CN109439111A - A kind of continuous phase emulsion of freeze thawing resistance water-soluble colorful coating, freeze thawing resistance water-soluble colorful coating and preparation method thereof - Google Patents
A kind of continuous phase emulsion of freeze thawing resistance water-soluble colorful coating, freeze thawing resistance water-soluble colorful coating and preparation method thereof Download PDFInfo
- Publication number
- CN109439111A CN109439111A CN201811072135.3A CN201811072135A CN109439111A CN 109439111 A CN109439111 A CN 109439111A CN 201811072135 A CN201811072135 A CN 201811072135A CN 109439111 A CN109439111 A CN 109439111A
- Authority
- CN
- China
- Prior art keywords
- freeze thawing
- continuous phase
- thawing resistance
- colorful coating
- soluble colorful
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention provides a kind of continuous phase emulsion of freeze thawing resistance water-soluble colorful coating, freeze thawing resistance water-soluble colorful coating and preparation method thereof, and the continuous phase emulsion of the freeze thawing resistance water-soluble colorful coating comprises the following components in parts by weight: 2-5 parts of bentonite;450-550 parts of silicone acrylic emulsion;35-45 parts of anti-icing fluid;20-30 parts of coalescing agent;0.1-5 parts of defoaming agent;0.5-5 parts of pH adjusting agent;2-8 parts of thickener;2-5 parts of sterilization antiseptic;200-250 parts of deionized water.The present invention prepares continuous phase emulsion by screening suitable auxiliary agent and lotion, guarantees product freeze-thaw stability, avoids the occurrence of the broken point of colorful particle and increase, and color spot is partially soft and color spot is freezing, the bad phenomenons such as rear thickening.
Description
Technical field
The present invention relates to technical field of coatings, specifically disclose a kind of freeze thawing resistance water-soluble colorful coating continuous phase emulsion,
Freeze thawing resistance water-soluble colorful coating and preparation method thereof.
Background technique
Liquid stone multicolor finish is rich in color with its, easy for construction, and primary spraying obtains the decorative effect of rock, and valence
Lattice economical rationality, the later period overhauls, update facilitates, and also gradually becomes a kind of trend in the application of building decoration engineering inner-outer wall,
It is precipitated by the technology of recent years, the fidelity of multicolor finish, production technology and normal temperature storage (heat storage) are all able to larger
Improve.But low-temperature storage is especially in the biggish the Northwest of day and night temperature, as temperature gradually lowers, causes to protect xanthan molecule
Movement dies down, and wraps up strength reduction, and the colorful broken point of particle increases when so as to cause production, and color spot is partially soft and color spot is freezing, rear to increase
The bad phenomenons such as thick.It is still multicolor finish urgent problem now.So the suitable usual auxiliaries of the screening of system and
Lotion guarantees product freeze-thaw stability, and reducing unnecessary loss in engineering is particularly important formula design.
Summary of the invention
It is an object of the invention to overcome the deficiencies of existing technologies, a kind of the continuous of freeze thawing resistance water-soluble colorful coating is provided
Phase emulsion, freeze thawing resistance water-soluble colorful coating and preparation method thereof, the present invention passes through the continuous phase to freeze thawing resistance water-soluble colorful coating
The formula of lotion improves, and greatly improves the freezing and thawing performance of coating, avoids the occurrence of the broken point of colorful particle and increases, color spot is partially soft
And color spot is freezing, the bad phenomenons such as rear thickening.
In order to realize that object above and other purposes, the present invention are by including that following technical scheme is realized: first party
Face, the present invention provide a kind of continuous phase emulsion of freeze thawing resistance water-soluble colorful coating, the freeze thawing resistance water-soluble colorful coating it is continuous
Phase emulsion comprises the following components in parts by weight: 2-5 parts of bentonite;450-550 parts of silicone acrylic emulsion;35-45 parts of anti-icing fluid;Film forming helps
20-30 parts of agent;0.1-5 parts of defoaming agent;0.5-5 parts of pH adjusting agent;2-8 parts of thickener;2-5 parts of sterilization antiseptic;First go from
Sub- water 350-500 parts.
