CN109431900A - A kind of shower wet tissue and preparation method thereof - Google Patents
A kind of shower wet tissue and preparation method thereof Download PDFInfo
- Publication number
- CN109431900A CN109431900A CN201811487734.1A CN201811487734A CN109431900A CN 109431900 A CN109431900 A CN 109431900A CN 201811487734 A CN201811487734 A CN 201811487734A CN 109431900 A CN109431900 A CN 109431900A
- Authority
- CN
- China
- Prior art keywords
- parts
- weight
- layer
- wet wipe
- wet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of shower wet tissue and preparation method thereof, including compound nonwoven cloth and wet wipe solution, the compound nonwoven cloth successively includes skin-friendly layer, middle layer and bottom from top to bottom；The middle layer includes the raw material of following parts by weight: 25-35 parts of soybean fibers, 10-20 parts of hemps, 35-50 parts of poly fibres, 1-3 parts of polyacrylamide amine dispersants；The skin-friendly layer of the compound nonwoven cloth is ecological cotton fiber layer, and bottom is alginate fibre layer, is uniformly distributed on the bottom in hemispheroidal protrusion；The wet wipe solution is adhered in middle layer, and the weight ratio of the middle layer of the wet wipe solution and the compound nonwoven cloth is 2-3:1.Shower wet tissue prepared by the present invention has the advantages that easy to carry, cleaning is thorough, clean hygiene.
Description
Technical field
The present invention relates to hygiene article sectors more particularly to a kind of shower wet tissue and preparation method thereof.
Background technique
Go out tourism, need of work other places of vacation is gone on business, and all unavoidably to consider the problems of hotel accommodations.Though in hotel
It so is ready for life bath accessory, but hygienic issues are unable to get guarantee.Secondly, hotel, for save the cost, what is provided exempts from
Taking bath article is all often the unknown brand for purchasing some simple processes.Using this product, generally all clean not completely,
It is also easy to the situations such as cause to have dry skin, itch all over, What is more will lead to allergic reaction.
People carry out strenuous exercise, after gymnasium carries out weight-reducing moulding exercise in gymnasium, and body is largely perspired, together
When with fine hair hole discharge part grease object.Present sports buildings is furnished with shower room mostly, it is convenient wash away in time with sweat,
The sticky sense caused by mixing of grease and floating dust, but carry shower cream cleaning body and seem inconvenient.If will take a shower
Dew be processed into shower wet tissue, it is not only easy to carry, and using when wet tissue can also act as bath balls, facilitate blistering and wiping
Skin.
Summary of the invention
Therefore, for the above content, the present invention provides a kind of shower wet tissue, and the solution prior art is unhygienic, cleaning is not thorough
Bottom, problem inconvenient to carry.
In order to achieve the above objectives, the present invention is achieved by the following technical solutions: a kind of shower wet tissue, including compound
Non-woven fabrics and wet wipe solution, the compound nonwoven cloth successively include skin-friendly layer, middle layer and bottom from top to bottom；The centre
Layer includes the raw material of following parts by weight: 25-35 parts of soybean fibers, 10-20 parts of hemps, 35-50 parts of polyglycolic acids
Fiber, 1-3 parts of polyacrylamide amine dispersants；The wet wipe solution is adhered in middle layer, and the wet wipe solution is by following heavy
Measure each raw material component composition of percentage:
A further improvement is that: the skin-friendly layer of the compound nonwoven cloth is ecological cotton fiber layer, and bottom is alginate fibre
Layer.
A further improvement is that: the step of preparation process of the shower wet tissue is as follows:
Step1: the preparation of wet wipe solution
(1) deionized water for weighing set parts by weight in formula first is heated to 75-85 DEG C, successively adds under stirring condition
Enter cocounut oil polyoxyethylene alcohol ether sodium sulfate, sodium laureth sulfate, stirring and dissolving is uniform；
(2) then above-mentioned steps (1) acquired solution is cooled to 56-60 DEG C, C8-C14 alkyl polyglycoside, coconut palm is added
The more sodium of seed oil diglycollic amide, glycerol, Cocoamidopropyl betaine, Hamposyl L, stirring and dissolving are uniform；
(3) finally step (2) acquired solution is cooled to 40-45 DEG C hereinafter, soapberry extract, spring Huang is added
Chrysanthemum extracting solution, radix scutellariae extract, licorice, Phenoxyethanol, Sensiva SC50, fragrance of a flower fruity, are uniformly mixed system
Obtain wet wipe solution.
