CN109395149A - 一种纳米材料抗菌保健女士护垫 - Google Patents

一种纳米材料抗菌保健女士护垫 Download PDF

Info

Publication number
CN109395149A
CN109395149A CN201811504502.2A CN201811504502A CN109395149A CN 109395149 A CN109395149 A CN 109395149A CN 201811504502 A CN201811504502 A CN 201811504502A CN 109395149 A CN109395149 A CN 109395149A
Authority
CN
China
Prior art keywords
parts
chitosan
layer
protection pad
mrs
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN201811504502.2A
Other languages
English (en)
Inventor
不公告发明人
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Changsha Is As Small As Mdt Infotech Ltd
Original Assignee
Changsha Is As Small As Mdt Infotech Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Changsha Is As Small As Mdt Infotech Ltd filed Critical Changsha Is As Small As Mdt Infotech Ltd
Priority to CN201811504502.2A priority Critical patent/CN109395149A/zh
Publication of CN109395149A publication Critical patent/CN109395149A/zh
Withdrawn legal-status Critical Current

Abstract

本发明公开了一种纳米材料抗菌保健女士护垫，属于卫生用品技术领域。所述的护垫包括自上而下依次叠合在一起的网面层、中药层、吸水层、防水层以及胶粘剂层，所述的网面层为经过中药浸液浸泡并干燥后纳米银抗菌无纺布织物面料，包括以下主要成分：纳米银、5，5‑二甲基海因、壳聚糖、蛋壳粉、聚乙烯、ES纤维、负离子纤维；所述中药浸液由以下中药原料提取制成：当归、香附、金银花、蒲公英、艾叶、炒楂曲、干地龙、益母草；所述的中药层包括以下药物：藏红花、蛇床子、连翘、鱼腥草、地肤子、黄连、苦参、当归、柴胡。本发明通过采用5，5‑二甲基海因、壳聚糖、聚乙烯构成的补强体系提高女士护垫的抑菌性能。

Description

一种纳米材料抗菌保健女士护垫
技术领域
本发明属于卫生用品技术领域，具体涉及一种纳米材料抗菌保健女士护垫。
背景技术
目前，随着人们生活水平的提高，妇女受环境、生活习惯等因素的影响，生理周期出现痛经的越来越多，大多患者依靠中药来治疗、调理，中药熬制不方便，中成药价格又高，况且疗效都不十分理想。
