CN109456569A - A kind of environment-friendly type foam board - Google Patents
A kind of environment-friendly type foam board Download PDFInfo
- Publication number
- CN109456569A CN109456569A CN201811025128.8A CN201811025128A CN109456569A CN 109456569 A CN109456569 A CN 109456569A CN 201811025128 A CN201811025128 A CN 201811025128A CN 109456569 A CN109456569 A CN 109456569A
- Authority
- CN
- China
- Prior art keywords
- parts
- foam board
- environment
- friendly type
- stabilizer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of environment-friendly type foam boards, the foam board is made of following components by mass fraction: 30-40 parts of thermosetting phenolic resin, 10-20 parts of stearic acid, 2-5 parts of metallocene PE A, 10-20 parts of ammonium polyphosphate, 2-5 parts of flyash, 1-3 parts of surfactant, 5-10 parts of refractory fibre mixture, 1-3 parts of fire retardant, 1-3 parts of stabilizer.The invention has the beneficial effects that: preparation process is simple, low raw-material cost, realizes the efficient utilization of flyash, reduces its pollution to environment, fire resistance is good, is suitable for popularization and application.
Description
Technical field
The present invention relates to foam board manufacture fields, are specifically related to a kind of environment-friendly type foam board.
Background technique
Polystyrene foam plate-- also known as cystosepiment, EPS sheet are gathered by the expandability containing volatile fluid foaming agent
Styrene beads, the white object of hot briquetting in a mold after heated pre- hair, have the design feature of fine closed pore, mainly
For construction wall, roof heat insulation, composite plate heat preservation, freezer, air-conditioning, vehicle, ship insulation, floor heating, decoration
The purposes such as engraving are very extensive.
Summary of the invention
The object of the present invention is to provide a kind of environment-friendly type foam board, the foam board presses mass parts by following components
Array at: 30-40 parts of thermosetting phenolic resin, 10-20 parts of stearic acid, 2-5 parts of metallocene PE A, ammonium polyphosphate 10-
20 parts, 2-5 parts of flyash, 1-3 parts of surfactant, 5-10 parts of refractory fibre mixture, 1-3 parts of fire retardant, stabilizer 1-3
Part.
It is further preferred that the foam board is made of following components by mass fraction: thermosetting phenolic resin 40
Part, 20 parts of stearic acid, 5 parts of metallocene PE A, 20 parts of ammonium polyphosphate, 5 parts of flyash, 3 parts of surfactant, fire resisting is fine
10 parts of mixture, 3 parts of fire retardant, 3 parts of stabilizer of dimension.
It is further preferred that the foam board is made of following components by mass fraction: thermosetting phenolic resin 30
Part, 10 parts of stearic acid, 2 parts of metallocene PE A, 10 parts of ammonium polyphosphate, 2 parts of flyash, 1 part of surfactant, fire resisting is fine
5 parts of mixture, 1 part of fire retardant, 1 part of stabilizer of dimension.
It is further preferred that the foam board is made of following components by mass fraction: thermosetting phenolic resin 35
Part, 15 parts of stearic acid, 3 parts of metallocene PE A, 15 parts of ammonium polyphosphate, 3 parts of flyash, 2 parts of surfactant, fire resisting is fine
7 parts of mixture, 2 parts of fire retardant, 2 parts of stabilizer of dimension.
The stabilizer is dibutyl two (lauric acid/dodecanoic acid) tin, zinc stearate, epoxidized soybean oil, tin dilaurate di-n-octyl
One of tin is several.
The fire retardant is one of antimony trioxide, magnesium hydroxide or two kinds.
The invention has the beneficial effects that: preparation process is simple, low raw-material cost, realizes the efficient benefit of flyash
With reducing its pollution to environment, fire resistance is good, is suitable for popularization and application.
Specific embodiment
In order to deepen the understanding of the present invention and recognize, the present invention is made further With reference to embodiment
Illustrate and introduces.
