CN109455012A - A kind of chromaticity printing production technology of aluminium-base composite plate - Google Patents
A kind of chromaticity printing production technology of aluminium-base composite plate Download PDFInfo
- Publication number
- CN109455012A CN109455012A CN201811132282.5A CN201811132282A CN109455012A CN 109455012 A CN109455012 A CN 109455012A CN 201811132282 A CN201811132282 A CN 201811132282A CN 109455012 A CN109455012 A CN 109455012A
- Authority
- CN
- China
- Prior art keywords
- aluminium
- composite plate
- base composite
- glue film
- aluminium sheet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of chromaticity printing production technology of aluminium-base composite plate, including provide and roll aluminium sheet coiled material and glue film coiled material, aluminium sheet is sprawled along horizontal direction, aluminium sheet is carried out dehydrating, by chromatography roller in surface of aluminum plate chromatic jet printing layer, gloss oil processing is carried out to set chromatograph, aluminium sheet and glue film is sprawled simultaneously along horizontal direction, covers glue film, drying on set chromatograph by gloss oil machine after acquisition aluminium-base composite plate, painted, be dehydrated to aluminium-base composite plate, being dried and correction process；Using technical solution of the present invention, by first coating set chromatograph, the technique for covering glue film again, make glue film be easier to be connected as one with aluminium substrate, and also carry out set chromatograph using gloss oil machine and carry out gloss oil processing, keeps set chromatograph uniform in the surface of aluminum plate layout thickness, make the surface of aluminium-base composite plate obtained more evenly, it is smooth, product quality is improved, by being painted, being dehydrated to aluminium-base composite plate, dried and correction process, improves product appearance and quality.
Description
Technical field
The present invention relates to aluminium-base composite plate manufacturing process technology field more particularly to a kind of chromaticity printings of aluminium-base composite plate
Production technology.
Background technique
Aluminium-base composite plate is aluminium and its aluminum alloy plate materials as substrate, passes through the compound of attachment other materials on the surface thereof
Plate, compares individual aluminum alloy plate materials, and aluminium-base composite plate changes due to being provided with multilayer others adhesive layer according to various demands
It has been apt to the physical property of aluminium-base composite plate, has made it have the excellent performance such as high temperature resistant, fire prevention, heat preservation, heat-insulated, simultaneously as
Substrate is aluminum or aluminum alloy, very light weight, is commonly used for home decoration, furniture, the surface covering parts on household electrical appliance, by
Its surface sprays the paint vehicle of various colors, or the various textures of production, can further promote the appearance of aluminium-base composite plate, be promoted and produced
Product quality, makes enterprise win the market.In the prior art, for the manufacture of this aluminium-base composite plate, mostly use greatly manual method into
Row manufacture, since the quality of aluminium sheet and glue film is very light, it is difficult to sprawl it is smooth, and in pressing, by shadows such as wind, vibrations
It rings, causes raw material to be easy displacement, affect the quality of production of aluminium-base composite plate, while production efficiency is lower.
Summary of the invention
In order to solve the above technical problems, the present invention provides a kind of chromaticity printing production technologies of aluminium-base composite plate.
The present invention is achieved by the following technical programs.
The present invention provides a kind of chromaticity printing production technology of aluminium-base composite plate, comprising the following steps:
Step 1: offer rolls aluminium sheet coiled material, is wound with multi-turn aluminium sheet on the aluminium sheet coiled material；
Step 2: apply active force to the aluminium sheet end being wound in aluminium sheet coiled material described in step 1, make the aluminium sheet
It is at the uniform velocity sprawled along horizontal direction；
Step 3: extend to aluminium sheet described in step 2 at one layer of oil is sprayed on horizontal surface, obtained in surface of aluminum plate
One layer of set chromatograph；
Step 4: the surface that chromatograph is covered described in step 3 covers one layer of glue film；
Step 5: toasting the aluminium sheet for being attached with set chromatograph, glue film, makes oil solidification therein, by rubber moulding and aluminium sheet
It is connected as one, obtains aluminium-base composite plate.