医学实践表明，女性经期护理对妇女身体健康具有十分重要的意义。经期时女性身体抵抗力微弱的阶段，极易受到细菌的感染，尤其使用卫生巾形成潮湿封闭环境促使厌氧细菌滋生，侵袭人体，使用不当会促使慢性妇科疾病的形成。针对上述问题，近年来市场上推出了多种具有抗菌杀毒功能的多层结构卫生巾及护垫，一般具有网面层、抗菌芯片层、吸水层、防水膜层及胶粘剂层，但其多层结构会由于层间阻挡的作用导致抗菌效果降低，尤其在潮湿液体环境下不能充分发挥杀菌作用。
目前的抗菌卫生巾的研究主要通过选用刺激性相对较小的抗菌剂对卫生巾的面层进行处理，所使用的抗菌剂包括纳米银、季铵盐、植物提取物以及中药等，但仍然存在许多问题和隐患。近年来已证实作为长效抗菌剂的小颗粒纳米银容易被生殖细胞吸收，从而引起生殖器官超微水平的病理改变，增加生殖毒性风险。季铵盐抗菌剂的刺激性相对较小，但其属于溶出型的抗菌剂，它们在卫生巾的面层较易被吸收液洗脱，从而减弱了卫生巾的抗菌性。同时，它们容易在人体细胞逐渐富集，长期使用易产生耐药性，引起接触性皮炎。此外，植物提取物和中药的抗菌性能较为微弱，无法有效地抑制细菌的滋生，并容易引起皮肤过敏。
中国专利申请文献“一种具有抗菌保健功能的女士护垫(专利号：ZL201610388396.0)”公开了一种具有抗菌保健功能的女士护垫，包括自上而下依次叠合在一起的网面层、中药层、吸水层、防水层以及胶粘剂层。所述的网面层为经过中药浸液浸泡并干燥后的珍珠面料。所述的中药浸液由包括以下重量份的中药原料提取制成：当归2-4份、香附15-20份、艾叶7-9份、炒楂曲7-9份、干地龙7-9份。所述的中药层，包括以下药物:藏红花10-15份、蛇床子12-17份、地肤子15-18份、苦参10-17份、当归2-5份、柴胡10-15份、白芍10-15份。所述珍珠面料包括以下主要成分：粘胶纤维90-95％，珍珠粉2-7％，构树汁0.05-0.1％，膨胀蛭石-纳米银复合材料2-3％，分散剂余量。该发明具有采用网面层与中药层相互配合，具备较好的抗菌抑菌作用，但是存在对细菌的抑制作用针对性不强的问题。
发明内容
本发明的目的是提供一种纳米材料抗菌保健女士护垫，以解决在中国专利申请文献“一种具有抗菌保健功能的女士护垫(专利号：ZL201610388396.0)”公开的基础上，如何优化组份、用量、工艺等，提高护垫对细菌抑制作用针对性不强的问题。
为了解决以上技术问题，本发明采用以下技术方案：
一种纳米材料抗菌保健女士护垫，包括自上而下依次叠合在一起的网面层、中药层、吸水层、防水层以及胶粘剂层，所述的网面层为经过中药浸液浸泡并干燥后纳米银抗菌无纺布织物面料，包括以下主要成分：纳米银、5，5-二甲基海因、壳聚糖、蛋壳粉、聚乙烯、ES纤维(Ethylene-Propylene Side By Side，日本智索公司开发出来的一种聚烯烃系纤维)、负离子纤维；所述中药浸液由以下中药原料提取制成：当归、香附、金银花、蒲公英、艾叶、炒楂曲、干地龙、益母草；所述的中药层包括以下药物：藏红花、蛇床子、连翘、鱼腥草、地肤子、黄连、苦参、当归、柴胡；
所述的5，5-二甲基海因、壳聚糖、聚乙烯的用量比为(0.5-0.8)：(1.5-2.2)：(45-60)。
优选地，所述的5，5-二甲基海因、壳聚糖、聚乙烯的用量比为0.7:1.8:55。
