise, this
It is contrary when the direction additionally arranged when the photovoltaic module preparation of invention is come into operation with photovoltaic module.
As shown in Figure 1, from top to bottom successively including transparent panel 1, battery according to a kind of photovoltaic module provided by the invention
Piece 2 and backboard 3, further include the first glass layer 41, and the first glass layer 41 is the glass containing fatty acid amide acetate
The glass fabric of glass fiber composition.
It include the glass that fatty acid amide acetate is added in raw material in the glass layer of photovoltaic module in the present embodiment
Fiber in the laminating process of solar panel, can be warming up to 105-165 DEG C in post-production, packaging adhesive film and glass fibers
Dimension layer interpenetrates, and glass fabric can be converted into transparent by milky under this processing environment, be applied in flexible solar
It not only can increase the strength of solar panel in solar panel, make solar panel that there is toughness and flexibility, and do not influence solar energy
The translucency of solar panel does not influence the Generation Rate of solar panel.
Wherein, it is 0.005-0.02wt% that the fatty acid amide acetate, which accounts for the weight percent of raw material total amount,；It is preferred that
Ground, the fatty acid amide acetate including 0.008-0.015wt%, most preferably, the fatty acid amide vinegar including 0.01wt%
Hydrochlorate.
Further include in glass fibre raw material SiO2, Al2O3, Fe2O3, TiO2, SO3, Na2O, K2O, Na2Cl, Na2CO3,
Li2O, MgO and CaO.Wherein, the weight percent of raw material is respectively as follows: the SiO2 of 45-65wt%；The Al2O3 of 10-20wt%；
The Fe2O3 of 0.1-0.6wt%；The TiO2 of 0.2-1.6wt%；The SO3 of 0.05-0.1wt%；The Na2O of 0.2-0.5wt%；
The K2O of 0.05-0.5wt%；The Na2Cl of 0.05-0.5wt%；The Na2CO3 of 0.05-0.5wt%；The Li2O of 0.1-1.0wt%；
The MgO and CaO of 16-19wt%.
Wherein, the first glass layer 41 is arranged above panel 1 by packaging adhesive film or the first glass layer 41 is logical
Packaging adhesive film is crossed to be arranged between panel 1 and cell piece 2.
Preferably, the first glass layer 41 is arranged between panel 1 and cell piece 2 by packaging adhesive film.In this way, glass
Protection of the fibrous layer by panel 1 prevents hook silk to be destroyed.
Wherein, the first packaging adhesive film 51, the first glass layer 41 are provided between panel 1 and the first glass layer 41
The second packaging adhesive film 52 is provided between cell piece 2.In this way, there is a packaging adhesive film on glass layer two sides, two sides when lamination
By the diffusion from packaging adhesive film, glass layer receiving diffusion is comprehensively and uniform, in the work of fatty acid amide acetate
It is more preferable to switch to transparent effect under.
Wherein, 41 outer surface of the first glass layer is also wrapped on acrylic acid.Wherein, the quality of glass fibre and acrylic acid
Than for 8-4, it is preferable that the mass ratio of glass fibre and acrylic acid is 6.Wherein, acrylic acid is acrylate glue.That is, 105 Ke/㎡
Be coated in the glass fibre of acrylic acid, the acrylic acid amount of cladding is 12-18 grams or so, and the content of glass fibre is 70-120
Gram；Preferably, the acrylic acid amount of cladding is 15 grams or so, and the content of glass fibre is 90 grams.
In this way, it can be warming up to 105-165 DEG C in the laminating process of solar panel, and under this processing environment, cladding
Acrylic acid can be diffused into one another with the packaging adhesive film in solar panel, the connection effect being optimal also makes glass fibre
The transparency of layer is higher, and does not influence the performance of glass fibre and solar panel, and the ultraviolet energy of anti-UV also can be improved
Power.