Aluminium sheet described in step 2 is less than 500mm/s along the speed that horizontal direction is at the uniform velocity sprawled.
One layer of set chromatograph is obtained in surface of aluminum plate described in step 3, further comprising the steps of:
Step 1: chromatography roller is provided；
Step 2: while sprawling the aluminium sheet at the uniform velocity along horizontal direction, chromatography described in surface of aluminum plate and step 1
Roller outer peripheral surface is tangent；
Step 3: to chromatography roller outer peripheral surface upper oil plant.
The chromaticity printing production technology of the aluminium-base composite plate further include after carrying out step 3, it is right before step 4
The set chromatograph carries out gloss oil processing using gloss oil machine, keeps set chromatograph uniform in the surface of aluminum plate layout thickness.
Described in step 4 set chromatograph surface cover one layer of glue film the following steps are included:
Step 1: offer rolls glue film coiled material, is wound with multi-turn glue film on the glue film coiled material；
Step 2: will be attached with the aluminium sheet end of set chromatograph with after the glue film end part aligning that is wound on glue film coiled material to it
Apply active force, makes it along horizontal direction while at the uniform velocity sprawling, be covered in glue film on aluminium sheet during sprawling.
The chromaticity printing production technology of the aluminium-base composite plate further includes after carrying out step 5, further includes following step
It is rapid:
Step 1: the surface lacquer of the aluminium-base composite plate of acquisition is handled:；
Step 2: the aluminium-base composite plate having by spray painting processing is carried out dehydrating；
Step 3: the aluminium-base composite plate described in baking step 2 after dehydration；
Step 4: the aluminium-base composite plate in aligning step 3 after drying and processing.
It include simultaneously to the upper and lower of aluminium-base composite plate to the surface lacquer processing of the aluminium-base composite plate of acquisition in step 1
It paints simultaneously on surface.
Being carried out dehydrating in step 2 to the aluminium-base composite plate is carried out dehydrating using wringing machine.
Being corrected processing to the aluminium-base composite plate in step 4 is to be corrected processing using uncoiling tension machine.
The chromaticity printing production technology of the aluminium-base composite plate further includes making the aluminium sheet edge before carrying out step 3
Horizontal direction while at the uniform velocity sprawl, be carried out dehydrating using the part that wringing machine has sprawled the aluminium sheet.
The beneficial effects of the present invention are: technical solution of the present invention is used, aluminium sheet coiled material is directly made to make aluminum-base composite
Plate then covers the technique of glue film by covering chromatograph in the technique of overlay film to one layer of its external coating, is easier glue film and aluminium base
Plate is connected as one, and is also carried out set chromatograph using gloss oil machine and carried out gloss oil processing, makes to cover chromatograph in the surface of aluminum plate cloth
Set that thickness is uniform, make the surface of aluminium-base composite plate obtained more evenly, it is smooth, product quality is improved, in addition, direct when overlay film
It is made using glue film coiled material, by applying horizontal pull difference appropriate to it for glue film coiled material and aluminium sheet coiled material end part aligning
Make aluminium sheet coiled material and glue film coiled material synchronous expansion, then handled by hot setting, is attached together aluminium sheet tightly with glue film,
The preparation process for simplifying existing aluminium-base composite plate can also be corrected aluminium-base composite plate in rear process, apply on its surface
The paint of other colors, or the various textures of production are brushed, to promote the appearance and production quality of aluminium-base composite plate.
Detailed description of the invention
Fig. 1 is process flow chart of the invention.
Specific embodiment
Be described further below technical solution of the present invention, but claimed range be not limited to it is described.
The present invention provides a kind of chromaticity printing production technology of aluminium-base composite plate, as shown in Figure 1, comprising the following steps:
Step 1: offer rolls aluminium sheet coiled material, and multi-turn aluminium sheet is wound on aluminium sheet coiled material；
Step 2: the aluminium sheet end being wound in aluminium sheet coiled material into step 1 applies active force, makes aluminium sheet along level
It at the uniform velocity sprawls in direction；Further, it is preferable to which aluminium sheet is less than 500mm/s along the speed that horizontal direction is at the uniform velocity sprawled.
