CN109385913A - A kind of manufacturing method of PU gum shoes surfacing material - Google Patents

A kind of manufacturing method of PU gum shoes surfacing material Download PDF

Info

Publication number
CN109385913A
CN109385913A CN201811258474.0A CN201811258474A CN109385913A CN 109385913 A CN109385913 A CN 109385913A CN 201811258474 A CN201811258474 A CN 201811258474A CN 109385913 A CN109385913 A CN 109385913A
Authority
CN
China
Prior art keywords
mold
resin
mixture
graphene
oven
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201811258474.0A
Other languages
Chinese (zh)
Inventor
洪佳源
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangzhou Hengzheng Science And Technology Development Co Ltd
Original Assignee
Guangzhou Hengzheng Science And Technology Development Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guangzhou Hengzheng Science And Technology Development Co Ltd filed Critical Guangzhou Hengzheng Science And Technology Development Co Ltd
Priority to CN201811258474.0A priority Critical patent/CN109385913A/en
Publication of CN109385913A publication Critical patent/CN109385913A/en
Pending legal-status Critical Current

Abstract

A kind of manufacturing method of PU gum shoes surfacing material, comprising the following steps: (1) PU resin and graphene are stirred evenly in the ratio of 2-6:100-500, obtain the surface layer mixture of PU resin and graphene；(2) mold is handled, jet mould has mould release on mold, handles mold, the surface layer mixture of PU resin and graphene that step (1) obtains is filled on mold by (3)；(4) mold that mixture is perfused is placed in vacuum tank and is vacuumized, remove the bubble in PU resin；(5) mould is scraped, (6) clear mould further cleans out mixture extra on mold；(7) it will be fed into the mold in step (6) after cleaning, be put into baking oven and toasted, until superficial drying, baking oven out；The above-mentioned base fabric with mixture cuts into vamp shape, obtains the ventilative vamp with PU resin and graphene.It is prepared simply, and stereoscopic effect is good, have good air permeability and surfacing is bright.

