CN109486300A - A kind of elastic rubber product metal anti-corrosion paint and its processing method - Google Patents
A kind of elastic rubber product metal anti-corrosion paint and its processing method Download PDFInfo
- Publication number
- CN109486300A CN109486300A CN201811184270.7A CN201811184270A CN109486300A CN 109486300 A CN109486300 A CN 109486300A CN 201811184270 A CN201811184270 A CN 201811184270A CN 109486300 A CN109486300 A CN 109486300A
- Authority
- CN
- China
- Prior art keywords
- parts
- resin
- rubber product
- paint
- corrosion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of elastic rubber product metal anti-corrosion paints, its raw material include: by weight 10-20 parts of superchlorinated polyvinyl chloride resin, 1-5 parts of silver chloride particle powder, 5-10 parts of alkyd resin, 5-10 parts of biocide mildewcide, 1-5 parts of toughener, chlorinated polyethylene it is resin 5-10 parts dilute, 0.1-1 parts of wetting dispersing agent, 0.2-1 parts of defoaming agent, 0.1-1 parts of substrate wetting agents, thixotropic agent 0.2-1 parts of thickening, 1-5 parts of mill base material and 10-20 parts of deionized water, are related to chemical technology field.The elastic rubber product metal anti-corrosion paint and its processing method, realization is separately added into silver chlorate and biocide mildewcide in anti-decaying paint to enhance the antibacterial ability of anti-decaying paint, microorganism can be inhibited to breed on anti-decaying paint well, avoid the surface of rubber product occur part fester, hole and generation situations such as spot, it realizes and had both carried out anti-chemical corrosion to rubber product and have to carry out anti-biological corrosion, achieve the purpose that guarantee rubber article integrality well, has ensured that the normal use of rubber product.
Description
Technical field
The present invention relates to chemical technology field, specially a kind of elastic rubber product metal anti-corrosion paint and its processing method.
Background technique
Anti-decaying paint, which is used in body surface, can be used to protect interior of articles not by one kind paint corroded, it is industry
More more common than anti-decaying paint a kind of paint in construction, be widely used in aviation, ship, chemical industry, the road Shu You Guanxi, Gang Jie Agencies, bridge,
The fields such as petroleum briquet well platform, deep to be favored by vast building manufacturer, anti-decaying paint is many kinds of to be can be generally divided into according to ingredient: ring
Oxygen anti-decaying paint, polyurethane anti-corrosion paint, acrylic acid anti-decaying paint, inorganic anti-corrosion paint, vinyl perchloride anti-corrosion paint, chlorinated rubber anticorrosive paint,
Highly-chlorinated polyethylene anti-decaying paint；It can be divided into according to purposes: pipeline anti-decaying paint, ship anti-decaying paint, metal anti-decaying paint, furniture
With anti-decaying paint, automobile anti-decaying paint, rubber anti-decaying paint；It can be divided into according to solvent: aqueous anticorrosion paint, oiliness anti-decaying paint；Anti-corrosion
Paint is the mixture of a variety of hydrosilicate mineral, and primary chemical group is Al2O3 and SiO2 two oxides, and Al2O3 mainly comes
Derived from clay mineral, SiO2 is also from addition to from clay mineral in particle quartz, Al2O3 content and Al2O3/SiO2 ratio
Value then shows that the purity of such clay is higher closer to the theoretical value of kaolinite mineral, and anti-decaying paint can make under severe conditions
With, and there is preferable durability, weather resistance, can ocean, use 10 years or 15 years or more under inferior mal-condition, i.e.,
Make in acid, alkali, salt and solvent medium, coating anti-decaying paint is also required to for the surface of some rubber products, to guarantee rubber system
The normal use of product.
The anti-decaying paint of rubber article coating at present is only to carry out anti-chemical corrosion mostly, and the corruption for rubber product
Erosion is handled except extraneous chemical attack, influences more seriously biological corrosion, and many microbes are viscous on the surface of rubber product
Attached breeding, so as to cause many rubber products surface occur part fester, hole and situations such as spot, can not achieve to rubber
Product, which had both carried out anti-chemical corrosion, the anti-biological corrosion of progress, can not reach the mesh for guaranteeing rubber article integrality well
, thus to the use of rubber product produce greatly it is unfavorable.
