CN109485982A - A kind of mobile phone foamed material - Google Patents
A kind of mobile phone foamed material Download PDFInfo
- Publication number
- CN109485982A CN109485982A CN201811001047.4A CN201811001047A CN109485982A CN 109485982 A CN109485982 A CN 109485982A CN 201811001047 A CN201811001047 A CN 201811001047A CN 109485982 A CN109485982 A CN 109485982A
- Authority
- CN
- China
- Prior art keywords
- parts
- mobile phone
- added
- silane coupling
- coupling agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of mobile phone foamed materials, its raw material includes: 100 parts of ethylene-vinyl acetate copolymer by weight, 8-20 parts of butadiene-styrene rubber, 2-8 parts of ethylene propylene diene rubber, 3-12 parts of polyformaldehyde, 2-10 parts of polyethylene, 2-10 parts of filler, 1-3 parts of lignin, 1-2 parts of foaming agent, 0.3-1.3 parts of zinc oxide, 1-1.5 parts of stearic acid, 0.2-0.5 parts of benzoyl peroxide, 0.1-0.35 parts of tetramethylthiuram monosulfide, 0.05-0.28 parts of sulphur, 0.1-0.2 parts of Triallyl isocyanurate, 0.1-2 parts of paraffin, 0.1-1 parts of glycerol, 0.1-1 parts of silane coupling agent.Mobile phone composite foam material proposed by the present invention, flexibility is good, and hardness is low, and heat resistance and ageing-resistant performance are excellent.
Description
Technical field
The present invention relates to mobile phone field of material technology more particularly to a kind of mobile phone foamed materials.
Background technique
Mobile phone has become essential means of communication in modern society, with the development of society, people use mobile phone
Higher requirements are also raised for the performance of material.Ethylene-vinyl acetate copolymer (EVA) product of rubber and plastic is novel environment friendly plastics hair
Foam material has many advantages, such as good water-fast, corrosion-resistant, processability, buffering, antidetonation, heat preservation, heat-insulated, environmentally friendly, wide at present
It is general to be used for the fields such as foaming shoe material, functional greenhouse film, packaging film, hot melt adhesive, wire and cable and toy.But existing ethylene-
Vinyl acetate co-polymer rubber-plastics material is harder, is not easy that relatively thin product is made, therefore can not carry out in field of mobile phones extensive
Using, and while applying in field of mobile phones there are resistance to ag(e)ing and heat resistance is not good defect, is limited its application.
Summary of the invention
Technical problems based on background technology, the invention proposes a kind of mobile phone foamed materials, and flexibility is good,
Hardness is low, and heat resistance and ageing-resistant performance are excellent.
A kind of mobile phone foamed material proposed by the present invention, raw material includes: ethylene-vinyl acetate copolymer by weight
100 parts, 8-20 parts of butadiene-styrene rubber, 2-8 parts of ethylene propylene diene rubber, 3-12 parts of polyformaldehyde, 2-10 parts of polyethylene, 2-10 parts of filler,
1-3 parts of lignin, 1-2 parts of foaming agent, 0.3-1.3 parts of zinc oxide, 1-1.5 parts of stearic acid, 0.2-0.5 parts of benzoyl peroxide,
0.1-0.35 parts of tetramethylthiuram monosulfide, 0.05-0.28 parts of sulphur, 0.1-0.2 parts of Triallyl isocyanurate, paraffin
0.1-2 parts, 0.1-1 parts of glycerol, 0.1-1 parts of silane coupling agent.
Preferably, in ethylene-vinyl acetate copolymer, the mass fraction of vinyl acetate is 18-20wt%.
Preferably, in butadiene-styrene rubber, the mass fraction of styrene is 24-25wt%.
Preferably, the filler is modified filler;The modified filler is prepared according to following technique: by carbon black, being received
Rice calcium carbonate, iron oxide, carbon nanotube, hydrotalcite are added in ethyl alcohol, and adjusting pH value after mixing evenly is 3-4, and it is even that silane is added
Join agent KH570, is warming up to 48-58 DEG C of reaction 15-22h after mixing evenly, is filtered, washed after reaction, is dried to obtain object
Expect A;Material A is added in dimethylformamide and is stirred evenly, styrene, butyl acrylate, first are added after being warming up to 70-85 DEG C
Base acrylic acid -2- hydroxyl ethyl ester, vinyl phosphoric acid dimethyl ester and azodiisobutyronitrile, insulation reaction 4-5h, reacts after mixing evenly
After be added naphthalene diisocyanate, stir 50-100min, obtain the modified filler after dry.