It wherein, further include the second glass layer 42, the second glass layer 42 is pasted onto 3 lower surface of backboard and/or back
Between plate 3 and cell piece 2.In this way, further increasing the strength and toughness of photovoltaic module.
On the basis of the above embodiments, preferred embodiment includes:
Embodiment 1
Wherein, panel 1 is to apply fluorine flexibility glue film, and backboard 3 is white double-side fluorine flexibility glue film.With a thickness of 0.2-0.4mm,
Preferably with a thickness of 0.3mm.In this way, light transmittance reaches 98%, the ultraviolet ability of anti-UV is also improved.And make photovoltaic module can be with
It applies on the surface of arbitrary shape, there is excellent flexibility and morphotropism, have wide range of applications.
Backboard 3 is preferably two-sided fluorine integrated film glue, structure are as follows: FFC//PET//FFC；Using plasma chemistry changes
Property technology and Fu Gui institute surface grafting technology.
It wherein, further include the second glass layer 42, the second glass layer 42 is pasted onto 3 lower surface of backboard and/or back
Between plate 3 and cell piece 2.In this way, further increasing the strength and toughness of photovoltaic module.
Second glass layer, 42 outer surface is also wrapped on acrylic acid.Wherein, the mass ratio of glass fibre and acrylic acid is
8-4, it is preferable that the acrylic acid amount of cladding is 15 grams or so, and the content of glass fibre is 90 grams.In this way, the acrylic acid of cladding can
It is diffused into one another with the packaging adhesive film in solar panel, the connection effect being optimal.
Further, the second glass layer 42 is encapsulated in battery by third packaging adhesive film 53 and the 4th packaging adhesive film 54
Between plate and backboard 3.
Embodiment 2
Wherein, panel 1 and backboard 3 are to apply fluorine flexibility glue film, with a thickness of 0.2-0.4mm, preferably with a thickness of 0.3mm.
In this way, light transmittance reaches 98%, the ultraviolet ability of anti-UV is also improved.And photovoltaic module is allowed to apply the table in arbitrary shape
Face has excellent flexibility and morphotropism, has wide range of applications.
It wherein, further include the second glass layer 42, the second glass layer 42 is pasted onto 3 lower surface of backboard and/or back
Between plate 3 and cell piece 2.Wherein, the glass fabric that the second glass layer 42 is made of glass fibre contains in glass fibre
There is fatty acid amide acetate.The weight percent that the fatty acid amide acetate accounts for raw material total amount is 0.005-
0.02wt%；Preferably, the fatty acid amide acetate including 0.008-0.015wt%, most preferably, including 0.01wt%'s
Fatty acid amide acetate.
Second glass layer, 42 outer surface is also wrapped on acrylic acid.Wherein, the mass ratio of glass fibre and acrylic acid is
8-4, it is preferable that the acrylic acid amount of cladding is 15 grams or so, and the content of glass fibre is 90 grams.In this way, the acrylic acid of cladding can
It is diffused into one another with the packaging adhesive film in solar panel, the connection effect being optimal.
Further, the second glass layer 42 is encapsulated in battery by third packaging adhesive film 53 and the 4th packaging adhesive film 54
Between plate and backboard 3.
The present embodiment provides a kind of preparation methods of photovoltaic module, comprising steps of
S1: successively lay panel 1, the first packaging adhesive film 51, the first glass layer 41, the second packaging adhesive film 52, battery
Just photovoltaic module is made in plate and backboard 3；
S2: sending first photovoltaic module into one chamber of laminating machine, and set temperature is 105~145 DEG C, vacuumizes and is pressurised into -11kpa
~-9kpa, 350~450s of pressure maintaining；
S3: being re-fed into two chamber of laminating machine, and set temperature is 125~165 DEG C, vacuumizes and is pressurised into -11kpa~-9kpa, protects
730~880s is pressed, photovoltaic module is made.
