CN109456698A - A kind of uncured modified asphalt waterproofing paint and preparation method thereof - Google Patents
A kind of uncured modified asphalt waterproofing paint and preparation method thereof Download PDFInfo
- Publication number
- CN109456698A CN109456698A CN201811213356.8A CN201811213356A CN109456698A CN 109456698 A CN109456698 A CN 109456698A CN 201811213356 A CN201811213356 A CN 201811213356A CN 109456698 A CN109456698 A CN 109456698A
- Authority
- CN
- China
- Prior art keywords
- rubber powder
- styrene butadiene
- mixed liquor
- thermoplastic styrene
- butadiene rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention belongs to water-repellent paint technical fields, propose a kind of uncured modified asphalt waterproofing paint and preparation method thereof, including pitch 30-45, thermoplastic styrene butadiene rubber 8-15, thermoplastic styrene butadiene rubber powder 1-3, silicone rubber powder 2-7, solid paraffin 5-15, soybean oil 30-45, epoxidized soybean oil 1-3, second line of distillation oil subtracts third fractional oil 2-3, solvent naphtha 15-25, cyclic acid anhydride type compatilizer 0.5-0.8.The invention also provides a kind of preparation methods of uncured modified asphalt waterproofing paint.Through the above technical solutions, solving the problems, such as prior art rubberized asphalt non-cured water-proof coating heat resistance and low temperature flexibility is poor.
Description
Technical field
The invention belongs to water-repellent paint technical field, it is related to a kind of uncured modified asphalt waterproofing paint and its preparation side
Method.
Background technique
Rubberized asphalt non-cured water-proof coating will not solidify long-time is placed after construction, keep waterproof material
Original performance can be improved the service life of waterproof layer.It " is never solidified " performance and is mainly determined with its solid content.Other are anti-
Mixing water or other solvents make it possess application property when water paint is constructed, but waterproof layer solidifies as the solvent evaporates after construction.
Itself solid content of rubberized asphalt non-cured water-proof coating is 99% or more, and special equipment is used when construction, molten without adding
Agent, therefore will not solidify after constructing even across long-time and keep its performance.
But uncured modified asphalt waterproofing paint in the prior art has that heat resistance is poor to ask in use
Topic, when temperature is higher, mobility is big;And low temperature flexibility is poor, thus make the use of uncured modified asphalt waterproofing paint by
Limitation has been arrived, use environment and construction environment are limited.
CN13937407B discloses uncured rubber asphalt waterproof coating, this coating is by pitch, rubber, dispersing agent, thickening
Agent and filler composition, the coating is in -30 DEG C of flawlesses, and not brittle failure, 80 DEG C of product do not trickle.But the heat resistance of this degree and low
Tenderness is not able to satisfy the requirement of some adverse circumstances still.
Therefore, it invents and a kind of have excellent heat resistance and the rubberized asphalt non-cured water-proof coating of low temperature flexibility and still have very much
It is necessary.
Summary of the invention
The present invention proposes a kind of uncured modified asphalt waterproofing paint and preparation method thereof, solves rubberization in the prior art
The uncured water-repellent paint heat resistance of pitch and the poor problem of low temperature flexibility.
The technical scheme of the present invention is realized as follows:
A kind of uncured modified asphalt waterproofing paint, the component including following quality proportioning:
Pitch 30-45, thermoplastic styrene butadiene rubber 8-15, thermoplastic styrene butadiene rubber powder 1-3, silicone rubber powder 2-7, solid
Paraffin 5-15, soybean oil 30-45, epoxidized soybean oil 1-3, second line of distillation is oily or subtracts third fractional oil 2-3, solvent naphtha 15-25, cyclic acid anhydride
Type compatilizer 0.5-0.8.
Further, the granularity of the thermoplastic styrene butadiene rubber powder is in 90-120, silicone rubber powder 30-60.
Further, the solvent naphtha is 120# rubber solvent naphtha or 200# paint naphtha.
The invention also provides a kind of preparation methods of uncured modified asphalt waterproofing paint, include the following steps,
A) it is stirred evenly after thermoplastic styrene butadiene rubber is added after soybean oil being warming up to 160-180 DEG C, obtains mixed liquor one,
B) solid paraffin, thermoplastic styrene butadiene rubber powder are added in the mixed liquor one and stirs evenly, is subsequently added into
Silicone rubber powder simultaneously stirs evenly, and obtains mixed liquor two,
C) by the second line of distillation oil and subtract one of third fractional oil and pitch, the solvent naphtha, the epoxidized soybean oil,
The cyclic acid anhydride type compatilizer is added into the mixed liquor two, and it is 160 ± 10 that the temperature of mixed liquor two is kept in this step
℃。
It the working principle of the invention and has the beneficial effect that
1, the water-repellent paint in the present invention, non-volatile object have preferable heat resistance and low temperature flexibility, 90 DEG C of nothings of high temperature resistant
Sliding, trickling and drippage;Low temperature flexibility is good, and 30 DEG C of ﹣, without fracture, are adapted to various adverse circumstances, overcomes non-in the prior art
Cured modified asphalt waterproofing paint heat resistance and the poor problem of low temperature flexibility.
