CN109402519A - A kind of processing technology of the intelligent Bus slot port case for data center - Google Patents
A kind of processing technology of the intelligent Bus slot port case for data center Download PDFInfo
- Publication number
- CN109402519A CN109402519A CN201811257298.9A CN201811257298A CN109402519A CN 109402519 A CN109402519 A CN 109402519A CN 201811257298 A CN201811257298 A CN 201811257298A CN 109402519 A CN109402519 A CN 109402519A
- Authority
- CN
- China
- Prior art keywords
- sheet alloy
- port case
- data center
- intelligent bus
- bus slot
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of processing technologys of intelligent Bus slot port case for data center, belong to fire-fighting equipment technical field.This is used for the processing technology of the intelligent Bus slot port case of data center the following steps are included: (i) making sheet alloy;(ii) sheet alloy is heat-treated;(iii) sheet alloy obtained is cut into corresponding size and shape as needed;(iv) the sheet alloy outer surface after cutting covers insulating plastic layer;(v) port case obtained is put into steam vulcanization tank with plate and is vulcanized;(vi) it washes;(vii) to port case plate spray insulation coating in dustfree environment;(viii) case plate assembling in port is made to the intelligent Bus slot port case for being used for data center.Using the technique with sheet alloy surface covering insulating plastic layer and insulating coating in processing technology for the intelligent Bus slot port case of data center of the invention, pass through double insulation, can effectively prevent fire caused by electric leakage, electric arc etc., ensure that bus duct using safe.
Description
Technical field
The present invention relates to a kind of processing technologys of intelligent Bus slot port case for data center, belong to power equipment skill
Art field.
Background technique
Modern high-rise building and large-scale workshop need huge electric energy, and in face of hundreds and thousands of peaces needed for this huge load
The powerful electric current of training will select safe and reliable transmission equipment, and bus duct system is an efficient conveying electric current with Denso
It sets, has especially adapted to the needs of higher and higher building and large-scale plant economical rationality wiring.
But in actual use, general bus duct cooperation bus duct port case uses, and bus duct port case needs to carry out
Insulation processing, while also needing good heat dissipation performance.Bus duct can cause to generate heat when passing through electric current, in this way, if not compared with
Good insulation and cooling measure, easily cause bus duct catch fire and failure, constitute great accident, serious property caused to damage
Personnel safety of becoming estranged hidden danger.
Summary of the invention
The technical problem to be solved by the present invention is in view of the shortcomings of the prior art, propose a kind of good insulation preformance, service life
The processing technology of the long intelligent Bus slot port case for data center.
The technical solution that the present invention proposes to solve above-mentioned technical problem is: a kind of intelligent Bus slot for data center
The processing technology of port case, comprising the following steps:
(i) sheet alloy is made, the specific steps are as follows:
A, ingredient: the mass percent ingredient of sheet alloy are as follows: C:0.01-0.03%, Cr:0.05-0.16%, Mn:1.12-
1.24%, Zn:1.02-1.18%, Cu:1.35-1.66%, Al:1.67-2.13%, Pt:0.02-0.05%, Ni:0.58-0.86%,
Mo:0.05-0.08%, Nd:0.05-0.07%, Ce:0.01-0.02%, Eu:0.06-0.08%, Lu:0.12-0.15%, surplus are
Fe;
B, the raw material of sheet alloy is subjected to ingredient according to the mass percent of each ingredient of sheet alloy, by the alloy after ingredient