Furthermore it is preferred that the chromaticity printing production technology of aluminium-base composite plate further includes making aluminium sheet before carrying out step 3
While at the uniform velocity being sprawled along horizontal direction, the part that aluminium sheet has been sprawled is carried out dehydrating using wringing machine.
Step 3: into step 2, aluminium sheet extends at one layer of oil is sprayed on horizontal surface, obtains one layer in surface of aluminum plate
Cover chromatograph；Further, the chromaticity printing production technology of aluminium-base composite plate further include after carrying out step 3, step 4 it
Before, gloss oil processing is carried out using gloss oil machine to set chromatograph, keeps set chromatograph uniform in surface of aluminum plate layout thickness.
Step 4: the surface that chromatograph is covered in step 3 covers one layer of glue film；
Step 5: toasting the aluminium sheet for being attached with set chromatograph, glue film, makes oil solidification therein, by rubber moulding and aluminium sheet
It is connected as one, obtains aluminium-base composite plate.
In addition, one layer of set chromatograph is obtained in surface of aluminum plate in step 3, it is further comprising the steps of:
Step 1: chromatography roller is provided；
Step 2: while sprawling aluminium sheet at the uniform velocity along horizontal direction, chromatography roller outer peripheral surface in surface of aluminum plate and step 1
It is tangent；
Step 3: to chromatography roller outer peripheral surface upper oil plant.
Further, in step 4 set chromatograph surface cover one layer of glue film the following steps are included:
Step 1: offer rolls glue film coiled material, and multi-turn glue film is wound on glue film coiled material；
Step 2: will be attached with the aluminium sheet end of set chromatograph with after the glue film end part aligning that is wound on glue film coiled material to it
Apply active force, makes it along horizontal direction while at the uniform velocity sprawling, be covered in glue film on aluminium sheet during sprawling.
Further, the chromaticity printing production technology of aluminium-base composite plate further include after carrying out step 5, further include with
Lower step:
Step 1: the surface lacquer of the aluminium-base composite plate of acquisition is handled:；Further, to the aluminium-base composite plate of acquisition
Surface lacquer processing includes painting simultaneously to the upper and lower surface of aluminium-base composite plate simultaneously.
Step 2: the aluminium-base composite plate having by spray painting processing is carried out dehydrating；Further, to aluminium-base composite plate
Be carried out dehydrating is carried out dehydrating using wringing machine.
Step 3: the aluminium-base composite plate in baking step 2 after dehydration；
Step 4: the aluminium-base composite plate in aligning step 3 after drying and processing.Further, aluminium-base composite plate is carried out
Correction process is corrected processing using uncoiling tension machine.
Using technical solution of the present invention, aluminium sheet coiled material is directly made to make aluminium-base composite plate, by its external coating one
Layer covers chromatograph in the technique of overlay film, then covers the technique of glue film, makes glue film be easier to be connected as one with aluminium substrate, and also make
Set chromatograph is carried out with light oil machine and carries out gloss oil processing, keeps set chromatograph uniform in surface of aluminum plate layout thickness, keeps aluminium base obtained multiple
The surface of plywood more evenly, it is smooth, product quality is improved, in addition, directly use glue film coiled material to make when overlay film, by by glue
Film coiled material and aluminium sheet coiled material end part aligning, apply horizontal pull appropriate to it makes the exhibition synchronous with glue film coiled material of aluminium sheet coiled material respectively
It opens, then is handled by hot setting, be attached together aluminium sheet tightly with glue film, simplify the preparation of existing aluminium-base composite plate
Technique can also be corrected aluminium-base composite plate in rear process, each in the paint of other colors of its external coating, or production
Kind texture, to promote the appearance and production quality of aluminium-base composite plate.
