CN109385746A - A kind of bamboo fiber filler material of high-hydroscopicity and preparation method thereof - Google Patents
A kind of bamboo fiber filler material of high-hydroscopicity and preparation method thereof Download PDFInfo
- Publication number
- CN109385746A CN109385746A CN201811164157.2A CN201811164157A CN109385746A CN 109385746 A CN109385746 A CN 109385746A CN 201811164157 A CN201811164157 A CN 201811164157A CN 109385746 A CN109385746 A CN 109385746A
- Authority
- CN
- China
- Prior art keywords
- bamboo
- fiber
- filler material
- hydroscopicity
- bamboo fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of bamboo fiber filler material of high-hydroscopicity and preparation method thereof, the bamboo fiber filler material of high-hydroscopicity includes the raw material of following parts by weight: not siliceous bamboo fiber 30~60,15~40,4080 eutectic polyester fiber 5~35 of ferment fiber crops.Alternatively, the not siliceous bamboo fiber 35~57,18~38,4080 eutectic polyester fiber 7.5~32.5 of ferment fiber crops.The production method of the bamboo fiber filler material of high-hydroscopicity, comprising the following steps: step 1 weighs each raw material in parts by weight first, obtains mixture after being then mixed evenly each raw material feeding batch mixer;Mixture is sequentially sent to double doffer card, baking oven, needing machine and hot-rolling mill by step 2, finally by cutting volume and winder, obtains finished product.The bamboo fiber filler material for the high-hydroscopicity that the present invention obtains, flexibility, antibacterial bacteriostatic, water imbibition and hygroscopicity are significantly improved, and reduce cost of material.
Description
Technical field
The present invention relates to bamboo fiber filler materials of a kind of high-hydroscopicity and preparation method thereof.
Background technique
105078662 A of Chinese patent literature CN discloses a kind of medical adult diaper on November 25th, 2015,
Including diaper body, the top of the diaper body is equipped with elastic band;It sews up at the surface middle part both ends of the elastic band
There is the first velcro;The both ends of the elastic band are stitched with the first connecting band;The lower inside of the diaper body is pasted
There is nappy;The nappy be successively closely pasted with from top to bottom water suction nonwoven layer, ventilative salient point layer, anti-inflammation and sterilization layer,
Water absorption layer and waterproof counterdie;The bottom of the diaper body be equipped with diversion pipe, and the diversion pipe and be located at diversion pipe lower part
Urine storage bottle be threadedly coupled;The second connecting band is symmetrically arranged at left and right sides of the urine storage bottle;The end of second connecting band
Equipped with the second velcro.The water absorbing capacity of this medical adult diaper is not ideal enough, has much room for improvement.
Summary of the invention
The purpose of the present invention is intended to provide bamboo fiber filler material and its production of a kind of high-hydroscopicity that water absorbing properties are good
Method, to overcome shortcoming in the prior art.
By a kind of bamboo fiber filler material of high-hydroscopicity of this purpose design, it is characterized in that including following parts by weight
Raw material: not siliceous bamboo fiber 30~60,15~40,4080 eutectic polyester fiber 5~35 of ferment fiber crops.
Further, the not siliceous bamboo fiber 35~57,18~38,4080 eutectic polyester fiber 7.5 of ferment fiber crops~
32.5。
Further, the not siliceous bamboo fiber 38.5~55.5,21~38,4080 eutectic polyester fiber of ferment fiber crops
11.5~30.
Further, the not siliceous bamboo fiber 40~55,23~30,4080 eutectic polyester fiber 5~28 of ferment fiber crops.
Further, the not siliceous bamboo fiber 42~50,28~35,4080 eutectic polyester fiber 20 of ferment fiber crops~
30。
Further, the not siliceous bamboo fiber 33~48,27~37,4080 eutectic polyester fiber 18 of ferment fiber crops~
27。
Further, the length of the not siliceous bamboo fiber is greater than 2.5cm, the fineness of bamboo fiber be 50 public branch~
100 public branch.
A kind of production method of the bamboo fiber filler material of high-hydroscopicity, it is characterized in that the following steps are included:
Step 1 weighs each raw material in parts by weight first, obtains after being then mixed evenly each raw material feeding batch mixer
Mixture;
Mixture is sequentially sent to hopper, is sent to opener progress shredding by pin curtain conveyer belt, then passed through again by step 2
Cross that the combing of comb vehicle, lapping, hot-air oven hot rolling, needle thorn finally by cutting volume and winding obtain finished product on auxiliary net machine.
