CN109488672A - A kind of packet stainless steel tap rivet and preparation method thereof - Google Patents
A kind of packet stainless steel tap rivet and preparation method thereof Download PDFInfo
- Publication number
- CN109488672A CN109488672A CN201910041523.3A CN201910041523A CN109488672A CN 109488672 A CN109488672 A CN 109488672A CN 201910041523 A CN201910041523 A CN 201910041523A CN 109488672 A CN109488672 A CN 109488672A
- Authority
- CN
- China
- Prior art keywords
- stainless steel
- rivet
- manufactured head
- head
- packet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of packet stainless steel tap rivets and preparation method thereof, the packet stainless steel tap rivet includes: aluminium rivet, and it is connect with the manufactured head of the aluminium rivet, and the stainless steel cup for coating the manufactured head, the stainless steel cup is close to the manufactured head of the aluminium rivet and the flush edge corrugationless of stainless steel cup.By the present invention in that with aluminium rivet, and a stainless steel cup is added on aluminium rivet, the manufactured head of aluminium rivet is coated, the aluminium rivet advantage good because of the ductility of its material itself, it is easier to fill up the gap of riveting when riveting with device, effectively prevent the risk of leak, and stainless steel cup also guarantees that the smoothness at riveting in aesthetics, avoids occurring the defects of burr at riveting.
Description
Technical field
The present invention relates to riveting part technical fields, and in particular to a kind of packet stainless steel tap rivet and preparation method thereof.
Background technique
In the prior art, most of rivet is all carbon steel, when using rivet on some devices, due to carbon steel material
Rivet it is harder, deformation is less prone to when being riveted, cause riveting when gap be not easy to be filled out completely by rivet
It is full, therefore there are drainages.For example, in the riveting of panhandle and pot body, if using the rivet of carbon steel material as connection
If component, since pot body is punched, and the rivet of carbon steel material is unlikely to deform, therefore is easy for the presence of leak,
Big inconvenience is brought to the use of user.
Therefore, the existing technology needs to be improved and developed.
Summary of the invention
The technical problem to be solved in the present invention is that in view of the above drawbacks of the prior art, providing a kind of packet stainless steel tap
Rivet and preparation method thereof, it is intended to solve stainless steel rivet in the prior art be rivet when can not filling chink, be also easy to produce
The problems such as leak.
The technical proposal for solving the technical problem of the invention is as follows:
A kind of packet stainless steel tap rivet, wherein the packet stainless steel tap rivet includes: aluminium rivet, and with the aluminium rivet
Manufactured head connection, and the stainless steel cup for coating the manufactured head, the riveting of the stainless steel cup and the aluminium rivet
Ailhead is close to and the flush edge corrugationless of stainless steel cup.
Preferably, the packet stainless steel tap rivet, wherein the aluminium rivet include: manufactured head and with the rivet
The polished rod of head connection, the manufactured head is with the polished rod at T-shaped.
Preferably, the packet stainless steel tap rivet, wherein the manufactured head is at thin flat head rivet head, snap rivet
Head, any one in sunk head rivet head.
Preferably, the packet stainless steel tap rivet, wherein the aluminium rivet is an integral molding structure.
Preferably, the packet stainless steel rivet, wherein the stainless steel cup be arranged to it is bowl-shape, be convenient for and the rivet
Head combines.
Preferably, the packet stainless steel tap rivet, wherein the internal diameter of bowl-shape stainless steel cup is greater than the rivet
The outer diameter of head.
A kind of production method of packet stainless steel tap rivet, wherein the described method includes:
Step A, moulding process prepares aluminium rivet through the stamping process in advance；
Step B, the preparatory stainless steel cup prepared that cuts tentatively is combined with the manufactured head of the aluminium rivet, makes stainless steel cup
Coat entire manufactured head；
Step C, stainless steel cup and manufactured head are compacted using Sheet Metal Forming Technology, make to keep tight between the stainless steel cup and manufactured head
Patch and tight.
Preferably, the production method of the packet stainless steel tap rivet, wherein the method also includes:
Step D, the edge of the stainless steel cup is flattened, removes the fold and burr at edge.
Preferably, the production method of the packet stainless steel tap rivet, wherein the stainless steel cup be arranged to it is bowl-shape, just
In in conjunction with the manufactured head.
Preferably, the production method of the packet stainless steel tap rivet, wherein the internal diameter of bowl-shape stainless steel cup is big
In the outer diameter of the manufactured head.
Beneficial effects of the present invention: by the present invention in that adding a stainless steel cup to aluminium with aluminium rivet, and on aluminium rivet
The manufactured head of rivet is coated, the aluminium rivet advantage good because of the ductility of its material itself, when riveting with device more
The gap for easily filling up riveting, effectively prevents the risk of leak, and stainless steel cup also guarantees the smoothness at riveting in beauty
Degree, avoids occurring the defects of burr at riveting.
Detailed description of the invention
Fig. 1 is the perspective view of packet stainless steel tap rivet of the invention.