Wherein, the first glass layer 41 is the glass fibre of the glass fibre composition containing fatty acid amide acetate
Cloth.
In laminating process, packaging adhesive film interpenetrates with glass layer, the glass fabric under this processing environment
It can be converted by milky transparent, apply the strength that not only can increase solar panel in flexible solar panel, make
Solar panel has toughness and flexibility, and does not influence the translucency of solar panel, does not influence the power generation of solar panel
Rate.
And product weight is light, the only 30-40% weight of conventional crystalline silicon product, about 6-7kg；It is readily transported, number of casing
Measure the quantity of extra conventional products about 40%.It is suitble to a variety of occasion installations such as roof, bicycle shed, non-specification region.
Wherein, third packaging adhesive film 53, the second glass fibre are also successively equipped in step S1 between solar panel and backboard 3
Layer 42 and the 4th packaging adhesive film 54.
Wherein, it is further comprised the steps of: before step S1
S0-1: high temperature base fabric is laid on substrate；
S0-2: the lay panel 1 in high temperature base fabric；
Wherein, it is further comprised the steps of: after step S3
S4: base fabric and substrate are removed.
Because this photovoltaic module is flexible unit, be laid with photovoltaic module using the technique of float glass feeding,
Keep each layer shape conformal, facilitates the progress of subsequent step.
Embodiment described above, only one kind of the present invention more preferably specific embodiment, those skilled in the art
The usual variations and alternatives carried out within the scope of technical solution of the present invention should be all included within the scope of the present invention.
Claims (10)
- It from top to bottom successively include transparent panel, cell piece and backboard 1. a kind of photovoltaic module, which is characterized in that further include the One glass layer, first glass layer are the glass fibre of the glass fibre composition containing fatty acid amide acetate Cloth.
- 2. a kind of photovoltaic module according to claim 1, which is characterized in that first glass layer passes through packaging plastic Film is arranged between the panel and the cell piece.
- 3. a kind of photovoltaic module according to claim 2, which is characterized in that the panel and first glass layer Between be provided with the first packaging adhesive film, be provided with the second packaging adhesive film between first glass layer and the cell piece.
- 4. a kind of photovoltaic module according to claim 3, which is characterized in that also wrap first glass layer outer surface It is covered with acrylic acid.
- 5. a kind of photovoltaic module according to claim 1-4, which is characterized in that further include the second glass fibre Layer, second glass layer are pasted between the backboard lower surface and/or the backboard and the cell piece.
- 6. a kind of photovoltaic module according to claim 5, which is characterized in that also wrap second glass layer outer surface It is covered with acrylic acid.
- 7. a kind of photovoltaic module described in any one of -4 and 6 according to claim 1, which is characterized in that the panel is flexibility Glue film, the backboard are white double-side fluorine flexibility glue film.
- 8. a kind of photovoltaic module according to claim 7, which is characterized in that the panel is to be total to by ethylene and tetrafluoroethene Film made of poly-.
- 9. a kind of preparation method of photovoltaic module, which is characterized in that comprising steps ofS1: successively lay panel, the first packaging adhesive film, the first glass layer, the second packaging adhesive film, solar panel and backboard, system At first photovoltaic module；S2: by first photovoltaic module be sent into one chamber of laminating machine, set temperature be 105~145 DEG C, vacuumize be pressurised into -11kpa~- 9kpa, 350~450s of pressure maintaining；S3: being re-fed into two chamber of laminating machine, and set temperature is 125~165 DEG C, vacuumizes and is pressurised into -11kpa~-9kpa, pressure maintaining Photovoltaic module is made in 730~880s；Wherein, first glass layer is the glass fabric of the glass fibre composition containing fatty acid amide acetate.
- 10. a kind of preparation method of photovoltaic module according to claim 9, which is characterized in that in step S1 solar panel and Third packaging adhesive film, the second glass layer and the 4th packaging adhesive film are also successively equipped between backboard.