Preferably, in the preparation process of modified filler, carbon black, nanometer calcium carbonate, iron oxide, carbon nanotube, hydrotalcite,
The weight ratio of silane coupling agent KH570 is 15-21:3-9:2-10:1-5:3-14:5-12.
Preferably, in the preparation process of modified filler, material A, styrene, butyl acrylate, methacrylic acid -2- hydroxyl
Ethyl ester, vinyl phosphoric acid dimethyl ester, azodiisobutyronitrile, naphthalene diisocyanate weight ratio be 3-9:5-12:4-8:3-9:1-
5:0.3-0.8:5-16.
Preferably, the modified filler is prepared according to following technique: by weight by 18 parts of carbon blacks, 7 parts of nano-sized carbons
Sour calcium, 6 parts of iron oxide, 3 parts of carbon nanotubes, 9 parts of hydrotalcites are added in 50 parts of ethyl alcohol, and adjusting pH value after mixing evenly is 3.5, add
Enter 10 parts of silane coupling agent KH570, is warming up to 55 DEG C of reaction 20h after mixing evenly, is filtered, washed, is dried after reaction
Obtain material A;8 parts of material As are added in 50 parts of dimethylformamides by weight and are stirred evenly, are added 6 after being warming up to 75 DEG C
Part styrene, 5 parts of butyl acrylates, 7 parts of 2-hydroxyethyl methacry-lates, 3 parts of vinyl phosphoric acid dimethyl esters and 0.5 part of azo
Bis-isobutyronitrile, insulation reaction 4.5h, is added 12 parts of naphthalene diisocyanates after reaction after mixing evenly, stirs 80min, dry
After obtain the modified filler.
Preferably, the foaming agent be azodicarbonamide, azodiisobutyronitrile, dinitrosopentamethylene tetramine, 4,
One of 4 '-oxobenzenesulfonyl hydrazide, sodium bicarbonate or a variety of mixtures.
Preferably, the silane coupling agent is silane resin acceptor kh-550, silane coupling agent KH-560, silane coupling agent
The mixture of one or more of KH-570.
Mobile phone foamed material of the present invention, using ethylene-vinyl acetate copolymer as major ingredient, while joined butylbenzene
Rubber, ethylene propylene diene rubber, polyformaldehyde, polyethylene are modified it, and have regulated and controled five ratio, keep five performances best
Synergistic effect, assign the lower hardness of composite foam material, good flexibility and fatigue resistance;In the preparation of modified filler
In the process, carbon black, nanometer calcium carbonate, iron oxide, carbon nanotube, hydrotalcite is modified using silane coupling agent KH570, to make
Graft reaction has occurred in silane coupling agent KH570 and carbon black, nanometer calcium carbonate, iron oxide, carbon nanotube, hydrotalcite, by double bond
It has been introduced into carbon black, nanometer calcium carbonate, iron oxide, carbon nanotube, obtained material A in hydrotalcite;Material A and styrene, third
Olefin(e) acid butyl ester, 2-hydroxyethyl methacry-late, vinyl phosphoric acid dimethyl ester are polymerize under the action of azodiisobutyronitrile
Reaction, mixes, the two is reacted, so that polyurethane has been introduced into carbon black, nanometer calcium carbonate, oxygen with naphthalene diisocyanate
Change iron, carbon nanotube, obtained modified filler in hydrotalcite, is added into system, on the one hand, because being suitably added poly- ammonia
Ester significantly improves the plastic deformation of matrix, suitably reduces while keeping composite foam material compared with high elongation at tear
Relatively thin material can be made in the hardness of composite foam material, be applied in field of mobile phones, on the other hand, poly- ammonia therein
Ester structure can with the polymer in matrix occur physical entanglement, form network structure, make carbon black, nanometer calcium carbonate, iron oxide,
Carbon nanotube, hydrotalcite can be evenly dispersed in matrix, improve the associativity of filler and matrix, it is big to have postponed polymer
The degradation of molecule assigns composite foam material excellent tensile strength, tearing strength, heat resistance and resistance to ag(e)ing, while and second
Alkenyl dimethyl phosphate cooperation, hence it is evident that be catalyzed system into charcoal, improved Char Residues Structure, assigned the certain anti-flammability of system and heat-resisting
Property;Zinc oxide, benzoyl peroxide, tetramethylthiuram monosulfide, sulphur, in Triallyl isocyanurate addition system,
Cooperation is used as vulcanizing system, and curingprocess rate is fast, and effect is good, and the foamed material heat resistance and ageing-resistant performance made is excellent.