It 2, can be further by the thermoplastic styrene butadiene rubber powder and silicone rubber powder of setting different-grain diameter in the present invention
Increase the heat resistance and low temperature flexibility of entire water-repellent paint.
Specific embodiment
In order to better understand the present invention, the present invention will be further described in detail below with reference to the embodiments.But this
The protection scope of invention is not limited to the range that embodiment is stated.Experimental method described in following embodiment and comparative examples,
It unless otherwise specified, is conventional method;The reagent and material commercially obtain unless otherwise specified.
Embodiment 1:
A kind of uncured modified asphalt waterproofing paint, the component including following quality proportioning:
Pitch 30, thermoplastic styrene butadiene rubber 8, thermoplastic styrene butadiene rubber powder 1, silicone rubber powder 2, solid paraffin 5, soybean
Oil 30, epoxidized soybean oil 1, second line of distillation oil 2,120# of oil rubber solvent naphtha 15, cyclic acid anhydride type compatilizer 0.5.
Wherein, the granularity of thermoplastic styrene butadiene rubber powder and the granularity of silicone rubber powder are 90-120.
The preparation method is as follows:
A) it is stirred evenly after thermoplastic styrene butadiene rubber is added after soybean oil being warming up to 160-180 DEG C, obtains mixed liquor one,
B) solid paraffin, thermoplastic styrene butadiene rubber powder are added in mixed liquor one and stirs evenly, is subsequently added into silicon rubber
Rubber powder end simultaneously stirs evenly, and obtains mixed liquor two,
C) by second line of distillation oil and pitch, 120# rubber solvent naphtha, epoxidized soybean oil, cyclic acid anhydride type compatilizer be added to
In mixed liquor two, it is 160 ± 10 DEG C that the temperature of mixed liquor two is kept in this step.
Embodiment 2:
Pitch 45, thermoplastic styrene butadiene rubber 15, thermoplastic styrene butadiene rubber powder 3, silicone rubber powder 7, solid paraffin 15, greatly
Soya-bean oil 45, epoxidized soybean oil 3, second line of distillation oil 3,120# rubber solvent naphtha 25, cyclic acid anhydride type compatilizer 0.8.
Wherein, the granularity of thermoplastic styrene butadiene rubber powder and the granularity of silicone rubber powder are 90-120.
The preparation method is as follows:
A) it is stirred evenly after thermoplastic styrene butadiene rubber is added after soybean oil being warming up to 160-180 DEG C, obtains mixed liquor one,
B) solid paraffin, thermoplastic styrene butadiene rubber powder are added in mixed liquor one and stirs evenly, is subsequently added into silicon rubber
Rubber powder end simultaneously stirs evenly, and obtains mixed liquor two,
C) by second line of distillation oil and pitch, 120# rubber solvent naphtha, epoxidized soybean oil, cyclic acid anhydride type compatilizer be added to
In mixed liquor two, it is 160 ± 10 DEG C that the temperature of mixed liquor two is kept in this step.
Embodiment 3:
Pitch 37, thermoplastic styrene butadiene rubber 12, thermoplastic styrene butadiene rubber powder 2, silicone rubber powder 5, solid paraffin 10, greatly
Soya-bean oil 39, epoxidized soybean oil 2, second line of distillation oil 2.5,120# rubber solvent naphtha 29, cyclic acid anhydride type compatilizer 0.6.
Wherein, the granularity of thermoplastic styrene butadiene rubber powder and the granularity of silicone rubber powder are 90-120.
The preparation method is as follows:
A) it is stirred evenly after thermoplastic styrene butadiene rubber is added after soybean oil being warming up to 160-180 DEG C, obtains mixed liquor one,
B) solid paraffin, thermoplastic styrene butadiene rubber powder are added in mixed liquor one and stirs evenly, is subsequently added into silicon rubber
Rubber powder end simultaneously stirs evenly, and obtains mixed liquor two,
C) by second line of distillation oil and pitch, epoxidized soybean oil, 120# rubber solvent naphtha, cyclic acid anhydride type compatilizer be added to
In mixed liquor two, it is 160 ± 10 DEG C that the temperature of mixed liquor two is kept in this step.
Embodiment 4:
Pitch 37, thermoplastic styrene butadiene rubber 12, thermoplastic styrene butadiene rubber powder 2, silicone rubber powder 4, solid paraffin 10, greatly
Soya-bean oil 38, epoxidized soybean oil 2 subtract third fractional oil 2.5,120# rubber solvent naphtha 30, cyclic acid anhydride type compatilizer 0.6.
