CN109485089A - A kind of low angle dependence blue cadmium sulfide schemochrome film and preparation method thereof - Google Patents
A kind of low angle dependence blue cadmium sulfide schemochrome film and preparation method thereof Download PDFInfo
- Publication number
- CN109485089A CN109485089A CN201811408875.XA CN201811408875A CN109485089A CN 109485089 A CN109485089 A CN 109485089A CN 201811408875 A CN201811408875 A CN 201811408875A CN 109485089 A CN109485089 A CN 109485089A
- Authority
- CN
- China
- Prior art keywords
- cadmium sulfide
- preparation
- schemochrome
- low angle
- angle dependence
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of low angle dependence blue cadmium sulfide schemochrome film and preparation method thereof, comprising the following steps: step 1, prepares the cadmium source that obtains, sulphur source and mixing based sols respectively；Step 2, sulphur source and cadmium source are added in mixing based sols, seed solution is made in pyroreaction；Step 3, after step 2 has been reacted, gained seed solution is placed in 0-10 DEG C of ice water, is rapidly cooled to room temperature, and centrifugation retains the supernatant of bright orange clear；Step 4, four nitric hydrate cadmiums and thiocarbamide are added into step 3 gained supernatant, reacts and the emulsion containing cadmium sulfide microballoon is made, ultrasonic disperse obtains the ethanol solution of monodisperse CdS microballoon in alcohol solvent after washing；Step 5, plated film is carried out using vertical sedimentation method.The cadmium sulfide schemochrome film that the present invention obtains, structure isotropism, in colour-stable, not fugitive color, dependence of angle is weak, and color will not change with the variation of viewing angle.
Description
Technical field
The invention belongs to schemochrome technical field of material, and in particular to a kind of low angle dependence blue cadmium sulfide knot
Structure color film and preparation method thereof.
Background technique
Photonic crystal (PC) is a kind of novel optical fine structure material that dielectric constant changes with space periodicity, be exactly it will
The dielectric material of differing dielectric constant has the refractive index periodic of optical wavelength magnitude in one-dimensional, two-dimentional or three-dimensional space composition
The structural material of variation.Schemochrome is a kind of physics colour generation, has bright-colored, will never fade, environmental-friendly, short preparation period
The advantages that.Schemochrome because it has the characteristics that high brightness, high saturation, never fades, iris phenomenon, polarization effect, and these
It is all the concern not available for common pigments color or pigmentary color, therefore increasingly by scientific circles and engineering circles.
The orderly self-assembly method for passing through colloid micro ball in recent years, is capable of forming photonic crystal of opals structure, last light
Line have the effects that periodic structure photon crystal surface formed by it is dry penetrate, diffraction, scattering, to generate bright and colourful
Schemochrome, but because having rainbow effect, i.e. the color observed of different directions is different, greatly limits schemochrome flat
Plate shows, the application of printed medium and optical device etc..
In general, the photonic crystal powder state of preparation generally shows white.It is only brilliant by being assembled into orderly photon
Schemochrome (CN108059829A, CN107987216A) can be just showed after body thin film.Adding micro black pigment can mention
High color saturation, and can be effectively reduced schemochrome to the dependence of angle, reach as viewing angle changes schemochrome
The effect (CN105174302B, 105175015 A, 103788770A) remained unchanged, the wherein effect of carbon black or melanin
It is there can be stronger absorption in visible light wave range, so that incoherent scattering is reduced, so that schemochrome film has in short distance
Also higher color saturation, while the knot of this shortrange order, longrange disorder can be shown in the state of sequence, longrange disorder
Structure has low angle dependence, i.e., with the variation of viewing angle, color is basically unchanged, Neng Gouying because of isotropism
For show, print etc..
But powder is mixed into film with a certain amount of atrament, technique is more complex, and the ultrasound for generally requiring the long period is mixed
It closes；And opal structural is very high to film coating environment requirement, vulnerable to external environmental interference, the melanin of nanostructure will cause film
The defect of structure, and faint environmental fluctuating can all have a great impact to the quality of film, therefore be difficult to be widely used.
Meanwhile nanoscale carbon black surface with higher can, therefore there is difficult dispersion, easy to reunite, and be difficult in most solution molten
The disadvantages of solution, and organic black dyes needs to carry out the technical process such as colorant match, colour mixture, process is complicated and the Organic Black for preparing
Color dyestuff is unstable.In recent years, semiconductor sulfide (such as cadmium sulfide) material is because of its higher color saturation, it is main to make
For the use of single yellow colorant, furthermore cadmium sulfide is mainly used as pigment.Cadmium sulfide and cadmium selenide are for manufacturing photo resistance, the sun
Energy battery, photochemical catalyst etc..
