CN109485242A - A kind of quartz ripple pearl rotary polishing apparatus and polishing method - Google Patents
A kind of quartz ripple pearl rotary polishing apparatus and polishing method Download PDFInfo
- Publication number
- CN109485242A CN109485242A CN201811366554.8A CN201811366554A CN109485242A CN 109485242 A CN109485242 A CN 109485242A CN 201811366554 A CN201811366554 A CN 201811366554A CN 109485242 A CN109485242 A CN 109485242A
- Authority
- CN
- China
- Prior art keywords
- ripple pearl
- quartzy
- quartz
- polishing
- ripple
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of quartzy ripple pearl rotary polishing apparatus, including workbench, workbench, which is equipped with, carries out preheating resistance furnace and turntable motor-driven to quartzy bead, and turntable is equipped with the quartz socket tube for carry quartz ripple pearl after preheating；Described device further includes for driving the hand-held polisher that quartzy ripple pearl rotary course is polished in quartz socket tube in turntable.Compared with prior art, the quartz ripple pearl rotary polishing apparatus and polishing method, quartzy ripple pearl in quartz socket tube is driven to be rotated using turntable, hand-held polisher carries out rotation polishing to quartzy ripple pearl, thus is avoided that the problems such as cracking, polishing is uneven, Internal Hole Deformation, edge form wedge angle occurs during the polishing process in quartzy ripple pearl.
Description
Technical field
The present invention relates to short arc mercury xenon lamps to fabricate field, especially a kind of quartzy ripple pearl rotary polishing apparatus and polishing
Method.
Background technique
Mercury shot arc lamp generates the point light source that mercury vapour obtains visible light, high brightness, high photosynthetic efficiency, longevity when utilizing mercury discharge
Face and as comparatively ideal special source, mainly apply to exposure device.But during lamp processed, it is found that bead is in life
It is easy to appear cracking during producing, has seriously affected the production of fluorescent tube.Therefore, relatively stable reliable bead polishing process is researched and developed
It is the main target of research staff.
Summary of the invention
In view of the above-mentioned problems, being rotated the present invention provides a kind of quartzy ripple pearl rotary polishing apparatus to quartzy ripple pearl
The problems such as polishing avoids quartzy ripple pearl from occurring cracking during the polishing process, polishes uneven, Internal Hole Deformation, and edge forms wedge angle.
The technical solution adopted by the present invention are as follows:
A kind of quartz ripple pearl rotary polishing apparatus, including workbench, workbench, which is equipped with, carries out preheating electricity to quartzy bead
Hinder furnace and turntable motor-driven, turntable is equipped with the quartz socket tube for carry quartz ripple pearl after preheating；It is described
Device further includes for driving the hand-held polisher that quartzy ripple pearl rotary course is polished in quartz socket tube in turntable.
Preferably, the hand-held polisher is polishing firelock, and the polisher is connected with for hydrogen-oxygen pipeline.
It is highly preferred that being equipped in the workbench for controlling the control valve for hydrogen-oxygen.
Preferably, the height of the quartz socket tube is lower than the height of quartzy ripple pearl.
Preferably, the height of the quartz socket tube is the height 1/3 of quartzy ripple pearl.
The present invention also provides a kind of polishings polished using above-mentioned quartzy ripple pearl rotary polishing apparatus to quartzy ripple pearl
Method, which comprises the following steps:
1) quartzy ripple pearl is placed in resistance furnace and is preheated, be preheated to 600 ~ 1000 DEG C；
2) by the quartz socket tube on the quartzy ripple pearl merging turntable after preheating, motor driven turntable is rotated；
3) control valve is opened, ripple pearl quartzy in the quartz socket tube of rotation is polished using hand-held polisher；
4) the quartzy ripple pearl after the completion of polishing is taken out, and progress is air-cooled, and quartzy ripple pearl is air-cooled to room temperature；
5) the quartzy ripple pearl after air-cooled is made annealing treatment；
6) the quartzy ripple pearl after making annealing treatment checks stress using stress gauge.
Preferably, the preset temperature of resistance furnace is 600 ~ 1000 DEG C in step 1), and soaking time is 8 ~ 12 minutes.
Preferably, hand-held polisher overturns quartzy ripple pearl in quartzy ripple pearl polishing process repeatedly in step 3), it is ensured that
Each face of quartzy ripple pearl is polished.
Preferably, polisher is 10 ~ 15mm with a distance from quartzy ripple pearl in step 3) polishing process.
Preferably, it is made annealing treatment in step 5) using annealing furnace.
