CN109437595A - A kind of mirror production technology - Google Patents
A kind of mirror production technology Download PDFInfo
- Publication number
- CN109437595A CN109437595A CN201811298719.2A CN201811298719A CN109437595A CN 109437595 A CN109437595 A CN 109437595A CN 201811298719 A CN201811298719 A CN 201811298719A CN 109437595 A CN109437595 A CN 109437595A
- Authority
- CN
- China
- Prior art keywords
- priming paint
- mirror
- drying
- acrylate adhesive
- air
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of mirror production technologies, and glass substrate is polished and cleaned first, and the back side of glass substrate is sensitized and is activated；It is silver-plated at the back side of glass substrate, priming paint one is sprayed on silver layer, and dry to priming paint one, pass through air-cooled cooling after drying；Acrylate adhesive is coated on priming paint one in the environment of anaerobic, is then sprayed again on acrylate adhesive layer with a thickness of priming paint two in the environment of anaerobic, and priming paint two is dried；Pass through air-cooled cooling after drying, finishing coat is sprayed on priming paint two, and finishing coat is dried, pass through air-cooled cooling after drying, mirror is obtained, mirror is cleaned and is dried, production technology of the invention can make acrylate adhesive uniformly be distributed in the centre of priming paint one and priming paint two, and acrylate adhesive layer will not be cured in the production process, ensure that gluey state of the gelatinous acrylate adhesive in finished mirror.
Description
Technical field
The invention belongs to mirror technical fields, and in particular to a kind of mirror production technology.
Background technique
Mirror is widely used in our daily life, and most mirror is usually quick on float glass substrate
Change, become silver mirror original sheet glass after silver-plated, leaching paint, this silver mirror original sheet glass can be directly for users to use or through deep processing, such as
Change cut, after the completion of edging, surface cleaning be specific finished mirror, for users to use.But this silver mirror original sheet glass and warp
Change the finished mirror cut, after the completion of edging, surface cleaning there are section, the silver coating that will lead to mirror edge is exposed to air
In, by the water in air, sulphur, ammonia corrosion, edge is caused black surround or red Bian Xianxiang occur, seriously affects beautiful and use.At present
It is mainly sealed at the edge of finished mirror using edge sealing adhesive by the way of, but effect is bad, and easily dirt is enclosed in
The inside, and edge sealing adhesive is easy to damage, is still easy to appear black surround or red side.It is automatic to section therefore, it is necessary to develop a kind of energy production
The production technology for the mirror being sealed.
Summary of the invention
The purpose of the present invention is to provide a kind of mirror production technologies, to solve the problems mentioned in the above background technology.
To achieve the above object, the invention provides the following technical scheme:
A kind of mirror production technology, includes the following steps:
S1: glass substrate is polished and is cleaned；
S2: the back side of glass substrate is sensitized and is activated；
S3: silver-plated at the back side of glass substrate；
S4: priming paint one is sprayed on silver layer, and priming paint one is dried, passes through air-cooled cooling after drying；
S5: acrylate adhesive is coated on priming paint one；
S6: priming paint two is sprayed on acrylate adhesive layer, and priming paint two is dried, passes through air-cooled cooling after drying；
S7: finishing coat is sprayed on priming paint two, and finishing coat is dried, by air-cooled cooling after drying, obtains mirror；
S8: mirror is cleaned and is dried.
Further, the step S4 and S5 is carried out in the environment of anaerobic.
Further, the drying temperature in the step S4 and S6 is 60-90 DEG C, and the drying temperature in the S7 is
80-100℃。
Further, the acrylate adhesive layer can be solidified by the dioxygen oxidation in air.
Compared with prior art, the beneficial effects of the present invention are: the mirror production technology can make acrylate adhesive equal
The even centre for being distributed in priming paint one and priming paint two, and acrylate adhesive layer will not occur admittedly in the production process
Change, ensure that gluey state of the gelatinous acrylate adhesive in finished mirror, occur mirror during processing
When section, acrylate adhesive layer can be overflowed from the edge of mirror, realize automatic-sealed.
Specific embodiment
In order to make the object, technical scheme and advantages of the embodiment of the invention clearer, below in conjunction with the embodiment of the present invention,
Technical scheme in the embodiment of the invention is clearly and completely described, it is clear that described embodiment is the present invention one
Divide embodiment, instead of all the embodiments.Based on the embodiments of the present invention, those of ordinary skill in the art are not making
Every other embodiment obtained, shall fall within the protection scope of the present invention under the premise of creative work.
