CN109454963A - A kind of antistatic composite thermal fabric - Google Patents
A kind of antistatic composite thermal fabric Download PDFInfo
- Publication number
- CN109454963A CN109454963A CN201811415236.6A CN201811415236A CN109454963A CN 109454963 A CN109454963 A CN 109454963A CN 201811415236 A CN201811415236 A CN 201811415236A CN 109454963 A CN109454963 A CN 109454963A
- Authority
- CN
- China
- Prior art keywords
- antistatic
- lining
- composite thermal
- thermal fabric
- face cloth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of antistatic composite thermal fabric, including face cloth and lining, face cloth and lining are bonded to each other, and all have preset thickness;Antistatic wire mesh is woven in lining.It is simple that the beneficial effects of the invention are as follows structures, has good antistatic property, while warming, moisture absorbing and sweat releasing, crease-resistant and ventilative performance are preferable, practicability is stronger.
Description
Technical field
The present invention relates to belong to technical field of textile fabric, and in particular to a kind of antistatic composite thermal fabric.
Background technique
With the improvement of living standards, people are higher and higher for the various functions needs of fabric, fabric is for making
The material of clothes, it can not only annotate the style and characteristic of clothes, but also directly control the performance of the color of clothes, moulding
Effect.
Traditional antibacterial fabric only has single function, and many fabrics do not have antistatic function, and fabric is in drying
Winter it is easy to produce static electricity, cause harm to the human body, especially to the elderly, it is easier to be influenced by electrostatic.Cardiovascular system
Natively there is a elderly of various lesions, electrostatic but will aggravate disease or induce the arrhythmia cordis such as ventricular premature beat.Excessively high is quiet
Electricity also usually makes one lather, headache, uncomfortable in chest, expiratory dyspnea, cough.
Fabric in the prior art, the method for mostly using auxiliary agent to handle eliminates electrostatic, but after repeatedly washing, resists quiet
Electric effect can be worse and worse.
Summary of the invention
Technical problem to be solved by the invention is to provide a kind of antistatic composite thermal fabrics, it is intended to solve background technique
The problems in.
The technical scheme to solve the above technical problems is that
A kind of antistatic composite thermal fabric, including face cloth and lining, the face cloth and the lining are bonded to each other, and
With preset thickness;Antistatic wire mesh is woven in the lining.
The beneficial effects of the present invention are: that the beneficial effects of the invention are as follows structures is simple, there is good antistatic property, together
Shi Baonuan, moisture absorbing and sweat releasing, crease-resistant and ventilative performance are preferable, and practicability is stronger.
Based on the above technical solution, the present invention can also be improved as follows.
Further, the face cloth is Oxford spinning or T/C plain cloth.
Beneficial effect using above-mentioned further scheme is that frivolous with quality, soft, good waterproof performance, durability are good
Performance, while crease-resistant and permeability is preferable.
Further, the lining is to wash not fall suede entirely.
Beneficial effect using above-mentioned further scheme is soft, warm good warmth retention effect.
Anti-metal silk screen described further is formed by several antistatic metal wire knitteds.
Beneficial effect using above-mentioned further scheme is that structure is simple, easy to make.
Further, several antistatic wires are interweaved to form the antistatic wire by warp and weft
Net.
Beneficial effect using above-mentioned further scheme is that structure is simple, easy to make.
Further, the face cloth and the lining are pasted by adhesive.
Beneficial effect using above-mentioned further scheme is that production is simple.
Further, described adhesive is polyurethane.
Beneficial effect using above-mentioned further scheme is that cohesive force is strong, good hand touch, and good permeability does not influence the color of face cloth
Degree.
Further, the thickness ratio of the face cloth and the lining is 1:(2-3).
Beneficial effect using above-mentioned further scheme is that its thickness is moderate, and texture and comfort level are preferable.
Further, the weight of every square metre of the thermal fabric is (250-550) g.
Beneficial effect using above-mentioned further scheme be it is light-weight, comfort level is preferable.
Detailed description of the invention
Fig. 1 is the structural diagram of the present invention;
Fig. 2 is the structural schematic diagram of antistatic wire mesh in the present invention.
In attached drawing, parts list represented by the reference numerals are as follows:
1, face cloth, 2, lining, 3, antistatic wire mesh.
Specific embodiment
Principles and features of the present invention are described below in conjunction with drawings and the specific embodiments, example is served only for solving
The present invention is released, is not intended to limit the scope of the present invention.