Compared with prior art, the beneficial effects of the present invention are: the present invention to provide a kind of quartzy ripple pearl rotation polishing dress
It sets and polishing method, drives quartzy ripple pearl in quartz socket tube to be rotated using turntable, hand-held polisher is to quartzy ripple pearl
Rotation polishing is carried out, thus is avoided that quartzy ripple pearl occurs cracking during the polishing process, polishes uneven, Internal Hole Deformation, edge shape
The problems such as being pointed at.
Detailed description of the invention
Fig. 1, for a kind of schematic diagram of quartzy ripple pearl rotary polishing apparatus provided by the invention；
Fig. 2 is the temperature made annealing treatment in a kind of quartzy ripple pearl rotary polishing apparatus provided by the invention using annealing furnace
Curve graph.
Specific embodiment
Preferred embodiment provided by the invention is illustrated with reference to the accompanying drawings.
Fig. 1, for a kind of preferred embodiment of quartzy ripple pearl rotary polishing apparatus provided by the invention.As shown in Figure 1, should
Quartzy ripple pearl rotary polishing apparatus, including workbench 10, workbench 10, which is equipped with, carries out preheating resistance to quartzy bead 100
Furnace 20 and the turntable 40 driven by motor 30, turntable 40 be equipped with for carry preheating after quartz ripple pearl quartz socket tube
50；Described device further includes hand-held for driving in quartz socket tube quartzy 100 rotary course of ripple pearl to be polished in turntable
Formula polisher 60 drives quartzy ripple pearl in quartz socket tube to be rotated, 60 pairs of hand-held polisher quartzy waves using turntable 40
Pearl carries out rotation polishing, thus is avoided that quartzy ripple pearl occurs cracking during the polishing process, polishes uneven, Internal Hole Deformation, edge
The problems such as forming wedge angle.The turntable 40 is rotation polishing charcoal mould.
The quartz ripple pearl 100 has inner hole.The height of the quartz socket tube 50 is lower than the height of quartzy ripple pearl 100, in this way
Quartzy ripple pearl exposes the top of the quartz socket tube 50.As an implementation, the height of the quartz socket tube 50 is quartzy wave
The height 1/3 of pearl 100 first polishes the upper surface of quartzy ripple pearl when being polished, and then polishes inner hole, again
Outer edge is polished, quartzy bead outer surface is finally from top to bottom polished；Quartzy ripple pearl 100 is overturn again, repeats above-mentioned throwing again
Photoreduction process is polished, it is ensured that each face of quartzy ripple pearl can be polished.
The hand-held polisher 60 is polishing firelock, and the polisher is connected with for hydrogen-oxygen pipeline, passes through the hydrogen-oxygen that burns
It is polished；It is equipped in the workbench 10 for controlling the control valve 11 for hydrogen-oxygen, opens control valve 11 when in use,
By being hand-held polisher 60 for oxyhydrogen combustion for hydrogen-oxygen pipeline, hydrogen-oxygen fire is adjusted, so that flame is reached polishing and requires (pipeline hydrogen
Atmospheric pressure is 0.3MPa, and oxygen pipeline pressure is 0.2MPa).
The present invention also provides a kind of polishings polished using above-mentioned quartzy ripple pearl rotary polishing apparatus to quartzy ripple pearl
Method, specifically includes the following steps:
1) quartzy ripple pearl 100 is placed in resistance furnace 20 and is preheated, be preheated to 600 ~ 1000 DEG C；
2) by the quartz socket tube 50 on the quartzy ripple pearl merging turntable 40 after preheating, motor 30 drives 40 turns of turntable
It is dynamic；
3) control valve 11 is opened, quartzy ripple pearl polishes in the quartz socket tube 50 rotated using 60 Duis of hand-held polisher；
4) the quartzy ripple pearl after the completion of polishing is taken out, and progress is air-cooled, and quartzy ripple pearl is air-cooled to room temperature；
5) the quartzy ripple pearl after air-cooled is made annealing treatment；
6) the quartzy ripple pearl after making annealing treatment checks stress using stress gauge.
The preset temperature of resistance furnace is 600 ~ 1000 DEG C in step 1), and soaking time is 8 ~ 12 minutes.As a kind of preferred
Scheme, the preset temperature of resistance furnace are 850 DEG C, quartzy ripple pearl are preheated to 850 DEG C, soaking time is 10 minutes.The resistance
Furnace is preferably chamber type electric resistance furnace.
Preheating quartz ripple pearl is placed on before quartz socket tube 50 in step 2, and quartz socket tube 50 is first placed in turntable
40 centre opens motor, revolving speed is adjusted to 200r/min, observes the rotational case of quartz socket tube, it is ensured that at the center of rotation.