Wherein, the granularity of thermoplastic styrene butadiene rubber powder and the granularity of silicone rubber powder are 30-60.
The preparation method is as follows:
A) it is stirred evenly after thermoplastic styrene butadiene rubber is added after soybean oil being warming up to 160-180 DEG C, obtains mixed liquor one,
B) solid paraffin, thermoplastic styrene butadiene rubber powder are added in mixed liquor one and stirs evenly, is subsequently added into silicon rubber
Rubber powder end simultaneously stirs evenly, and obtains mixed liquor two,
C) will subtract third fractional oil and pitch, epoxidized soybean oil, 120# rubber solvent naphtha, cyclic acid anhydride type compatilizer be added to
In mixed liquor two, it is 160 ± 10 DEG C that the temperature of mixed liquor two is kept in this step.
Embodiment 5:
Pitch 37, thermoplastic styrene butadiene rubber 12, thermoplastic styrene butadiene rubber powder 2, silicone rubber powder 4, solid paraffin 10, greatly
Soya-bean oil 38, epoxidized soybean oil 2 subtract third fractional oil 2.5,200# paint naphtha 30, cyclic acid anhydride type compatilizer 0.6.
Wherein, the granularity of thermoplastic styrene butadiene rubber powder and the granularity of silicone rubber powder are 90-120.
The preparation method is as follows:
A) it is stirred evenly after thermoplastic styrene butadiene rubber is added after soybean oil being warming up to 160-180 DEG C, obtains mixed liquor one,
B) solid paraffin, thermoplastic styrene butadiene rubber powder are added in mixed liquor one and stirs evenly, is subsequently added into silicon rubber
Rubber powder end simultaneously stirs evenly, and obtains mixed liquor two,
C) will subtract third fractional oil and pitch, 200# paint naphtha, epoxidized soybean oil, cyclic acid anhydride type compatilizer be added to
In mixed liquor two, it is 160 ± 10 DEG C that the temperature of mixed liquor two is kept in this step.
Embodiment 6:
Pitch 37, thermoplastic styrene butadiene rubber 12, thermoplastic styrene butadiene rubber powder 2, silicone rubber powder 5, solid paraffin 10, greatly
Soya-bean oil 39, epoxidized soybean oil 2, second line of distillation oil 2.5,120# rubber solvent naphtha 29, cyclic acid anhydride type compatilizer 0.6.
Wherein, the granularity of thermoplastic styrene butadiene rubber powder is in 90-120, silicone rubber powder 30-60.
The preparation method is as follows:
A) it is stirred evenly after thermoplastic styrene butadiene rubber is added after soybean oil being warming up to 160-180 DEG C, obtains mixed liquor one,
B) solid paraffin, thermoplastic styrene butadiene rubber powder are added in mixed liquor one and stirs evenly, is subsequently added into silicon rubber
Rubber powder end simultaneously stirs evenly, and obtains mixed liquor two,
C) by second line of distillation oil and pitch, epoxidized soybean oil, 120# rubber solvent naphtha, cyclic acid anhydride type compatilizer be added to
In mixed liquor two, it is 160 ± 10 DEG C that the temperature of mixed liquor two is kept in this step.
Comparative example 1:
Pitch 37, thermoplastic styrene butadiene rubber 12, thermoplastic styrene butadiene rubber powder 2, solid paraffin 10, soybean oil 39, epoxy
Soybean oil 2, second line of distillation oil 2.5,120# rubber solvent naphtha 29, cyclic acid anhydride type compatilizer 0.6.
Wherein, the granularity of thermoplastic styrene butadiene rubber powder is 90-120.
The preparation method is as follows:
A) it is stirred evenly after thermoplastic styrene butadiene rubber is added after soybean oil being warming up to 160-180 DEG C, obtains mixed liquor one,
B) solid paraffin, thermoplastic styrene butadiene rubber powder are added in mixed liquor one and stirs evenly, obtains mixed liquor two,
C) by second line of distillation oil and pitch, epoxidized soybean oil, 120# rubber solvent naphtha, cyclic acid anhydride type compatilizer be added to
In mixed liquor two, it is 160 ± 10 DEG C that the temperature of mixed liquor two is kept in this step.
Comparative example 2:
Pitch 37, thermoplastic styrene butadiene rubber 12, silicone rubber powder 5, solid paraffin 10, soybean oil 39, epoxidized soybean oil 2,
Second line of distillation oil 2.5,120# rubber solvent naphtha 29, cyclic acid anhydride type compatilizer 0.6.
Wherein, the granularity of thermoplastic styrene butadiene rubber powder is 90-120.