Specific embodiment
In the following, technical solution of the present invention is described in detail by specific embodiment.
Embodiment 1
A kind of mobile phone foamed material proposed by the present invention, raw material includes: ethylene-vinyl acetate copolymer by weight
100 parts, 20 parts of butadiene-styrene rubber, 2 parts of ethylene propylene diene rubber, 12 parts of polyformaldehyde, 2 parts of polyethylene, 10 parts of filler, 1 part of lignin, hair
2 parts of infusion, 0.3 part of zinc oxide, 1.5 parts of stearic acid, 0.2 part of benzoyl peroxide, 0.35 part of tetramethylthiuram monosulfide, sulphur
0.05 part of sulphur, 0.2 part of Triallyl isocyanurate, 0.1 part of paraffin, 1 part of glycerol, 0.1 part of silane coupling agent.
Embodiment 2
A kind of mobile phone foamed material proposed by the present invention, raw material includes: ethylene-vinyl acetate copolymer by weight
100 parts, 10 parts of butadiene-styrene rubber, 8 parts of ethylene propylene diene rubber, 3 parts of polyformaldehyde, 10 parts of polyethylene, 2 parts of filler, 3 parts of lignin, hair
1 part of infusion, 1.3 parts of zinc oxide, 1 part of stearic acid, 0.5 part of benzoyl peroxide, 0.1 part of tetramethylthiuram monosulfide, sulphur
0.28 part, 0.1 part of Triallyl isocyanurate, 2 parts of paraffin, 0.1 part of glycerol, 1 part of silane coupling agent.
Embodiment 3
A kind of mobile phone foamed material proposed by the present invention, raw material includes: ethylene-vinyl acetate copolymer by weight
100 parts, 18 parts of butadiene-styrene rubber, 3 parts of ethylene propylene diene rubber, 10 parts of polyformaldehyde, 4 parts of polyethylene, 8 parts of filler, 1.6 parts of lignin,
1.7 parts of foaming agent, 0.6 part of zinc oxide, 1.3 parts of stearic acid, 0.3 part of benzoyl peroxide, tetramethylthiuram monosulfide 0.32
Part, 0.1 part of sulphur, 0.17 part of Triallyl isocyanurate, 0.8 part of paraffin, 0.8 part of glycerol, 0.4 part of silane coupling agent;
Wherein, in ethylene-vinyl acetate copolymer, the mass fraction of vinyl acetate is 20wt%;
In butadiene-styrene rubber, the mass fraction of styrene is 24wt%;
The filler is modified filler;The modified filler is prepared according to following technique: by carbon black, nano-calcium carbonate
Calcium, iron oxide, carbon nanotube, hydrotalcite are added in ethyl alcohol, and adjusting pH value after mixing evenly is 3, and silane coupling agent is added
KH570 is warming up to 58 DEG C of reaction 15h after mixing evenly, is filtered, washed after reaction, is dried to obtain material A;By material A
It is added in dimethylformamide and stirs evenly, styrene, butyl acrylate, methacrylic acid -2- hydroxyl are added after being warming up to 85 DEG C
Ethyl ester, vinyl phosphoric acid dimethyl ester and azodiisobutyronitrile, insulation reaction 4h, it is different to be added naphthalene two after reaction after mixing evenly
Cyanate stirs 100min, obtains the modified filler after dry;
In the preparation process of modified filler, carbon black, nanometer calcium carbonate, iron oxide, carbon nanotube, hydrotalcite, silane are even
The weight ratio for joining agent KH570 is 15:9:2:5:3:12;Material A, styrene, butyl acrylate, 2-hydroxyethyl methacry-late,
Vinyl phosphoric acid dimethyl ester, azodiisobutyronitrile, naphthalene diisocyanate weight ratio be 3:12:4:9:1:0.8:5;
The foaming agent is azodiisobutyronitrile;
The silane coupling agent is silane resin acceptor kh-550.