Summary of the invention
(1) the technical issues of solving
In view of the deficiencies of the prior art, the present invention provides a kind of elastic rubber product metal anti-corrosion paint and its processing sides
Method, solving, which can not achieve, had both carried out anti-chemical corrosion to rubber product and had had to carry out anti-biological corrosion, can not reach guarantor well
The purpose of rubber article integrality is demonstrate,proved, to produce greatly unfavorable problem to the use of rubber product.
(2) technical solution
In order to achieve the above object, the present invention is achieved by the following technical programs: a kind of elastic rubber product metal is anti-
Corruption paint, raw material includes: 10-20 parts of superchlorinated polyvinyl chloride resin, 1-5 parts of silver chloride particle powder, alkyd resin 5- by weight
10 parts, 5-10 parts of biocide mildewcide, 1-5 parts of toughener, chlorinated polyethylene it is resin 5-10 parts dilute, 0.1-1 parts of wetting dispersing agent, defoaming
0.2-1 parts of agent, 0.1-1 parts of substrate wetting agents, thixotropic agent 0.2-1 parts of thickening, 1-5 parts of mill base material and 10-20 parts of deionized water.
Preferably, the biocide mildewcide is pentachlorophenol and sodium salt, heterocyclic compound such as 2- benzimidazole etc. and double sulphur
For one or more of carbamate.
Preferably, the thickening thixotropic agent is hydrophobically modified polyurethane thickener, the water-swellable thickener of hydrophobically modified and gathers
One or more of urea-modified thickener.
The invention also discloses a kind of processing methods of elastic rubber product metal anti-corrosion paint, specifically includes the following steps:
S1, choose 1-5 parts of silver chloride particle powder first, by the silver chloride particle powder of selection pour into grinder into
Row is fully ground, until calcium hydroxide particle is ground into required powder size, to can be prepared by chlorination silver powder；
S2,10-20 parts of superchlorinated polyvinyl chloride resin, 5-10 parts of alkyd resin and 5-10 parts of the dilute tree of chlorinated polyethylene are chosen
Rouge, and respectively by the superchlorinated polyvinyl chloride resin, 5-10 parts of alkyd resin and the dilute tree of 5-10 parts of chlorinated polyethylene of 10-20 part of selection
Rouge pours into the tempering tank of mixer, then pours into 10-12 parts of water in tempering tank, with turning for 200-300r/min
Resin base material can be obtained after stirring 20-30min in speed；
S3, chlorination silver powder made from S1 is poured into the tempering tank in S2, starts mixing machine then with 200-300r/
The revolving speed of min, stir 20-30min, be sufficiently mixed chlorination silver powder with the resin base material in tempering tank, it is backward mix
It closes and 0.1-1 parts of substrate wetting agents and 0.1-1 parts of wetting dispersing agent is added in bucket, carry out being again stirring for mixing, make silver chlorate
Powder can be carried out in resin base material it is fully dispersed, to obtain the first mixing anti-decaying paint；
S4, it chooses in the first mixing anti-decaying paint made from 5-10 parts of biocide mildewcides addition S3, with 100-200r/min's
Revolving speed stirs 10-20min, dry, is cooled to room temperature, the second mixing anti-decaying paint can be obtained；
S5,1-5 parts of toughener, 0.2-1 parts of defoaming agent, 0.2-1 parts of thickening thixotropic agent, 1-5 parts of mill base are chosen
Material and remaining deionized water, and respectively by the toughener of 1-5 part of selection, 0.2-1 parts of defoaming agent, 0.2-1 parts of thickening
Thixotropic agent, 1-5 parts of mill base material and remaining deionized water are added in the second mixing anti-decaying paint made from S4, with 900-1000r/
The revolving speed of min stirs 15-20min, so that final metal anti-corrosion paint be made.