As depicted in figs. 1 and 2, the present invention provides a kind of antistatic composite thermal fabric, including face cloth 1 and lining 2, face cloth
1 and lining 2 be bonded to each other, and all have preset thickness;Antistatic wire mesh 3 is woven in lining 2.Of the invention is beneficial
Effect is that structure is simple, has good antistatic property, while warming and moisture absorbing and sweat releasing effect is preferable, practicability compared with
By force.
In the present invention, lining 2 is to wash not fall suede entirely, not the production of falling velvet fabric clothes, so that clothes have gloss fabulous, rich
The many merits such as flexible, soft and warmth retention property is good, it is very popular and pursue, the quilt in Modern Home Textile industry
It is a large amount of to use.
Embodiment 1
In the present embodiment, face cloth 1 is Oxford spinning, and Oxford textile fabric has the advantage that first, and Oxford textile fabric has resistance to
Mill, it is resistance to fall and the superperformance of pressure resistance, Oxford textile fabric itself has certain toughness, and crease-resistant and permeability is preferable, because
This is longer using the time, save the cost;Second, Oxford textile fabric can be prevented scratching, and it is close, solid that material is spun in Oxford;Third, when use
Between it is long, can still keep original complexion after using for a longer period.
Embodiment 2
The difference between this embodiment and the first embodiment lies in: face cloth 1 is T/C plain cloth, has quality frivolous, soft, anti-
Aqueous performance good, durability is good, crease-resistant and permeability are preferable.Wherein T is terylene, the abbreviation generation of TERYLENE (polyester-cotton blend)
Code;C is cotton, the abbreviation code of COTTON (cotton);And before the biggish composition of accounting example is placed on composition statement by habit of weaving
Face, so T/C is exactly the polyester-mixed cotton cloth that terylene accounts for main body ratio.In T/C, 20 × 16 refer to through to the yarn of washing for being 20, and broadwise is
16 cotton yarns, 128 × 60 refer to density, there is 128, warp thread, weft yarn 60 in every 1 inch.
In addition, also there are good moisture absorption sweat discharging functions using shirt made of above-mentioned fabric.
In the present invention, anti-metal silk screen 3 is formed by several antistatic metal wire knitteds, and several antistatic wires press warp
Be interweaved with weft to form antistatic wire mesh 3, i.e., be distributed along the length direction or width direction of lining 2, it is adjacent and
The spacing between two antistatic wires being parallel to each other is 0.5~1.0cm, and entire antistatic wire mesh 3 is reasonably distributed,
Size design is moderate, so that surface layer antistatic property is preferable.
It should be noted that antistatic wire mesh 3 is woven using the electric conductivity of wire, wherein antistatic
Wire is made from the electric conductivity using metal, and main method is direct fiber elongation method, and metal wire is crossed to mold repeatedly, is drawn
It stretches, the filament that diameter is 4~16 μm is made.Common metal has stainless steel, copper, aluminium, gold, silver etc..Similar method is also cut
Method is cut, metal is directly cut into the filament of threadiness.In addition, there are also spray-gun process, general fibre is first carried out at surface
Reason, then fiber surface is deposited metal in airless spraying or chemical-electrical plating method, the electric conductivity for making fiber have metal the same.It is anti-
The conducting electricity very well of electrostatic metal silk screen 3, resistivity are low.
Antistatic wire refers to that (20 DEG C, 65% relative humidity) volume resistivity is less than 10 in normal conditions10Ω·
The fiber of cm or static charge dissipation half-life period are less than the fiber of 60s.Antistatic wire is not easy build up of electrostatic charge.Such as the electricity of silver
Resistance rate is 1.65 × 10-6Ω cm, the resistivity of copper are 1.75 × 10-6Ω cm, the resistivity of aluminium are 2.83 × 10-6Ω·
cm.By above-mentioned data it is found that the resistivity of antistatic metal is all smaller, antistatic effect is preferable.
In addition, the antistatic of fabric generallys use antistatic dosage form antistatic fibre in the prior art, antistatic dosage form is anti-
Electrostatic fibre processing technology is simple, and antistatic agent influences original performance of fiber less, to form conduction in fiber surface
Layer, reduces its surface resistivity, leaks the electrostatic generated rapidly.Meanwhile can also assign the certain lubricity of fiber surface with
Coefficient of friction is reduced, the generation of electrostatic charge is inhibited and reduce.Common antistatic agent is mainly some surfactants, molecule
Contain two kinds of groups of lipophilic group and hydrophilic group in structure.For lipophilic group in conjunction with polymer, hydrophilic group is arranged in material towards air
Surface is formed " moisture film ".Therefore, the using effect of antistatic agent depends on dosage and many extraneous factors, such as temperature, relatively wet
Degree etc..And the antistatic wire mesh 3 in the application is woven in lining 2, is not influenced by extraneous factor, antistatic effect compared with
It is good.