优选地，所述纳米银抗菌无纺布织物面料以重量份为单位包括以下主要成分：纳米银5-8份、5，5-二甲基海因0.5-0.8份、壳聚糖1.5-2.2份、蛋壳粉0.5-1.2份、聚乙烯45-60份、ES纤维20-35份、负离子纤维8-15份；所述中药浸液由以下重量份的中药原料提取制成：当归1-3份、香附10-15份、金银花5-8份、蒲公英6-10份、艾叶10-13份、炒楂曲8-10份、干地龙1-3份、益母草7-11份；所述的中药层包括以下重量份的药物：藏红花5-9份、蛇床子5-8份、连翘10-13份、鱼腥草12-15份、地肤子18-20份、黄连5-7份、苦参4-9份、当归6-8份、柴胡4-10份。
优选地，所述网面层的制备方法包括以下步骤：将所述的各中药去除杂质，漂洗干净后，加原料药总量3-4倍的水，煎煮1-2h，过滤，煎煮两次后合并滤液，滤液浓缩后将纳米银抗菌无纺布织物面料放入药液中浸泡10-15min，然后于50-70℃下烘干。
优选地，所述中药层制备方法，包括以下步骤：
S1：称取藏红花、蛇床子、连翘、鱼腥草、地肤子、黄连、苦参、当归、柴胡，洗净后干燥，备用；
S2：将干燥后的中药粉碎后过100目筛，得到细粉；
S3：将细粉与棉絮混配制浆，再把得到的纸浆制成中药层。
6、根据权利要求1或4所述的纳米材料抗菌保健女士护垫，其特征在于，所述纳米银抗菌无纺布织物面料的制备方法包括以下步骤：
A:将纳米银和蛋壳粉于在80-100℃下快速搅拌3-5min，然后超声15-20min制得蛋壳粉纳米银复合材料备用；
B：将5，5-二甲基海因于180℃下熔化，加入壳聚糖和甲醇，用200-300r/min的速度搅拌10-20min，形成改性壳聚糖；
C：将蛋壳粉纳米银复合材料和十分之一的聚乙烯混合、熔化，再加入改性壳聚糖，然后用220-250r/min的速度搅拌10-15min，用挤塑机制粒，得纳米银壳聚糖抗菌无纺布母料备用；
D：将纳米银壳聚糖抗菌无纺布母料与剩余的聚乙烯混合后加入制膜机料仓熔化，后经螺杆从膜头挤出，然后打孔成抗菌打孔膜，再加入ES纤维和负离子纤维，用纤维拉丝机拉丝，制成纳米银抗菌无纺布织物面料。
优选地，所述步骤A中快速搅拌的速度为400-500r/min。
优选地，所述步骤A纳米银采用粒径为10-30nm的超微颗粒。
优选地，所述步骤B中甲醇浓度为2mol/L。
本发明具有以下有益效果：
(1)由实施例1-3和对比例5的数据可见，实施例1-3女士护垫的抑菌率明显高于对比例5的女士护垫的抑菌率，最小抑菌浓度明显小于对比例5的最好抑菌浓度；同时由实施例1-3的数据可见，实施例1为最优实施例。
(2)由实施例1和对比例1-4的数据可见，女士护垫中5，5-二甲基海因、壳聚糖、聚乙烯在女士护垫抑菌效果中起到了协同作用，协同提高了女士护垫的抑菌率，这可能是：
5，5-二甲基海因为小分子卤胺化合物，具有良好的稳定性和很强的抗菌性，通过释放出氧化性的卤正离子，然后转移到微生物细胞上，使其失活；且5，5-二甲基海因在水中有较小的溶解度，可缓慢释放出自由卤素，具有很强的杀菌功效。壳聚糖分子中铵根离子带正电荷，吸附在细胞表面，形成一层高分子膜，阻止营养物质向细胞内运输，也可使细胞壁和细胞膜上的负电荷分布不均，破坏细胞壁的合成与溶解平衡，溶解细胞壁，从而起到抑菌杀菌的作用。虽然5，5-二甲基海因具有较强的抗菌性，但是它不能直接被固载到各种基体材料的表面以形成非溶出型抗菌材料，因此本发明利用5，5-二甲基海因对壳聚糖进行改性，生成改性壳聚糖，在壳聚糖分子中引入卤素抗菌基团，提高壳聚糖的抗菌性能。将改性壳聚糖与纳米银、聚乙烯基材共熔形成打孔膜，此时聚乙烯基材作为载体，使得改性壳聚糖能够均匀的分散在纤维原料中，形成卤胺壳聚糖抗菌纤维，就像给卫生巾穿上一层抑菌防护服，当与细菌接触时，改性壳聚糖中的卤正离子、铵根离子均能起到杀菌作用，从而提高抑菌效率，降低最低抑菌浓度，使护垫具有抗菌性能的长效性，不但使用起来更卫生，更能消除异味。
