CN109402644A - A kind of degreased cleaning agent for metallic conduit - Google Patents
A kind of degreased cleaning agent for metallic conduit Download PDFInfo
- Publication number
- CN109402644A CN109402644A CN201811464709.1A CN201811464709A CN109402644A CN 109402644 A CN109402644 A CN 109402644A CN 201811464709 A CN201811464709 A CN 201811464709A CN 109402644 A CN109402644 A CN 109402644A
- Authority
- CN
- China
- Prior art keywords
- parts
- minutes
- metallic conduit
- added
- cleaning agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to metal welded tube processing technique fields, and in particular to a kind of degreased cleaning agent for metallic conduit.The present invention is prepared from the following raw materials: 15-30 parts of lauryl sodium sulfate, 5-15 parts of sodium carboxymethylcellulose, 5-10 parts of microcrystalline cellulose, 5-10 parts of flake asbestos, 5-10 parts of pre-gelatinized cornstarch, 4-8 parts of beta-cyclodextrin, 4-8 parts of polyethylene glycol, 3-5 parts of pectin, 1-3 parts of isopropyl acetone, 1-3 parts of sodium carbonate, 2-8 parts of acetic acid, 2-6 parts of oxalic acid, 120-150 parts of water.The degreaser that the present invention makes, degreasing cleaning effect is good, can effectively remove grease on metallic conduit, spot, it can effectively avoid grease to the subsequent spray painting to metallic conduit, have an impact, and after the degreaser use of the application, easy cleaning, noresidue will not damage metallic conduit.
Description
Technical field:
The present invention relates to the processing fields of metal welded tube, and in particular to a kind of cleaning by degreasing for metallic conduit
Agent.
Background technique:
Metal surface spray painting is a kind of method for protecting the not oxidized corrosion of metal.The corrosion phenomenon around us occurs
Refer to that various types of materials (comprehensive function for having chemistry, electrochemistry and several physical factors) under environmental activity is damaged, performance
Decline or the deterioration of state.It and is then a kind of critically important anticorrosive metal holding means in metal surface spray painting coating.Well
Spray painting coating protection layer keep it is continuous whole lossless, be well combined, can become inhibit corrosive medium intrusion barrier.
Since corrosion is irreversible spontaneous process, even good spray painting coating retaining layer, it is also difficult to protection gold
Category do not corrode, especially when metal surface spray painting coating layer combine it is bad, be damaged, or have pin hole, be bubbled, cracking,
The defects of falling off, varnished protective effect will be greatly reduced, or even the disastrous effect for causing metal erosion to aggravate.So to spray painting
Coating metal corrosion factor carries out serious analysis, and it is very necessary for taking effective countermeasure prevention.
The clean-up performance of metal surface seriously affects the binding force of coating layer of paint, the water of article surface residual or absorption,
The elimination such as greasy dirt and other foreign matters is not clean, often generates pin hole, dross, peeling or combines the failures such as bad.
Summary of the invention:
The technical problem to be solved by the present invention lies in overcoming the defects of the prior art, provides a kind of for metallic conduit
Degreased cleaning agent.
The following technical solution is employed for the technical problems to be solved by the invention to realize:
A kind of degreased cleaning agent for metallic conduit, which is characterized in that be prepared from the following raw materials:
15-30 parts of lauryl sodium sulfate, 5-15 parts of sodium carboxymethylcellulose, 5-10 parts of microcrystalline cellulose, flake asbestos 5-
10 parts, 5-10 parts of pre-gelatinized cornstarch, 4-8 parts of beta-cyclodextrin, 4-8 parts of polyethylene glycol, 3-5 parts of pectin, 1-3 parts of isopropyl acetone,
1-3 parts of sodium carbonate, 2-8 parts of acetic acid, 2-6 parts of oxalic acid, 120-150 parts of water.
The degreased cleaning agent for metallic conduit, which is characterized in that preferred following raw material is made:
25 parts of lauryl sodium sulfate, 10 parts of sodium carboxymethylcellulose, 8 parts of microcrystalline cellulose, 8 parts of flake asbestos, pre-gelatinized
8 parts of cornstarch, 6 parts of beta-cyclodextrin, 6 parts of polyethylene glycol, 4 parts of pectin, 2 parts of isopropyl acetone, 2 parts of sodium carbonate, 5 parts of acetic acid, oxalic acid 4
Part, 140 parts of water.
