CN109468090A - A kind of hot-fusible pressure-sensitive adhesive and its combination process - Google Patents
A kind of hot-fusible pressure-sensitive adhesive and its combination process Download PDFInfo
- Publication number
- CN109468090A CN109468090A CN201811329649.2A CN201811329649A CN109468090A CN 109468090 A CN109468090 A CN 109468090A CN 201811329649 A CN201811329649 A CN 201811329649A CN 109468090 A CN109468090 A CN 109468090A
- Authority
- CN
- China
- Prior art keywords
- sensitive adhesive
- hot
- pressure
- fusible pressure
- antioxidant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of hot-fusible pressure-sensitive adhesives, including following component (by mass percentage): matrix resin 20-40%, tackifier 45%, plasticizer 15-35%, antioxidant 1%;The invention also discloses a kind of combination process of hot-fusible pressure-sensitive adhesive, comprising the following steps: pressure-sensitive adhesive agent is scratched sample on HDPE sheet material, HDPE sheet material is then heated to 60-100 DEG C, then paste coating, will and apply uniform pressure on entire splicing face;The present invention selects special material by penetrating into not dry cement mortar, since the system material is an electron rich system, and the metal ion in not dry cement mortar is short of electricity subsystem, so electron rich system and short of electricity subsystem produce complex by complexation reaction, the coiled material and cement basal plane made forms a densification and has the entirety of some strength, to achieve the effect that completely viscous;And combination process of the invention is easy to operate, and equipment requirement is low, has good promotion effect.
Description
Technical field
The present invention relates to technical field of hot-melt pressure-sensitive adhesive, specially a kind of hot-fusible pressure-sensitive adhesive and its combination process.
Background technique
Non-bituminous based high molecular adhesive waterproof coil is a kind of novel environmentally protective waterproofer, due to its excellent physics
Mechanical property, reliable installation and process are used for a long time confirmed excellent performance and have been obtained for being widely recognized as, and are overlaying
During waterproof construction, non-bituminous based high molecular adhesive waterproof coil has self-healing function, can be with liquid concrete slurry reaction
The waterproof layer formed after consolidation prevents waterproof interlayer channeling water hidden danger, can effectively improve waterproof in conjunction with concrete structure gapless
The validity of system.
Summary of the invention
The purpose of the present invention is to provide a kind of hot-fusible pressure-sensitive adhesive and its combination process, to solve asking for background technique proposition
Topic.
To achieve the above object, the invention provides the following technical scheme: a kind of hot-fusible pressure-sensitive adhesive, including following component (are pressed
Mass percent meter): matrix resin 20-40%, tackifier 45%, plasticizer 15-35%, antioxidant 1%.
Preferably, including following component (by mass percentage): matrix resin 20%, tackifier 45%, plasticizer
35%, antioxidant 1%.
Preferably, including following component (by mass percentage): matrix resin 30%, tackifier 45%, plasticizer
25%, antioxidant 1%.
Preferably, including following component (by mass percentage): matrix resin 40%, tackifier 45%, plasticizer
15%, antioxidant 1%.
Preferably, described matrix resin is amorphous poly-alpha-olefin, and the trade mark specification of the amorphous poly-alpha-olefin is
Any one of APAO792 or APAO508.
Preferably, the tackifier are C5 hydrogenated petroleum resin;The plasticizer is polyisobutene 2700, poly-1-butylene
950, any one of poly-1-butylene 300, paraffin oil P1 or paraffin oil P2;The antioxidant is antioxidant 1010.
A kind of combination process of hot-fusible pressure-sensitive adhesive as described above, comprising the following steps:
Step 1: hot-fusible pressure-sensitive adhesive is prepared according to above-mentioned formula, first lotion is sprayed on barrier paper, length is cut after surface drying
250mm, the HDPE sheet material of width 50mm size are spare;The HDPE sheet material for preparing long 250mm, width 50mm size again, then will be pressure-sensitive
Adhesive scratches sample on HDPE sheet material, HDPE sheet material is then heated to 60-100 DEG C, then paste coating, incites somebody to action and entire
Apply uniform pressure on splicing face, recommends to apply pressure up to 1MPa, test specimen is prepared;
Step 2: the test specimen being prepared in step 1 is placed on (23 ± 2) DEG C and relative humidity (30~70) %
Under the conditions of place at least 120-180 minutes, test specimen is finally subjected to cement testing, the cement conservation period is 7 days, each lot number examination
The number for testing test specimen is no less than five.