Step2: the preparation of the middle layer of wet wipe solution is adhered to
(1) soybean fiber, hemp, poly fibre, polyacrylamide dispersion of above-mentioned parts by weight are taken
Agent, then plus 200-300 parts by weight of deionized water, then loosened, mixed in opener, fiber suspension slurries are made；
(2) fiber suspension slurries obtained above are delivered on wet-web former, filter out water and forms web；
(3) above-mentioned web is subjected to spun lacing reinforcing, antimicrobial treatment process；
Wherein spun lacing reinforces process and shares 6 water jets, and spun lacing pressure is gradually successively decreased from middle part to two sides, along advance side
To being followed successively by 8MPa, 10MPa, 12MPa, 12MPa, 10MPa, 8Mpa；
Antimicrobial fluid in antimicrobial treatment process includes the raw material of following parts by weight: 1-3 parts by weight Rosemary Oil, 0.8-
1.5 parts by weight Rhizoma Curcumae extracts, 2-4 parts by weight cymbopogon distans extract, 90-120 parts by weight of deionized water；
(4) the adherency process for finally carrying out prebake, blowing hot-air, wet wipe solution, is made and is stained with wet wipe solution
Middle layer；
110-130 DEG C of prebake temperature, drying time 40-50min；The wet wipe solution and the compound nonwoven cloth
The weight ratio of middle layer is 2-3:1；
The adhesion method of the wet wipe solution is using any one in spin-coating method, rolling method or infusion method；
Step3: the surrounding edge of skin-friendly layer and bottom is sutured by bonding mode, to wrap middle layer；Then
By dotting process, the bounding point of a plurality of connection middle layers, bottom is formed at the middle part of skin-friendly layer, by skin-friendly layer, middle layer
It is got ready with bottom hot pressing compound；
Bonding mode selects any one of hot melt adhesive bonding or ultrasonic bonds.
A further improvement is that: it is uniformly distributed on the bottom in hemispheroidal protrusion.
By using preceding solution, the beneficial effects of the present invention are:
(1) raw material of compound nonwoven cloth is Biodegradable fibers, and burden will not be brought to environment, is met sustainable
The theory of development.
(2) before adhering to wet wipe solution, the process that the middle layer of compound nonwoven cloth carries out blowing hot-air can both be risen
To the effect of secondary drying, additionally it is possible to which, so that middle layer becomes more fluffy, soft, gap helps to improve down greatly between fiber
The adherency speed of procedure wet wipe solution.
(3) compound nonwoven cloth both can be used as Disposable tower exclusive use, can also cooperate to be made with wet wipe solution and wash one's hair
Wet tissue is bathed, realizes the dual function of Wet-dry.
(4) traditional shower mode is effectively substituted, solves the disadvantage that original shower cream and towel have a single function, more defends
Raw, convenient, the efficient economizing time.
(5) shower wet tissue prepared by the present invention has the advantages that antibacterial, softness are good.
(6) wet tissue product of the invention is suitble to after being used in outdoor or indoor activity, use when being taken a shower, non-woven fabrics
Bottom can serve as the effects of bath balls, facilitate the skin that blisters and scrub.
Specific embodiment
Carry out the embodiment that the present invention will be described in detail below with reference to specific embodiment, how the present invention is applied whereby
Technological means solves technical problem, and the realization process for reaching technical effect can fully understand and implement.
Unless otherwise specified, the conventional hand that technological means employed in embodiment is well known to those skilled in the art
Section, used reagent and product are also available commercial.The source of agents useful for same, trade name and it is necessary to list
Its constituent person is indicated on the first occurrence.
Embodiment one
A kind of shower wet tissue, including compound nonwoven cloth and wet wipe solution, the compound nonwoven cloth successively include from top to bottom
Skin-friendly layer, middle layer and bottom；The skin-friendly layer of the compound nonwoven cloth is ecological cotton fiber layer, and bottom is alginate fibre layer, institute
It states and is uniformly distributed on bottom in hemispheroidal protrusion.