Description

A kind of manufacturing method of PU gum shoes surfacing material
Technical field
The present invention relates to the manufacturing method of gum shoes surfacing material more particularly to a kind of manufacturing methods of PU gum shoes surfacing material.
Background technique
In traditional shoe-making industry, printing ink printing art, the figure of ink printing are used usually on the vamp of sport footwear Case is plane pattern, does not have support and defencive function, can only play role in decoration, and pattern does not have three-dimensional sense.
There are mainly two types of the processing methods of space pattern on existing vamp: one is by hot-melt adhesive, will make Good vamp space pattern pasted after hot melt vamp surface layer either by sewing by way of pattern vehicle that will make It is sewn on vamp upper layer cloth, such method manufacture craft is more complicated, and the low efficiency of production simultaneously influences entire vamp appearance The gas permeability of aesthetic feeling, existing vamp is bad.
Summary of the invention
For above-mentioned deficiency in the prior art, the present invention provides a kind of manufacturing method of PU gum shoes surfacing material, preparation letters Single, stereoscopic effect is good, have good air permeability and surfacing is bright.
In order to achieve the above object of the invention, the present invention use the specific scheme is that
A kind of manufacturing method of PU gum shoes surfacing material, comprising the following steps:
(1) PU resin and graphene are stirred evenly in the ratio of 2-6:100-500, the surface layer for obtaining PU resin and graphene is mixed Close material；
(2) mold is handled, jet mould has mould release on mold, handles mold, mold is warmed to 40-60 DEG C；
(3) the surface layer mixture of PU resin and graphene that step (1) obtains is filled on mold；
(4) mold that mixture is perfused is placed in vacuum tank and is vacuumized, remove the bubble in PU resin；The time vacuumized is 30-35 seconds；
(5) mould is scraped, mixture extra on mold is cleaned out；Mold passes through oven heat, the molding of PU semi-finished product, mold Time by oven is 60-65 seconds, and the temperature of oven is 120-125 DEG C；
(6) clear mould further cleans out mixture extra on mold；
(7) it will be fed into the mold in step (6) after cleaning, be put into baking oven and toasted, until superficial drying, baking oven out；It is above-mentioned Base fabric with mixture cuts into vamp shape, obtains the ventilative vamp with PU resin and graphene.
Further, the mould release is glassine paper.
Further, in step (7) a metallic, the PU gum shoes surfacing material semi-finished product are placed in oven and toast 2-3h, the temperature of oven It is 45-60 DEG C.
The invention has the benefit that
Graphene, which is added, makes vamp stereoscopic effect of the present invention is non-to feel, and gives the different visual experience of people, meanwhile, graphene On vamp, air permeability effect is preferable, and the present invention enables graphene and PU resin layer firm using special process means and method Solid be combined together, it is not easily to fall off.
Specific embodiment
The present invention is further described below by way of specific embodiment, but the present invention is not limited only to following embodiment.At this In the range of invention or the contents of the present invention are not being departed from, in spirit and scope, the change that carries out to the present invention is combined or replaced It changes, will be apparent to the person skilled in the art, and be included within the scope of the present invention.
A kind of embodiment 1: manufacturing method of PU gum shoes surfacing material, comprising the following steps:
(1) PU resin and graphene are stirred evenly in the ratio of 3:200, obtains the surface layer mixture of PU resin and graphene；
(2) mold is handled, jet mould has mould release on mold, handles mold, mold is warmed to 40 DEG C；
(3) the surface layer mixture of PU resin and graphene that step (1) obtains is filled on mold；
(4) mold that mixture is perfused is placed in vacuum tank and is vacuumized, remove the bubble in PU resin；The time vacuumized is 30 seconds；
(5) mould is scraped, mixture extra on mold is cleaned out；Mold passes through oven heat, the molding of PU semi-finished product, mold warp The time for crossing oven is 60 seconds, and the temperature of oven is 120 DEG C；
(6) clear mould further cleans out mixture extra on mold；
(7) it will be fed into the mold in step (6) after cleaning, be put into baking oven and toasted, until superficial drying, baking oven out；It is above-mentioned Base fabric with mixture cuts into vamp shape, obtains the ventilative vamp with PU resin and graphene.
The mould release is glassine paper.
In step (7) a metallic, the PU gum shoes surfacing material semi-finished product are placed in oven and toast 2h, the temperature of oven is 45 DEG C.
A kind of embodiment 2: manufacturing method of PU gum shoes surfacing material, comprising the following steps:
(1) PU resin and graphene are stirred evenly in the ratio of 5:300, obtains the surface layer mixture of PU resin and graphene；
(2) mold is handled, jet mould has mould release on mold, handles mold, mold is warmed to 50 DEG C；
(3) the surface layer mixture of PU resin and graphene that step (1) obtains is filled on mold；
(4) mold that mixture is perfused is placed in vacuum tank and is vacuumized, remove the bubble in PU resin；The time vacuumized is 33 seconds；
(5) mould is scraped, mixture extra on mold is cleaned out；Mold passes through oven heat, the molding of PU semi-finished product, mold Time by oven is 63 seconds, and the temperature of oven is 123 DEG C；
(6) clear mould further cleans out mixture extra on mold；
(7) it will be fed into the mold in step (6) after cleaning, be put into baking oven and toasted, until superficial drying, baking oven out；It is above-mentioned Base fabric with mixture cuts into vamp shape, obtains the ventilative vamp with PU resin and graphene.
In step (7) a metallic, the PU gum shoes surfacing material semi-finished product are placed in oven and toast 2.5h, the temperature of oven is 50 DEG C.
A kind of embodiment 3: manufacturing method of PU gum shoes surfacing material, comprising the following steps:
(1) PU resin and graphene are stirred evenly in the ratio of 6:500, obtains the surface layer mixture of PU resin and graphene；
(2) mold is handled, jet mould has mould release on mold, handles mold, mold is warmed to 60 DEG C；
(3) the surface layer mixture of PU resin and graphene that step (1) obtains is filled on mold；
(4) mold that mixture is perfused is placed in vacuum tank and is vacuumized, remove the bubble in PU resin；The time vacuumized is 35 seconds；
(5) mould is scraped, mixture extra on mold is cleaned out；Mold passes through oven heat, the molding of PU semi-finished product, mold warp The time for crossing oven is 65 seconds, and the temperature of oven is 125 DEG C；
(6) clear mould further cleans out mixture extra on mold；
(7) it will be fed into the mold in step (6) after cleaning, be put into baking oven and toasted, until superficial drying, baking oven out；It is above-mentioned Base fabric with mixture cuts into vamp shape, obtains the ventilative vamp with PU resin and graphene.
In step (7) a metallic, the PU gum shoes surfacing material semi-finished product are placed in oven and toast 3h, the temperature of oven is 60 DEG C.
The above description is only a preferred embodiment of the patent of the present invention, is not intended to limit the invention patent, all at this Made any modifications, equivalent replacements, and improvements etc., should be included in the invention patent within the spirit and principle of patent of invention Protection scope within.

Claims (3)

1. a kind of manufacturing method of PU gum shoes surfacing material, which comprises the following steps:
(1) PU resin and graphene are stirred evenly in the ratio of 2-6:100-500, the surface layer for obtaining PU resin and graphene is mixed Close material；
(2) mold is handled, jet mould has mould release on mold, handles mold, mold is warmed to 40-60 DEG C；
(3) the surface layer mixture of PU resin and graphene that step (1) obtains is filled on mold；
(4) mold that mixture is perfused is placed in vacuum tank and is vacuumized, remove the bubble in PU resin；The time vacuumized is 30-35 seconds；
(5) mould is scraped, mixture extra on mold is cleaned out；Mold passes through oven heat, the molding of PU semi-finished product, mold Time by oven is 60-65 seconds, and the temperature of oven is 120-125 DEG C；
(6) clear mould further cleans out mixture extra on mold；
(7) it will be fed into the mold in step (6) after cleaning, be put into baking oven and toasted, until superficial drying, baking oven out；It is above-mentioned Base fabric with mixture cuts into vamp shape, obtains the ventilative vamp with PU resin and graphene.
2. a kind of manufacturing method of PU gum shoes surfacing material according to claim 1, it is characterised in that: the mould release is glass Paper.
3. a kind of manufacturing method of PU gum shoes surfacing material according to claim 1, it is characterised in that: in step (7) a metallic, will be described PU gum shoes surfacing material semi-finished product, which are placed in oven, toasts 2-3h, and the temperature of oven is 45-60 DEG C.
CN201811258474.0A 2018-10-26 2018-10-26 A kind of manufacturing method of PU gum shoes surfacing material Pending CN109385913A (en)