Preferably, the glass bar of one section of long 150mm is selected when scratching in the step 1, and the both ends of glass bar twine respectively
Around the copper wire of a loop diameter 0.3mm.
Compared with prior art, the beneficial effects of the present invention are: the present invention selects special material not dry by penetrating into
Cement mortar in, since the system material is an electron rich system, and the metal ion in not dry cement mortar is
Short of electricity subsystem, so electron rich system and short of electricity subsystem produce complex, the coiled material made and cement base by complexation reaction
Face forms a densification and has the entirety of some strength, to achieve the effect that completely viscous;And combination process behaviour of the invention
Make simply, equipment requirement is low, has good promotion effect.
Detailed description of the invention
Fig. 1 is the schematic diagram of the APAO792 influence to stripping performance mixed with POE8180 in the present invention;
Fig. 2 is the schematic diagram of influence of the C5 Petropols dosage to stripping performance in the present invention;
Fig. 3 is the schematic diagram of influence of the different plasticizer to stripping performance in the present invention;
Fig. 4 is the schematic diagram of the PB2700 influence to stripping performance mixed with P1 in the present invention;
Fig. 5 is the schematic diagram of the PB2700 influence to stripping performance mixed with P2 in the present invention;
Fig. 6 is the schematic diagram of the PB2700 influence to stripping performance mixed with PB950 in the present invention;
Fig. 7 is the schematic diagram of the PB2700 influence to stripping performance mixed with PB300 in the present invention.
Specific embodiment
Below in conjunction with the embodiment of the present invention, technical scheme in the embodiment of the invention is clearly and completely described,
Obviously, described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.Based in the present invention
Embodiment, every other embodiment obtained by those of ordinary skill in the art without making creative efforts, all
Belong to the scope of protection of the invention.
First part: the selection of elastic gel:
The main component of hot-fusible pressure-sensitive adhesive includes matrix resin, tackifier, plasticizer and antioxidant, and matrix is selected in this test
Resin is amorphous poly-alpha-olefin (APAO792 and APAO508) and polyolefin elastomer (POE8180), and selection tackifier are
C5 hydrogenated petroleum resin, select plasticizer are as follows: polyisobutene 2700, poly-1-butylene 950, poly-1-butylene 300, paraffin oil P1 and
Paraffin oil P2, selection antioxidant are antioxidant 1010.
It prepares hot-fusible pressure-sensitive adhesive materials and summarizes 2-1
According to anatomy as a result, design basis formula are as follows: APAO (matrix resin) -20%, tackifier -45%, plasticising
Agent -35%, antioxidant -1%.Wherein APAO selects APAO792 and APAO508, and tackifier select C5 hydrogenated petroleum resin,
Plasticizer selects PB2700, PB950, PB300, paraffin oil P1 and paraffin oil P2, and antioxidant selects antioxidant 1010.
A series of adjustment have been carried out to basic components in R&D process: having changed matrix resin type and dosage, change increasing
It moulds agent type and dosage and changes tackifying resin dosage.
2-1. changes matrix resin type and dosage
The campaign matrix resin first selects one of APAO792 and APAO508, and tackifier select C5 petroleum tree
Rouge, plasticizer select PIB, and antioxidant selects antioxidant 1010 (formula is shown in Table 2-2 and table 2-3), and sense organ is found after glue
APAO792 hot-fusible pressure-sensitive adhesive performance is obviously better than APAO508 hot-fusible pressure-sensitive adhesive, then carries out formula adjustment, selects main matrix
Resin is APAO792, adds another matrix resin (having selected APAO508, POE8180), matrix resin total amount wherein
It is still 20% (formula is shown in Table 2-4 and table 2-5).