The flake asbestos passes through modification, processing method using preceding are as follows: flake asbestos is added in 2 times of parts by weight water,
30min is stood after fully dispersed, adds disodium hydrogen phosphate and silane coupling agent, utilizes Surface Treatment with Plasma after mixing
Machine handles 15s, and after treatment, which is transferred to rapidly in 5-10 DEG C of environment, stands 5h, and sesbania gum is then added, aluminium polychloride, rests in peace
Perfume (or spice), microwave treatment 3min, gained mixture are sent into spray drying under microwave frequency 2450MHz, power 700W after being sufficiently mixed
Machine, finally by dry gained particulate abrasive at powder.
The flake asbestos, disodium hydrogen phosphate, silane coupling agent, sesbania gum, aluminium polychloride, styrax weight fraction ratio are
5:1:0.5:0.5:0.3:0.1.
The degreased cleaning agent for metallic conduit, the production method is as follows:
(1) flake asbestos, pre-gelatinized cornstarch, beta-cyclodextrin are added water and stirred into mixed solution, dodecyl sulphur is added
Sour sodium is put into the microwave treater under microwave frequency 2400MHz, power 600W and handles 10 minutes, stands 10 minutes, carboxylic first is added
Base sodium cellulosate is put into microwave treater and handles 10 minutes, stands 10 minutes, add microcrystalline cellulose, be put into microwave treatment
Device is handled 10 minutes, is stood 10 minutes, is obtained material I;
(2) polyethylene glycol, isopropyl acetone, sodium carbonate are added in material I, carry out heating stirring, heating speed be 5 DEG C/
Min is heated 15-20 minutes, and is stirred continuously, and obtains material II;
(3) pectin, acetic acid, oxalic acid are added in material II, are put into blender, with the speed of 800-1000r/min
Stirring 10-15 minutes, can be prepared by.
The beneficial effects of the present invention are:
1, the degreaser that makes of the present invention, degreasing cleaning effect is good, can effectively remove grease on metallic conduit, dirt
Stain can effectively avoid grease to the subsequent spray painting to metallic conduit, have an impact, and after the degreaser use of the application, easily
Cleaning, noresidue will not damage metallic conduit;
2, the present invention with lauryl sodium sulfate, sodium carboxymethylcellulose, microcrystalline cellulose be main cleaning raw material, it is compound
Cleaning proportion, has not only reached cleaning effect, but also remain gentle degree, the application also added modified flake asbestos, pre-gelatinized
Cornstarch, beta-cyclodextrin increase viscous stickiness and the adsorptivity to grease, enhance degreasing cleaning effect, also added acetic acid
And oxalic acid, softening grease, spot can be played, enables grease, spot are easier to be cleaned out, noresidue;
3, flake asbestos is passing through modification using preceding in the present invention, modified flake asbestos improve rheological characteristic, compatibility,
Viscous stickiness, lipophilicity and hydrophily can be improved the viscous stickiness of degreaser and the compatibility of each ingredient after being applied to degreaser,
Make greasy soils be easier to be sticked and washed away by viscous, plays emulsification.
Specific embodiment:
In order to be easy to understand the technical means, the creative features, the aims and the efficiencies achieved by the present invention, tie below
Specific embodiment is closed, the present invention is further explained.
Embodiment 1:
A kind of degreased cleaning agent for metallic conduit, which is characterized in that be prepared from the following raw materials:
15 parts of lauryl sodium sulfate, 5 parts of sodium carboxymethylcellulose, 5 parts of microcrystalline cellulose, 5 parts of flake asbestos, pre-gelatinized is beautiful
5 parts of rice starch, 4 parts of beta-cyclodextrin, 4 parts of polyethylene glycol, 3 parts of pectin, 1 part of isopropyl acetone, 1 part of sodium carbonate, 2 parts of acetic acid, oxalic acid 2
Part, 120 parts of water.
The flake asbestos passes through modification, processing method using preceding are as follows: flake asbestos is added in 2 times of parts by weight water,
30min is stood after fully dispersed, adds disodium hydrogen phosphate and silane coupling agent, utilizes Surface Treatment with Plasma after mixing
Machine handles 15s, and after treatment is transferred to rapidly in 5 DEG C of environment and stands 5h, and sesbania gum, aluminium polychloride, styrax is then added,
Microwave treatment 3min, gained mixture are sent into spray dryer under microwave frequency 2450MHz, power 700W after being sufficiently mixed,
Finally by dry gained particulate abrasive at powder.