Claims (10)
1. a kind of chromaticity printing production technology of aluminium-base composite plate, it is characterised in that: the following steps are included:
Step 1: offer rolls aluminium sheet coiled material, is wound with multi-turn aluminium sheet on the aluminium sheet coiled material；
Step 2: applying active force to the aluminium sheet end that is wound in aluminium sheet coiled material described in step 1, make the aluminium sheet along
Horizontal direction is at the uniform velocity sprawled；
Step 3: extend to aluminium sheet described in step 2 at one layer of oil is sprayed on horizontal surface, obtain one layer in surface of aluminum plate
Cover chromatograph；
Step 4: the surface that chromatograph is covered described in step 3 covers one layer of glue film；
Step 5: toasting the aluminium sheet for being attached with set chromatograph, glue film, makes oil solidification therein, rubber moulding is connect with aluminium sheet
It is integrated, obtains aluminium-base composite plate.
2. a kind of chromaticity printing production technology of aluminium-base composite plate as described in claim 1, it is characterised in that: institute in step 2
It states aluminium sheet and is less than 500mm/s along the speed that horizontal direction is at the uniform velocity sprawled.
3. a kind of chromaticity printing production technology of aluminium-base composite plate as described in claim 1, it is characterised in that: institute in step 3
It states and obtains one layer of set chromatograph in surface of aluminum plate, further comprising the steps of:
Step 1: chromatography roller is provided；
Step 2: while sprawling the aluminium sheet at the uniform velocity along horizontal direction, outside chromatography roller described in surface of aluminum plate and step 1
Circumferential surface is tangent；
Step 3: to chromatography roller outer peripheral surface upper oil plant.
4. a kind of chromaticity printing production technology of aluminium-base composite plate as described in claim 1, it is characterised in that: the aluminium base is multiple
The chromaticity printing production technology of plywood further includes before step 4, using gloss oil to the set chromatograph after carrying out step 3
Machine carries out gloss oil processing, keeps set chromatograph uniform in the surface of aluminum plate layout thickness.
5. a kind of chromaticity printing production technology of aluminium-base composite plate as described in claim 1, it is characterised in that: institute in step 4
State set chromatograph surface cover one layer of glue film the following steps are included:
Step 1: offer rolls glue film coiled material, is wound with multi-turn glue film on the glue film coiled material；
Step 2: the aluminium sheet end for being attached with set chromatograph is applied with after the glue film end part aligning being wound on glue film coiled material to it
Active force makes it along horizontal direction while at the uniform velocity sprawling, is covered in glue film on aluminium sheet during sprawling.
6. a kind of chromaticity printing production technology of aluminium-base composite plate as described in claim 1, it is characterised in that: the aluminium base is multiple
The chromaticity printing production technology of plywood further include after carrying out step 5, it is further comprising the steps of:
Step 1: the surface lacquer of the aluminium-base composite plate of acquisition is handled:；
Step 2: the aluminium-base composite plate having by spray painting processing is carried out dehydrating；
Step 3: the aluminium-base composite plate described in baking step 2 after dehydration；
Step 4: the aluminium-base composite plate in aligning step 3 after drying and processing.
7. a kind of chromaticity printing production technology of aluminium-base composite plate as claimed in claim 6, it is characterised in that: right in step 1
The surface lacquer processing of the aluminium-base composite plate obtained includes painting simultaneously to the upper and lower surface of aluminium-base composite plate simultaneously.
8. a kind of chromaticity printing production technology of aluminium-base composite plate as claimed in claim 6, it is characterised in that: right in step 2
The aluminium-base composite plate, which is carried out dehydrating, to be carried out dehydrating using wringing machine.
9. a kind of chromaticity printing production technology of aluminium-base composite plate as claimed in claim 6, it is characterised in that: right in step 4
It is to be corrected processing using uncoiling tension machine that the aluminium-base composite plate, which is corrected processing,.
10. a kind of chromaticity printing production technology of aluminium-base composite plate as described in claim 1, it is characterised in that: the aluminium base
The chromaticity printing production technology of composite plate further includes spreading the aluminium sheet at the uniform velocity along horizontal direction before carrying out step 3
While exhibition, it is carried out dehydrating using the part that wringing machine has sprawled the aluminium sheet.