(3)由对比例6-8的数据可见，5，5-二甲基海因、壳聚糖、聚乙烯的重量比不在(0.5-0.8)：(1.5-2.2)：(45-60)范围内时，制得的女士护垫的抑菌率和最低抑菌浓度数值与实施例1-3的数值相差甚大，与现有技术(对比例5)的数值相当。本发明5，5-二甲基海因、壳聚糖、聚乙烯作为补强体系，实施例1-3通过控制制备女士护垫时添加5，5-二甲基海因、壳聚糖、聚乙烯的重量比为(0.5-0.8)：(1.5-2.2)：(45-60)，实现在补强体系中利用5，5-二甲基海因释放出氧化性的卤正离子、壳聚糖分子中的铵根离子溶解细胞壁、聚乙烯基材与纳米银壳聚糖抗菌纤维共熔形成抗菌合成纤维原料等特点，使得5，5-二甲基海因、壳聚糖、聚乙烯构成的补强体系在本发明的女士护垫中，提高女士护垫的抑菌性能。
具体实施方式
为了更好地理解本发明，现通过以下实施例加以说明，以下实施例属于本发明的保护范围，但不限制本发明的保护范围。
以下实施例中，所述的纳米材料抗菌保健女士护垫，包括自上而下依次叠合在一起的网面层、中药层、吸水层、防水层以及胶粘剂层，所述的网面层为经过中药浸液浸泡并干燥后纳米银抗菌无纺布织物面料，包括以下主要成分：以重量份为单位包括以下主要成分：纳米银5-8份、5，5-二甲基海因0.5-0.8份、壳聚糖1.5-2.2份、蛋壳粉0.5-1.2份、聚乙烯45-60份、ES纤维20-35份、负离子纤维8-15份；所述中药浸液由以下重量份的中药原料提取制成：当归1-3份、香附10-15份、金银花5-8份、蒲公英6-10份、艾叶10-13份、炒楂曲8-10份、干地龙1-3份、益母草7-11份；所述的中药层包括以下重量份的药物：藏红花5-9份、蛇床子5-8份、连翘10-13份、鱼腥草12-15份、地肤子18-20份、黄连5-7份、苦参4-9份、当归6-8份、柴胡4-10份。
所述网面层的制备方法包括以下步骤：将所述的各中药去除杂质，漂洗干净后，加原料药总量3-4倍的水，煎煮1-2h，过滤，煎煮两次后合并滤液，滤液浓缩后将纳米银抗菌无纺布织物面料放入药液中浸泡10-15min，然后于50-70℃下烘干。
所述中药层制备方法，包括以下步骤：
S1：称取藏红花、蛇床子、连翘、鱼腥草、地肤子、黄连、苦参、当归、柴胡，洗净后干燥，备用；
S2：将干燥后的中药粉碎后过100目筛，得到细粉；
S3：将细粉与棉絮混配制浆，再把得到的纸浆制成中药层。
所述纳米银抗菌无纺布织物面料的制备方法包括以下步骤：
A:将粒径为10-30nm的超微纳米银颗粒和蛋壳粉于在80-100℃下以400-500r/min快速搅拌3-5min，然后超声15-20min制得蛋壳粉纳米银复合材料备用；
B：将5，5-二甲基海因于180℃下熔化，加入壳聚糖和甲醇，用200-300r/min的速度搅拌10-20min，形成改性壳聚糖；
C：将蛋壳粉纳米银复合材料和十分之一的聚乙烯混合、熔化，再加入改性壳聚糖，然后用220-250r/min的速度搅拌10-15min，用挤塑机制粒，得纳米银壳聚糖抗菌无纺布母料备用；
D：将纳米银壳聚糖抗菌无纺布母料与剩余的聚乙烯混合后加入制膜机料仓熔化，后经螺杆从膜头挤出，然后打孔成抗菌打孔膜，再加入ES纤维和负离子纤维，用纤维拉丝机拉丝，制成纳米银抗菌无纺布织物面料。
实施例1