So far, there are no documents to preparing shot-range ordered structure and high saturation schemochrome material using cadmium sulfide
Preparation carried out report.
Summary of the invention
Aiming at the problems existing in the prior art, it is thin to provide a kind of low angle dependence blue cadmium sulfide schemochrome by the present invention
Film and preparation method thereof successfully prepares a kind of photon crystal structure that low angle relies under the action of undoping melanin
Color film.
The present invention is to be achieved through the following technical solutions:
A kind of preparation method of low angle dependence blue cadmium sulfide schemochrome film, comprising the following steps:
Step 1, four nitric hydrate cadmiums are completely dissolved in diethylene glycol, obtain cadmium source；Thiocarbamide is completely dissolved in two
In ethylene glycol, sulphur source is obtained；Polyvinylpyrrolidone is dissolved in diethylene glycol, mixing based sols are made；
Step 2, sulphur source and cadmium source are added in mixing based sols, make the ratio of four nitric hydrate cadmiums and diethylene glycol
The ratio of (0.045-0.09): 60mL, thiocarbamide and diethylene glycol be (0.0135-0.03) g:60mL, polyvinylpyrrolidone with
The ratio of diethylene glycol is (0.6-1.0) g:60mL, and seed solution is made in pyroreaction；
Step 3, after step 2 has been reacted, gained seed solution is placed in 0-10 DEG C of ice water, is rapidly cooled to room temperature, centrifugation
Retain the supernatant of bright orange clear；
Step 4, four nitric hydrate cadmiums and thiocarbamide are added into step 3 gained supernatant, makes four nitric hydrate cadmiums and diethyl
The ratio of glycol is (3.644-3.944) g:60mL, and the ratio of thiocarbamide and diethylene glycol is (0.900-0.980) g:60mL；?
45-90min is reacted at 55-65 DEG C, is then heated to 160-170 DEG C of reaction 40-50 time, the cream containing cadmium sulfide microballoon is made
Turbid, ultrasonic disperse obtains the ethanol solution of monodisperse CdS microballoon in alcohol solvent after washing；
Step 5, plated film is carried out using vertical sedimentation method, obtains cadmium sulfide schemochrome film.
Preferably, in step 1, the preparation for mixing based sols is specifically: polyvinylpyrrolidone is added in diethylene glycol,
It is heated to 50-70 DEG C, magnetic agitation 1-4h.
Preferably, in step 2, pyroreaction is in 160-200 DEG C of reaction 5-6min.
Preferably, in step 3, the revolving speed of centrifugation is 7000-10000r/min, time 20-30min.
Preferably, in step 4, washing is to use ethanol washing twice, and washing is twice.
Preferably, in step 5, carrying out plated film using vertical sedimentation method is specifically: to the ethyl alcohol of monodisperse CdS microballoon
It is inserted into sheet glass in solution, is then dried in vacuo, cadmium sulfide schemochrome film is made.
Preferably, the sheet glass of use is that the sheet glass above for 24 hours is impregnated through hydrogen peroxide.
Preferably, in step 5, vacuum drying temperature is 40-50 DEG C, vacuum degree 0.05-0.09MPa, and drying time is
48-96h。
The cadmium sulfide microballoon that the preparation method is prepared.
The low angle dependence blue cadmium sulfide schemochrome film that the preparation method is prepared.
Compared with prior art, the invention has the following beneficial technical effects:
Preparation method of the present invention first uses the two step seed laws, prepares the cadmium sulfide microsphere nano of uniform particle diameter
Then particle uses vertical sedimentation method plated film, cadmium sulfide schemochrome film is prepared.Since cadmium sulfide microballoon is than great, no
Perfect face-centered cubic (FCC) arrangement is easily formed, shows shortrange order, " the defect state knot of longrange disorder on Microscopic
Structure ".This cadmium sulfide schemochrome film, structure isotropism, in colour-stable, not fugitive color, dependence of angle is weak, and color will not
Change with the variation of viewing angle.Principle is explained as follows.
Ideally, the forbidden photon band of photonic crystal and schemochrome meet Bragg equation (Bragg law):
In formula (1), m is diffraction progression, λpeakIt is the wavelength of reflection peak, dhklFor lattice of the crystal on the direction (hkl)
Spacing, it is related with the partial size of polymer microballoon, neffIt is the effective refractive index of lattice；θ is the angle of incident light.
