CN109434017A - A kind of wax material essence die manufacturing process - Google Patents
A kind of wax material essence die manufacturing process Download PDFInfo
- Publication number
- CN109434017A CN109434017A CN201811555736.XA CN201811555736A CN109434017A CN 109434017 A CN109434017 A CN 109434017A CN 201811555736 A CN201811555736 A CN 201811555736A CN 109434017 A CN109434017 A CN 109434017A
- Authority
- CN
- China
- Prior art keywords
- wax
- mold
- pattern
- maintained
- spraying machine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of wax material essence die manufacturing process, it is related to wax-pattern manufacturing field, the present invention is during mold is filled in material spraying machine shooting, mold is constantly moved horizontally back and forth by workbench, allow wax material that can preferably fill up mold inner-cavity, bubble is excluded, is very helpful to the precision and intensity that improve wax-pattern.After molding, cooling processing is carried out to mold and wax-pattern in time, avoids wax-pattern from occurring deforming etc. bad, is further ensured that the precision and yields of wax-pattern.
Description
Technical field
The present invention relates to wax-pattern manufacturing field, more specifically a kind of wax material essence die manufacturing process.
Background technique
Wax-pattern is a kind of common forging type.Investment pattern precision casting is mainly manufactured by mold manufacture, wax-pattern, shell mould manufactures and subsequent
The processes composition such as drying, roasting, casting, solidification.Wax-pattern is the apperance for forming casting type chamber, to obtain dimensional accuracy
The high casting with surface smoothness, first wax-pattern should inherently have high dimensional accuracy and surface smoothness.But wax-pattern
The factor that wax-pattern dimensional accuracy is influenced in manufacturing process is more complicated, and technological parameter is more, so existing manufacturing engineering of wax model is raw
The wax-pattern dimensional accuracy variation range for producing manufacture is bigger, it should need to design a kind of new, product size precision can be improved
Manufacturing engineering of wax model.
Summary of the invention
The invention discloses a kind of wax material essence die manufacturing process, it is therefore intended that solves existing in the prior art above-mentioned ask
Topic.
The present invention adopts the following technical scheme:
A kind of wax material essence die manufacturing process, comprising the following steps:
(1), the temperature of agitator is heated and maintained at 110 DEG C to 120 DEG C；Water temperature in cooling bucket is reduced and is maintained at 5
DEG C to 15 DEG C.
(2), by the perfusing hole of the nozzle access mold of material spraying machine, and the temperature of mold is heated and maintained at 110 DEG C extremely
120℃。
(3), the wax material got ready is poured into agitator and is poured into material spraying machine after mixing evenly, and start material spraying machine, by spraying
Material machine injects wax material in mold, until filling wax material in mold.
(4), graphene heat-conductive coating is filled up in stainless steel round tube, will be helped using air and be pushed glueballs three not
It is rolled around in rust steel round tube, forms the thermally conductive paint layer of graphene in the inner wall of electrode material layer, and carry out the processing that is heating and curing.
(6), cooled down with water cooling to mold and be maintained at 20 DEG C to 25 DEG C, be cooled and shaped wax material.
(7), mold is opened, wax-pattern after molding is removed from the molds, and is put into cooling bucket and impregnates 10 minutes.
Further, in the step (3), prior mold is fixed on horizontally movable workbench；In material spraying machine shooting
In the process, workbench constantly moves back and forth in the horizontal direction；It is first that workbench is static before penetrating wax and terminating, then by material spraying machine
Injection wax material 1 minute in mold, it is ensured that wax material is filled in mold.
Further, further include step (8): taking out wax-pattern, wax-pattern is repaired by repairing cured knife and wax material, and will give up
Wax is collected to temperature in the recycling bin for being maintained at 100 DEG C to 110 DEG C.
It further, further include step (9)；Wax-pattern packaging is sealed up for safekeeping in the incubator that temperature is maintained at 26 DEG C.
By the above-mentioned description to structure of the invention it is found that the present invention has the advantage that
The present invention constantly moves horizontally mold back and forth, makes wax material more preferable during mold is filled in material spraying machine shooting
Fill up mold inner-cavity, exclude bubble, be very helpful to the precision and intensity that improve wax-pattern.After molding, in time to mold
Cooling processing is carried out with wax-pattern, avoids wax-pattern from occurring deforming etc. bad, is further ensured that the precision and yields of wax-pattern.
Specific embodiment
Illustrate a specific embodiment of the invention below.