Fig. 2 is the exploded view of packet stainless steel tap rivet of the invention.
Fig. 3 is the side view of packet stainless steel tap rivet another kind embodiment of the invention.
Fig. 4 is the flow chart of the preferred embodiment of packet stainless steel tap rivet production method of the invention.
Specific embodiment
To make the objectives, technical solutions, and advantages of the present invention clearer and more explicit, right as follows in conjunction with drawings and embodiments
The present invention is further described.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, and do not have to
It is of the invention in limiting.
Since most of rivet in the prior art is all stainless steel material, when using rivet on some devices,
Since the rivet of stainless steel material is harder, deformation is less prone to when being riveted, cause riveting when gap not
It is easily fully filled with by rivet, therefore there are drainages.For example, in the riveting of panhandle and pot body, if using stainless steel riveting
Nail is as if connecting component, and since pot body is punched, and stainless steel rivet is unlikely to deform, therefore is easy for that there are leaks
Problem brings big inconvenience to the use of user.To solve the above-mentioned problems, the present invention provides a kind of packet stainless steel tap riveting
Nail, specific as shown in Figures 1 and 2, the packet stainless steel tap riveting includes: aluminium rivet 10, and the riveting with the aluminium rivet 10
Ailhead 110(is as shown in Figure 2) connection, and the stainless steel cup 20 for coating the manufactured head 110.
Firstly, in the present embodiment, used rivet material is aluminum material, that is, uses aluminium rivet 10, and aluminum material
Ductility is preferable, i.e., easily-deformable.Therefore, when being riveted using aluminium rivet 10, aluminium rivet 10 is easily-deformable, thus by riveting
The gap for connecing hole is fully filled with, thus the phenomenon that playing the effect being fully sealed, can preventing leak.In addition, in the present embodiment
It also adds a stainless steel cup 20 on the manufactured head 110 of aluminium rivet 10 to coat manufactured head 110, to guarantee the company of riveting
The beauty and glossiness at place are connect, while also avoiding aluminium rivet 10 and deforming caused corner angle and burr scuffing user.
Further, in this embodiment aluminium rivet 10 include: manufactured head 110 and connect with the manufactured head 110
Polished rod 120, the manufactured head 110 and the polished rod 120 are at T-shaped, and the length of polished rod 120 is 4-70mm.It can be with from Fig. 2
Find out, the aluminium rivet 10 mainly includes two parts, and polished rod 120 mainly plays riveting, and manufactured head 110 is mainly
Play the role of for two devices of riveting being fixed.Manufactured head 110 in the present embodiment can using thin flat head rivet head,
Any one in snap rivet head, sunk head rivet head, when it is implemented, can be carried out according to the device of required riveting autonomous
Selection.Preferably, the aluminium rivet 10 in the present embodiment is an integral molding structure, and can specifically be made of Sheet Metal Forming Technology.
Preferably, the end of the aluminium rivet 10 of the packet stainless steel tap rivet in the present embodiment Fig. 1 is flat.In other realities
It applies in example, round end shape also can be set into the end of the aluminium rivet 10, as shown in Figure 3, so that packet stainless steel tap rivet can be with
It is applicable in more usage scenarios.
Further, in this embodiment stainless steel cup 20 cut in advance, and be arranged to it is bowl-shape, so as to
It is combined with manufactured head 110.That is, bowl-shape stainless steel cup 20 is can directly to cover on manufactured head 110, therefore
The internal diameter of bowl-shape stainless steel cup 20 needs the outer diameter greater than the manufactured head 110, to guarantee that stainless steel cup 20 can
Be set on manufactured head 110 easily.After stainless steel cup 20 is set on manufactured head 110, using Sheet Metal Forming Technology to stainless
Steel bowl 20 is compacted, so as to be close between stainless steel cup 20 and manufactured head 110 and seamless, to ensure that the stainless steel
Cup 20 is not easy to fall off from manufactured head 110.
Further, in order to avoid fold and burr occurs in the edge of stainless steel cup 20, therefore, when by the stainless steel
After 20 compacting of cup, also the edge of stainless steel cup 20 is flattened in the present embodiment, so that the edge of the stainless steel cup 20
Also the same and manufactured head 110 fits closely, and ensure that beauty.It is stainless on manufactured head 110 and when aluminium rivet 10 is in riveting
The flush edge of steel bowl 20 is bonded manufactured head 110 and the device into intimate of riveting, further ensures the leakproofness of riveted holes,
Further prevent the risk of leak.
For example, applying packet stainless steel tap rivet on cooker, specially panhandle and cookware are riveted.Due to aluminium riveting
The ductility of material itself is followed closely, so that aluminium rivet is easily deformed when riveting, to carry out to the gap of riveted holes complete
It fills up.Also, due to also setting up a stainless steel cup on the manufactured head of aluminium rivet, and stainless steel cup and manufactured head fit closely and
Flush edge corrugationless, so that manufactured head and the panhandle of aluminium rivet fit closely, further to the gap of riveted holes after riveting
It is sealed, efficiently avoids the risk of leak.