As four nitric hydrate cadmiums and thiocarbamide reactant concentration increase, the increase of duration is reacted, cadmium sulfide microspherulite diameter increases
Greatly, red shift occurs for the reflection peak of spraying gained film, and theoretically, schemochrome can change from purple to red.
In general, (111) crystal face of photonic crystal is parallel to the surface of glass substrate.In spectral measurement, Wo Menshe
Incident light is determined perpendicular to (111) crystal face, it may be assumed that θ=0, m=1.For face-centred cubic structure, spacing of lattice can be by following public affairs
Formula calculates:
In formula (2): DsphereFor the diameter of cadmium sulfide microballoon.
For close-packed structure, effective refractive index can be calculated with following formula:
neff=[n2 spheref+n2 air(1-f)]1/2 (3)
In formula (3): nsphereAnd nairThe respectively refractive index of cadmium sulfide and air, f are the filling rate of cadmium sulfide.I.e.
nsphere=2.5, nair=1, f=0.74.By taking the cadmium sulfide microsphere diameter of embodiment 1 as an example, institute is calculated according to Bragg equation
The theoretical reflectance spike for obtaining cadmium sulfide schemochrome film is long are as follows: 764.62nm tests the wavelength measured are as follows: 485nm.It is found that anti-
Penetrate between the long calculated value of spike and actual measured value that there are biggish differences.This difference can be by analyzing cadmium sulfide
Microstructure in the fault of construction of photonic crystal explain.Since amorphous photonic crystal material is with unique overlapped
Photonic bandgap, the lowest-order energy gap of photonic crystal are to be determined completely by the short program of spatial dielectric structure.Therefore, structure is reduced
On order, repeatability, rainbow effect can be reduced.
Preparation manipulation method of the present invention is simple, without adding pigment or carbon black, it will be able to obtain high saturation non-angular
Dependence cadmium sulfide schemochrome film, repeatability is strong, low to extraneous environmental requirement, not only solves chemical organic compounds pigment and easily takes off
The technical problem of color, while it is stringent to substrate requirement to solve opal structural, the skills problem such as film coating environment harshness.Work of the present invention
Skill operating process is simple and easy, is suitable for constructing not changeable colors along with angle schemochrome colorant on various material surface, has wide answer
Use prospect.The present invention can expand the type of orderly photonic crystal structure color film material.
Further, plated film is carried out under vacuum conditions, is volatilized with facilitating ethanol solution fast and stable, to overcome vulcanization
The biggish vertical settlement effects of cadmium microballoon.
The cadmium sulfide microballoon good sphericity prepared through the method for the present invention, uniform particle diameter, key are the method using centrifugation,
Retain the supernatant of bright orange clear, because cadmium sulfide seed particle size is smaller in the supernatant retained, size is relatively uniform, should
Step will give up the seed of the greater particle size generated due to reunion, ensure that seed particle size is uniform, it is made to meet photonic crystal knot
The assembling condition of structure color.Red cadmium sulfide schemochrome film non-angular dependence obtained, display material, sensing, catalysis with
And various types of materials surface coloring field has a wide range of applications.
Detailed description of the invention
Fig. 1 is the X-ray diffractogram of the resulting cadmium sulfide microballoon of embodiment 1；
Fig. 2 is the scanning electron microscope (SEM) photograph of the resulting cadmium sulfide microballoon of embodiment 1；
Fig. 3 is the optical photograph of the resulting schemochrome film fragments of embodiment 1；
Fig. 4 is the optical photograph of the resulting schemochrome film of embodiment 1
Fig. 5 is the reflectance spectrum figure of 1 resulting structures color film of embodiment.
Specific embodiment
Below with reference to specific embodiment, the present invention is described in further detail, it is described be explanation of the invention and
It is not to limit.
The preparation method of low angle dependence blue cadmium sulfide schemochrome film of the present invention, comprising the following steps:
1) in the ratio of (20-30) g:80mL, four nitric hydrate cadmiums is completely dissolved in diethylene glycol, stands and matches to obtain cadmium
Source；In thiocarbamide: thiocarbamide is completely dissolved in diethylene glycol, obtains homogeneous solution by diethylene glycol=(6-10) g:80mL ratio
As sulphur source；
2) in the ratio of (0.6-1.0) g:60mL, polyvinylpyrrolidone is dissolved in diethylene glycol, heating magnetic force stirs
It mixes, be uniformly mixed based sols；Sulphur source and cadmium source in step 1), reaction a period of time is successively added in heating；Sulphur source and mixed
The ratio for closing based sols is (180-240) μ L:60mL, and cadmium source is (180-240) μ L:60mL with the ratio for mixing based sols.