一种纳米材料抗菌保健女士护垫，包括自上而下依次叠合在一起的网面层、中药层、吸水层、防水层以及胶粘剂层，所述的网面层为经过中药浸液浸泡并干燥后纳米银抗菌无纺布织物面料，包括以下主要成分：以重量份为单位包括以下主要成分：纳米银7份、5，5-二甲基海因0.7份、壳聚糖1.8份、蛋壳粉0.8份、聚乙烯55份、ES纤维20份、负离子纤维8-15份；所述中药浸液由以下重量份的中药原料提取制成：当归1份、香附12份、金银花8份、蒲公英6份、艾叶13份、炒楂曲8份、干地龙2份、益母草11份；所述的中药层包括以下重量份的药物：藏红花9份、蛇床子8份、连翘10份、鱼腥草15份、地肤子18份、黄连5份、苦参6份、当归7份、柴胡4-10份。
所述网面层的制备方法包括以下步骤：将所述的各中药去除杂质，漂洗干净后，加原料药总量4倍的水，煎煮1h，过滤，煎煮两次后合并滤液，滤液浓缩后将纳米银抗菌无纺布织物面料放入药液中浸泡12min，然后于50℃下烘干。
所述中药层制备方法，包括以下步骤：
S1：称取藏红花、蛇床子、连翘、鱼腥草、地肤子、黄连、苦参、当归、柴胡，洗净后干燥，备用；
S2：将干燥后的中药粉碎后过100目筛，得到细粉；
S3：将细粉与棉絮混配制浆，再把得到的纸浆制成中药层。
所述纳米银抗菌无纺布织物面料的制备方法包括以下步骤：
A:将粒径为10nm的超微纳米银颗粒和蛋壳粉于在100℃下以500r/min快速搅拌3min，然后超声18min制得蛋壳粉纳米银复合材料备用；
B：将5，5-二甲基海因于180℃下熔化，加入壳聚糖和浓度为2mol/L甲醇，用250r/min的速度搅拌15min，形成改性壳聚糖；
C：将蛋壳粉纳米银复合材料和十分之一的聚乙烯混合、熔化，再加入改性壳聚糖然后用220r/min的速度搅拌13min，用挤塑机制粒，得纳米银壳聚糖抗菌无纺布母料备用；
D：将纳米银壳聚糖抗菌无纺布母料与剩余的聚乙烯混合后加入制膜机料仓熔化，后经螺杆从膜头挤出，然后打孔成抗菌打孔膜，再加入ES纤维和负离子纤维，用纤维拉丝机拉丝，制成纳米银抗菌无纺布织物面料。
实施例2
一种纳米材料抗菌保健女士护垫，包括自上而下依次叠合在一起的网面层、中药层、吸水层、防水层以及胶粘剂层，所述的网面层为经过中药浸液浸泡并干燥后纳米银抗菌无纺布织物面料，包括以下主要成分：以重量份为单位包括以下主要成分：纳米银8份、5，5-二甲基海因0.5份、壳聚糖2.2、蛋壳粉1.2份、聚乙烯60份、ES纤维28份、负离子纤维8份；所述中药浸液由以下重量份的中药原料提取制成：当归2份、香附15份、金银花5份、蒲公英8份、艾叶10份、炒楂曲9份、干地龙3份、益母草7份；所述的中药层包括以下重量份的药物：藏红花5份、蛇床子5份、连翘12份、鱼腥草12份、地肤子19份、黄连6份、苦参9份、当归8份、柴胡4份。
所述网面层的制备方法包括以下步骤：将所述的各中药去除杂质，漂洗干净后，加原料药总量3倍的水，煎煮1.5h，过滤，煎煮两次后合并滤液，滤液浓缩后将纳米银抗菌无纺布织物面料放入药液中浸泡15min，然后于60℃下烘干。
所述中药层制备方法，包括以下步骤：
S1：称取藏红花、蛇床子、连翘、鱼腥草、地肤子、黄连、苦参、当归、柴胡，洗净后干燥，备用；
S2：将干燥后的中药粉碎后过100目筛，得到细粉；
S3：将细粉与棉絮混配制浆，再把得到的纸浆制成中药层。
所述纳米银抗菌无纺布织物面料的制备方法包括以下步骤：