Based on the above embodiment, the present invention also provides a kind of production methods of packet stainless steel tap rivet, specifically such as institute in Fig. 3
Show.The production method includes:
Step S100, moulding process prepares aluminium rivet through the stamping process in advance；
Step S200, the preparatory stainless steel cup prepared that cuts tentatively is combined with the manufactured head of the aluminium rivet, is made stainless
Steel bowl coats entire manufactured head；
Step S300, stainless steel cup and manufactured head are compacted using Sheet Metal Forming Technology, make to protect between the stainless steel cup and manufactured head
Hold abutting and tight.
In this city embodiment, stainless steel cup be cut in advance, and be arranged to it is bowl-shape, so as to and manufactured head
It is combined.Preferably, the internal diameter of bowl-shape stainless steel cup needs the outer diameter greater than the manufactured head, to guarantee not
Rust steel bowl can be set on manufactured head easily.After stainless steel cup is set on manufactured head, using Sheet Metal Forming Technology to stainless
Steel bowl is compacted, so as to be close between stainless steel cup and manufactured head and seamless, to ensure that the stainless steel cup is not easy
It falls off from manufactured head.
Further, also the edge of stainless steel cup is carried out after being compacted the stainless steel cup, in the present embodiment whole
It is flat, remove the fold and burr at edge, so that the edge of the stainless steel cup is also the same and manufactured head fits closely, ensure that beauty
It sees.And when aluminium rivet is in riveting, the flush edge of the stainless steel cup on manufactured head makes the device of manufactured head and riveting tight
Closely connected conjunction further ensures the leakproofness of riveted holes, further prevents the risk of leak.
In conclusion the present invention provides a kind of packet stainless steel tap rivet and preparation method thereof, the packet stainless steel tap riveting
Nail includes: aluminium rivet, and is connect with the manufactured head of the aluminium rivet, and the stainless steel for coating the manufactured head
Cup, the stainless steel cup is close to the manufactured head of the aluminium rivet and the flush edge corrugationless of stainless steel cup.The present invention passes through
Using aluminium rivet, and a stainless steel cup being added on aluminium rivet, the manufactured head of aluminium rivet being coated, aluminium rivet is because of its material
The good advantage of the ductility of itself is easier to fill up the gap of riveting when riveting with device, effectively prevents the wind of leak
Danger, and stainless steel cup also guarantees that the smoothness at riveting in aesthetics, avoids occurring the defects of burr at riveting.
It should be understood that the application of the present invention is not limited to the above for those of ordinary skills can
With improvement or transformation based on the above description, all these modifications and variations all should belong to the guarantor of appended claims of the present invention
Protect range.
Claims (10)
1. a kind of packet stainless steel tap rivet, which is characterized in that the packet stainless steel tap rivet includes: aluminium rivet, and with it is described
The manufactured head of aluminium rivet connects, and the stainless steel cup for coating the manufactured head, the stainless steel cup and the aluminium
The manufactured head of rivet is close to and the flush edge corrugationless of stainless steel cup.
2. packet stainless steel tap rivet according to claim 1, which is characterized in that the aluminium rivet include: manufactured head and
The polished rod connecting with the manufactured head, the manufactured head is with the polished rod at T-shaped.
3. packet stainless steel tap rivet according to claim 2, which is characterized in that the manufactured head at thin flat head rivet head,
Any one in snap rivet head, sunk head rivet head.
4. packet stainless steel rivet according to claim 1, which is characterized in that the aluminium rivet is an integral molding structure.
5. packet stainless steel rivet according to claim 1, which is characterized in that the stainless steel cup is arranged to bowl-shape, is convenient for
In conjunction with the manufactured head.
6. packet stainless steel rivet according to claim 5, which is characterized in that the internal diameter of bowl-shape stainless steel cup is greater than
The outer diameter of the manufactured head.
7. a kind of production method of packet stainless steel tap rivet, which is characterized in that the described method includes:
Step A, moulding process prepares aluminium rivet through the stamping process in advance；
Step B, the preparatory stainless steel cup prepared that cuts tentatively is combined with the manufactured head of the aluminium rivet, makes stainless steel cup
Coat entire manufactured head；
Step C, stainless steel cup and manufactured head are compacted using Sheet Metal Forming Technology, make to keep tight between the stainless steel cup and manufactured head
Patch and tight.
8. the production method of packet stainless steel tap rivet according to claim 7, which is characterized in that the method also includes:
Step D, the edge of the stainless steel cup is flattened, removes the fold and burr at edge.
9. the production method of packet stainless steel tap rivet according to claim 7, which is characterized in that the stainless steel cup setting
At bowl-shape, convenient in conjunction with the manufactured head.
10. the production method of packet stainless steel tap rivet according to claim 9, which is characterized in that bowl-shape stainless steel cup
Internal diameter be greater than the manufactured head outer diameter.