CN109435537A - A kind of four color perfume pencil-lead production technologies - Google Patents
A kind of four color perfume pencil-lead production technologies Download PDFInfo
- Publication number
- CN109435537A CN109435537A CN201811343816.9A CN201811343816A CN109435537A CN 109435537 A CN109435537 A CN 109435537A CN 201811343816 A CN201811343816 A CN 201811343816A CN 109435537 A CN109435537 A CN 109435537A
- Authority
- CN
- China
- Prior art keywords
- core material
- pencil
- perfume
- colors
- color
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention discloses a kind of four color perfume pencil-lead production technologies, comprising the following steps: the raw material of four color perfume pencil-leads is put into kneader and is kneaded into clod shape core material；Clod shape core material is put into three-roller and rolls grinding, sheet core material is made；Sheet core material is put into pulverizer and is crushed, graininess core material is made；Graininess core material is stood 48 hours or more；Cylindric core material is made in graininess core material, then cylindric core material is cut into fan-shaped column core material；The fan-shaped column core material permutation and combination for choosing four kinds of different colours is good, and is put into horizontal press, extrusion forming；It is put into dry room, dries, finished product is made.It is produced using the combination of vertical press and horizontal press, and joined releasing process in traditional production technology, four color perfume pencil-leads being combined by four kinds of color alignments can be made, color diversification, combination is diversified, and fragrant.
Description
Technical field
The present invention relates to pencil-lead production technical fields, it particularly relates to a kind of four color perfume pencil-lead production technologies.
Background technique
Traditional pencil-lead production technology is kneading → grinding → crushing → standing → molding → drying, and production process summarizes
The equipment of use has kneader, three-roller, pulverizer, vertical press, and the pencil of solid color can only be made in this production technology
Core.
For the problems in the relevant technologies, currently no effective solution has been proposed.
Summary of the invention
For above-mentioned technical problem in the related technology, the present invention proposes a kind of four color perfume pencil-lead production technologies,
It is produced using the combination of vertical press and horizontal press, and joined releasing process in traditional production technology, can be made
Four color perfume pencil-leads being combined by four kinds of color alignments, color diversification, combination diversification, and it is fragrant, make
Used time can be combined into various face since pen tip and drawing paper contact surface constantly change after red, yellow, blue, green 4 kinds of color additions
Color, so that the lines riot of color drawn, color be not single.
To realize the above-mentioned technical purpose, the technical scheme of the present invention is realized as follows:
A kind of four color perfume pencil-lead production technologies, comprising the following steps:
The raw material of four color perfume pencil-leads is put into kneader and is kneaded into clod shape core material by S1；
The clod shape core material is put into three-roller and rolls grinding by S2, and sheet core is made after so that its moisture is reached 12%~14%
Material；
The sheet core material is put into pulverizer and crushes by S3, and graininess core material is made；
Graininess core material standing 48 hours or more are made its temperature reach room temperature by S4；
The graininess core material is put into mold after vertical press squeezes and demoulds and cylindric core material is made by S5, then by institute
It states the cylindric core material quartering and is cut into fan-shaped column core material；
The fan-shaped column core material permutation and combination that S6 chooses four kinds of different colours is good, and is put into horizontal press, extrusion forming, is made
The four colors perfume pencil-lead；
The four colors perfume pencil-lead is put into dry room by S7, and drying makes its moisture < 1.5%, finished product is made.
Further, the four colors perfume pencil-lead is made of the raw material of following quality proportioning: 50-60 parts of kaolin, face
Expect toner 6-15 parts, 10-15 parts of zinc stearate, 6-10 parts of CMC carboxymethyl cellulose, 25-30 parts of wax, 3 parts of essence.
Further, in S1, first by kaolin, pigment toner and the CMC carboxymethyl cellulose weighted by quality proportioning
In element investment kneader, dry powder is stirred 30~60 minutes, then will dissolve by the weighted zinc stearate of quality proportioning, wax and essence
After pour into kneader after stirring mediates, the clod shape core material is made.
Further, in S4, the temperature range of the room temperature is 23 DEG C ± 2 DEG C.
Further, in S5, the diameter of the cylindric core material is 7cm, length 15cm.
Further, in S6, respectively red, yellow, blue, the green four kinds of colors of four kinds of different colours.