Preferably, the model 8087 of the silicone acrylic emulsion.Silicone acrylic emulsion is will be containing the organic silicon monomer of unsaturated bond
Suitable auxiliary agent is added with acrylic monomer, the lotion that polymerization technique is polymerized is coated by nucleocapsid, combines organosilicon
Heat-resisting quantity, weatherability, chemical-resistant, hydrophobic, surface can low not v ulnerability and acrylic resin high colour retention, soft
Toughness, adhesion.
Preferably, the defoaming agent is mineral oil defoaming agent or silicon class defoaming agent.Adding defoaming agent reduces surface tension,
Inhibit foam to generate, avoids foam coating adverse effect caused by brushing technique.
Preferably, the coalescing agent is Lauryl Alcohol ester.It adds coalescing agent and promotes high-molecular compound Plastic Flow
And flexible deformation, improve coalescence performance, be conducive to coating fast filming, reduces the coating application time.
Preferably, the antifreezing agent is propylene glycol or ethylene glycol.Antifreezing agent is added coating is had and is easy to brush, is dry
Rapidly, the advantage that paint film is water-fast, scrub resistance is good, it is ensured that normal construction under subzero temperature reduces the freezing point of lotion in coating.
Preferably, the pH adjusting agent is amine pH adjusting agent.
Preferably, the sterilization antiseptic is selected from mixture, the benzisothiazole of chloromethyl and methylisothiazolinone
Ketones derivant it is one or two kinds of.The mixture of chloromethyl and methylisothiazolinone belongs to Kathon CG series bactericidal agent, intolerant to
High temperature, pH range is relatively narrow, and effect is preferable within pH8, but sterilization speed is fast: the sterilization of benzoisothiazolinone analog derivative is anti-
Rotten agent sterilization speed is slow, but high temperature resistant, and alkaline-resisting range is relatively strong (3-12).
Preferably, the thickener is hydrophobically modified alkali-soluble emulsion type thickener.It adds thickener and improves base paint
Viscosity keeps the stability of base paint, improves the physical characteristic of base paint, and has emulsification, stabilization concurrently or make in suspended state
Effect.
Second aspect, the present invention provide a kind of freeze thawing resistance water-soluble colorful coating, including component and the weight of each component contain
Amount are as follows: base paint: 35-45%;Protect glue: 25-35%;The continuous phase cream of freeze thawing resistance water-soluble colorful coating described above
Liquid: 25-35%.
The third aspect, the present invention provide a kind of side of base paint for preparing freeze thawing resistance water-soluble colorful coating as described above
Method, comprising the following steps: dispersion machine is added in a part of first deionized water, is stirred under 400-700r/min speed conditions,
It is repeatedly slowly added to the bentonite, improves revolving speed to 1400-1700r/min, high speed dispersion 15-25min, then according to weight
Proportion sequentially adds the silicone acrylic emulsion, the anti-icing fluid, the coalescing agent, the defoaming agent, the pH adjusting agent, stirs
5-15min improves revolving speed, is repeatedly slowly added to the mixture of the thickener and the first deionized water, stirs 5-15min, most
It is slowly added to the mixture of the sterilization antiseptic and the first deionized water afterwards, is stirred under 400-700r/min speed conditions equal
It is even, continuous phase emulsion is prepared;It is according to the weight ratio that the base paint, the protection glue, the continuous phase emulsion is equal
Even mixing obtains freeze thawing resistance water-soluble colorful coating.
Preferably, the preparation method of the base paint of the freeze thawing resistance water-soluble colorful coating further includes the mistake of preparation protection glue
Journey, the process of preparation protection glue are as follows: the second deionized water is added to dispersion machine, is stirred under 400-700r/min speed conditions
It mixes, is repeatedly slowly added to protection rubber powder, improve revolving speed to 1400-1700r/min, high speed dispersion 40-80min, place.
Preferably, second deionized water and the weight ratio of the protection rubber powder are (900-940): (30-100).
Preferably, the model GTS or GS of the protection rubber powder.
In conclusion the present invention provides a kind of freeze thawing resistance water-soluble colorful coating and preparation method thereof, beneficial effect of the invention
Fruit: the present invention avoids occurring the broken point of colorful particle in process of production increasing, and color spot is partially soft and color spot is freezing, and rear thickening etc. is bad
Phenomenon, the present invention guarantee product freeze-thaw stability, coating normal construction under subzero temperature by screening suitable auxiliary agent and lotion;,
The present invention has many advantages, such as good hot storage stability, low-temperature storage stability, film performance, is conducive to be widely applied, especially
It is suitable for the biggish the Northwests of day and night temperature.