Table 2-2. melt pressure sensitive glue formula-change APAO792 dosage
Sample number into spectrum | 7-20-PB2700 | 7-30-PB2700 | 7-40-PB2700 |
APAO792 | 100 (20%) | 100 (30%) | 100 (40%) |
C5 | 225 (45%) | 150 (45%) | 112.5 (45%) |
PIB2700 | 175 (35%) | 83 (25%) | 37.5 (15%) |
Antioxidant 1010 | 5 (1%) | 3.3 (1%) | 2.5 (1%) |
Table 2-3. melt pressure sensitive glue formula-change APAO508 dosage
Table 2-4. melt pressure sensitive glue formula-APAO792 is mixed with APAO508
Sample number into spectrum | 7-19-5-1-PB2700 | 7-18-5-2-PB2700 | 7-16-5-4-PB2700 | 7-14-5-6-PB2700 |
APAO792 | 95 (19%) | 90 (18%) | 80 (16%) | 70 (14%) |
APAO508 | 5 (1%) | 10 (2%) | 20 (4%) | 30 (6%) |
C5 | 225 (45%) | 225 (45%) | 225 (45%) | 225 (45%) |
PIB2700 | 175 (35%) | 175 (35%) | 175 (35%) | 175 (35%) |
Antioxidant 1010 | 5 (1%) | 5 (1%) | 5 (1%) | 5 (1%) |
Table 2-5. melt pressure sensitive glue formula-APAO792 is mixed with POE8180
Sample number into spectrum | 7-19-8-1-PB2700 | 7-18-8-2-PB2700 | 7-16-8-4-PB2700 | 7-14-8-6-PB2700 |
APAO792 | 95 (19%) | 90 (18%) | 80 (16%) | 70 (14%) |
POE8180 | 5 (1%) | 10 (2%) | 20 (4%) | 30 (6%) |
C5 | 225 (45%) | 225 (45%) | 225 (45%) | 225 (45%) |
PIB2700 | 175 (35%) | 175 (35%) | 175 (35%) | 175 (35%) |
Antioxidant 1010 | 5 (1%) | 5 (1%) | 5 (1%) | 5 (1%) |
2-2. changes plasticizer type and dosage
The campaign matrix resin selects APAO792, and tackifier select C5 Petropols, and plasticizer is first selected
One of PB2700, PB950, PB300, paraffin oil P1 and paraffin oil P2, antioxidant selects antioxidant 1010, and (formula is shown in Table 2-
6, table 2-7 and table 2-8).Then formula adjustment is carried out, selection primary plasticizer is PB2700, adds another plasticising wherein
Agent (has selected PB950, PB300, paraffin oil P1 and paraffin oil P2), and plasticizer total amount is still that 35% (formula is shown in Table 2-9, table 2-
10, table 2-11 and table 2-12).
Table 2-6. melt pressure sensitive glue formula-plasticizer selects paraffin oil P1
Table 2-7. melt pressure sensitive glue formula-plasticizer selects paraffin oil P2
Sample number into spectrum | 7-20-P2 | 7-30-P2 | 7-40-P2 |
APAO792 | 100 (20%) | 100 (30%) | 100 (40%) |
C5 Petropols | 225 (45%) | 150 (45%) | 112.5 (45%) |
P2 | 175 (35%) | 83 (25%) | 37.5 (15%) |
Antioxidant 1010 | 5 (1%) | 3.3 (1%) | 2.5 (1%) |
Table 2-8. melt pressure sensitive glue formula-plasticizer selects PB
Sample number into spectrum | 7-20-PB2700 | 7-20-PB950 | 7-20-PB300 |
APAO792 | 100 (20%) | 100 (20%) | 100 (20%) |
C5 | 225 (45%) | 225 (45%) | 225 (45%) |
PB2700 | 175 (35%) | —— | —— |
PB950 | —— | 175 (35%) | —— |
PB300 | —— | —— | 175 (35%) |
Antioxidant 1010 | 5 (1%) | 5 (1%) | 5 (1%) |
Table 2-9. melt pressure sensitive glue formula-PB2700 is mixed with PB950
Table 2-10. melt pressure sensitive glue formula-PB2700 is mixed with PB300
Table 2-11. melt pressure sensitive glue formula-PB2700 is mixed with P1
Table 2-12. melt pressure sensitive glue formula-PB2700 is mixed with P2
2-3. changes tackifier dosage
The campaign matrix resin selects APAO792, and tackifier select C5 Petropols (C5 and C5-100R), plasticising
PB2700 is selected in agent, and antioxidant selects antioxidant 1010.In the case where matrix resin, plasticizer and constant antioxidant dosage,
Only change the dosage of tackifier (formula is shown in Table 2-13).When selecting C5-100R hydrogenated petroleum resin as plasticizer, sense organ hair
The stripping performance and tack of existing glue are all obviously not so good as C5, therefore abandon using C5-100R hydrogenated petroleum resin as plasticizer.
Table 2-13. melt pressure sensitive glue formula-change C5 Petropols dosage
Three .APAO hot-fusible pressure-sensitive adhesive performance tests
The test of 3-1.T- stripping performance
3-1-1. testing standard:
GB/T2791-1995 (adhesive T- peeling strength test method).
