CN109467348A - The method of ardealite production baking-free ceramicite - Google Patents
The method of ardealite production baking-free ceramicite Download PDFInfo
- Publication number
- CN109467348A CN109467348A CN201710800136.4A CN201710800136A CN109467348A CN 109467348 A CN109467348 A CN 109467348A CN 201710800136 A CN201710800136 A CN 201710800136A CN 109467348 A CN109467348 A CN 109467348A
- Authority
- CN
- China
- Prior art keywords
- ardealite
- pan
- pelletizer
- production
- baking
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of methods of ardealite production baking-free ceramicite, its designing points is after drying the ardealite that water content is 20%-30%, powder is formed after sieving or crushing, ardealite powder and cement mixing are uniformly put into pan-pelletizer, with pan-pelletizer rotation atomized water spray balling-up simultaneously, through natural curing 72-120 hours after balling-up, production forms baking-free ceramicite.The present invention has the advantages that the blending amount of 1, ardealite is higher, 70%-85% can be reached, so that ardealite be made to make full use of, improve utilization and utilization rate.2, obtained haydite quality is preferable, and intensity is higher, especially later strength.3, process is relatively simple, flexible, can be required to carry out proportion production according to the different purposes and different quality of haydite.4, equipment and it is artificial less input, production production cost is greatly reduced.
Description
Technical field
The present invention relates to haydite production fields, are a kind of methods of ardealite production baking-free ceramicite.
Background technique
Currently, ardealite about 1.5 hundred million or more that the whole world is discharged every year, ardealite discharge amount is about every year for the country
50000000 tons.China's ardealite comprehensive utilization technique is roughly divided into following three kinds: first is that method of chemical treatment, such as prepares producing sulfuric acid and jointly
Cement, preparation sulphur ammonium, potassium sulfate by-product ammonium chloride etc.;Second is that calcination processing method, as ardealite makes building gypsum plaster and downstream
Painting material, gypsum block, plasterboard, cement retarder etc.;Third is that blending method, is such as used as composite fertilizer fillers, salt-soda soil soil
Earth modifying agent, builds bank material and baking-free brick etc. at solidification filling mine, stabilized zone of building the road.Although there is many-sided diversification
Technology comprehensively utilizes ardealite, but utilization is little, and utilization rate is not high, is not desired to work as with the quantum of output of ardealite, greatly
The ardealite waste material of amount not only poses a serious threat environment, and occupies large amount of land resources.For this purpose, there is a kind of energy to be designed
Enough schemes that existing ardealite is sufficiently comprehensively utilized.
Summary of the invention
To overcome above-mentioned deficiency, the purpose of the present invention is provide a kind of side of ardealite production baking-free ceramicite to this field
Method, solving it, existing ardealite utilization is little, utilization rate is not high, the technical issues of easily causing damages to environment.Its purpose
It is achieved by the following technical solution.
A kind of method of ardealite production baking-free ceramicite, is characterized by and dries the ardealite that water content is 20%-30%
Afterwards, powder is formed after sieving or crushing, ardealite powder and cement mixing are uniformly put into pan-pelletizer, are rotated with pan-pelletizer same
When atomized water spray balling-up, through natural curing 72-120 hours after balling-up, production form baking-free ceramicite.
In the above method, the ardealite powder and cement-weighting pass through conveyer after mixing and are delivered to pan-pelletizer
In, pan-pelletizer rotates clockwise, and ardealite powder and cement are in reversed relative to pan-pelletizer under the scrapper conveyor effect of pan-pelletizer
Movement, with pan-pelletizer rotation, atomized water spray, ardealite powder and cement make balling-up, are delivered to after balling-up through belt conveyor simultaneously
Flat library stacks natural curing.
In the above method, the ardealite, cement, water proportion be ardealite account for 70%-85%, cement accounts for 5%-10%, water
Account for 10%-20%.
In the above method, pigment is added in the ardealite powder and cement mixing simultaneously, and final production forms colored unburned
Haydite.
The present invention has the advantages that
1, the blending amount of ardealite is higher, can reach 70%-85%, so that ardealite be made to make full use of, improves utilization and benefit
With rate.
2, obtained haydite quality is preferable, and intensity is higher, especially later strength.
3, process is relatively simple, flexible, can be required to carry out proportion system according to the different purposes and different quality of haydite
Make.
4, equipment and it is artificial less input, production production cost is greatly reduced.
Detailed description of the invention
Fig. 1 is the process block schematic diagram of present invention production building porcelain granule.
Fig. 2 is the process block schematic diagram that the present invention makes colored haydite.
Specific embodiment
Now in conjunction with attached drawing, the invention will be further described.
As shown in Figure 1, the method for ardealite production baking-free ceramicite are as follows: dry the ardealite that water content is 20%-30%
Afterwards, powder is formed after sieving or crushing, ardealite powder measures respectively with cement to be delivered to by conveyer after mixing
In pan-pelletizer, pan-pelletizer is rotated clockwise, and ardealite powder and cement are under the scrapper conveyor effect of pan-pelletizer relative to pan-pelletizer
In counter motion, with pan-pelletizer rotation while atomized water spray, ardealite powder and cement make balling-up, through belt conveyor after balling-up
It is delivered to flat library to stack natural curing 72-120 hours, i.e. production forms baking-free ceramicite finished product.In the above method, ardealite, water
Mud, water proportion be ardealite account for 70%-85%, cement accounts for 5%-10%, and water accounts for 10%-20%.
As shown in Fig. 2, the above method can also make colored baking-free ceramicite, i.e., above-mentioned ardealite powder and cement mixing are simultaneously
Pigment is added, final production forms colored baking-free ceramicite.
Claims (4)
1. a kind of method of ardealite production baking-free ceramicite, it is characterised in that after the ardealite that water content is 20%-30% is dried,
Powder is formed after sieving or crushing, ardealite powder and cement mixing are uniformly put into pan-pelletizer, simultaneously with pan-pelletizer rotation
Atomized water spray balling-up, through natural curing 72-120 hours after balling-up, production forms baking-free ceramicite.
2. the method for ardealite according to claim 1 production baking-free ceramicite, it is characterised in that the ardealite powder with
Cement-weighting passes through conveyer after mixing and is delivered in pan-pelletizer, and pan-pelletizer rotates clockwise, ardealite powder and cement
Relative to pan-pelletizer in counter motion under the scrapper conveyor effect of pan-pelletizer, with pan-pelletizer rotation while atomized water spray, phosphogypsum powder
Material makes balling-up with cement, is delivered to flat library through belt conveyor after balling-up and stacks natural curing.
3. the method for ardealite according to claim 1 production baking-free ceramicite, it is characterised in that the ardealite, cement,
The proportion of water is that ardealite accounts for 70%-85%, and cement accounts for 5%-10%, and water accounts for 10%-20%.
4. the method for ardealite according to claim 1 production baking-free ceramicite, it is characterised in that the ardealite powder with
Pigment is added simultaneously in cement mixing, and final production forms colored baking-free ceramicite.