Specific embodiment
Illustrate embodiments of the present invention below by way of specific specific example, those skilled in the art can be by this specification
Other advantages and efficacy of the present invention can be easily understood for disclosed content.The present invention can also pass through in addition different specific realities
The mode of applying is embodied or practiced, the various details in this specification can also based on different viewpoints and application, without departing from
Various modifications or alterations are carried out under spirit of the invention.
1. primary raw material
Deionized water, PH regulator: AMP-95 (DOW Chemical), cellulose: the Asia 250HBR, HE3KB, HE10K:(bodyguard
It is blue), ammonium salt dispersing agent 1124 (DOW Chemical), hydrophobic sodium salt dispersing agent 731A (DOW Chemical), defoaming agent: 321C (Sheng Nuopu
Section), 2410 (BASF), antifreezing agent: propylene glycol, ethylene glycol (technical grade), coalescing agent (TEX), alcohol ester-12 (Yi Siman),
Pure-acrylic emulsion: RS-6733, RS-2788;Silicone acrylic emulsion: RS-3799A (Ahmedabad is rich), 8087 (Wan Hua), sterilization antiseptic:
BIT20 (DOW Chemical), HF-1 (Clariant), thickener TT-935 (DOW Chemical), bentonite KW (Shanghai grid), protection
Glue: S482 (Lockwood), GS (Shanghai grid), RD (BYK), GTS (Shanghai grid), SH997 (Guangdong distillation).
2. the selection of base paint lotion
2.1 base paint formulations (1% titanium white)
The each component and weight proportion of base paint in 1 embodiment 1 to 2 of table
Base paint preparation method, comprising the following steps:
According to the weight proportion of each component shown in table 1,540g deionized water 1 is first added, starts dispersion machine, 600r/
Min revolving speed sequentially adds 250HBR, HE10K, BIT20,731A, 321C, TEX, AMP-95, stirs 10min, sequentially adds
R298, DB-80, RD (6.7%) improve revolving speed to 1800r/min, high speed dispersion 30min, scrape fineness to 70um, reduce revolving speed
To 500r/min, be slowly added to pure-acrylic emulsion RS-2788/RS6733, after mixing evenly, sequentially add 2410, CI-15HS and
The mixture of deionized water 2 stirs 10min to get base paint.
Base paint state: the base paint viscosity 128.5KU for the embodiment 1 prepared, in good condition, bubble-free, surface light
Sliding, high resilience.The base paint viscosity 122KU for the embodiment 2 prepared is in good condition, and viscosity is lower, there is microvesicle.
2.2 protective glue solution formulas
The formula that 2 embodiment 1 to 2 of table protects sol solution to use
Raw material | Weight (g) |
Deionized water | 920 |
It protects rubber powder (GS) | 80 |
It is total | 1000 |
Protective glue solution manufacturing method, comprising the following steps:
According to the weight proportion of table 2,920g deionized water is added, starts dispersion machine, 600r/min revolving speed slowly repeatedly adds
Enter 80g protection rubber powder (GS) (forbid to topple over, in order to avoid conglomeration), improves revolving speed to 1500r/min, high speed dispersion 60min, such as winter
Preparation need to promote the temperature of deionized water or increase jitter time, stand more than for 24 hours, can use.
2.3 continuous phase emulsion formulations
The formula that the continuous phase emulsion of 3 embodiment of table 1 to 2 uses
Raw material | Weight (g) |
Deionized water 1 | 182 |
Silicone acrylic emulsion (RS-3799A) | 500 |
Ethylene glycol (EG) | 40 |
Coalescing agent (TEX) | 25 |
Defoaming agent (2410) | 2 |
PH adjusting agent (AMP-95) | 3 |
Thickener (TT-935) | 6 |
Deionized water 2 | 18 |
Sterilization antiseptic (HF-1) | 3 |
Deionized water 3 | 221 |
It is total | 1000 |
The preparation method of continuous phase emulsion, comprising the following steps:
According to the weight proportion of table 3, deionized water 1 is added, starts dispersion machine, 600r/min revolving speed sequentially adds silicon third
Lotion RS-3799A, ethylene glycol, coalescing agent TEX, defoaming agent 2410, pH adjusting agent AMP-95 stir 10min, then suitably mention
High revolving speed, but dispersion axis cannot be leaked out, in order to avoid bringing bubble into, the mixture of TT-935 and deionized water 2 is slowly repeatedly added,
5min is stirred, is finally slowly added to the mixture of sterilization antiseptic CI-15HS and deionized water 3,500r/min is stirred evenly.