The flake asbestos, disodium hydrogen phosphate, silane coupling agent, sesbania gum, aluminium polychloride, styrax weight fraction ratio are
5:1:0.5:0.5:0.3:0.1.
The degreased cleaning agent for metallic conduit, the production method is as follows:
(1) flake asbestos, pre-gelatinized cornstarch, beta-cyclodextrin are added water and stirred into mixed solution, dodecyl sulphur is added
Sour sodium is put into the microwave treater under microwave frequency 2400MHz, power 600W and handles 10 minutes, stands 10 minutes, carboxylic first is added
Base sodium cellulosate is put into microwave treater and handles 10 minutes, stands 10 minutes, add microcrystalline cellulose, be put into microwave treatment
Device is handled 10 minutes, is stood 10 minutes, is obtained material I;
(2) polyethylene glycol, isopropyl acetone, sodium carbonate are added in material I, carry out heating stirring, heating speed be 5 DEG C/
Min is heated 15 minutes, and is stirred continuously, and obtains material II;
(3) pectin, acetic acid, oxalic acid are added in material II, are put into blender, stir 10 with the speed of 800r/min
Minute, it can be prepared by.
Embodiment 2:
The degreased cleaning agent for metallic conduit, which is characterized in that preferred following raw material is made:
25 parts of lauryl sodium sulfate, 10 parts of sodium carboxymethylcellulose, 8 parts of microcrystalline cellulose, 8 parts of flake asbestos, pre-gelatinized
8 parts of cornstarch, 6 parts of beta-cyclodextrin, 6 parts of polyethylene glycol, 4 parts of pectin, 2 parts of isopropyl acetone, 2 parts of sodium carbonate, 5 parts of acetic acid, oxalic acid 4
Part, 140 parts of water.
The flake asbestos passes through modification, processing method using preceding are as follows: flake asbestos is added in 2 times of parts by weight water,
30min is stood after fully dispersed, adds disodium hydrogen phosphate and silane coupling agent, utilizes Surface Treatment with Plasma after mixing
Machine handles 15s, and after treatment is transferred to rapidly in 10 DEG C of environment and stands 5h, and sesbania gum is then added, aluminium polychloride, rests in peace
Perfume (or spice), microwave treatment 3min, gained mixture are sent into spray drying under microwave frequency 2450MHz, power 700W after being sufficiently mixed
Machine, finally by dry gained particulate abrasive at powder.
The flake asbestos, disodium hydrogen phosphate, silane coupling agent, sesbania gum, aluminium polychloride, styrax weight fraction ratio are
5:1:0.5:0.5:0.3:0.1.
The degreased cleaning agent for metallic conduit, the production method is as follows:
(1) flake asbestos, pre-gelatinized cornstarch, beta-cyclodextrin are added water and stirred into mixed solution, dodecyl sulphur is added
Sour sodium is put into the microwave treater under microwave frequency 2400MHz, power 600W and handles 10 minutes, stands 10 minutes, carboxylic first is added
Base sodium cellulosate is put into microwave treater and handles 10 minutes, stands 10 minutes, add microcrystalline cellulose, be put into microwave treatment
Device is handled 10 minutes, is stood 10 minutes, is obtained material I;
(2) polyethylene glycol, isopropyl acetone, sodium carbonate are added in material I, carry out heating stirring, heating speed be 5 DEG C/
Min is heated 20 minutes, and is stirred continuously, and obtains material II;
(3) pectin, acetic acid, oxalic acid are added in material II, are put into blender, stir 15 with the speed of 900r/min
Minute, it can be prepared by.
Embodiment 3:
A kind of degreased cleaning agent for metallic conduit, which is characterized in that be prepared from the following raw materials:
It is 30 parts of lauryl sodium sulfate, 15 parts of sodium carboxymethylcellulose, 10 parts of microcrystalline cellulose, 10 parts of flake asbestos, pre- to paste
10 parts of cornstarch of change, 8 parts of beta-cyclodextrin, 8 parts of polyethylene glycol, 5 parts of pectin, 3 parts of isopropyl acetone, 3 parts of sodium carbonate, 8 parts of acetic acid, grass
6 parts, 150 parts of water of acid.