Further, in S7, the temperature range of drying is 35 DEG C~45 DEG C.
Beneficial effects of the present invention: it is produced using the combination of vertical press and horizontal press, and in traditional production work
It joined releasing process in skill, four color perfume pencil-leads being combined by four kinds of color alignments, color diversification, group can be made
Diversification is closed, and fragrant.
Detailed description of the invention
It in order to more clearly explain the embodiment of the invention or the technical proposal in the existing technology, below will be to institute in embodiment
Attached drawing to be used is needed to be briefly described, it should be apparent that, the accompanying drawings in the following description is only some implementations of the invention
Example, for those of ordinary skill in the art, without creative efforts, can also obtain according to these attached drawings
Obtain other attached drawings.
Fig. 1 is the flow diagram of the four described according to embodiments of the present invention color perfume pencil-lead production technologies.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, those of ordinary skill in the art's every other embodiment obtained belong to what the present invention protected
Range.
As shown in Figure 1, the four color perfume pencil-lead production technology of one kind, including following step according to embodiments of the present invention
It is rapid:
The raw material of four color perfume pencil-leads is put into kneader and is kneaded into clod shape core material by S1；
The clod shape core material is put into three-roller and rolls grinding by S2, and sheet core is made after so that its moisture is reached 12%~14%
Material；
The sheet core material is put into pulverizer and crushes by S3, and graininess core material is made；
Graininess core material standing 48 hours or more are made its temperature reach room temperature by S4；
The graininess core material is put into mold after vertical press squeezes and demoulds and cylindric core material is made by S5, then by institute
It states the cylindric core material quartering and is cut into fan-shaped column core material；
The fan-shaped column core material permutation and combination that S6 chooses four kinds of different colours is good, and is put into horizontal press, extrusion forming, is made
The four colors perfume pencil-lead；
The four colors perfume pencil-lead is put into dry room by S7, and drying makes its moisture < 1.5%, finished product is made.
In one particular embodiment of the present invention, the four colors perfume pencil-lead by following quality proportioning raw material system
At: 50-60 parts of kaolin, 6-15 parts of pigment toner, 10-15 parts of zinc stearate, 6-10 parts of CMC carboxymethyl cellulose, wax 25-30
Part, 3 parts of essence.
It in one particular embodiment of the present invention, first will be by the weighted kaolin of quality proportioning, pigment colour in S1
In powder and CMC carboxymethyl cellulose investment kneader, dry powder is stirred 30~60 minutes, then will press the weighted tristearin of quality proportioning
Sour zinc, wax and essence are poured into kneader after dissolving after stirring mediates, and the clod shape core material is made.
In one particular embodiment of the present invention, in S4, the temperature range of the room temperature is 23 DEG C ± 2 DEG C.
In one particular embodiment of the present invention, in S5, the diameter of the cylindric core material is 7cm, and length is
15cm。
In one particular embodiment of the present invention, in S6, respectively red, yellow, blue, the green four kinds of face of four kinds of different colours
Color.
In one particular embodiment of the present invention, in S7, the temperature range of drying is 35 DEG C~45 DEG C.
In order to facilitate above-mentioned technical proposal of the invention is understood, below by way of specifically used mode to above-mentioned skill of the invention
Art scheme is described in detail.
The manufacturing technique of the present invention are as follows kneading → grinding → crushing → standing → demoulding → molding → drying, production process
The equipment of middle use has kneader, three-roller, pulverizer, vertical press, horizontal press
Kneading of the present invention by the raw material of four color perfume pencil-leads by traditional pencil-lead production technology, grinds, crushes, stand
Afterwards, then with vertical press it squeezes and demoulds, be cut into fan-shaped column core material, then by the fan-shaped column core of four kinds of required colors
Material is put into horizontal press, extrusion forming, after permutation and combination by drying, finished product after molding.
Specifically: 1) it mediates: first throwing the weighted kaolin of quality proportioning, pigment toner and CMC carboxymethyl cellulose
Enter in kneader, dry powder stirs 30~60 minutes, then falls after dissolving by the weighted zinc stearate of quality proportioning, wax and essence
Enter in kneader after stirring kneading, obtained clod shape or clay shape core material.Each raw material mass mixture ratio of four color perfume pencil-leads
It is as shown in the table:
2) grind: core material the rolling using three-roller after kneading distributes the moisture in core material, reaches its moisture
12%~14%, and the large particulate matter in core material is crushed, adequately guarantee that the fine and smooth of core material crushes.