3-1-2. test material preparation:
Long 200mm, HDPE sheet material 2 of wide 25mm, the gluing on wherein a piece of entire width are cut, gluing length is
150mm (selects the glass bar of one section of long 150mm, both ends wind the copper wire of a loop diameter 0.3mm respectively) when blade coating.Sample applies
It after the completion of glue, is bonded together with another HDPE piece, and apply uniform pressure on entire splicing face, recommends application pressure can
Up to 1MPa, 2h, 5 test specimens of every group of test should be placed under conditions of 23 DEG C and relative humidity 30% before specimen test.
3-1-3. test procedure:
Test specimen should be tightly clipped in the fixture of cupping machine, make the longitudinal axis and cupping machine and fixture of test specimen
Axis is overlapped, and entire distance is 100mm between fixture, is not subject to preload.Specimen test temperature is 23 DEG C, and tensile speed is
90mm/min。
The test of 3-2. tack
3-2-1. testing standard:
GB/T4852-2002 (pressure-sensitive tape tack testing standard).
3-2-2. test material preparation:
Specimen size: 30mm × 250mm, length of run up 100mm.4 test specimens of every group of test.
3-2-3. test procedure:
Test temperature: 21 DEG C, relative humidity: 40%, inclined surface angle: 30 °;It first takes a test specimen to be tested, preselects
Maximum steel ball out, then carry out the test of the other three test specimen.
3-3. holds sticky test
3-3-1. testing standard:
GB/T4851-1998 (pressure-sensitive tape holds sticky testing standard).
3-3-2. test material preparation:
Specimen size: 20mm × 70mm.3 test specimens of every group of test.
3-3-3. test procedure:
Test temperature: 23 DEG C, relative humidity: 50%.Test specimen is pasted onto the middle part of breadboard and load plate, it is past with pressure roller
Multiple rolling three times, is fixed on test stand after 20min and hangs up counterweight, starts timing.
3-4. shearing performance test
3-4-1. testing standard:
GB/T328.23-2007 (polymer membranes joint shear performance test standard).
3-4-2. test material preparation:
For overlapped, test piece places at least 20h under conditions of 25 DEG C and relative humidity 70% in advance.Each overlap joint examination
Piece cuts out 5 rectangular coupons, and width 50mm is vertical with overlap edge, and length should ensure that two fixtures are shown in when overlapped for centre
Initial distance is 200mm.This test specimen size are as follows: 50mm × 190mm.It, should be at 25 DEG C and opposite before specimen test after overlap joint
At least 2h is placed under conditions of humidity 70%.5 test specimens of every group of test.
3-4-3. test procedure:
Test specimen should be tightly clipped in the fixture of cupping machine, make the longitudinal axis and cupping machine and fixture of test specimen
Axis is overlapped.Entire distance is 200mm between fixture, is not subject to preload.Specimen test temperature is 25 DEG C, and tensile speed is
100mm/min。
The present invention has carried out the experiment of three kinds of combination process altogether:
1. then spraying one layer of coating on glue surface first hot-fusible pressure-sensitive adhesive blade coating to applying on silicon barrier paper;Table to be coated
After dry, coating and glue-line are integrally pasted on HDPE sheet material.Such bonding effect is preferable, but will appear cracking after coating surface drying
Phenomenon, therefore abandon such combination process.
2. first spraying one layer of coating on applying silicon barrier paper, then hot-fusible pressure-sensitive adhesive is scratched onto coating, finally in glue
Surface mount on HDPE sheet material.When lab scale, since condition is more simple and crude, when scraping rubberised layer, easily coating is swept (due to applying
Layer and painting silicon barrier paper are easy to be detached from).But the production after industrialization amplification of such combination process is feasible.
3. first spraying one layer of coating on applying silicon barrier paper, then hot-fusible pressure-sensitive adhesive is scratched onto HDPE sheet material, finally
Coating is pasted on film surface again.Such combination process is preferable, but when making cement test, coating occurs and glue-line is detached from now
As, therefore combination process is adjusted are as follows: after on hot-fusible pressure-sensitive adhesive blade coating to HDPE sheet material, painting is pasted again after being heated to 80 DEG C
Layer.
Two, adhesive layers and cement mortar peeling strength test
180 ° of disbonded tests of the splicing sample that flexible material is bonded with rigid material are: two pieces by viscous material adhesive
It is prepared into splicing sample, then will be glued sample and peeled off with defined rate from the opening of splicing, two pieces of adherends are along quilt
The direction of viscous face length is gradually disengaged.Splicing face is arranged essentially parallel to by the peeling force that flexible adherend is applied.