A:将粒径为20nm的超微纳米银颗粒和蛋壳粉于在80℃下以400r/min快速搅拌4min，然后超声20min制得蛋壳粉纳米银复合材料备用；
B：将5，5-二甲基海因于180℃下熔化，加入壳聚糖和浓度为2mol/L甲醇，用300r/min的速度搅拌10min，形成改性壳聚糖；
C：将蛋壳粉纳米银复合材料和十分之一的聚乙烯混合、熔化，再加入改性壳聚糖然后用240r/min的速度搅拌15min，用挤塑机制粒，得纳米银壳聚糖抗菌无纺布母料备用；
D：将纳米银壳聚糖抗菌无纺布母料与剩余的聚乙烯混合后加入制膜机料仓熔化，后经螺杆从膜头挤出，然后打孔成抗菌打孔膜，再加入ES纤维和负离子纤维，用纤维拉丝机拉丝，制成纳米银抗菌无纺布织物面料。
实施例3
一种纳米材料抗菌保健女士护垫，包括自上而下依次叠合在一起的网面层、中药层、吸水层、防水层以及胶粘剂层，所述的网面层为经过中药浸液浸泡并干燥后纳米银抗菌无纺布织物面料，包括以下主要成分：以重量份为单位包括以下主要成分：纳米银5份、5，5-二甲基海因0.8份、壳聚糖1.5份、蛋壳粉0.5份、聚乙烯45份、ES纤维35份、负离子纤维13份；所述中药浸液由以下重量份的中药原料提取制成：当归3份、香附10份、金银花6份、蒲公英10份、艾叶12份、炒楂曲10份、干地龙1份、益母草9份；所述的中药层包括以下重量份的药物：藏红花8份、蛇床子7份、连翘13份、鱼腥草14份、地肤子20份、黄连7份、苦参4份、当归6份、柴胡8份。
所述网面层的制备方法包括以下步骤：将所述的各中药去除杂质，漂洗干净后，加原料药总量4倍的水，煎煮2h，过滤，煎煮两次后合并滤液，滤液浓缩后将纳米银抗菌无纺布织物面料放入药液中浸泡10min，然后于70℃下烘干。
所述中药层制备方法，包括以下步骤：
S1：称取藏红花、蛇床子、连翘、鱼腥草、地肤子、黄连、苦参、当归、柴胡，洗净后干燥，备用；
S2：将干燥后的中药粉碎后过100目筛，得到细粉；
S3：将细粉与棉絮混配制浆，再把得到的纸浆制成中药层。
所述纳米银抗菌无纺布织物面料的制备方法包括以下步骤：
A:将粒径为30nm的超微纳米银颗粒和蛋壳粉于在90℃下以450r/min快速搅拌5min，然后超声15min制得蛋壳粉纳米银复合材料备用；
B：将5，5-二甲基海因于180℃下熔化，加入壳聚糖和浓度为2mol/L的甲醇，用200r/min的速度搅拌1020min，形成改性壳聚糖；
C：将蛋壳粉纳米银复合材料和十分之一的聚乙烯混合、熔化，再加入改性壳聚糖，然后用250r/min的速度搅拌10min，用挤塑机制粒，得纳米银壳聚糖抗菌无纺布母料备用；
D：将纳米银壳聚糖抗菌无纺布母料与剩余的聚乙烯混合后加入制膜机料仓熔化，后经螺杆从膜头挤出，然后打孔成抗菌打孔膜，再加入ES纤维和负离子纤维，用纤维拉丝机拉丝，制成纳米银抗菌无纺布织物面料。
对比例1
制备方法与实施例1基本相同，不同之处在于制备女士护垫网面层中缺少5，5-二甲基海因、壳聚糖、聚乙烯。
对比例2
制备方法与实施例1基本相同，不同之处在于制备女士护垫网面层中缺少纳米银。
对比例3
制备方法与实施例1基本相同，不同之处在于制备女士护垫网面层中缺少蛋壳粉。
对比例4
制备方法与实施例1基本相同，不同之处在于制备女士护垫网面层中缺少聚乙烯。
对比例5
按照中国专利申请文献“一种具有抗菌保健功能的女士护垫(专利号：ZL201610388396.0)”中实施例1所述的方法制备女士护垫。
对比例6
制备方法与实施例1基本相同，不同之处在于制备女士护垫网面层中纳米银用量为1份、蛋壳粉用量为3份、聚乙烯用量为80份。