3) it after step 2) has been reacted, is placed in rapid cooling in 0-10 DEG C of ice water and post-processes, post-processing refers specifically to be cooled to room
Temperature, centrifugation retain the supernatant of bright orange clear；
4) four nitric hydrate cadmiums and thiocarbamide is added in supernatant obtained by step 3), makes four nitric hydrate cadmiums and diethylene glycol
Ratio is (3.644-3.944) g:60mL, and the ratio of thiocarbamide and diethylene glycol is (0.900-0.980) g:60mL, in water-bath 55-
45-90min is reacted at 65 DEG C, 160-170 DEG C of reaction 40-50min is then heated under magnetic agitation 400r/min, is made and is contained
The emulsion of cadmium sulfide microballoon finally obtains the ethanol solution of monodisperse CdS microballoon using washing and ultrasonic disperse；
5) plated film is carried out using vertical sedimentation method: is inserted through hydrogen oxide into the ethanol solution of monodisperse CdS microballoon
The sheet glass above for 24 hours is impregnated, dry, standing plated film, obtained cadmium sulfide schemochrome film are subsequently placed under vacuum condition.
In step 1), sufficiently dissolution is using magnetic stirrer 6-8h.
In step 2), the temperature for heating magnetic agitation is 50-70 DEG C, mixing time 1-4h, revolving speed 500r/min.It is described
Heating refer to and be warming up to 160-200 DEG C, react 5-6min after sulphur source and cadmium source is added.
In step 3), revolving speed is 7000-10000r/min, time 20-30min in centrifugally operated.
In step 4), the washing refers to that twice of alcohol is washed with ultrasonic disperse and is with twice of washing, each ultrasonic disperse time
10-30min。
In step 5), vacuum drying temperature is 40-50 DEG C, vacuum degree 0.05-0.09MPa, dry 48-96h.
The present invention is uniform using the cadmium sulfide microspherulite diameter of above-mentioned seed law preparation, the indigo plant prepared using the cadmium sulfide microballoon
Color cadmium sulfide schemochrome film non-angular dependence.
Embodiment 1
A kind of preparation method of low angle dependence blue cadmium sulfide schemochrome film, comprising the following steps:
1) in the ratio of 20g:80mL, four nitric hydrate cadmiums stirring 6h is completely dissolved in 80mL diethylene glycol, stands 1h
With cadmium source；In thiocarbamide: thiocarbamide is dissolved in 80mL diethylene glycol by diethylene glycol=6g:80mL ratio, and magnetic agitation 6h fills
Divide and be uniformly mixed, obtains homogeneous solution as sulphur source.
2) in the ratio of 0.6g:60mL, polyvinylpyrrolidone (PVP) is dissolved in 60mL diethylene glycol, heats magnetic force
Stirring, mixing time 2h, revolving speed 500r/min, the temperature of heating are 60 DEG C, and be uniformly mixed based sols；It is warming up to 190
DEG C, be first added the sulphur source in 180 μ L steps 1), then with the cadmium source that is added in 180 μ L steps 1).
3) after step 2) being reacted 6min, it is placed in rapid cooling in 10 DEG C of ice water, is cooled to room temperature, be centrifuged in 8000r/min
20min retains the supernatant of bright orange clear.
4) tetra- nitric hydrate cadmium of 3.644g and 0.90g thiocarbamide are added in supernatant, at 55 DEG C, water-bath 50min, magnetic
Power stirring 400r/min is heated to 160 DEG C of reaction 40min, and the emulsion containing cadmium sulfide microballoon is made, washes using twice of alcohol
It is washed with twice, the ultrasonic disperse time is 15min when washing every time, and then cadmium sulfide microballoon ultrasonic disperse in ethanol, obtains
The ethanol solution of monodisperse CdS microballoon；
5) it uses vertical sedimentation method plated film: being inserted through hydrogen oxide immersion into the ethanol solution of monodisperse CdS microballoon
Above sheet glass for 24 hours, vacuum drying stand 72h plated film, and vacuum drying temperature is 45 DEG C, vacuum degree 0.08MPa, and sulphur is made
Cadmium schemochrome film.