Needle thorn includes two stages: pre-needling stage and main acupuncture stage, wherein the needle plate in pre-needling stage is
2200~2500/m2, the needle plate of main acupuncture stage is 2800~3000/m2。
It is divided into heating and lower heating in the baking oven, wherein the temperature above heated is 110 DEG C, and the temperature of lower heating is
110 DEG C, mixture conveys between upper heating and lower heating.
Bamboo fiber in the present invention also have antibacterial bacteriostatic is anti-mite, moisture absorption is ventilative, natural health, can generate negative oxygen from
The function that son, heat accumulation thermal, damping noise control, anti-mould and anti-moth, Antistatic radiation-proof, antiultraviolet, deodorization are adsorbed.Due to bamboo fibril
Dimension remains the structural form of natural bamboo cellulose, and there is groove on surface, and there is cavity in inside, these special constructions are because of capillary
Effect, can easily adsorb moisture content, and moment moisture absorption is simultaneously evaporated, to have excellent moisture permeability;And reduce original
Expect cost.
4080 eutectic polyester fibers in the present invention are the composite fibre of skin-core structure, the not siliceous bamboo mixed
Fibrinogen, ferment fiber crops and 4080 eutectic polyester fibers are paved into after shredding, combing and lapping process with certain thickness
Web, when which passes through hot-air oven, under the heating temperature condition in hot-air oven, 4080 eutectic polyester fibers
Cortex melts and sandwich layer still keeps physical structure, and the cortex after fusing both can be with surrounding other 4080 eutectic polyester fibers
Cortex be adhered together, can also be adhered together with surrounding bamboo fiber or ferment fiber crops, then, bamboo fiber, ferment
Bonding strength between plain fiber crops and 4080 eutectic polyester fibers is improved, using hot-air oven leading portion hot rolling when, bamboo
Fibrinogen, ferment fiber crops and the volume of 4080 eutectic polyester fibers are compressed, and density is improved, and integral strength is enhanced.With
Afterwards, process is pierced into needle, bamboo fiber, ferment fiber crops and 4080 eutectic polyester fibers can be both twisted together by needle thorn, and may be used also
To form fine channel on the semi-finished product by hot-air oven hot-roll forming, and the fine channel can in bamboo fiber
Portion's cavity is connected;Extraneous air is entered between bamboo fiber, ferment fiber crops and 4080 eutectic polyester fibers
Gap can also pass into the cavity of bamboo fiber, to improve soaking effect and adsorptivity.
The bamboo fiber filler material for the high-hydroscopicity that the present invention obtains by adopting the above technical scheme has the spy for inhaling fastly fastly arranging
Point, hygroscopicity and water imbibition are significantly improved, and reduce cost of material;Also, the bamboo fiber of high-hydroscopicity is filled out
Charge can be reused, more environmental protection and energy saving after washing.
The product that the present invention obtains can be used to make the filler material, sanitary napkin, medical dressing packet, shoes of diaper or paper diaper
Pad, upper of a shoe etc., with the biggish scope of application.
In conclusion the present invention has the characteristics that flexibility, antibacterial bacteriostatic, soaking effect are good.
Specific embodiment
The present invention will be further described below with reference to examples.
First embodiment
The bamboo fiber filler material of this high-hydroscopicity, the raw material including following parts by weight: not siliceous bamboo fiber 30
~60,15~40,4080 eutectic polyester fiber 5~35 of ferment fiber crops.
When making bamboo fiber, bamboo fiber is obtained after bamboo is removed photoresist using solvent physical method.
A kind of production method of the bamboo fiber filler material of high-hydroscopicity, comprising the following steps:
Step 1 weighs each raw material in parts by weight first, obtains after being then mixed evenly each raw material feeding batch mixer
Mixture;
Mixture is sequentially sent to hopper, is sent to opener progress shredding by pin curtain conveyer belt, then passed through again by step 2
Cross that the combing of comb vehicle, lapping, hot-air oven hot rolling, needle thorn finally by cutting volume and winding obtain finished product on auxiliary net machine.By opening
Loose machine mixture can be broken up with it is fluffy.
The needing machine includes two stages: pre-needling stage and main acupuncture stage, wherein the needle plate in pre-needling stage is
2200~2500/m2, the needle plate of main acupuncture stage is 2800~3000/m2.Be first by the pre-needling stage, followed by
By main acupuncture stage.
The pricker that diameter is 0.5mm is respectively arranged on the needle plate in pre-needling stage and the needle plate of main acupuncture stage.Pre- needle
The needle plate of thorn and main needle thorn carries out upper knit stitch thorn respectively with 500~600 frequencies per minute.