The raw material of plate carries out melting, obtains alloy solution;
C, obtained alloy solution is subjected to continuous casting and rolling, sheet alloy is made;
D, sheet alloy is carried out heating to forge to a thickness of 0.5-1.5mm, forges time 40-50min, final alloy is made
Plate;
(ii) sheet alloy is heat-treated, specifically:
A, it heats: sheet alloy being heated to 650-685 DEG C, and keeps the temperature 65-85min;
B, cooling: water cooling is used to be cooled to room temperature sheet alloy acceleration with the cooling rate of 13-15 DEG C/s;
C, quench: the quenching and preserving heat temperature of sheet alloy is 520 DEG C ± 20 DEG C, and soaking time is 1.5~2.5h;Sheet alloy adds
Sink water cooling is quickly put into 5-15 minutes after the completion of heat, and cooling bath water temperature is controlled at 30~35 DEG C;
(iii) by sheet alloy obtained according to the intelligent Bus slot port case for being used for data center need to cut into it is corresponding big
Small and shape;
(iv) the sheet alloy outer surface after cutting covers insulating plastic layer by Shooting Technique, and port case plate is made;Absolutely
The mass percent ingredient of edge plastic layer are as follows: urethanes: 0.55~1.12%, butyl acrylate: 0.71~0.98%, benzene
Ethylene: 6.23-8.67%, butadiene-styrene rubber: 5.21-7.45%, ethylene propylene diene rubber: 3.45-4.25%, magnesia: 2.45-
2.89%, magnesium chloride: 2.37-2.68%, zinc oxide: 1.12-1.24%, glass fibre: 6.35-8.16%, epoxy resin:
1.45-1.78%, ultraviolet absorbing agent: 2.32-2.56%, surplus are phenolic resin;
(v) port case obtained being put into steam vulcanization tank with plate and is vulcanized, sulfuration steam pressure is 0.3-0.55Mpa,
Vulcanization time is 15-20 minutes;
(vi) it washes: being washed using flow-type, the port case after vulcanization is put into Rinsing Area with plate, cleaned with the clear water of flowing
Port case plate, the port case after cleaning are hung drained in orbit with plate;
(vii) to port case plate spray insulation coating in dustfree environment, the raw material components of insulating coating include: by weight
20-30 parts of magnesia, 30-35 parts of magnesium chloride, 15-25 parts of aluminium oxide, 4-6 parts of stick, 6-8 parts of resin, 3-5 parts of age resister,
2-3 parts of curing agent;
(viii) case plate assembling in port is made to the intelligent Bus slot port case for being used for data center.
The improvement of above-mentioned technical proposal is: step (i) in sheet alloy mass percent ingredient are as follows: C:0.01%, Cr:
0.06%, Mn:1.14%, Zn:1.08%, Cu:1.36%, Al:1.69%, Pt:0.03%, Ni:0.59%, Mo:0.06%, Nd:
0.05%, Ce:0.01%, Eu:0.06%, Lu:0.13%, surplus Fe.
The improvement of above-mentioned technical proposal is: step (i) in sheet alloy mass percent ingredient are as follows: C:0.03%, Cr:
0.15%, Mn:1.24%, Zn:1.18%, Cu:1.66%, Al:2.11%, Pt:0.04%, Ni:0.83%, Mo:0.08%, Nd:
0.07%, Ce:0.02%, Eu:0.08%, Lu:0.15%, surplus Fe.
The improvement of above-mentioned technical proposal is: step (iv) in insulating plastic layer mass percent ingredient are as follows: urethane
Ester: 0.58%, butyl acrylate: 0.76%, styrene: 6.27%, butadiene-styrene rubber: 5.25%, ethylene propylene diene rubber: 3.45%, oxygen
Change magnesium: 2.49%, magnesium chloride: 2.38%, zinc oxide: 1.14%, glass fibre: 6.36%, epoxy resin: 1.48%, ultraviolet light
Absorbent: 2.36%, surplus is phenolic resin.
The improvement of above-mentioned technical proposal is: step (iv) in insulating plastic layer mass percent ingredient are as follows: urethane
Ester: 1.12%, butyl acrylate: 0.98%, styrene: 8.67%, butadiene-styrene rubber: 7.45%, ethylene propylene diene rubber: 4.25%, oxygen
Change magnesium: 2.89%, magnesium chloride: 2.68%, zinc oxide: 1.24%, glass fibre: 8.16%, epoxy resin: 1.78%, ultraviolet light
Absorbent: 2.56%, surplus is phenolic resin.