对比例7
制备方法与实施例1基本相同，不同之处在于制备女士护垫网面层中纳米银用量为14份、蛋壳粉用量为0.1份、聚乙烯用量为70份。
对比例8
制备方法与实施例1基本相同，不同之处在于制备女士护垫网面层中纳米银用量为1.2份、蛋壳粉用量为3.5份、聚乙烯用量为20份。
按照实施例1-3和对比例1-8所述的方法制备女士护垫，并检测各组女士护垫的抑菌性能。按照《消毒技术规范》2002年版-3.1的规范进行实验，结果见下表所示。
由上表可知：(1)由实施例1-3和对比例5的数据可见，实施例1-3女士护垫的抑菌率明显高于对比例5的女士护垫的抑菌率，最小抑菌浓度明显小于对比例5的最好抑菌浓度；同时由实施例1-3的数据可见，实施例1为最优实施例。
(2)由实施例1和对比例1-4的数据可见，女士护垫中5，5-二甲基海因、壳聚糖、聚乙烯在女士护垫抑菌效果中起到了协同作用，协同提高了女士护垫的抑菌率，这可能是：
5，5-二甲基海因为小分子卤胺化合物，具有良好的稳定性和很强的抗菌性，通过释放出氧化性的卤正离子，然后转移到微生物细胞上，使其失活；且5，5-二甲基海因在水中有较小的溶解度，可缓慢释放出自由卤素，具有很强的杀菌功效。壳聚糖分子中铵根离子带正电荷，吸附在细胞表面，形成一层高分子膜，阻止营养物质向细胞内运输，也可使细胞壁和细胞膜上的负电荷分布不均，破坏细胞壁的合成与溶解平衡，溶解细胞壁，从而起到抑菌杀菌的作用。虽然5，5-二甲基海因具有较强的抗菌性，但是它不能直接被固载到各种基体材料的表面以形成非溶出型抗菌材料，因此本发明利用5，5-二甲基海因对壳聚糖进行改性，生成改性壳聚糖，在壳聚糖分子中引入卤素抗菌基团，提高壳聚糖的抗菌性能。将改性壳聚糖与纳米银、聚乙烯基材共熔形成打孔膜，此时聚乙烯基材作为载体，使得改性壳聚糖能够均匀的分散在纤维原料中，形成卤胺壳聚糖抗菌纤维，就像给卫生巾穿上一层抑菌防护服，当与细菌接触时，改性壳聚糖中的卤正离子、铵根离子均能起到杀菌作用，从而提高抑菌效率，降低最低抑菌浓度，使护垫具有抗菌性能的长效性，不但使用起来更卫生，更能消除异味。
(3)由对比例6-8的数据可见，5，5-二甲基海因、壳聚糖、聚乙烯的重量比不在(0.5-0.8)：(1.5-2.2)：(45-60)范围内时，制得的女士护垫的抑菌率和最低抑菌浓度数值与实施例1-3的数值相差甚大，与现有技术(对比例5)的数值相当。本发明5，5-二甲基海因、壳聚糖、聚乙烯作为补强体系，实施例1-3通过控制制备女士护垫时添加5，5-二甲基海因、壳聚糖、聚乙烯的重量比为(0.5-0.8)：(1.5-2.2)：(45-60)，实现在补强体系中利用5，5-二甲基海因释放出氧化性的卤正离子、壳聚糖分子中的铵根离子溶解细胞壁、聚乙烯基材与纳米银壳聚糖抗菌纤维共熔形成抗菌合成纤维原料等特点，使得5，5-二甲基海因、壳聚糖、聚乙烯构成的补强体系在本发明的女士护垫中，提高女士护垫的抑菌性能。
以上内容不能认定本发明具体实施只局限于这些说明，对于本发明所属技术领域的普通技术人员来说，在不脱离本发明构思前提下，还可以做出若干简单推演或替换，都应当视为属于本发明由所提交的权利要求书确定的专利保护范围。

Claims (9)

1.一种纳米材料抗菌保健女士护垫，其特征在于，包括自上而下依次叠合在一起的网面层、中药层、吸水层、防水层以及胶粘剂层，所述的网面层为经过中药浸液浸泡并干燥后纳米银抗菌无纺布织物面料，包括以下主要成分：纳米银、5，5-二甲基海因、壳聚糖、蛋壳粉、聚乙烯、ES纤维、负离子纤维；所述中药浸液由以下中药原料提取制成：当归、香附、金银花、蒲公英、艾叶、炒楂曲、干地龙、益母草；所述的中药层包括以下药物：藏红花、蛇床子、连翘、鱼腥草、地肤子、黄连、苦参、当归、柴胡；