Embodiment 4
A kind of mobile phone foamed material proposed by the present invention, raw material includes: ethylene-vinyl acetate copolymer by weight
100 parts, 14 parts of butadiene-styrene rubber, 7 parts of ethylene propylene diene rubber, 5 parts of polyformaldehyde, 9 parts of polyethylene, 5 parts of filler, 2.7 parts of lignin, hair
1.3 parts of infusion, 1 part of zinc oxide, 1.2 parts of stearic acid, 0.45 part of benzoyl peroxide, 0.16 part of tetramethylthiuram monosulfide,
0.21 part of sulphur, 0.13 part of Triallyl isocyanurate, 1.6 parts of paraffin, 0.2 part of glycerol, 0.5 part of silane coupling agent;
Wherein, in ethylene-vinyl acetate copolymer, the mass fraction of vinyl acetate is 18wt%;
In butadiene-styrene rubber, the mass fraction of styrene is 25wt%;
The filler is modified filler;The modified filler is prepared according to following technique: by carbon black, nano-calcium carbonate
Calcium, iron oxide, carbon nanotube, hydrotalcite are added in ethyl alcohol, and adjusting pH value after mixing evenly is 4, and silane coupling agent is added
KH570 is warming up to 48 DEG C of reaction 22h after mixing evenly, is filtered, washed after reaction, is dried to obtain material A;By material A
It is added in dimethylformamide and stirs evenly, styrene, butyl acrylate, methacrylic acid -2- hydroxyl are added after being warming up to 70 DEG C
Ethyl ester, vinyl phosphoric acid dimethyl ester and azodiisobutyronitrile, insulation reaction 5h, it is different to be added naphthalene two after reaction after mixing evenly
Cyanate stirs 50min, obtains the modified filler after dry;
In the preparation process of modified filler, carbon black, nanometer calcium carbonate, iron oxide, carbon nanotube, hydrotalcite, silane are even
The weight ratio for joining agent KH570 is 21:3:10:1:14:5;Material A, styrene, butyl acrylate, methacrylic acid -2- hydroxyl second
Ester, vinyl phosphoric acid dimethyl ester, azodiisobutyronitrile, naphthalene diisocyanate weight ratio be 9:5:8:3:5:0.3:16;
The foaming agent is azodicarbonamide;
The silane coupling agent is silane coupling agent KH-560.
Embodiment 5
A kind of mobile phone foamed material proposed by the present invention, raw material includes: ethylene-vinyl acetate copolymer by weight
100 parts, 14 parts of butadiene-styrene rubber, 6 parts of ethylene propylene diene rubber, 9 parts of polyformaldehyde, 7 parts of polyethylene, 5 parts of filler, 2 parts of lignin, foaming
1.6 parts of agent, 1 part of zinc oxide, 1.2 parts of stearic acid, 0.38 part of benzoyl peroxide, 0.3 part of tetramethylthiuram monosulfide, sulphur
0.13 part, 0.14 part of Triallyl isocyanurate, 0.9 part of paraffin, 0.6 part of glycerol, 1 part of silane coupling agent;
Wherein, in ethylene-vinyl acetate copolymer, the mass fraction of vinyl acetate is 19wt%;
In butadiene-styrene rubber, the mass fraction of styrene is 24.6wt%;
The modified filler is prepared according to following technique: by weight by 18 parts of carbon blacks, 7 parts of nanometer calcium carbonates, 6 parts
Iron oxide, 3 parts of carbon nanotubes, 9 parts of hydrotalcites are added in 50 parts of ethyl alcohol, and adjusting pH value after mixing evenly is 3.5, and 10 parts of silicon are added
Alkane coupling agent KH570 is warming up to 55 DEG C of reaction 20h after mixing evenly, is filtered, washed after reaction, is dried to obtain material
A;8 parts of material As are added in 50 parts of dimethylformamides by weight and be stirred evenly, be added after being warming up to 75 DEG C 6 parts of styrene,
5 parts of butyl acrylates, 7 parts of 2-hydroxyethyl methacry-lates, 3 parts of vinyl phosphoric acid dimethyl esters and 0.5 part of azodiisobutyronitrile,
12 parts of naphthalene diisocyanates are added in insulation reaction 4.5h after mixing evenly after reaction, stir 80min, obtain institute after dry
State modified filler;
The foaming agent is azodicarbonamide, azodiisobutyronitrile, dinitrosopentamethylene tetramine, 4,4 '-oxos
The mixture of double benzene sulfonyl hydrazides, sodium bicarbonate, and azodicarbonamide, azodiisobutyronitrile, dinitrosopentamethylene tetramine,
4,4 '-oxobenzenesulfonyl hydrazide, the weight ratio of sodium bicarbonate are 4:3:6:2:1;
The silane coupling agent is silane resin acceptor kh-550, silane coupling agent KH-560, Silane coupling reagent KH-570
Mixture, and the weight ratio of silane resin acceptor kh-550, silane coupling agent KH-560, Silane coupling reagent KH-570 is 3:5:2.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (9)
1. a kind of mobile phone foamed material, which is characterized in that its raw material includes: ethylene-vinyl acetate copolymer 100 by weight
It is part, 8-20 parts of butadiene-styrene rubber, 2-8 parts of ethylene propylene diene rubber, 3-12 parts of polyformaldehyde, 2-10 parts of polyethylene, 2-10 parts of filler, wooden
1-3 parts plain, 1-2 parts of foaming agent, 0.2-1.1 parts of zinc oxide, 1-1.5 parts of stearic acid, 0.2-0.5 parts of benzoyl peroxide, a sulphur
Change tetra methylthiuram 0.1-0.35 parts, 0.05-0.28 parts of sulphur, 0.1-0.2 parts of Triallyl isocyanurate, paraffin 0.1-
2 parts, 0.1-1 parts of glycerol, 0.2-1.3 parts of silane coupling agent.