The continuous phase viscosity of preparation is 97.8KU, and in good condition, bubble-free is spare.
The finished product paint formula of 2.4 water-soluble colorful coatings
The each component and weight proportion of 4 embodiment of table, 1 to 2 water-soluble colorful coating
The preparation method of water-soluble colorful coating, comprising the following steps:
(1) base paint is weighed, required color is recalled, mixes slowly, in order to avoid bubble is brought into, by base paint by certain ratio
Example is divided into several parts, mixes colours respectively, then base paint according to the weight ratio: mass fraction is added in protection latex solution=1.0~1.5:1
It for 8% protection sol solution, is stirred in 1000r/min revolving speed uniform and smooth to color-mixed base paint surface state, is reducing revolving speed
10min de-soak is stirred at low speed to 600r/min, taking-up placement 20min is stand-by, and several lotions are mixed in a certain ratio, and obtains
Color grain.
(2) the protection sol solution that mass fraction is 8% is converted into mass fraction is 3.5% protection sol solution.
(3) the continuous phase emulsion by 400g color grain, 300g mass fraction for 3.5% protection sol solution, 300g uniformly mixes,
Never strong stirring destroys particle, obtains finished product paint;The viscosity of finished product paint is adjusted to 60-70KU.
2.5 testing result
Freeze thawing test condition: -15 DEG C of low temperature/15H;23 DEG C/9H of room temperature: cycle-index is 3 times.
Freeze thawing test result is as shown in table 5.
The freeze thawing test result of the water-soluble colorful coating of 5 embodiment 1 to 2 of table
From the freeze thawing test result of the water-soluble colorful coating of table 5 it can be seen that RS-6733 pure-acrylic emulsion with contain epoxy group
RS-2788 pure-acrylic emulsion compared in colorful base paint system, thermmal storage viscosity change is little;But to freeze-thaw stability
Speech RS-6733 pure-acrylic emulsion is substantially better than the RS-2788 pure-acrylic emulsion containing epoxy group.So larger for the high/low temperature temperature difference
Northern place answer preferred RS-6733 pure-acrylic emulsion.
3. the selection of protective glue type
3.1 protective glue solution formulas
The each component and weight proportion of 6 embodiment 3 to 6 of table protection sol solution
Raw material | Embodiment 3 | Embodiment 4 | Embodiment 5 | Embodiment 6 |
Deionized water | 920 | 920 | 920 | 920 |
It protects rubber powder (SH997) | 80 | - | - | - |
It protects rubber powder (GS) | - | 80 | - | - |
It protects rubber powder (S482) | - | - | 80 | - |
It protects rubber powder (GTS) | - | - | - | 80 |
It is total | 1000 | 1000 | 1000 | 1000 |
Protective glue solution manufacturing method, comprising the following steps: 920g deionized water is added, starts dispersion machine, 600r/min
Protection rubber powder (forbid to topple over, in order to avoid conglomeration) is slowly repeatedly added in revolving speed, as prepared by winter, it is proposed that promote the temperature of deionized water
Degree increases jitter time, improves revolving speed to 1500r/min, high speed dispersion 60min, places more than for 24 hours, can use.
Protective glue solution state: being in uniform translucent, and standing is granulated afterwards for 24 hours.
3.2 preparation processes:
3.2.1 base paint is the formula of embodiment 2 in table 1;Continuous phase is temporarily the formula of the continuous phase emulsion of table 3.
3.2.2 finished product paint: with reference to the preparation method of water-soluble colorful coating in 2.4.
3.3 performance tests:
Test condition: -15 DEG C of low temperature/15H;23 DEG C/9H of room temperature;Cycle-index is 3 times
Freeze thawing test result is as shown in table 7.