Embodiment 2
A kind of preparation method of low angle dependence blue cadmium sulfide schemochrome film, comprising the following steps:
1) in the ratio of 25g:80mL, four nitric hydrate cadmiums stirring 7h is completely dissolved in 80mL diethylene glycol, stands 1h
With cadmium source；In thiocarbamide: thiocarbamide is dissolved in 80mL diethylene glycol by diethylene glycol=8g:80mL ratio, and magnetic agitation 7h fills
Divide and be uniformly mixed, obtains homogeneous solution as sulphur source.
2) in the ratio of 0.8g:60mL, polyvinylpyrrolidone (PVP) is dissolved in 60mL diethylene glycol, heats magnetic force
Stirring, mixing time 1h, revolving speed 500r/min, the temperature of heating are 50 DEG C, and be uniformly mixed based sols；It is warming up to 160
DEG C, be first added the sulphur source in 200 μ L steps 1), then with the cadmium source that is added in 200 μ L steps 1).
3) after step 2) being reacted 5min, it is placed in rapid cooling in 0 DEG C of ice water, is cooled to room temperature, be centrifuged in 7000r/min
25min retains the supernatant of bright orange clear.
4) tetra- nitric hydrate cadmium of 3.788g and 0.950g thiocarbamide are added in supernatant, at 60 DEG C, water-bath 45min,
Magnetic agitation 400r/min is heated to 165 DEG C of reaction 45min, the emulsion containing cadmium sulfide microballoon is made, using twice of alcohol
It washes and is washed with twice, the ultrasonic disperse time is 10min when washing every time, and then cadmium sulfide microballoon ultrasonic disperse in ethanol, obtains
To the ethanol solution of monodisperse CdS microballoon；
5) it uses vertical sedimentation method plated film: being inserted through hydrogen oxide immersion into the ethanol solution of monodisperse CdS microballoon
Above sheet glass for 24 hours, vacuum drying stand 48h plated film, and vacuum drying temperature is 40 DEG C, vacuum degree 0.05MPa, and sulphur is made
Cadmium schemochrome film.
Embodiment 3
A kind of preparation method of low angle dependence blue cadmium sulfide schemochrome film, comprising the following steps:
1) in the ratio of 30g:80mL, four nitric hydrate cadmiums stirring 8h is completely dissolved in 80mL diethylene glycol, stands 1h
With cadmium source；In thiocarbamide: thiocarbamide is dissolved in 80mL diethylene glycol, magnetic agitation 8h by diethylene glycol=10g:80mL ratio
It is sufficiently mixed uniformly, obtains homogeneous solution as sulphur source.
2) in the ratio of 1.0g:60mL, polyvinylpyrrolidone (PVP) is dissolved in 60mL diethylene glycol, heats magnetic force
Stirring, mixing time 4h, revolving speed 500r/min, the temperature of heating are 70 DEG C, and be uniformly mixed based sols；It is warming up to 200
DEG C, be first added the sulphur source in 240 μ L steps 1), then with the cadmium source that is added in 240 μ L steps 1).
3) after step 2) being reacted 6min, it is placed in rapid cooling in 5 DEG C of ice water, is cooled to room temperature, be centrifuged in 10000r/min
30min retains the supernatant of bright orange clear.
4) tetra- nitric hydrate cadmium of 3.944g and 0.98g thiocarbamide are added in supernatant, at 65 DEG C, water-bath 90min, magnetic
Power stirring 400r/min is heated to 170 DEG C of reaction 50min, and the emulsion containing cadmium sulfide microballoon is made, washes using twice of alcohol
It is washed with twice, the ultrasonic disperse time is 30min when washing every time, and then cadmium sulfide microballoon ultrasonic disperse in ethanol, obtains
The ethanol solution of monodisperse CdS microballoon；
5) it uses vertical sedimentation method plated film: being inserted through hydrogen oxide immersion into the ethanol solution of monodisperse CdS microballoon
Above sheet glass for 24 hours, vacuum drying stand 96h plated film, and vacuum drying temperature is 50 DEG C, vacuum degree 0.09MPa, and sulphur is made
Cadmium schemochrome film.
The XRD analysis of monodisperse CdS microballoon made from embodiment 1 is as shown in Figure 1, three strongest ones' peak value is distinguished: 2 θ=
26.6 °, 44.3 ° and 52.4 °, respectively corresponding (111), (220) and (311) crystal face of CdS, it was demonstrated that CdS is cubic system, and
And other than CdS characteristic peak, no miscellaneous peak occurs, and shows that using sample prepared by this method be pure CdS, by standard drawing
CdS crystallite known to spectrum is corresponding is cube wurtzite structure.