Preferably, quartzy ripple pearl, example are overturn repeatedly in 60 pairs of hand-held polisher quartzy ripple pearl polishing process in step 3)
If first polished to the upper surface of quartzy ripple pearl, inner hole is then polished, outer edge is polished again, finally from top to bottom polishes
Quartzy bead outer surface；Quartzy ripple pearl 100 is overturn again, is repeated above-mentioned polishing process again and is polished, it is ensured that quartzy ripple pearl
Each face can be polished.Polisher is 10 ~ 15mm with a distance from quartzy ripple pearl in step 3) polishing process.
In step 4) by after the completion of polishing quartzy ripple pearl take out, can be placed on quartz boat carry out it is air-cooled, and wait under
One quartzy ripple pearl is polished.Quartzy ripple pearl after polishing at normal temperature, is air-cooled to 50 DEG C, air cooling time is 30 minutes.
It is made annealing treatment in step 5) using annealing furnace, annealing furnace temperature curve is as shown in Figure 2.In all quartzy ripple pearls
After the completion of polishing and being air-cooled, all quartzy ripple pearls are put into quartz curette, then the quartz curette is put into annealing furnace and is moved back
Fire processing.
In step 6) on inspection, have abnormal need to anneal again.
In conclusion technical solution of the present invention can sufficiently effective realization foregoing invention purpose, and knot of the invention
Structure and the principle of work and power have all adequately been verified in embodiment, can reach expected effect and purpose, without departing substantially from this
Under the premise of the principle and essence of invention, various changes or modifications can be made to the embodiment of invention.Therefore, the present invention includes
All are previously mentioned all replacement contents in range in patent claim, any to be made in scope of the present invention patent
Equivalence changes, all category this case application the scope of the patents within.
Claims (10)
1. a kind of quartz ripple pearl rotary polishing apparatus, which is characterized in that including workbench, workbench be equipped with to quartzy bead into
Row preheating resistance furnace and turntable motor-driven, turntable be equipped with for carry preheating after quartz ripple pearl stone
English casing；Described device further includes hand-held for driving in quartz socket tube quartzy ripple pearl rotary course to be polished in turntable
Formula polisher.
2. quartz ripple pearl rotary polishing apparatus according to claim 1, it is characterised in that: the hand-held polisher is to throw
Flare up rifle, the polisher are connected with for hydrogen-oxygen pipeline.
3. quartz ripple pearl rotary polishing apparatus according to claim 2, it is characterised in that: be equipped with and be used in the workbench
Control the control valve for hydrogen-oxygen.
4. quartz ripple pearl rotary polishing apparatus according to claim 1, it is characterised in that: the height of the quartz socket tube is low
In the height of quartzy ripple pearl.
5. quartz ripple pearl rotary polishing apparatus according to claim 4, it is characterised in that: the height of the quartz socket tube is
The height 1/3 of quartzy ripple pearl.
Using any quartzy ripple pearl rotary polishing apparatus of claim 1 to 5 quartzy ripple pearl is polished 6. a kind of
Quartzy ripple pearl polishing method, which comprises the following steps:
1) quartzy ripple pearl is placed in resistance furnace and is preheated, be preheated to 600 ~ 1000 DEG C；
2) by the quartz socket tube on the quartzy ripple pearl merging turntable after preheating, motor driven turntable is rotated；
3) control valve is opened, ripple pearl quartzy in the quartz socket tube of rotation is polished using hand-held polisher；
4) the quartzy ripple pearl after the completion of polishing is taken out, and carries out being air-cooled to room temperature；
5) the quartzy ripple pearl after air-cooled is made annealing treatment；
6) the quartzy ripple pearl after making annealing treatment checks stress using stress gauge.
7. quartz ripple pearl polishing method according to claim 6, it is characterised in that: the preset temperature of resistance furnace in step 1)
It is 600 ~ 1000 DEG C, soaking time is 8 ~ 12 minutes.
8. quartz ripple pearl polishing method according to claim 6, it is characterised in that: hand-held polisher is to stone in step 3)
In English ripple pearl polishing process, quartzy ripple pearl is overturn repeatedly, it is ensured that each face of quartzy ripple pearl is polished.
9. quartz ripple pearl polishing method according to claim 6, it is characterised in that: in step 3) polishing process polisher from
Quartzy ripple pearl distance is 10 ~ 15mm.
10. quartz ripple pearl polishing method according to claim 6, it is characterised in that: carried out in step 5) using annealing furnace
Annealing.