The freeze thawing test result of 7 embodiment of table, 3 to 6 water-soluble colorful coating
As can be seen from Table 7, four kinds of protection sol solution thermmal storage viscosity changes are substantially little: but freeze-thaw stability GTS and
GS protective glue is substantially better than S482 and SH997.Place biggish for the high/low temperature temperature difference should select the guarantor of model GTS or GS
Protect rubber powder.
4. the selection of continuous phase emulsion
The formula of 4.1 continuous phase emulsions
The each component and weight proportion of the continuous phase emulsion of 8 embodiment 7 to 8 of table
4.2 preparation process
4.2.1 base paint selects: the base paint for selecting embodiment 2 is test formulations;Protection glue formula select embodiment 4 be
Test formulations.
4.2.2 continuous phase emulsion: according to the weight proportion of table 8, being added deionized water 1, starts dispersion machine, and 600r/min turns
Slowly bentonite KW (forbid to topple over, in order to avoid conglomeration) is repeatedly added in speed, and 2 trimming of deionized water is added, and improves revolving speed extremely
1500r/min, high speed dispersion 20min after waiting bentonites to be completely dissolved, sequentially add silicone acrylic emulsion RS-3799A/8087, second
Glycol, TEX, 2410, AMP-95 stir 10min, then properly increase revolving speed, but cannot leak out dispersion axis, in order to avoid bring bubble into,
The mixture of TT-935 and deionized water 3 is slowly repeatedly added, stirs 5min, is finally slowly added to CI-15HS and deionized water
4 mixture, 500r/min are stirred evenly.The continuous phase viscosity of preparation is 97.8KU, and in good condition, bubble-free is spare.
4.2.3 finished product paint: with reference to the preparation method of water-soluble colorful coating in 2.4.
4.3 performance tests:
Freeze thawing test condition: -15 DEG C of low temperature/15H;23 DEG C/9H of room temperature;Cycle-index is 3 times.
Test result is as shown in table 9.
The freeze thawing test result of 9 embodiment of table, 7 to 8 water-soluble colorful coating
As can be seen from Table 9, embodiment 7 and the thermmal storage viscosity change of 8 two kinds of embodiment continuous phase emulsions are substantially little:
For permeability, embodiment 8 is better than embodiment 7;For freeze-thaw stability, embodiment 8 is better than embodiment 7;For round the clock
Stronger 8087 silicone acrylic emulsion of inertia is more particularly suitable in the biggish local selection example 8 of the temperature difference.
5. the selection of base paint auxiliary agent type
5.1 base paint selection formula
The each component and weight proportion of base paint in 10 embodiment 9 to 16 of table
Formula auxiliary changes direction: cellulose main body determines that mass fraction is in embodiment 9,12,13,14,15,16
1.1%, the hydroxyethyl cellulose of model 250HBR.Cellulose is by model 250HBR hydroxyethyl cellulose (matter in embodiment 10
Amount score is that hydroxyethyl cellulose (mass fraction 0.2%) compounding 0.8%) is compounded with model HE10K.Embodiment 11 is by type
Number 250HBR hydroxyethyl cellulose (mass fraction 1.1%) compounds hydroxyethyl cellulose with model HE10K, and (mass fraction is
0.1%) it compounds.Dispersing agent selects ammonium salt dispersing agent (model 1124) and hydrophobic sodium salt dispersing agent (model 731A) to compare through row.
According to color grain state, plate face effect adjusts coarse whiting and kaolin usage amount.Thickener selects TT935/SN612 to adjust to 120-
125KU。
The preparation method of base paint, comprising the following steps:
Deionized water 1 is added, starts dispersion machine, 600r/min revolving speed, sequentially add 250HBR, HE10K, HE3KB,
BIT20,1124,731A, 321C, TEX, AMP-95, deionized water 2 stir 10min, sequentially add R298, DB-80, CC-
1000, revolving speed is improved to 1800r/min, high speed dispersion 30min, scrapes fineness to 70um, reduces revolving speed to 500r/min, slowly
Pure-acrylic emulsion RS-6733 is added and sequentially adds the mixture of 2410, HF-I and deionized water 3 after mixing evenly, stirs
10min is slowly added to the mixture of TT-935 and deionized water 4, and stirring 10min or so is to get base paint.