The scanning electron microscope (SEM) photograph of monodisperse CdS microballoon made from embodiment 1 is as shown in Fig. 2, it can be seen from the figure that sulphur
Cadmium photon crystal surface is coarse, cadmium sulfide microballoon height monodisperse, uniform particle diameter, in 210 ± 20nm, and can be with from figure
Find out, monodisperse CdS microballoon soilless sticking phenomenon occurs.
Optical photograph through blue cadmium sulfide schemochrome film made from the present embodiment 1 as shown in figure 4, film fragments light
Photo is learned as shown in figure 3, being presented always experiments have shown that cadmium sulfide schemochrome film does not change with the change of observer's angle
Distinct blue.
The reflectance spectrum figure of cadmium sulfide schemochrome film made from embodiment 1 is as shown in Figure 5, it can be seen that its reflection peak exists
Blue is presented in 407-550nm.
Claims (10)
1. a kind of preparation method of low angle dependence blue cadmium sulfide schemochrome film, which comprises the following steps:
Step 1, four nitric hydrate cadmiums are completely dissolved in diethylene glycol, obtain cadmium source；Thiocarbamide is completely dissolved in diethyl two
In alcohol, sulphur source is obtained；Polyvinylpyrrolidone is dissolved in diethylene glycol, mixing based sols are made；
Step 2, sulphur source and cadmium source are added in mixing based sols, make the ratio of four nitric hydrate cadmiums and diethylene glycol
The ratio of (0.045-0.09): 60mL, thiocarbamide and diethylene glycol be (0.0135-0.03) g:60mL, polyvinylpyrrolidone with
The ratio of diethylene glycol is (0.6-1.0) g:60mL, and seed solution is made in pyroreaction；
Step 3, after step 2 has been reacted, gained seed solution is placed in 0-10 DEG C of ice water, is rapidly cooled to room temperature, and centrifugation retains
The supernatant of bright orange clear；
Step 4, four nitric hydrate cadmiums and thiocarbamide are added into step 3 gained supernatant, makes four nitric hydrate cadmiums and diethylene glycol
Ratio be (3.644-3.944) g:60mL, the ratio of thiocarbamide and diethylene glycol is (0.900-0.980) g:60mL；In 55-65
45-90min is reacted at DEG C, is then heated to 160-170 DEG C of reaction 40-50 time, and the emulsion containing cadmium sulfide microballoon is made,
Ultrasonic disperse obtains the ethanol solution of monodisperse CdS microballoon in alcohol solvent after washing；
Step 5, plated film is carried out using vertical sedimentation method, obtains cadmium sulfide schemochrome film.
2. the preparation method of low angle dependence blue cadmium sulfide schemochrome film according to claim 1, feature exist
In in step 1, the preparation for mixing based sols is specifically: polyvinylpyrrolidone being added in diethylene glycol, 50-70 is heated to
DEG C, magnetic agitation 1-4h.
3. the preparation method of low angle dependence blue cadmium sulfide schemochrome film according to claim 1, feature exist
In in step 2, pyroreaction is in 160-200 DEG C of reaction 5-6min.
4. the preparation method of low angle dependence blue cadmium sulfide schemochrome film according to claim 1, feature exist
In in step 3, the revolving speed of centrifugation is 7000-10000r/min, time 20-30min.
5. the preparation method of low angle dependence blue cadmium sulfide schemochrome film according to claim 1, feature exist
In in step 4, washing is to use ethanol washing twice, and washing is twice.
6. the preparation method of low angle dependence blue cadmium sulfide schemochrome film according to claim 1, feature exist
In in step 5, carrying out plated film using vertical sedimentation method is specifically: being inserted into glass into the ethanol solution of monodisperse CdS microballoon
Glass piece, is then dried in vacuo, and cadmium sulfide schemochrome film is made.
7. the preparation method of low angle dependence blue cadmium sulfide schemochrome film according to claim 6, feature exist
In the sheet glass of use is to impregnate the sheet glass above for 24 hours through hydrogen peroxide.
8. the preparation method of low angle dependence blue cadmium sulfide schemochrome film according to claim 1, feature exist
In in step 5, vacuum drying temperature is 40-50 DEG C, vacuum degree 0.05-0.09MPa, drying time 48-96h.
9. the cadmium sulfide microballoon that the described in any item preparation methods of claim 1-8 are prepared.
10. the low angle dependence blue cadmium sulfide schemochrome that the described in any item preparation methods of claim 1-8 are prepared
Film.