2. mobile phone foamed material according to claim 1, which is characterized in that in ethylene-vinyl acetate copolymer, acetic acid
The mass fraction of ethylene is 18-20wt%.
3. mobile phone foamed material according to claim 1 or claim 2, which is characterized in that in butadiene-styrene rubber, the quality of styrene
Score is 24-25wt%.
4. mobile phone foamed material described in any one of -3 according to claim 1, which is characterized in that the filler is that modification is filled out
Material;The modified filler is prepared according to following technique: by carbon black, nanometer calcium carbonate, iron oxide, carbon nanotube, hydrotalcite
It is added in ethyl alcohol, adjusting pH value after mixing evenly is 3-4, and silane coupling agent KH570 is added, is warming up to 48-58 after mixing evenly
DEG C reaction 15-22h, be filtered, washed after reaction, be dried to obtain material A;Material A is added in dimethylformamide and is stirred
It mixes uniformly, styrene, butyl acrylate, 2-hydroxyethyl methacry-late, vinyl phosphoric acid two is added after being warming up to 70-85 DEG C
Methyl esters and azodiisobutyronitrile, insulation reaction 4-5h, is added naphthalene diisocyanate after reaction after mixing evenly, stirs 50-
100min obtains the modified filler after dry.
5. mobile phone foamed material according to claim 4, which is characterized in that in the preparation process of modified filler, carbon black,
Nanometer calcium carbonate, iron oxide, carbon nanotube, hydrotalcite, silane coupling agent KH570 weight ratio be 15-21:3-9:2-10:1-
5:3-14:5-12.
6. mobile phone foamed material according to claim 4 or 5, which is characterized in that in the preparation process of modified filler, object
Expect A, styrene, butyl acrylate, 2-hydroxyethyl methacry-late, vinyl phosphoric acid dimethyl ester, azodiisobutyronitrile, naphthalene two
The weight ratio of isocyanates is 3-9:5-12:4-8:3-9:1-5:0.3-0.8:5-16.
7. according to mobile phone foamed material described in any one of claim 4-5, which is characterized in that the modified filler according to
Prepared by lower technique: by weight by 18 parts of carbon blacks, 7 parts of nanometer calcium carbonates, 6 parts of iron oxide, 3 parts of carbon nanotubes, 9 parts of neatlys
Stone is added in 50 parts of ethyl alcohol, and adjusting pH value after mixing evenly is 3.5, and 10 parts of silane coupling agent KH570 are added, rise after mixing evenly
Temperature is filtered, washed after reaction to 55 DEG C of reaction 20h, is dried to obtain material A;8 parts of material As are added 50 by weight
It is stirred evenly in part dimethylformamide, 6 parts of styrene, 5 parts of butyl acrylates, 7 parts of metering systems is added after being warming up to 75 DEG C
Acid -2- hydroxyl ethyl ester, 3 parts of vinyl phosphoric acid dimethyl esters and 0.5 part of azodiisobutyronitrile, insulation reaction 4.5h after mixing evenly, instead
12 parts of naphthalene diisocyanates are added after answering, stirs 80min, obtains the modified filler after dry.
8. mobile phone foamed material described in any one of -7 according to claim 1, which is characterized in that the foaming agent is azo two
One of formamide, azodiisobutyronitrile, dinitrosopentamethylene tetramine, 4,4 '-oxobenzenesulfonyl hydrazide, sodium bicarbonate
Or a variety of mixture.
9. mobile phone foamed material described in any one of -8 according to claim 1, which is characterized in that the silane coupling agent is silicon
The mixture of one or more of alkane coupling agent KH-550, silane coupling agent KH-560, Silane coupling reagent KH-570.