(3) beneficial effect
The present invention provides a kind of elastic rubber product metal anti-corrosion paint and its processing methods.Have compared with prior art
Below the utility model has the advantages that the elastic rubber product metal anti-corrosion paint and its processing method, by including: by weight in its raw material
10-20 parts of superchlorinated polyvinyl chloride resin, 1-5 parts of silver chloride particle powder, 5-10 parts of alkyd resin, 5-10 parts of biocide mildewcide, toughening
1-5 parts of agent, chlorinated polyethylene be resin 5-10 parts dilute, 0.1-1 parts of wetting dispersing agent, and 0.2-1 parts of defoaming agent, substrate wetting agents 0.1-1
Part, thixotropic agent 0.2-1 part of thickening, 1-5 parts of mill base material and 10-20 parts of deionized water, biocide mildewcide is pentachlorophenol and sodium salt,
Heterocyclic compound such as 2- benzimidazole etc. and one or more of double thiocarbamates, thickening thixotropic agent are hydrophobic change
One or more of property polyurethane thickener, the water-swellable thickener of hydrophobically modified and polyurea modified thickener, elastic rubber
The processing method of product metal anti-corrosion paint, specifically includes the following steps: the silver chloride particle powder of S1,1-5 parts of selection first, it will
The silver chloride particle powder of selection, which pours into grinder, to be fully ground, until calcium hydroxide particle is ground into required powder
Until granularity, to can be prepared by chlorination silver powder, S2,10-20 parts of superchlorinated polyvinyl chloride resin, 5-10 parts of alkyd resin are chosen
The dilute resin of chlorinated polyethylene with 5-10 parts, S3, pours into chlorination silver powder made from S1 in the tempering tank in S2, and then starting is mixed
Conjunction machine is stirred 20-30min, fills chlorination silver powder with the resin base material in tempering tank with the revolving speed of 200-300r/min
Divide mixing, S4, chooses in the first mixing anti-decaying paint made from 5-10 parts of biocide mildewcides addition S3, with turn of 100-200r/min
Speed stirring 10-20min, it is dry, be cooled to room temperature, can be obtained the second mixing anti-decaying paint, S5, choose 1-5 parts toughener,
0.2-1 parts of defoaming agent, 0.2-1 parts of thickening thixotropic agent, 1-5 parts of mill base material and remaining deionized water are realized well
Silver chlorate and biocide mildewcide are separately added into anti-decaying paint to enhance the antibacterial ability of anti-decaying paint, micro- life can be inhibited well
Object is bred on anti-decaying paint, thus avoid the surface of rubber product occur part fester, hole and generation situations such as spot, realize
It had both carried out to rubber product anti-chemical corrosion and had had to carry out anti-biological corrosion, it is complete to have reached guarantee rubber article well
The purpose of property, ensures that the normal use of rubber product.
Specific embodiment
The technical scheme in the embodiments of the invention will be clearly and completely described below, it is clear that described implementation
Example is only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, this field is common
Technical staff's every other embodiment obtained without making creative work belongs to the model that the present invention protects
It encloses.
The embodiment of the present invention provides three kinds of technical solutions: a kind of elastic rubber product metal anti-corrosion paint, raw material is by weight
Part ratio includes: 10-20 parts of superchlorinated polyvinyl chloride resin, 1-5 parts of silver chloride particle powder, 5-10 parts of alkyd resin, biocide mildewcide 5-
10 parts, 1-5 parts of toughener, chlorinated polyethylene it is resin 5-10 parts dilute, 0.1-1 parts of wetting dispersing agent, 0.2-1 parts of defoaming agent, substrate profit
0.1-1 parts of humectant, thixotropic agent 0.2-1 parts of thickening, 1-5 parts of mill base material and 10-20 parts of deionized water.
In the present invention, biocide mildewcide is pentachlorophenol and sodium salt, heterocyclic compound such as 2- benzimidazole etc. and double thio
One or more of carbamate.
In the present invention, thickening thixotropic agent is hydrophobically modified polyurethane thickener, the water-swellable thickener of hydrophobically modified and polyureas
One or more of modified thickener.
Embodiment 1
S1, the silver chloride particle powder for choosing 3 parts first, the silver chloride particle powder of selection is poured into grinder and is carried out
It is fully ground, until calcium hydroxide particle is ground into required powder size, to can be prepared by chlorination silver powder；
S2,15 parts of superchlorinated polyvinyl chloride resin, 7 parts of alkyd resin and 7 parts of the dilute resin of chlorinated polyethylene are chosen, and respectively will
15 parts of superchlorinated polyvinyl chloride resin, 7 parts of alkyd resin and 7 parts of the dilute resin of chlorinated polyethylene chosen pour into the mixed of mixer
It closes in bucket, then pours into 15 parts of water in tempering tank, resin base can be obtained after stirring 25min with the revolving speed of 250r/min
Material；
S3, chlorination silver powder made from S1 is poured into the tempering tank in S2, starts mixing machine then with 250r/min's
Revolving speed stirs 25min, is sufficiently mixed chlorination silver powder with the resin base material in tempering tank, backward tempering tank interior add
Enter 0.5 part of substrate wetting agents and 0.5 part of wetting dispersing agent, carries out being again stirring for mixing, chlorination silver powder is enable to set
Progress is fully dispersed in aliphatic radical material, to obtain the first mixing anti-decaying paint；
S4, it chooses in the first mixing anti-decaying paint made from 5-10 parts of biocide mildewcides addition S3, with the revolving speed of 150r/min
15min is stirred, it is dry, it is cooled to room temperature, the second mixing anti-decaying paint can be obtained；
S5,3 parts of toughener, 0.6 part of defoaming agent, 0.6 part of thickening thixotropic agent, 3 parts of mill base material and residue are chosen
Deionized water, and respectively by 3 parts of toughener of selection, 0.6 part of defoaming agent, 0.6 part of thickening thixotropic agent, 3 parts of color
Slurry and remaining deionized water are added in the second mixing anti-decaying paint made from S4, stir 17min with the revolving speed of 950r/min, from
And final metal anti-corrosion paint is made.