Embodiment 1
A kind of environment-friendly type foam board, the foam board are made of following components by mass fraction: thermosetting phenolic
40 parts of resin, 20 parts of stearic acid, 5 parts of metallocene PE A, 20 parts of ammonium polyphosphate, 5 parts of flyash, 3 parts of surfactant,
10 parts of refractory fibre mixture, 3 parts of fire retardant, 3 parts of stabilizer.
The stabilizer is dibutyl two (lauric acid/dodecanoic acid) tin, zinc stearate, epoxidized soybean oil, tin dilaurate di-n-octyl
One of tin is several.
The fire retardant is one of antimony trioxide, magnesium hydroxide or two kinds.
Embodiment 2
A kind of environment-friendly type foam board, the foam board are made of following components by mass fraction: thermosetting phenolic
30 parts of resin, 10 parts of stearic acid, 2 parts of metallocene PE A, 10 parts of ammonium polyphosphate, 2 parts of flyash, 1 part of surfactant,
5 parts of refractory fibre mixture, 1 part of fire retardant, 1 part of stabilizer.
The stabilizer is dibutyl two (lauric acid/dodecanoic acid) tin, zinc stearate, epoxidized soybean oil, tin dilaurate di-n-octyl
One of tin is several.
The fire retardant is one of antimony trioxide, magnesium hydroxide or two kinds.
Embodiment 3
A kind of environment-friendly type foam board, the foam board are made of following components by mass fraction: thermosetting phenolic
35 parts of resin, 15 parts of stearic acid, 3 parts of metallocene PE A, 15 parts of ammonium polyphosphate, 3 parts of flyash, 2 parts of surfactant,
7 parts of refractory fibre mixture, 2 parts of fire retardant, 2 parts of stabilizer.
The stabilizer is dibutyl two (lauric acid/dodecanoic acid) tin, zinc stearate, epoxidized soybean oil, tin dilaurate di-n-octyl
One of tin is several.
The fire retardant is one of antimony trioxide, magnesium hydroxide or two kinds.
Claims (6)
1. a kind of environment-friendly type foam board, which is characterized in that the foam board is made of following components by mass fraction: heat
30-40 parts of solidity phenolic resin, 10-20 parts of stearic acid, 2-5 parts of metallocene PE A, 10-20 parts of ammonium polyphosphate, fine coal
It is 2-5 parts grey, 1-3 parts of surfactant, 5-10 parts of refractory fibre mixture, 1-3 parts of fire retardant, 1-3 parts of stabilizer.
2. a kind of environment-friendly type foam board according to claim 1, which is characterized in that the foam board is by with the following group
Divide and is formed by mass fraction: 40 parts of thermosetting phenolic resin, 20 parts of stearic acid, 5 parts of metallocene PE A, ammonium polyphosphate 20
Part, 5 parts of flyash, 3 parts of surfactant, 10 parts of refractory fibre mixture, 3 parts of fire retardant, 3 parts of stabilizer.
3. a kind of environment-friendly type foam board according to claim 1, which is characterized in that the foam board is by with the following group
Divide and is formed by mass fraction: 30 parts of thermosetting phenolic resin, 10 parts of stearic acid, 2 parts of metallocene PE A, ammonium polyphosphate 10
Part, 2 parts of flyash, 1 part of surfactant, 5 parts of refractory fibre mixture, 1 part of fire retardant, 1 part of stabilizer.
4. a kind of environment-friendly type foam board according to claim 1, which is characterized in that the foam board is by with the following group
Divide and is formed by mass fraction: 35 parts of thermosetting phenolic resin, 15 parts of stearic acid, 3 parts of metallocene PE A, ammonium polyphosphate 15
Part, 3 parts of flyash, 2 parts of surfactant, 7 parts of refractory fibre mixture, 2 parts of fire retardant, 2 parts of stabilizer.
5. a kind of environment-friendly type foam board according to claim 1, which is characterized in that the stabilizer is dibutyl two
One of (lauric acid/dodecanoic acid) tin, zinc stearate, epoxidized soybean oil, Bis(lauroyloxy)dioctyltin are several.
6. a kind of environment-friendly type foam board according to claim 1, which is characterized in that the fire retardant is three oxidations
One of antimony, magnesium hydroxide or two kinds.