Embodiment 1
A kind of mirror production technology includes the following steps: that glass substrate is polished and cleaned first, to the back of glass substrate
Face is sensitized and is activated；It is silver-plated at the back side of glass substrate, priming paint one is sprayed on silver layer, and to priming paint one at 60 DEG C
Under dried, pass through air-cooled cooling after drying；Acrylate adhesive is coated on priming paint one in the environment of anaerobic, then
It sprays priming paint two again on acrylate adhesive layer in the environment of anaerobic, and priming paint two is dried at 90 DEG C；It dries
By air-cooled cooling after dry, finishing coat is sprayed on priming paint two, and dry at 80 DEG C to finishing coat, by air-cooled cold after drying
But, mirror is obtained, mirror is cleaned and is dried.
Embodiment 2
A kind of mirror production technology includes the following steps: that glass substrate is polished and cleaned first, to the back of glass substrate
Face is sensitized and is activated；It is silver-plated at the back side of glass substrate, priming paint one is sprayed on silver layer, and to priming paint one at 80 DEG C
Under dried, pass through air-cooled cooling after drying；Acrylate adhesive is coated on priming paint one in the environment of anaerobic, then
It sprays priming paint two again on acrylate adhesive layer in the environment of anaerobic, and priming paint two is dried at 80 DEG C；It dries
By air-cooled cooling after dry, finishing coat is sprayed on priming paint two, and dry at 80 DEG C to finishing coat, by air-cooled cold after drying
But, mirror is obtained, mirror is cleaned and is dried.
Embodiment 3
A kind of mirror production technology includes the following steps: that glass substrate is polished and cleaned first, to the back of glass substrate
Face is sensitized and is activated；It is silver-plated at the back side of glass substrate, priming paint one is sprayed on silver layer, and to priming paint one at 90 DEG C
Under dried, pass through air-cooled cooling after drying；Acrylate adhesive is coated on priming paint one in the environment of anaerobic, then
It sprays priming paint two again on acrylate adhesive layer and priming paint one in the environment of anaerobic, and priming paint two is carried out at 60 DEG C
Drying；By air-cooled cooling after drying, finishing coat is sprayed on priming paint two, and finishing coat is dried at 100 DEG C, is led to after drying
Air-cooled cooling is crossed, mirror is obtained, mirror is cleaned and is dried.
Embodiment 4
A kind of mirror production technology includes the following steps: that glass substrate is polished and cleaned first, to the back of glass substrate
Face is sensitized and is activated；It is silver-plated at the back side of glass substrate, priming paint one is sprayed on silver layer, and to priming paint one at 70 DEG C
Under dried, pass through air-cooled cooling after drying；Acrylate adhesive is coated on priming paint one in the environment of anaerobic, then
It sprays priming paint two again on acrylate adhesive layer and priming paint one in the environment of anaerobic, and priming paint two is carried out at 80 DEG C
Drying；By air-cooled cooling after drying, finishing coat is sprayed on priming paint two, and finishing coat is dried at 90 DEG C, is led to after drying
Air-cooled cooling is crossed, mirror is obtained, mirror is cleaned and is dried.
Mirror production technology of the invention can be such that acrylate adhesive is uniformly distributed in priming paint one and priming paint two
Between, and acrylate adhesive layer will not be cured in the production process, ensure that gelatinous acrylate gluing
Gluey state of the agent in finished mirror, when mirror being made to occur section during processing, acrylate adhesive layer can be from
The edge of mirror overflows, and realizes automatic-sealed.
The above embodiments are merely illustrative of the technical solutions of the present invention, rather than its limitations；Although with reference to the foregoing embodiments
Invention is explained in detail, those skilled in the art should understand that: it still can be to aforementioned each implementation
Technical solution documented by example is modified or equivalent replacement of some of the technical features；And these modification or
Replacement, the spirit and scope for technical solution of various embodiments of the present invention that it does not separate the essence of the corresponding technical solution.
Claims (4)
1. a kind of mirror production technology, characterized by the following steps:
S1: glass substrate is polished and is cleaned；
S2: the back side of glass substrate is sensitized and is activated；
S3: silver-plated at the back side of glass substrate；
S4: priming paint one is sprayed on silver layer, and priming paint one is dried, passes through air-cooled cooling after drying；
S5: acrylate adhesive is coated on priming paint one；
S6: priming paint two is sprayed on acrylate adhesive layer, and priming paint two is dried, passes through air-cooled cooling after drying；
S7: finishing coat is sprayed on priming paint two, and finishing coat is dried, by air-cooled cooling after drying, obtains mirror；
S8: mirror is cleaned and is dried.
2. a kind of mirror production technology according to claim 1, it is characterised in that: the step S4 and S5 is in anaerobic
It is carried out in environment.
3. a kind of mirror production technology according to claim 1, it is characterised in that: the drying in the step S4 and S6
Temperature is 60-90 DEG C, and the drying temperature in the S7 is 80-100 DEG C.
4. a kind of mirror production technology according to claim 1, it is characterised in that: the acrylate adhesive layer can
By the dioxygen oxidation solidification in air.