3) crush: the core material after grinding, because not easy to operate in the form of sheets, and core material marginal portion moisture distributes speed ratio center
Position it is fast, core material moisture can be made uneven, it is therefore desirable to which sheet core material is ground into graininess (granular size be in beans shape) core
Material, graininess core material not only facilitates operation but also smashed core material particle is uniformly mixed, and moisture is uniform.
4) it stands: smashed core material being stood into a period of time (48 hours or more), its temperature is made to reach room temperature, room temperature
Temperature range is 23 DEG C ± 2 DEG C.
5) it demoulds: the core material after standing is put into mold and squeezed by vertical press, core material can be in circle after demoulding
Column (diameter 7cm, length 15cm), then the cylindric core material quartering is cut into fan-shaped column core material
6) form: the fan-shaped column core material permutation and combination for choosing four kinds of different colours (red, yellow, blue, green four kinds of colors) is good, and same
When be put into horizontal press, four color perfume pencil-leads are made in extrusion forming.
7) dry: by four color perfume pencil-leads of forming, to be put into dry room, (temperature range of drying is 35 for drying
DEG C~45 DEG C), make its moisture < 1.5%, finished product is made.
In conclusion by means of above-mentioned technical proposal of the invention, using the group symphysis of vertical press and horizontal press
It produces, and joined releasing process in traditional production technology, four color perfume lead being combined by four kinds of color alignments can be made
Pen core, color diversification, combination diversification, and it is fragrant.
The above is merely preferred embodiments of the present invention, be not intended to limit the invention, it is all in spirit of the invention and
Within principle, any modification, equivalent replacement, improvement and so on be should all be included in the protection scope of the present invention.
Claims (7)
1. a kind of four color perfume pencil-lead production technologies, which comprises the following steps:
The raw material of four color perfume pencil-leads is put into kneader and is kneaded into clod shape core material by S1；
The clod shape core material is put into three-roller and rolls grinding by S2, and sheet core material is made after so that its moisture is reached 12% ~ 14%；
The sheet core material is put into pulverizer and crushes by S3, and graininess core material is made；
Graininess core material standing 48 hours or more are made its temperature reach room temperature by S4；
The graininess core material is put into mold after vertical press squeezes and demoulds and cylindric core material is made by S5, then by institute
It states the cylindric core material quartering and is cut into fan-shaped column core material；
The fan-shaped column core material permutation and combination that S6 chooses four kinds of different colours is good, and is put into horizontal press, extrusion forming, is made
The four colors perfume pencil-lead；
The four colors perfume pencil-lead is put into dry room by S7, and drying makes its moisture < 1.5%, finished product is made.
2. four colors perfume pencil-lead production technology according to claim 1, which is characterized in that the four colors perfume pencil-lead
It is made of the raw material of following quality proportioning: 50-60 parts of kaolin, 6-15 parts of pigment toner, 10-15 parts of zinc stearate, CMC carboxylic first
6-10 parts of base cellulose, 25-30 parts of wax, 3 parts of essence.
3. four colors perfume pencil-lead production technology according to claim 2, which is characterized in that, first will be by quality in S1
It matching in weighted kaolin, pigment toner and CMC carboxymethyl cellulose investment kneader, dry powder stirs 30 ~ 60 minutes, then
It is poured into after being dissolved by the weighted zinc stearate of quality proportioning, wax and essence in kneader after stirring kneading, the mud is made
Blocky core material.
4. four colors perfume pencil-lead production technology according to claim 1, which is characterized in that in S4, the room temperature
Temperature range is 23 DEG C ± 2 DEG C.
5. four colors perfume pencil-lead production technology according to claim 1, which is characterized in that described cylindric in S5
The diameter of core material is 7cm, length 15cm.
6. four colors perfume pencil-lead production technology according to claim 1, which is characterized in that in S6, four kinds of different face
Respectively red, yellow, blue, the green four kinds of colors of color.
7. four colors perfume pencil-lead production technology according to claim 1, which is characterized in that in S7, the temperature of drying
Range is 35 DEG C ~ 45 DEG C.