The preparation method is as follows:
A) it is stirred evenly after thermoplastic styrene butadiene rubber is added after soybean oil being warming up to 160-180 DEG C, obtains mixed liquor one,
B) solid paraffin, silicone rubber powder are added in mixed liquor one and stirs evenly, obtains mixed liquor two,
C) by second line of distillation oil and pitch, 120# rubber solvent naphtha, epoxidized soybean oil, cyclic acid anhydride type compatilizer be added to
In mixed liquor two, it is 160 ± 10 DEG C that the temperature of mixed liquor two is kept in this step.
Comparative example 3:
Pitch 37, thermoplastic styrene butadiene rubber 12, thermoplastic styrene butadiene rubber powder 2, silicone rubber powder 5, solid paraffin 10, greatly
Soya-bean oil 39, second line of distillation oil 2.5,120# rubber solvent naphtha 29, cyclic acid anhydride type compatilizer 0.6.
Wherein, the granularity of thermoplastic styrene butadiene rubber powder and the granularity of silicone rubber powder are 90-120.
The preparation method is as follows:
A) it is stirred evenly after thermoplastic styrene butadiene rubber is added after soybean oil being warming up to 160-180 DEG C, obtains mixed liquor one,
B) solid paraffin, thermoplastic styrene butadiene rubber powder are added in mixed liquor one and stirs evenly, is subsequently added into silicon rubber
Rubber powder end simultaneously stirs evenly, and obtains mixed liquor two,
C) second line of distillation oil and pitch, 120# rubber solvent naphtha, cyclic acid anhydride type compatilizer are added into mixed liquor two,
The temperature that mixed liquor two is kept in this step is 160 ± 10 DEG C.
Product obtained above is carried out to the test of flash-point, low temperature flexibility and heat resistance respectively,
1.1 low temperature flexibility test methods
In (70-90) g/m of (100 × 100) mm3Blank sheet of paper on heat sample, with a thickness of (2.0 ± 0.2) mm, cut
After maintenance for 24 hours, it is adjusted under predetermined temperature to be that φ 20mm pole is put by 3 pieces of (100 × 25) mm test specimen for test specimen and diameter
In low temperature refrigerator, then carried out by 13 chapters regulation in GB/T 16777-2008, coating faces outwardly when test.
1.2 heat resistance test methods
By on sample hot melt blade coating to 120mm × 50mm × (2-4) mm aluminium sheet, coated area is 100mm × 50mm, thickness
For (2.0 ± 0.2) mm, placed under standard test conditions for 24 hours, by test specimen 50mm short side and bracket lower contacts, and with level
Face angle at 45 ° is put into constant temperature to the electric drying oven with forced convection of predetermined temperature, test specimen between dry tank wall at a distance from be not less than
50mm, the center of test specimen is preferably with the probe of thermometer in the same horizontal position.It is taken out after test specimen processing 2h ± 15min, observes table
Face.3 test specimens are tested altogether, and test specimen is recorded after test, and whether there is or not generate sliding, trickling, drippage.
Test result is as follows:
The above is merely preferred embodiments of the present invention, be not intended to limit the invention, it is all in spirit of the invention and
Within principle, any modification, equivalent replacement, improvement and so on be should all be included in the protection scope of the present invention.
Claims (4)
1. a kind of uncured modified asphalt waterproofing paint, it is characterised in that: the component including following quality proportioning:
Pitch 30-45, thermoplastic styrene butadiene rubber 8-15, thermoplastic styrene butadiene rubber powder 1-3, silicone rubber powder 2-7, solid paraffin
5-15, soybean oil 30-45, epoxidized soybean oil 1-3, second line of distillation is oily or subtracts third fractional oil 2-3, solvent naphtha 15-25, cyclic acid anhydride type phase
Hold agent 0.5-0.8.
2. a kind of uncured modified asphalt waterproofing paint according to claim 1, it is characterised in that: the thermoplasticity butylbenzene
The granularity of rubber powder is in 90-120, silicone rubber powder 30-60.
3. a kind of uncured modified asphalt waterproofing paint according to claim 1, it is characterised in that: the solvent naphtha is
120# rubber solvent naphtha or 200# paint naphtha.
4. the preparation method of any one of -2 uncured modified asphalt waterproofing paints according to claim 1, it is characterised in that: packet
Include following steps,
A) it is stirred evenly after thermoplastic styrene butadiene rubber is added after soybean oil being warming up to 160-180 DEG C, obtains mixed liquor one,
B) solid paraffin, thermoplastic styrene butadiene rubber powder are added in the mixed liquor one and stirs evenly, is subsequently added into silicon rubber
Rubber powder end simultaneously stirs evenly, and obtains mixed liquor two,
C) by the second line of distillation oil and subtract one of third fractional oil and pitch, the solvent naphtha, the epoxidized soybean oil, described
Cyclic acid anhydride type compatilizer is added into the mixed liquor two, and it is 160 ± 10 DEG C that the temperature of mixed liquor two is kept in this step.