Embodiment 2
S1, the silver chloride particle powder for choosing 1 part first, the silver chloride particle powder of selection is poured into grinder and is carried out
It is fully ground, until calcium hydroxide particle is ground into required powder size, to can be prepared by chlorination silver powder；
S2,10 parts of superchlorinated polyvinyl chloride resin, 5 parts of alkyd resin and 5 parts of the dilute resin of chlorinated polyethylene are chosen, and respectively will
10 parts of superchlorinated polyvinyl chloride resin, 5 parts of alkyd resin and 5 parts of the dilute resin of chlorinated polyethylene chosen pour into the mixed of mixer
It closes in bucket, then pours into 10 parts of water in tempering tank, resin base can be obtained after stirring 20min with the revolving speed of 200r/min
Material；
S3, chlorination silver powder made from S1 is poured into the tempering tank in S2, starts mixing machine then with 200r/min's
Revolving speed stirs 20min, is sufficiently mixed chlorination silver powder with the resin base material in tempering tank, backward tempering tank interior add
Enter 0.1 part of substrate wetting agents and 0.1 part of wetting dispersing agent, carries out being again stirring for mixing, chlorination silver powder is enable to set
Progress is fully dispersed in aliphatic radical material, to obtain the first mixing anti-decaying paint；
S4, it chooses in the first mixing anti-decaying paint made from 5 parts of biocide mildewcides addition S3, is stirred with the revolving speed of 100r/min
10min, it is dry, it is cooled to room temperature, the second mixing anti-decaying paint can be obtained；
S5,1 part of toughener, 0.2 part of defoaming agent, 0.2 part of thickening thixotropic agent, 1 part of mill base material and residue are chosen
Deionized water, and respectively by 1 part of toughener of selection, 0.2 part of defoaming agent, 0.2 part of thickening thixotropic agent, 1 part of color
Slurry and remaining deionized water are added in the second mixing anti-decaying paint made from S4, stir 15min with the revolving speed of 900r/min, from
And final metal anti-corrosion paint is made.
Embodiment 3
S1, the silver chloride particle powder for choosing 5 parts first, the silver chloride particle powder of selection is poured into grinder and is carried out
It is fully ground, until calcium hydroxide particle is ground into required powder size, to can be prepared by chlorination silver powder；
S2,20 parts of superchlorinated polyvinyl chloride resin, 10 parts of alkyd resin and 10 parts of the dilute resin of chlorinated polyethylene are chosen, and respectively
20 parts of superchlorinated polyvinyl chloride resin of selection, 10 parts of alkyd resin and 10 parts of the dilute resin of chlorinated polyethylene are poured into mixer
Tempering tank in, then 12 parts of water is poured into tempering tank, with the revolving speed of 300r/min, after stirring 30min, tree can be obtained
Aliphatic radical material；
S3, chlorination silver powder made from S1 is poured into the tempering tank in S2, starts mixing machine then with 300r/min's
Revolving speed stirs 30min, is sufficiently mixed chlorination silver powder with the resin base material in tempering tank, backward tempering tank interior add
Enter 1 part of substrate wetting agents and 1 part of wetting dispersing agent, carries out being again stirring for mixing, enable chlorination silver powder in resin base
Progress is fully dispersed in material, to obtain the first mixing anti-decaying paint；
S4, it chooses in the first mixing anti-decaying paint made from 10 parts of biocide mildewcides addition S3, is stirred with the revolving speed of 200r/min
20min is mixed, it is dry, it is cooled to room temperature, the second mixing anti-decaying paint can be obtained；
S5,5 parts of toughener, 1 part of defoaming agent, 1 part of thickening thixotropic agent, 5 parts of mill base material are chosen and remaining is gone
Ionized water, and by 5 parts of toughener of selection, 1 part of defoaming agent, 1 part of thickening thixotropic agent, 5 parts of mill base material and remain respectively
Remaining deionized water is added in the second mixing anti-decaying paint made from S4, stirs 20min with the revolving speed of 1000r/min, to be made
Final metal anti-corrosion paint.