In the present invention, face cloth 1 and lining 2 are pasted by adhesive, and adhesive is preferably polyurethane, the cohesive force of polyurethane
By force, good hand touch, good permeability do not influence the coloration of face cloth 1, will not influence the quality of entire fabric.
In the present invention, the thickness ratio of face cloth 1 and lining 2 is 1:(2-3), entire composite thermal fabric with a thickness of (0.5-
2.0) mm, preferably (0.8-1.8) mm.
In the present invention, the weight of every square metre of thermal fabric is (250-550) g, preferably (300-450) g.
The manufacture craft of thermal fabric disclosed in this invention is as follows:
S1: having debugged hot melt adhesive compounding machine, while the size of check surface cloth 1 and lining 2,2 specific surface cloth of lining, 1 width 2-5cm,
Lining 2 takes the width of setting according to production requirement;
S2: mounting surface cloth 1 and lining 2 are rolled up greatly, and face cloth 1 is mounted on head, and lining 2 is mounted on machine, and face cloth 1 and lining 2 are anti-
To unreeling;
S3: head is into face cloth 1, while upper hot melt adhesive, and for tail into lining 2, the two is bonded it, solidifies to hot melt adhesive.
It should be noted that hot melt adhesive compounding machine (model FS-66TYPE) is the prior art, how into face cloth 1 and lining 2
Also it is the prior art, is well known to those of ordinary skill in the art;Hot melt adhesive compounding machine is electrically connected with the controller, controller with
Control circuit between hot melt adhesive compounding machine is the prior art.
In addition, the temperature of hot melt adhesive needs to reach 110 DEG C, pressure during making thermal fabric disclosed in this invention
Power needs to reach 8Pa, and it is 7-8r/min that hot melt adhesive compounding machine, which send the speed of fabric,;Face cloth 1 and lining 2 need after the completion of applying glue bond
Stand 8-10 hours, it is ensured that the quality of bonding.
After fabric completes, need to carry out quality testing to fabric, produce qualified fabric need to meet it is claimed below:
First, it is washed 50 times/24 hours through washing machine, face cloth 1 and lining 2 do not disengage, and the smooth no bubbling of cloth cover, feel is changed
It is kind;Second, free from extraneous odour is surveyed pH value and content of formaldehyde and meets national fabric environmental requirement.
The foregoing is merely presently preferred embodiments of the present invention, is not intended to limit the invention, it is all in spirit of the invention and
Within principle, any modification, equivalent replacement, improvement and so on be should all be included in the protection scope of the present invention.
Claims (9)
1. a kind of antistatic composite thermal fabric, it is characterised in that: including face cloth (1) and lining (2), the face cloth (1) and institute
It states lining (2) to be bonded to each other, and all has preset thickness;Antistatic wire mesh (3) are woven in the lining (2).
2. a kind of antistatic composite thermal fabric according to claim 1, it is characterised in that: the face cloth (1) is Oxford
Spinning or T/C plain cloth.
3. a kind of antistatic composite thermal fabric according to claim 1, it is characterised in that: the lining (2) is Quan Di
Not fall suede.
4. a kind of antistatic composite thermal fabric according to claim 1, it is characterised in that: the anti-metal silk screen (3)
It is formed by several antistatic metal wire knitteds.
5. a kind of antistatic composite thermal fabric according to claim 4, it is characterised in that: several antistatic metals
Silk is interweaved to form the antistatic wire mesh (3) by warp and weft.
6. a kind of antistatic composite thermal fabric according to claim 1-5, it is characterised in that: the face cloth
(1) it is pasted with the lining (2) by adhesive.
7. a kind of antistatic composite thermal fabric according to claim 6, it is characterised in that: described adhesive is poly- ammonia
Ester.
8. a kind of antistatic composite thermal fabric according to claim 1-5, it is characterised in that: the face cloth
(1) and the thickness ratio of the lining (2) is 1:(2-3).
9. a kind of antistatic composite thermal fabric according to claim 1-5, it is characterised in that: the thermal surface
The weight for expecting every square metre is (250-550) g.