The flake asbestos passes through modification, processing method using preceding are as follows: flake asbestos is added in 2 times of parts by weight water,
30min is stood after fully dispersed, adds disodium hydrogen phosphate and silane coupling agent, utilizes Surface Treatment with Plasma after mixing
Machine handles 15s, and after treatment is transferred to rapidly in 10 DEG C of environment and stands 5h, and sesbania gum is then added, aluminium polychloride, rests in peace
Perfume (or spice), microwave treatment 3min, gained mixture are sent into spray drying under microwave frequency 2450MHz, power 700W after being sufficiently mixed
Machine, finally by dry gained particulate abrasive at powder.
The flake asbestos, disodium hydrogen phosphate, silane coupling agent, sesbania gum, aluminium polychloride, styrax weight fraction ratio are
5:1:0.5:0.5:0.3:0.1.
The degreased cleaning agent for metallic conduit, the production method is as follows:
(1) flake asbestos, pre-gelatinized cornstarch, beta-cyclodextrin are added water and stirred into mixed solution, dodecyl sulphur is added
Sour sodium is put into the microwave treater under microwave frequency 2400MHz, power 600W and handles 10 minutes, stands 10 minutes, carboxylic first is added
Base sodium cellulosate is put into microwave treater and handles 10 minutes, stands 10 minutes, add microcrystalline cellulose, be put into microwave treatment
Device is handled 10 minutes, is stood 10 minutes, is obtained material I;
(2) polyethylene glycol, isopropyl acetone, sodium carbonate are added in material I, carry out heating stirring, heating speed be 5 DEG C/
Min is heated 20 minutes, and is stirred continuously, and obtains material II;
(3) pectin, acetic acid, oxalic acid are added in material II, are put into blender, stirred with the speed of 1000r/min
It 15 minutes, can be prepared by.
Control group 1:
This control group content and 2 content of embodiment are essentially identical, and something in common no longer repeats, the difference is that: asbestos
Powder is using preceding without modification.
Control group 2:
This control group content and 2 content of embodiment are essentially identical, and something in common no longer repeats, the difference is that: raw material
In do not add acetic acid and oxalic acid.
Control group 3:
Commercially available common degreasing agent.
Table 1 is the Experimental Comparison result of the present invention with control group
Table 1
The above shows and describes the basic principles and main features of the present invention and the advantages of the present invention.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and improvements may be made to the invention, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (3)
1. a kind of degreased cleaning agent for metallic conduit, which is characterized in that be prepared from the following raw materials: lauryl sodium sulfate
15-30 parts, 5-15 parts of sodium carboxymethylcellulose, 5-10 parts of microcrystalline cellulose, 5-10 parts of flake asbestos, pre-gelatinized cornstarch 5-10
Part, 4-8 parts of beta-cyclodextrin, 4-8 parts of polyethylene glycol, 3-5 parts of pectin, 1-3 parts of isopropyl acetone, 1-3 parts of sodium carbonate, 2-8 parts of acetic acid, grass
It is 2-6 parts sour, 120-150 parts of water.
2. the degreased cleaning agent according to claim 1 for metallic conduit, which is characterized in that preferred following raw material system
At: 25 parts of lauryl sodium sulfate, 10 parts of sodium carboxymethylcellulose, 8 parts of microcrystalline cellulose, 8 parts of flake asbestos, pre-gelatinized corn forms sediment
8 parts of powder, 6 parts of beta-cyclodextrin, 6 parts of polyethylene glycol, 4 parts of pectin, 2 parts of isopropyl acetone, 2 parts of sodium carbonate, 5 parts of acetic acid, 4 parts of oxalic acid, water
140 parts.
3. the degreased cleaning agent according to claim 1 or 2 for metallic conduit, which is characterized in that its production method is such as
Under:
(1) flake asbestos, pre-gelatinized cornstarch, beta-cyclodextrin are added water and stirred into mixed solution, lauryl sodium sulfate are added,
It is put into the microwave treater under microwave frequency 2400MHz, power 600W to handle 10 minutes, stands 10 minutes, it is fine that carboxymethyl is added
Plain sodium is tieed up, microwave treater is put into and handles 10 minutes, stand 10 minutes, add microcrystalline cellulose, be put at microwave treater
Reason 10 minutes stands 10 minutes, obtains material I;
(2) polyethylene glycol, isopropyl acetone, sodium carbonate being added in material I, carries out heating stirring, heating speed is 5 DEG C/min,
Heating 15-20 minutes, and be stirred continuously, obtain material II;
(3) pectin, acetic acid, oxalic acid are added in material II, are put into blender, stirred with the speed of 800-1000r/min
It 10-15 minutes, can be prepared by.