The beneficial effect of the present invention by adopting the above technical scheme is:
(1) using with sheet alloy surface in the processing technology for the intelligent Bus slot port case of data center of the invention
The technique for covering insulating plastic layer and insulating coating, by double insulation, the insulation performance of port case promotes 60-70%, Neng Gouyou
Effect prevent fire caused by electric leakage, electric arc etc., ensure that bus duct using safe;
(2) sheet alloy makes this be used to count in the processing technology for the intelligent Bus slot port case of data center of the invention
While there is extremely strong mechanical strength and certain corrosion resistance according to the intelligent Bus slot port case at center, insulating plastic layer
So that the intelligent Bus slot port case for data center of the invention is provided with extremely strong insulation and corrosion resistance, ensure that
Stablizing for intelligent Bus slot port case for data center uses and substantially prolongs its service life;
(3) processing technology of the intelligent Bus slot port case for data center of the invention is by sulfuration process, so that port
The mechanical strength of case plate greatly improves, and strengthens the structure of the intelligent Bus slot port case for data center of the invention
Intensity extends service life.
Specific embodiment
Embodiment one
The processing technology of the intelligent Bus slot port case for data center of the present embodiment, comprising the following steps:
(i) sheet alloy is made, the specific steps are as follows:
A, ingredient: the mass percent ingredient of sheet alloy are as follows: C:0.01%, Cr:0.06%, Mn:1.14%, Zn:1.08%, Cu:
1.36%, Al:1.69%, Pt:0.03%, Ni:0.59%, Mo:0.06%, Nd:0.05%, Ce:0.01%, Eu:0.06%, Lu:
0.13%, surplus Fe;
B, the raw material of sheet alloy is subjected to ingredient according to the mass percent of each ingredient of sheet alloy, by the alloy after ingredient
The raw material of plate carries out melting, obtains alloy solution;
C, obtained alloy solution is subjected to continuous casting and rolling, sheet alloy is made;
D, sheet alloy is carried out heating to forge to a thickness of 0.5-1.5mm, forges time 40-50min, final alloy is made
Plate;
(ii) sheet alloy is heat-treated, specifically:
A, it heats: sheet alloy being heated to 650-685 DEG C, and keeps the temperature 65-85min;
B, cooling: water cooling is used to be cooled to room temperature sheet alloy acceleration with the cooling rate of 13-15 DEG C/s;
C, quench: the quenching and preserving heat temperature of sheet alloy is 520 DEG C ± 20 DEG C, and soaking time is 1.5~2.5h;Sheet alloy adds
Sink water cooling is quickly put into 5-15 minutes after the completion of heat, and cooling bath water temperature is controlled at 30~35 DEG C;
(iii) by sheet alloy obtained according to the intelligent Bus slot port case for being used for data center need to cut into it is corresponding big
Small and shape;
(iv) the sheet alloy outer surface after cutting covers insulating plastic layer by Shooting Technique, and port case plate is made;Absolutely
The mass percent ingredient of edge plastic layer are as follows: urethanes: 0.58%, butyl acrylate: 0.76%, styrene: 6.27%,
Butadiene-styrene rubber: 5.25%, ethylene propylene diene rubber: 3.45%, magnesia: 2.49%, magnesium chloride: 2.38%, zinc oxide: 1.14%,
Glass fibre: 6.36%, epoxy resin: 1.48%, ultraviolet absorbing agent: 2.36%, surplus is phenolic resin;
(v) port case obtained being put into steam vulcanization tank with plate and is vulcanized, sulfuration steam pressure is 0.3-0.55Mpa,
Vulcanization time is 15-20 minutes;
(vi) it washes: being washed using flow-type, the port case after vulcanization is put into Rinsing Area with plate, cleaned with the clear water of flowing
Port case plate, the port case after cleaning are hung drained in orbit with plate;
(vii) to port case plate spray insulation coating in dustfree environment, the raw material components of insulating coating include: by weight
23 parts of magnesia, 31 parts of magnesium chloride, 16 parts of aluminium oxide, 4 parts of stick, 6 parts of resin, 3 parts of age resister, 2 parts of curing agent;
(viii) case plate assembling in port is made to the intelligent Bus slot port case for being used for data center.