The preparation of 2-1. sample
First lotion is sprayed on barrier paper, it is spare that long 250mm, the piece of width 50mm size are cut after surface drying.Prepare to grow again
The HDPE sheet material of 250mm, width 50mm size.Then pressure-sensitive adhesive agent is scratched to coating or HDPE on piece and (selects one when blade coating
The glass bar of segment length 150mm, both ends wind the copper wire of a loop diameter 0.3mm respectively).After the completion of sample, and entirely it is being glued
Apply uniform pressure on face, recommends to apply pressure up to 1MPa.Cement testing is finally carried out, the cement conservation period is 7 days.Often
The number of a lot number test is no less than five.
2-2. experimental condition
This test carries out on SANA type micro-control electronic universal tester, selects tensile speed 100mm/min, is tried
It is as shown in the table for the Average peel force of sample and average peel strength data.
2-3. test result
This experimental test raw sample, 7-20-P1 waterproof roll and 7-20-PB2700 waterproof roll and cement mortar bond
Stripping performance afterwards, test result is as shown in table 4-1, table 4-2 and table 4-3.In table 4-3, sample 1,2,3,4 is all to use
The third combination process, wherein 1 is direct combination, 2,3,4 be heated to 100 DEG C, 80 DEG C, 60 DEG C respectively after carry out it is compound.
Stripping performance after 7-20-PB2700 waterproof roll is bonded with cement mortar is integrally relatively low, and individual number is too low.
It is influence of each component of the present invention to APAO hot-fusible pressure-sensitive adhesive performance below
The mixed influence to stripping performance of two kinds of matrix resins of 5-1.
When preparing hot-fusible pressure-sensitive adhesive, two kinds of matrix resins is selected to use (total amount 20% is constant) with, two kinds of matrix resin difference
Are as follows: APAO792 and POE8180, tackifier are C5 Petropols (mass fraction 45%), and plasticizer is PB2700 (mass fraction
35%) stripping performance of hot-fusible pressure-sensitive adhesive, is measured, as shown in Figure 1;
As shown in Figure 1, the stripping performance of glue is best when APAO792 dosage maximum (20%), with the addition of POE8180,
Stripping performance gradually weakens.
When two kinds of matrix resins selections are APAO792 and APAO508, sense organ finds that its tack is obviously poor, therefore abandons
Secondary series formula.
5-2. changes influence of the tackifier dosage to stripping performance
When preparing hot-fusible pressure-sensitive adhesive, select matrix resin for APAO792 (100 parts), plasticizer is PB2700 (175 parts),
Change tackifier C5 Petropols dosage (to be respectively as follows: 175 parts, 200 parts, 225 parts, 250 parts, 275 parts, be converted into mass fraction
Be respectively as follows: 39%, 42%, 45%, 48%, 50%).The stripping performance of hot-fusible pressure-sensitive adhesive is measured, as shown in Figure 2;
As shown in Figure 2, with the increase of C5 Petropols dosage, the peel strength of glue is gradually increased, when C5 Petropols
When dosage reaches 45%, peel strength reaches maximum, and later with the increase of C5 Petropols dosage, peel strength gradually drops again
It is low.
5-3. changes influence of the plasticizer type to stripping performance
Under identical formula: m (APAO792): m (C5 Petropols): m (tackifier)=20:45:35 is selected different
Hot-fusible pressure-sensitive adhesive is made in type plasticizer (P1, P2, PB2700, PB950 and PB300).The stripping performance of hot-fusible pressure-sensitive adhesive is measured,
As shown in Figure 3;
From the figure 3, it may be seen that for different types of plasticizer, it is maximum using the peel strength of glue when PB2700.For difference
The PB of molecular weight, with the reduction of molecular weight, peel strength is gradually decreased, when molecular weight drops to 300, peel strength decline compared with
Fastly, stripping performance is very poor at this time.
The mixed influence to stripping performance of two kinds of plasticizer of 5-4.
When preparing hot-fusible pressure-sensitive adhesive, two kinds of plasticizer is selected to use (total amount 35% is constant) with, two kinds of plasticizer from P1, P2,
It is chosen in PB2700, PB950 and PB300, matrix resin is APAO792 (mass fraction 20%), and tackifier are C5 petroleum tree
Rouge (mass fraction 45%).
5-4-1.PB2700 the influence to stripping performance mixed with P1
This group of formula selects PB2700 mixed with P1, the stripping performance of hot-fusible pressure-sensitive adhesive is measured, as shown in Fig. 4;
As shown in Figure 4, the stripping performance of glue is best when PB2700 dosage maximum (35%), with the addition of P1, fissility
First can comparatively fast it decline, after P1 is added to half, decrease speed is slack-off.