A kind of wax material essence die manufacturing process, comprising the following steps:
(1), the temperature of agitator is heated and maintained at 110 DEG C to 120 DEG C；Water temperature in cooling bucket is reduced and is maintained at 5
DEG C to 15 DEG C.
(2), by the perfusing hole of the nozzle access mold of material spraying machine, and the temperature of mold is heated and maintained at 110 DEG C extremely
120℃。
(3), the wax material got ready is poured into agitator and is poured into material spraying machine after mixing evenly, and start material spraying machine, by spraying
Material machine injects wax material in mold, until filling wax material in mold.Specifically, prior mold is fixed on horizontally movable
On workbench；In material spraying machine material shooting process, workbench constantly moves back and forth in the horizontal direction；Before penetrating wax and terminating, first will
Workbench is static, then is injected in mold from material spraying machine wax material 1 minute, it is ensured that wax material is filled in mold.
(4), graphene heat-conductive coating is filled up in stainless steel round tube, will be helped using air and be pushed glueballs three not
It is rolled around in rust steel round tube, forms the thermally conductive paint layer of graphene in the inner wall of electrode material layer, and carry out the processing that is heating and curing.
(6), cooled down with water cooling to mold and be maintained at 20 DEG C to 25 DEG C, be cooled and shaped wax material.
(7), mold is opened, wax-pattern after molding is removed from the molds, and is put into cooling bucket and impregnates 10 minutes.
(8): taking out wax-pattern, wax-pattern is repaired by repairing cured knife and wax material, and slop wax is collected to temperature and is maintained at
In 100 DEG C to 110 DEG C of recycling bin.
(9)；Wax-pattern packaging is sealed up for safekeeping in the incubator that temperature is maintained at 26 DEG C.
The present invention constantly moves horizontally mold during mold is filled in material spraying machine shooting back and forth, allows wax material can be with
Mold inner-cavity is preferably filled up, bubble is excluded, is very helpful to the precision and intensity that improve wax-pattern.It is right in time after molding
Mold and wax-pattern carry out cooling processing, avoid wax-pattern from occurring deforming etc. bad, are further ensured that the precision and yields of wax-pattern.
The above is only a specific embodiment of the present invention, but the design concept of the present invention is not limited to this, all to utilize this
Design makes a non-material change to the present invention, and should all belong to behavior that violates the scope of protection of the present invention.
Claims (4)
1. a kind of wax material essence die manufacturing process, which comprises the following steps:
(1), the temperature of agitator is heated and maintained at 110 DEG C to 120 DEG C；Water temperature in cooling bucket is reduced and is maintained at 5
DEG C to 15 DEG C；
(2), by the perfusing hole of the nozzle access mold of material spraying machine, and the temperature of mold is heated and maintained at 110 DEG C to 120
℃；
(3), the wax material got ready is poured into agitator and is poured into material spraying machine after mixing evenly, and start material spraying machine, by material spraying machine
Wax material is injected in mold, until filling wax material in mold；
(4), graphene heat-conductive coating is filled up in stainless steel round tube, will be helped using air and be pushed glueballs three in stainless steel
It is rolled around in round tube, forms the thermally conductive paint layer of graphene in the inner wall of electrode material layer, and carry out the processing that is heating and curing；
(6), cooled down with water cooling to mold and be maintained at 20 DEG C to 25 DEG C, be cooled and shaped wax material；
(7), mold is opened, wax-pattern after molding is removed from the molds, and is put into cooling bucket and impregnates 10 minutes.
2. a kind of wax material essence die manufacturing process according to claim 1, it is characterised in that: in the step (3), in advance
Mold is fixed on horizontally movable workbench；In material spraying machine material shooting process, workbench is constantly in the horizontal direction back and forth
It is mobile；It is first that workbench is static before penetrating wax and terminating, then injected in mold from material spraying machine wax material 1 minute, it is ensured that note in mold
Full wax material.
3. a kind of wax material essence die manufacturing process according to claim 1, it is characterised in that: further include step (8): taking out
Wax-pattern repairs wax-pattern by repairing cured knife and wax material, and by slop wax collect to temperature be maintained at 100 DEG C to 110 DEG C return
It receives in bucket.
4. a kind of wax material essence die manufacturing process according to claim 1, it is characterised in that: further include step (9)；By wax
Mould packaging is sealed up for safekeeping in the incubator that temperature is maintained at 26 DEG C.