Embodiment two
The processing technology of the intelligent Bus slot port case for data center of the present embodiment, comprising the following steps:
(i) sheet alloy is made, the specific steps are as follows:
A, ingredient: the mass percent ingredient of sheet alloy are as follows: C:0.03%, Cr:0.15%, Mn:1.24%, Zn:1.18%, Cu:
1.66%, Al:2.11%, Pt:0.04%, Ni:0.83%, Mo:0.08%, Nd:0.07%, Ce:0.02%, Eu:0.08%, Lu:
0.15%, surplus Fe;
B, the raw material of sheet alloy is subjected to ingredient according to the mass percent of each ingredient of sheet alloy, by the alloy after ingredient
The raw material of plate carries out melting, obtains alloy solution;
C, obtained alloy solution is subjected to continuous casting and rolling, sheet alloy is made;
D, sheet alloy is carried out heating to forge to a thickness of 0.5-1.5mm, forges time 40-50min, final alloy is made
Plate;
(ii) sheet alloy is heat-treated, specifically:
A, it heats: sheet alloy being heated to 650-685 DEG C, and keeps the temperature 65-85min;
B, cooling: water cooling is used to be cooled to room temperature sheet alloy acceleration with the cooling rate of 13-15 DEG C/s;
C, quench: the quenching and preserving heat temperature of sheet alloy is 520 DEG C ± 20 DEG C, and soaking time is 1.5~2.5h;Sheet alloy adds
Sink water cooling is quickly put into 5-15 minutes after the completion of heat, and cooling bath water temperature is controlled at 30~35 DEG C;
(iii) by sheet alloy obtained according to the intelligent Bus slot port case for being used for data center need to cut into it is corresponding big
Small and shape;
(iv) the sheet alloy outer surface after cutting covers insulating plastic layer by Shooting Technique, and port case plate is made;Absolutely
The mass percent ingredient of edge plastic layer are as follows: urethanes: 1.12%, butyl acrylate: 0.98%, styrene: 8.67%,
Butadiene-styrene rubber: 7.45%, ethylene propylene diene rubber: 4.25%, magnesia: 2.89%, magnesium chloride: 2.68%, zinc oxide: 1.24%,
Glass fibre: 8.16%, epoxy resin: 1.78%, ultraviolet absorbing agent: 2.56%, surplus is phenolic resin;
(v) port case obtained being put into steam vulcanization tank with plate and is vulcanized, sulfuration steam pressure is 0.3-0.55Mpa,
Vulcanization time is 15-20 minutes;
(vi) it washes: being washed using flow-type, the port case after vulcanization is put into Rinsing Area with plate, cleaned with the clear water of flowing
Port case plate, the port case after cleaning are hung drained in orbit with plate;
(vii) to port case plate spray insulation coating in dustfree environment, the raw material components of insulating coating include: by weight
27 parts of magnesia, 34 parts of magnesium chloride, 19 parts of aluminium oxide, 6 parts of stick, 8 parts of resin, 5 parts of age resister, 3 parts of curing agent;
(viii) case plate assembling in port is made to the intelligent Bus slot port case for being used for data center.
The present invention is not limited to the above embodiment.All technical solutions formed using equivalent replacement, are all fallen within the present invention and wanted
The protection scope asked.
Claims (5)
1. a kind of processing technology of the intelligent Bus slot port case for data center, it is characterised in that: the following steps are included:
(i) sheet alloy is made, the specific steps are as follows:
A, ingredient: the mass percent ingredient of the sheet alloy are as follows: C:0.01-0.03%, Cr:0.05-0.16%, Mn:1.12-
1.24%, Zn:1.02-1.18%, Cu:1.35-1.66%, Al:1.67-2.13%, Pt:0.02-0.05%, Ni:0.58-0.86%,
Mo:0.05-0.08%, Nd:0.05-0.07%, Ce:0.01-0.02%, Eu:0.06-0.08%, Lu:0.12-0.15%, surplus are
Fe;
B, the raw material of sheet alloy is subjected to ingredient according to the mass percent of each ingredient of sheet alloy, by the alloy after ingredient
The raw material of plate carries out melting, obtains alloy solution;
C, obtained alloy solution is subjected to continuous casting and rolling, sheet alloy is made;