Base paint makes result: done base paint viscosity is controlled in 120-125KU, and state is good, bubble-free, surface
Smooth, high resilience.
5.2 protection sol solutions
The formula that 11 embodiment 9 to 16 of table protects sol solution to use
The method for preparing protective glue, comprising the following steps: 920g deionized water is added, starts dispersion machine, 600r/min turns
Speed is slowly repeatedly added protection rubber powder (GS) (forbid to topple over, in order to avoid conglomeration), as prepared by winter, it is proposed that promote deionized water
Temperature increases jitter time, improves revolving speed to 1500r/min, high speed dispersion 60min, places more than for 24 hours, can use.
5.3 continuous phase emulsions
The formula that the continuous phase emulsion of 12 embodiment of table 9 to 16 uses
The preparation method of continuous phase, comprising the following steps: according to the weight proportion of table 12, deionized water 1 is added, starts point
Machine is dissipated, slowly bentonite KW (forbid to topple over, in order to avoid conglomeration) is repeatedly added in 600r/min revolving speed, 2 trimming of deionized water is added,
Revolving speed is improved to 1500r/min, high speed dispersion 20min, after waiting bentonites to be completely dissolved, sequentially add silicone acrylic emulsion 8087,
Ethylene glycol, TEX, 2410, AMP-95 stir 10min, then properly increase revolving speed, but cannot leak out dispersion axis, in order to avoid bring gas into
The mixture of TT-935 and deionized water 3 is slowly repeatedly added in bubble, stirs 5min, is finally slowly added to CI-15HS and deionization
The mixture of water 4,500r/min are stirred evenly.The continuous phase viscosity of preparation is 97.8KU, and in good condition, bubble-free is standby
With.
5.4 finished product paints
The component and weight proportion of 13 embodiment of table, 9 to 16 water-soluble colorful coating
Component | Dosage/g |
The color grain that the formula of embodiment 9 to 16 obtains | 400 |
It protects sol solution (3.5%GS) | 300 |
Continuous phase | 300 |
It is total | 1000 |
(1) base paint is weighed, required color is recalled, mixes slowly, in order to avoid bubble is brought into, by base paint by certain ratio
Example is divided into several parts, mixes colours respectively, then base paint according to the weight ratio: mass fraction is added in protection latex solution=1.0~1.5:1
It for 8% protection sol solution, is stirred in 1000r/min revolving speed uniform and smooth to color-mixed base paint surface state, is reducing revolving speed
10min de-soak is stirred at low speed to 600r/min, taking-up placement 20min is stand-by, and several lotions are mixed in a certain ratio, and obtains color
Grain.
(2) the protection sol solution that mass fraction is 8% is converted into mass fraction is 3.5% protection sol solution.
(3) the continuous phase emulsion by 400g color grain, 300g mass fraction for 3.5% protection sol solution, 300g uniformly mixes,
Never strong stirring destroys particle, obtains finished product paint;The viscosity of finished product paint is adjusted to 60-70KU.
5.5 result and discussion
5.5.1 it is granulated bleeding, seeps lotion
It sees whether bleeding occur when granulation, seep lotion phenomenon and particle suspension.
5.5.2 freeze thawing test condition:
Freezing-Melting Condition: -15 DEG C of low temperature/15H;23 DEG C/9H of room temperature;Cycle-index is 3 times.
Test result is as shown in table 14.
The performance test results of 14 embodiment of table, 9 to 16 water-soluble colorful coating
As can be seen from Table 14: finished product paint-like state is poor in embodiment 9 in the system, particle is not full, and application property is poor, freezes
It is poor to melt stability;Finished product paint-like state is good in embodiment 10,11,12,13, application property is preferable, but freeze thawing is poor: embodiment
14, the freeze thawing of finished product paint is preferable in 15, but application property is general.Finished product paint is in the best state in embodiment 16, and freeze-thaw stability is excellent,
Application property is good.