The step of preparation process of the shower wet tissue is as follows:
Step1: the preparation of wet wipe solution
(1) 54.28% deionized water of weight percent is weighed first, is heated to 75 DEG C, is sequentially added under stirring condition
20% cocounut oil polyoxyethylene alcohol ether sodium sulfate, 1% sodium laureth sulfate, stirring and dissolving are uniform；
(2) then step (1) acquired solution is cooled to 56 DEG C, 1%C8-C14 alkyl polyglycoside, 1% coconut is added
Oily diglycollic amide, 1% glycerol, 10% Cocoamidopropyl betaine, 5% sodium lauroyl sarcosine, stirring and dissolving are uniform；
(3) finally step (2) acquired solution is cooled to 40 DEG C hereinafter, 1% soapberry extract, 5% spring is added
Yellow chrysanthemum extracting solution, 0.1% radix scutellariae extract, 0.1% licorice, 0.5% Phenoxyethanol, 0.01% Sensiva SC50,
0.01% floral perfume is uniformly mixed obtained wet wipe solution.
Step2: the preparation of the middle layer of wet wipe solution is adhered to
(1) 25 parts by weight of soybean azelons, 10 parts by weight hemps, 35 parts by weight poly fibres, 1 are taken
Parts by weight of polypropylene amide dispersing agent, then plus 200 parts by weight of deionized water, then loosened, mixed in opener, make
At fiber suspension slurries；
(2) fiber suspension slurries obtained above are delivered on wet-web former, filter out water and forms web；
(3) above-mentioned web is subjected to spun lacing reinforcing, antimicrobial treatment process；
Wherein spun lacing reinforces process and shares 6 water jets, and spun lacing pressure is gradually successively decreased from middle part to two sides, along advance side
To being followed successively by 8MPa, 10MPa, 12MPa, 12MPa, 10MPa, 8Mpa；
Antimicrobial fluid in antimicrobial treatment process includes the raw material of following parts by weight: 1 parts by weight Rosemary Oil, 0.8 weight
Part Rhizoma Curcumae extract, 2 parts by weight cymbopogon distans extracts, 90 parts by weight of deionized water；
(4) the adherency process for finally carrying out prebake, blowing hot-air, wet wipe solution, is made and is stained with wet wipe solution
Middle layer；
110 DEG C of prebake temperature, drying time 50min；The middle layer of the wet wipe solution and the compound nonwoven cloth
Weight ratio is 3:1；The adhesion method of the wet wipe solution uses spin-coating method；The centrifugal force generated when being rotated by middle layer,
The wet wipe solution fallen on middle layer non-woven fabrics is uniformly adhered；Rotation speed is adjustable, and range is in 0-1200r/min；
(4) surrounding edge of skin-friendly layer and bottom is sutured by hot melt adhesive bonding mode, to wrap middle layer；
Then by dotting process, the bounding points of a plurality of connection middle layers, bottom are formed at the middle part of skin-friendly layer, by skin-friendly layer, in
Interbed and bottom hot pressing are got ready compound.
Embodiment two
A kind of shower wet tissue, structure and embodiment one are consistent, and the step of preparation process of the shower wet tissue is as follows:
Step1: the preparation of wet wipe solution
(1) deionized water for weighing weight percent 50.7% first is heated to 80 DEG C, sequentially adds under stirring condition
10% cocounut oil polyoxyethylene alcohol ether sodium sulfate, 3% sodium laureth sulfate, stirring and dissolving are uniform；
(2) then step (1) acquired solution is cooled to 58 DEG C, 3%C8-C14 alkyl polyglycoside, 2% coconut is added
Oily diglycollic amide, 2% glycerol, 5% Cocoamidopropyl betaine, 10% sodium lauroyl sarcosine, stirring and dissolving are uniform；
(3) finally step (2) acquired solution is cooled to 42 DEG C hereinafter, 10% soapberry extract, 3% is added
Yellow chamomile extracting solution, 0.2% radix scutellariae extract, 0.3% licorice, 0.7% Phenoxyethanol, 0.05% ethylhexyl are sweet
Oil, 0.05% fruit essence, are uniformly mixed obtained wet wipe solution.