5-4-2.PB2700 the influence to stripping performance mixed with P2
This group of formula selects PB2700 mixed with P1, the stripping performance of hot-fusible pressure-sensitive adhesive is measured, as shown in Fig. 5;
As shown in Figure 5, the stripping performance of glue is best when PB2700 dosage maximum (35%), and with the addition of P2, removing is strong
Degree is gradually reduced.
5-4-3.PB2700 the influence to stripping performance mixed with PB950
This group of formula selects PB2700 mixed with PB950, measures the stripping performance of hot-fusible pressure-sensitive adhesive, as shown in Figure 6;
It will be appreciated from fig. 6 that with the increase of PB950 dosage, the peel strength of glue will appear a peak value, i.e., when PB950 is used
When amount reaches 10%, peel strength reaches maximum, and later with the increase of PB950 dosage, peel strength gradually decreases again.Simultaneously
We it can be found that with PB950 dosage increase, most start peel strength variation it is more slow, when PB950 dosage reaches one
After half, peel strength reduces very fast.
5-4-4.PB2700 the influence to stripping performance mixed with PB300
This group of formula selects PB2700 mixed with PB300, measures the stripping performance of hot-fusible pressure-sensitive adhesive, as shown in Figure 7:
As shown in Figure 7, with the increase of PB300 dosage, the peel strength of glue will appear a peak value, i.e., when PB300 is used
When amount reaches 2.5%, peel strength reaches maximum, and later with the increase of PB300 dosage, peel strength starts to reduce again, and
And it reduces very fast.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (8)
1. a kind of hot-fusible pressure-sensitive adhesive, which is characterized in that including following component (by mass percentage): matrix resin 20-40%,
Tackifier 45%, plasticizer 15-35%, antioxidant 1%.
2. a kind of hot-fusible pressure-sensitive adhesive according to claim 1, which is characterized in that (by mass percentage including following component
Meter): matrix resin 20%, tackifier 45%, plasticizer 35%, antioxidant 1%.
3. a kind of hot-fusible pressure-sensitive adhesive according to claim 1, which is characterized in that (by mass percentage including following component
Meter): matrix resin 30%, tackifier 45%, plasticizer 25%, antioxidant 1%.
4. a kind of hot-fusible pressure-sensitive adhesive according to claim 1, which is characterized in that (by mass percentage including following component
Meter): matrix resin 40%, tackifier 45%, plasticizer 15%, antioxidant 1%.
5. a kind of hot-fusible pressure-sensitive adhesive according to any one of claims 1-4, it is characterised in that: described matrix resin is nothing
Shape poly-alpha-olefin, and the trade mark specification of the amorphous poly-alpha-olefin is any one of APAO792 or APAO508.
6. a kind of hot-fusible pressure-sensitive adhesive according to any one of claims 1-4, it is characterised in that: the tackifier add for C5
Hydrogen Petropols;The plasticizer is polyisobutene 2700, poly-1-butylene 950, poly-1-butylene 300, paraffin oil P1 or paraffin
Any one of oily P2;The antioxidant is antioxidant 1010.
7. a kind of combination process of hot-fusible pressure-sensitive adhesive as claimed in any one of claims 1 to 6, which is characterized in that including following
Step:
Step 1: preparing hot-fusible pressure-sensitive adhesive according to above-mentioned formula, first lotion be sprayed on barrier paper, cut after surface drying long 250mm,
The HDPE sheet material of wide 50mm size is spare;The HDPE sheet material for preparing long 250mm, width 50mm size again, then by pressure-sensitive adhesive agent
Sample on HDPE sheet material is scratched, HDPE sheet material is then heated to 60-100 DEG C, then paste coating, will and entirely be glued face
It is upper to apply uniform pressure, recommend to apply pressure up to 1MPa, test specimen is prepared;
Step 2: the test specimen being prepared in step 1 is placed on (23 ± 2) DEG C and the condition of relative humidity (30~70) %
It is lower to place at least 120-180 minutes, test specimen is finally subjected to cement testing, the cement conservation period is 7 days, each lot number test examination
The number of part is no less than five.
8. a kind of combination process of hot-fusible pressure-sensitive adhesive according to claim 7, it is characterised in that: scratched in the step 1
The glass bar of mono- section of long 150mm of Shi Xuanyong, and the both ends of glass bar wind the copper wire of a loop diameter 0.3mm respectively.