所述的5，5-二甲基海因、壳聚糖、聚乙烯的用量比为(0.5-0.8)：(1.5-2.2)：(45-60)。
2.根据权利要求1所述的纳米材料抗菌保健女士护垫，其特征在于，所述的5，5-二甲基海因、壳聚糖、聚乙烯的用量比为0.7:1.8:55。
3.根据权利要求1或2所述的纳米材料抗菌保健女士护垫，其特征在于，所述纳米银抗菌无纺布织物面料以重量份为单位包括以下主要成分：纳米银5-8份、5，5-二甲基海因0.5-0.8份、壳聚糖1.5-2.2份、蛋壳粉0.5-1.2份、聚乙烯45-60份、ES纤维20-35份、负离子纤维8-15份；所述中药浸液由以下重量份的中药原料提取制成：当归1-3份、香附10-15份、金银花5-8份、蒲公英6-10份、艾叶10-13份、炒楂曲8-10份、干地龙1-3份、益母草7-11份；所述的中药层包括以下重量份的药物：藏红花5-9份、蛇床子5-8份、连翘10-13份、鱼腥草12-15份、地肤子18-20份、黄连5-7份、苦参4-9份、当归6-8份、柴胡4-10份。
4.根据权利要求1所述的纳米材料抗菌保健女士护垫，其特征在于，所述网面层的制备方法包括以下步骤：将所述的各中药去除杂质，漂洗干净后，加原料药总量3-4倍的水，煎煮1-2h，过滤，煎煮两次后合并滤液，滤液浓缩后将纳米银抗菌无纺布织物面料放入药液中浸泡10-15min，然后于50-70℃下烘干。
5.根据权利要求1所述的纳米材料抗菌保健女士护垫，其特征在于，所述中药层制备方法，包括以下步骤：
S1：称取藏红花、蛇床子、连翘、鱼腥草、地肤子、黄连、苦参、当归、柴胡，洗净后干燥，备用；
S2：将干燥后的中药粉碎后过100目筛，得到细粉；
S3：将细粉与棉絮混配制浆，再把得到的纸浆制成中药层。
6.根据权利要求1或4所述的纳米材料抗菌保健女士护垫，其特征在于，所述纳米银抗菌无纺布织物面料的制备方法包括以下步骤：
A:将纳米银和蛋壳粉于在80-100℃下快速搅拌3-5min，然后超声15-20min制得蛋壳粉纳米银复合材料备用；
B：将5，5-二甲基海因于180℃下熔化，加入壳聚糖和甲醇，用200-300r/min的速度搅拌10-20min，形成改性壳聚糖；
C：将蛋壳粉纳米银复合材料和十分之一的聚乙烯混合、熔化，再加入改性壳聚糖，然后用220-250r/min的速度搅拌10-15min，用挤塑机制粒，得纳米银壳聚糖抗菌无纺布母料备用；
D：将纳米银壳聚糖抗菌无纺布母料与剩余的聚乙烯混合后加入制膜机料仓熔化，后经螺杆从膜头挤出，然后打孔成抗菌打孔膜，再加入ES纤维和负离子纤维，用纤维拉丝机拉丝，制成纳米银抗菌无纺布织物面料。
7.根据权利要求6所述的纳米材料抗菌保健女士护垫，其特征在于，所述步骤A中快速搅拌的速度为400-500r/min。
8.根据权利要求6所述的纳米材料抗菌保健女士护垫，其特征在于，所述步骤A纳米银采用粒径为10-30nm的超微颗粒。
9.根据权利要求6所述的纳米材料抗菌保健女士护垫，其特征在于，所述步骤B中甲醇浓度为2mol/L。
CN201811504502.2A 2018-12-10 2018-12-10 一种纳米材料抗菌保健女士护垫 Withdrawn CN109395149A (zh)