Step2: the preparation of the middle layer of wet wipe solution is adhered to
(1) 30 parts by weight of soybean azelons, 15 parts by weight hemps, 42 parts by weight poly fibres, 2 are taken
Parts by weight of polypropylene amide dispersing agent, then plus 250 parts by weight of deionized water, then loosened, mixed in opener, make
At fiber suspension slurries；
(2) fiber suspension slurries obtained above are delivered on wet-web former, filter out water and forms web；
(3) above-mentioned web is subjected to spun lacing reinforcing, antimicrobial treatment process；
Wherein spun lacing reinforces process and shares 6 water jets, and spun lacing pressure is gradually successively decreased from middle part to two sides, along advance side
To being followed successively by 8MPa, 10MPa, 12MPa, 12MPa, 10MPa, 8Mpa；
Antimicrobial fluid in antimicrobial treatment process includes the raw material of following parts by weight: 2 parts by weight Rosemary Oils, 1.2 weight
Part Rhizoma Curcumae extract, 3 parts by weight cymbopogon distans extracts, 100 parts by weight of deionized water；
(4) the adherency process for finally carrying out prebake, blowing hot-air, wet wipe solution, is made and is stained with wet wipe solution
Middle layer；
120 DEG C of prebake temperature, drying time 45min；The middle layer of the wet wipe solution and the compound nonwoven cloth
Weight ratio is 2:1；The adhesion method of the wet wipe solution uses rolling method；Coating roll surface is uniformly distributed wet wipe solution,
It contacts, is coated with wet wipe solution in transfer roller rotation process coated in centre with coating transfer roller in middle layer non-woven fabrics transmit process
The surface of layer non-woven fabrics.
Step3: the surrounding edge of skin-friendly layer and bottom is sutured by ultrasonic bonds mode, to wrap centre
Layer；Then by dotting process, the bounding point of a plurality of connection middle layers, bottom is formed at the middle part of skin-friendly layer, by pro-skin
Layer, middle layer and bottom hot pressing are got ready compound.
Embodiment three
A kind of shower wet tissue, structure and embodiment one are consistent, and the step of preparation process of the compound nonwoven cloth is as follows:
Step1: the preparation of wet wipe solution
(1) deionized water for weighing weight percent 53% first is heated to 85 DEG C, sequentially adds 5% under stirring condition
Cocounut oil polyoxyethylene alcohol ether sodium sulfate, 5% sodium laureth sulfate, stirring and dissolving are uniform；
(2) then step (1) acquired solution is cooled to 60 DEG C, 6%C8-C14 alkyl polyglycoside, 3% coconut is added
Oily diglycollic amide, 3% glycerol, 1% Cocoamidopropyl betaine, 1% sodium lauroyl sarcosine, stirring and dissolving are uniform；
(3) finally step (2) acquired solution is cooled to 45 DEG C hereinafter, 20% soapberry extract, 1% is added
Yellow chamomile extracting solution, 0.3% radix scutellariae extract, 0.5% licorice, 1% Phenoxyethanol, 0.1% Sensiva SC50,
0.1% floral perfume is uniformly mixed obtained wet wipe solution.
Step2: the preparation of the middle layer of wet wipe solution is adhered to
(1) take the soybean fibers of 35 parts by weight, 20 parts by weight hemps, 50 parts by weight poly fibres,
3 parts by weight of polypropylene amide dispersing agents, then plus 300 parts by weight of deionized water, then loosened, mixed in opener, make
At fiber suspension slurries；
(2) fiber suspension slurries obtained above are delivered on wet-web former, filter out water and forms web；
(3) above-mentioned web is subjected to spun lacing reinforcing, antimicrobial treatment process；
Wherein spun lacing reinforces process and shares 6 water jets, and spun lacing pressure is gradually successively decreased from middle part to two sides, along advance side
To being followed successively by 8MPa, 10MPa, 12MPa, 12MPa, 10MPa, 8Mpa；
Antimicrobial fluid in antimicrobial treatment process includes the raw material of following parts by weight: 3 parts by weight Rosemary Oils, 1.5 weight
Part Rhizoma Curcumae extract, 4 parts by weight cymbopogon distans extracts, 120 parts by weight of deionized water；
(4) the adherency process for finally carrying out prebake, blowing hot-air, wet wipe solution, is made and is stained with wet wipe solution
Middle layer；
130 DEG C of prebake temperature, drying time 40min；The middle layer of the wet wipe solution and the compound nonwoven cloth
Weight ratio is 2.5:1；The adhesion method of the wet wipe solution uses infusion method, and the middle layer after blowing hot-air is impregnated
In wet wipe solution, taken out after 1h；
Step3: the surrounding edge of skin-friendly layer and bottom is sutured by ultrasonic bonds mode, to wrap centre
Layer；Then by dotting process, the bounding point of a plurality of connection middle layers, bottom is formed at the middle part of skin-friendly layer, by pro-skin
Layer, middle layer and bottom hot pressing are got ready compound.