In conclusion it is preferred that dispersed phase main choosing of the RS-6733 lotion as the Northwest's multicolor finish: preferred GS/GTS body
System selects protective glue system as main, the selection of cellulose based on 250HBR or HS30000 class, HE3KB containing hydrophobic function and
HE10KB is unfavorable to the freeze-thaw stability of system;For dispersing agent, hydrophobic sodium polycarboxylate dipersant is comprehensive in colorful system
It closes performance and is not so good as polycarboxylic acid ammonium salt dispersant.Under equal conditions, the increase of dispersing agent and kaolin amount will affect the freeze thawing of system
Stability.
The above-described embodiments merely illustrate the principles and effects of the present invention, and is not intended to limit the present invention.It is any ripe
The personage for knowing this technology all without departing from the spirit and scope of the present invention, carries out modifications and changes to above-described embodiment.Cause
This, institute is complete without departing from the spirit and technical ideas disclosed in the present invention by those of ordinary skill in the art such as
At all equivalent modifications or change, should be covered by the claims of the present invention.
Claims (8)
1. a kind of continuous phase emulsion of freeze thawing resistance water-soluble colorful coating, it is characterised in that: the freeze thawing resistance water-soluble colorful coating
Continuous phase emulsion comprises the following components in parts by weight:
2. the continuous phase emulsion of freeze thawing resistance water-soluble colorful coating as described in claim 1, it is characterised in that: the silicone acrylic emulsion
Model 8087.
3. the continuous phase emulsion of freeze thawing resistance water-soluble colorful coating as described in claim 1, it is characterised in that: further include following
It anticipates one or more features:
(1) defoaming agent is mineral oil defoaming agent or silicon class defoaming agent;
(2) coalescing agent is Lauryl Alcohol ester;
(3) antifreezing agent is propylene glycol or ethylene glycol;
(4) pH adjusting agent is amine pH adjusting agent;
(5) preferably, the sterilization antiseptic is selected from mixture, the benzoisothiazolinone of chloromethyl and methylisothiazolinone
Analog derivative it is one or two kinds of;
(6) thickener is hydrophobically modified alkali-soluble emulsion type thickener.
4. a kind of freeze thawing resistance water-soluble colorful coating, which is characterized in that including component and each component weight content are as follows:
Base paint: 35-45%;
Protect glue: 25-35%;
The continuous phase emulsion of freeze thawing resistance water-soluble colorful coating any one of claims 1 to 3: 25-35%.
5. a kind of method for preparing freeze thawing resistance water-soluble colorful coating as claimed in claim 4, it is characterised in that: including following step
It is rapid: dispersion machine is added in a part of first deionized water, is stirred under 400-700r/min speed conditions, is repeatedly slowly added to institute
Bentonite is stated, then raising revolving speed to 1400-1700r/min, high speed dispersion 15-25min sequentially adds institute according to the weight ratio
Silicone acrylic emulsion, the anti-icing fluid, the coalescing agent, the defoaming agent, the pH adjusting agent are stated, 5-15min is stirred, improves and turns
Speed is repeatedly slowly added to the mixture of the thickener and the first deionized water, stirs 5-15min, is finally slowly added to described
The mixture of sterilization antiseptic and the first deionized water stirs evenly, the company of being prepared under 400-700r/min speed conditions
Continuous phase emulsion;
The base paint, the protection glue, the continuous phase emulsion are uniformly mixed according to the weight ratio, obtain freeze-thaw resisting
Property multicolor finish.
6. the preparation method of the continuous phase emulsion of freeze thawing resistance water-soluble colorful coating as described in claim 1, it is characterised in that: institute
The preparation method for stating the base paint of freeze thawing resistance water-soluble colorful coating further includes the process of preparation protection glue, preparation protection glue
Process are as follows: the second deionized water is added to dispersion machine, is stirred under 400-700r/min speed conditions, is repeatedly slowly added to protect
Rubber powder is protected, revolving speed is improved to 1400-1700r/min, high speed dispersion 40-80min, places.
7. the preparation method of the continuous phase emulsion of freeze thawing resistance water-soluble colorful coating as claimed in claim 6, it is characterised in that: institute
The weight ratio for stating the second deionized water and the protection rubber powder is (900-940): (30-100).
8. the preparation method of the continuous phase emulsion of freeze thawing resistance water-soluble colorful coating as claimed in claims 6 or 7, feature exist
In: the model GTS or GS of the protection rubber powder.