It should be noted that, in this document, relational terms such as first and second and the like are used merely to a reality
Body or operation are distinguished with another entity or operation, are deposited without necessarily requiring or implying between these entities or operation
In any actual relationship or order or sequence.Moreover, the terms "include", "comprise" or its any other variant are intended to
Non-exclusive inclusion, so that the process, method, article or equipment including a series of elements is not only wanted including those
Element, but also including other elements that are not explicitly listed, or further include for this process, method, article or equipment
Intrinsic element.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (4)
1. a kind of elastic rubber product metal anti-corrosion paint, it is characterised in that: its raw material includes: superchlorinated polyvinyl chloride resin by weight
10-20 parts, 1-5 parts of silver chloride particle powder, 5-10 parts of alkyd resin, 5-10 parts of biocide mildewcide, 1-5 parts of toughener, chlorination
5-10 parts of polyethylene resin, 0.1-1 parts of wetting dispersing agent, 0.1-1 parts of substrate wetting agents, thicken thixotropic agent by 0.2-1 parts of defoaming agent
0.2-1 parts, 1-5 parts of mill base material and 10-20 parts of deionized water.
2. a kind of elastic rubber product metal anti-corrosion paint according to claim 1 and its processing method, it is characterised in that: institute
Biocide mildewcide is stated as one in pentachlorophenol and sodium salt, heterocyclic compound such as 2- benzimidazole and double thiocarbamates
Kind is a variety of.
3. a kind of elastic rubber product metal anti-corrosion paint according to claim 1 and its processing method, it is characterised in that: institute
Stating thickening thixotropic agent is one in hydrophobically modified polyurethane thickener, the water-swellable thickener of hydrophobically modified and polyurea modified thickener
Kind is a variety of.
4. a kind of processing method of elastic rubber product metal anti-corrosion paint according to claim 1, it is characterised in that: specific
The following steps are included:
S1, the silver chloride particle powder for choosing 1-5 parts first, the silver chloride particle powder of selection is poured into grinder and is filled
Divide grinding, until calcium hydroxide particle is ground into required powder size, to can be prepared by chlorination silver powder；
S2,10-20 parts of superchlorinated polyvinyl chloride resin, 5-10 parts of alkyd resin and 5-10 parts of the dilute resin of chlorinated polyethylene are chosen, and
The superchlorinated polyvinyl chloride resin, 5-10 parts of alkyd resin and the dilute resin of 5-10 parts of chlorinated polyethylene of 10-20 part of selection are fallen respectively
Enter in the tempering tank of mixer, then pour into 10-12 parts of water in tempering tank, with the revolving speed of 200-300r/min, stirs
After mixing 20-30min, resin base material can be obtained；
S3, chlorination silver powder made from S1 is poured into the tempering tank in S2, starts mixing machine then with 200-300r/min's
Revolving speed, stir 20-30min, be sufficiently mixed chlorination silver powder with the resin base material in tempering tank, backward tempering tank in
0.1-1 parts of substrate wetting agents and 0.1-1 parts of wetting dispersing agent is added, carries out being again stirring for mixing, enables chlorination silver powder
It is enough carried out in resin base material it is fully dispersed, to obtain the first mixing anti-decaying paint；
S4, it chooses in the first mixing anti-decaying paint made from 5-10 parts of biocide mildewcides addition S3, with the revolving speed of 100-200r/min
10-20min is stirred, it is dry, it is cooled to room temperature, the second mixing anti-decaying paint can be obtained；
S5, choose 1-5 parts of toughener, 0.2-1 parts of defoaming agent, 0.2-1 parts of thickening thixotropic agent, 1-5 parts of mill base material and
Remaining deionized water, and respectively by the toughener, 0.2-1 parts of defoaming agent, 0.2-1 parts of thickening thixotroping of 1-5 part of selection
Agent, 1-5 parts of mill base material and remaining deionized water are added in the second mixing anti-decaying paint made from S4, with 900-1000r/min
Revolving speed stir 15-20min, so that final metal anti-corrosion paint be made.