Cocounut oil polyoxyethylene alcohol ether sodium sulfate and sodium laureth sulfate is added under 75-85 DEG C of high temperature in deionized water
Its dissolubility and dispersion effect can be improved；In view of C8-C14 alkyl polyglycoside, coconut palm are added at 56-60 DEG C in terms of energy saving
Seed oil diglycollic amide, glycerol, Cocoamidopropyl betaine and sodium lauroyl sarcosine, do not influence raw material dissolubility and
Dispersibility；And the extract in natural goods source, essence, Phenoxyethanol and Sensiva SC50 are thermo-labile, therefore be further cooled to
45 DEG C are added again.
The foregoing descriptions are merely the embodiment using this origination techniques content, any those skilled in the art use this wound
Make done modifications and changes, all belong to the scope of the patents of this creation opinion, and is not limited to those disclosed embodiments.
Claims (4)
1. a kind of shower wet tissue, including compound nonwoven cloth and wet wipe solution, it is characterised in that: the compound nonwoven cloth is from top to bottom
It successively include skin-friendly layer, middle layer and bottom；The middle layer includes the raw material of following parts by weight: 25-35 portions of soybean proteins are fine
Dimension, 10-20 parts of hemps, 35-50 parts of poly fibres, 1-3 parts of polyacrylamide amine dispersants；The wet wipe solution is viscous
It invests in middle layer, the wet wipe solution is made of each raw material component of following weight percent:
2. a kind of shower wet tissue according to claim 1, it is characterised in that: the skin-friendly layer of the compound nonwoven cloth is ecology
Cotton fiber layer, bottom are alginate fibre layer.
3. the preparation method of -2 described in any item shower wet tissues according to claim 1, it is characterised in that: the preparation process step
It is rapid as follows:
Step1: the preparation of wet wipe solution
(1) deionized water for weighing set parts by weight in formula first, is heated to 75-85 DEG C, sequentially adds coconut palm under stirring condition
Oily polyoxyethylene alcohol ether sodium sulfate, sodium laureth sulfate, stirring and dissolving are uniform；
(2) then above-mentioned steps (1) acquired solution is cooled to 56-60 DEG C, C8-C14 alkyl polyglycoside, coconut oil two is added
The more sodium of glycollic amide, glycerol, Cocoamidopropyl betaine, Hamposyl L, stirring and dissolving are uniform；
(3) finally step (2) acquired solution is cooled to 40-45 DEG C hereinafter, soapberry extract is added, yellow chamomile is extracted
Liquid, radix scutellariae extract, licorice, Phenoxyethanol, Sensiva SC50, fragrance of a flower fruity, are uniformly mixed obtained wet tissue
Solution.
Step2: the preparation of the middle layer of wet wipe solution is adhered to
(1) soybean fiber, hemp, poly fibre, polyacrylamide amine dispersant of above-mentioned parts by weight are taken, then
Add 200-300 parts by weight of deionized water, then loosened, mixed in opener, fiber suspension slurries are made；
(2) fiber suspension slurries obtained above are delivered on wet-web former, filter out water and forms web；
(3) above-mentioned web is subjected to spun lacing reinforcing, antimicrobial treatment process；
Wherein spun lacing reinforces process and shares 6 water jets, and spun lacing pressure is gradually successively decreased from middle part to two sides, successively along direction of advance
For 8MPa, 10MPa, 12MPa, 12MPa, 10MPa, 8Mpa；
Antimicrobial fluid in antimicrobial treatment process includes the raw material of following parts by weight: 1-3 parts by weight Rosemary Oil, 0.8-1.5 weight
Measure part Rhizoma Curcumae extract, 2-4 parts by weight cymbopogon distans extract, 90-120 parts by weight of deionized water；
(4) the adherency process for finally carrying out prebake, blowing hot-air, wet wipe solution, is made the centre for being stained with wet wipe solution
Layer；
110-130 DEG C of prebake temperature, drying time 40-50min；The middle layer of the wet wipe solution and the compound nonwoven cloth
Weight ratio be 2-3:1；
The adhesion method of the wet wipe solution is using any one in spin-coating method, rolling method or infusion method；
Step3: the surrounding edge of skin-friendly layer and bottom is sutured by bonding mode, to wrap middle layer；Then pass through
Dotting process forms the bounding point of a plurality of connection middle layers, bottom at the middle part of skin-friendly layer, by skin-friendly layer, middle layer and bottom
Layer hot pressing is got ready compound；
Bonding mode selects any one of hot melt adhesive bonding or ultrasonic bonds.
4. the preparation method of shower wet tissue according to claim 3, it is characterised in that: be uniformly distributed on the bottom in half
The protrusion of sphere.