D, the sheet alloy is carried out heating to forge to a thickness of 0.5-1.5mm, forges time 40-50min, be made finally
Sheet alloy;
(ii) sheet alloy is heat-treated, specifically:
A, it heats: sheet alloy being heated to 650-685 DEG C, and keeps the temperature 65-85min;
B, cooling: water cooling is used to be cooled to room temperature sheet alloy acceleration with the cooling rate of 13-15 DEG C/s;
C, quench: the quenching and preserving heat temperature of the sheet alloy is 520 DEG C ± 20 DEG C, and soaking time is 1.5~2.5h;The institute
It states sheet alloy heating and is quickly put into sink water cooling 5-15 minutes after the completion, cooling bath water temperature is controlled at 30~35 DEG C;
(iii) by sheet alloy obtained according to the intelligent Bus slot port case for being used for data center need to cut into it is corresponding big
Small and shape;
(iv) the sheet alloy outer surface after cutting covers insulating plastic layer by Shooting Technique, and port case plate is made;Institute
State the mass percent ingredient of insulating plastic layer are as follows: urethanes: 0.55~1.12%, butyl acrylate: 0.71~
0.98%, styrene: 6.23-8.67%, butadiene-styrene rubber: 5.21-7.45%, ethylene propylene diene rubber: 3.45-4.25%, magnesia:
2.45-2.89%, magnesium chloride: 2.37-2.68%, zinc oxide: 1.12-1.24%, glass fibre: 6.35-8.16%, asphalt mixtures modified by epoxy resin
Rouge: 1.45-1.78%, ultraviolet absorbing agent: 2.32-2.56%, surplus are phenolic resin;
(v) port case obtained being put into steam vulcanization tank with plate and is vulcanized, sulfuration steam pressure is 0.3-0.55Mpa,
Vulcanization time is 15-20 minutes;
(vi) it washes: being washed using flow-type, the port case after vulcanization is put into Rinsing Area with plate, cleaned with the clear water of flowing
Port case plate, the port case after cleaning are hung drained in orbit with plate;
(vii) to port case plate spray insulation coating in dustfree environment, the raw material components of insulating coating include: by weight
20-30 parts of magnesia, 30-35 parts of magnesium chloride, 15-25 parts of aluminium oxide, 4-6 parts of stick, 6-8 parts of resin, 3-5 parts of age resister,
2-3 parts of curing agent;
(viii) case plate assembling in port is made to the intelligent Bus slot port case for being used for data center.
2. the processing technology of the intelligent Bus slot port case according to claim 1 for data center, it is characterised in that:
Step (i) described in sheet alloy mass percent ingredient are as follows: C:0.01%, Cr:0.06%, Mn:1.14%, Zn:1.08%, Cu:
1.36%, Al:1.69%, Pt:0.03%, Ni:0.59%, Mo:0.06%, Nd:0.05%, Ce:0.01%, Eu:0.06%, Lu:
0.13%, surplus Fe.
3. the processing technology of the intelligent Bus slot port case according to claim 1 for data center, it is characterised in that:
Step (i) described in sheet alloy mass percent ingredient are as follows: C:0.03%, Cr:0.15%, Mn:1.24%, Zn:1.18%, Cu:
1.66%, Al:2.11%, Pt:0.04%, Ni:0.83%, Mo:0.08%, Nd:0.07%, Ce:0.02%, Eu:0.08%, Lu:
0.15%, surplus Fe.
4. the processing technology of the intelligent Bus slot port case according to claim 1 for data center, it is characterised in that:
Step (iv) described in insulating plastic layer mass percent ingredient are as follows: urethanes: 0.58%, butyl acrylate: 0.76%,
Styrene: 6.27%, butadiene-styrene rubber: 5.25%, ethylene propylene diene rubber: 3.45%, magnesia: 2.49%, magnesium chloride: 2.38%,
Zinc oxide: 1.14%, glass fibre: 6.36%, epoxy resin: 1.48%, ultraviolet absorbing agent: 2.36%, surplus is phenolic aldehyde tree
Rouge.
5. the processing technology of the intelligent Bus slot port case according to claim 1 for data center, it is characterised in that:
Step (iv) described in insulating plastic layer mass percent ingredient are as follows: urethanes: 1.12%, butyl acrylate: 0.98%,
Styrene: 8.67%, butadiene-styrene rubber: 7.45%, ethylene propylene diene rubber: 4.25%, magnesia: 2.89%, magnesium chloride: 2.68%,
Zinc oxide: 1.24%, glass fibre: 8.16%, epoxy resin: 1.78%, ultraviolet absorbing agent: 2.56%, surplus is phenolic aldehyde tree
Rouge.