It is divided into heating and lower heating in the baking oven, wherein the temperature above heated is 110 DEG C, and the temperature of lower heating is
110 DEG C, mixture conveys between upper heating and lower heating.
Wherein, 4080 eutectic polyester fibers can use 4080 fibers of Fu Weier.The not siliceous bamboo fiber
Length is greater than 2.5cm, and the fineness of bamboo fiber is the 50 public branch of public branch~100.
In practice, ferment fiber crops can be using decoloration ferment fiber crops.
Second embodiment
In the present embodiment, the not siliceous bamboo fiber 35~57,18~38,4080 eutectic polyester fiber of ferment fiber crops
7.5~32.5.
First embodiment is seen in remaining not described part, repeats no more.
3rd embodiment
In the present embodiment, the not siliceous bamboo fiber 38.5~55.5,21~38,4080 eutectic polyester of ferment fiber crops
Fiber 11.5~30.
First embodiment is seen in remaining not described part, repeats no more.
Fourth embodiment
In the present embodiment, the not siliceous bamboo fiber 40~55,23~30,4080 eutectic polyester fiber of ferment fiber crops
5~28.
First embodiment is seen in remaining not described part, repeats no more.
5th embodiment
In the present embodiment, the not siliceous bamboo fiber 42~50,28~35,4080 eutectic polyester fiber of ferment fiber crops
20~30.
First embodiment is seen in remaining not described part, repeats no more.
5th embodiment
In the present embodiment, the not siliceous bamboo fiber 33~48,27~37,4080 eutectic polyester fiber of ferment fiber crops
18~27.
Sixth embodiment
In the present embodiment, the not siliceous bamboo fiber 33~35,18~20,4080 eutectic polyester fiber of ferment fiber crops
5~8.
First embodiment is seen in remaining not described part, repeats no more.
The above shows and describes the basic principles and main features of the present invention and the advantages of the present invention.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and the above embodiments and description only describe this
The principle of invention, without departing from the spirit and scope of the present invention, various changes and improvements may be made to the invention, these changes
Change and improvement all fall within the protetion scope of the claimed invention.The claimed scope of the invention by appended claims and its
Equivalent thereof.
Claims (10)
1. the bamboo fiber filler material of a kind of high-hydroscopicity, it is characterized in that including the raw material of following parts by weight: not siliceous bamboo
Fibrinogen 30~60,15~40,4080 eutectic polyester fiber 5~35 of ferment fiber crops.
2. the bamboo fiber filler material of high-hydroscopicity according to claim 1, it is characterized in that the not siliceous bamboo fibril
Dimension 35~57,18~38,4080 eutectic polyester fiber 7.5~32.5 of ferment fiber crops.
3. the bamboo fiber filler material of high-hydroscopicity according to claim 1, it is characterized in that the not siliceous bamboo fibril
Dimension 38.5~55.5,21~38,4080 eutectic polyester fiber 11.5~30 of ferment fiber crops.
4. the bamboo fiber filler material of high-hydroscopicity according to claim 1, it is characterized in that the not siliceous bamboo fibril
Dimension 40~55,23~30,4080 eutectic polyester fiber 5~28 of ferment fiber crops.
5. the bamboo fiber filler material of high-hydroscopicity according to claim 1, it is characterized in that the not siliceous bamboo fibril
Dimension 42~50,28~35,4080 eutectic polyester fiber 20~30 of ferment fiber crops.
6. the bamboo fiber filler material of high-hydroscopicity according to claim 1, it is characterized in that the not siliceous bamboo fibril
Dimension 33~48,27~37,4080 eutectic polyester fiber 18~27 of ferment fiber crops.
7. the bamboo fiber filler material of high-hydroscopicity according to claim 1, it is characterized in that the not siliceous bamboo fibril
The length of dimension is greater than 2.5cm, and the fineness of bamboo fiber is the 50 public branch of public branch~100.
8. a kind of production method of the bamboo fiber filler material of high-hydroscopicity according to claim 1, it is characterized in that including
Following steps:
Step 1 weighs each raw material in parts by weight first, is mixed after being then mixed evenly each raw material feeding batch mixer
Object;
Mixture is sequentially sent to hopper, is sent to opener progress shredding by pin curtain conveyer belt, then using comb by step 2
Lapping, hot-air oven hot rolling, needle thorn obtain finished product finally by cutting volume and winding in vehicle combing, auxiliary net machine.
9. the production method of the bamboo fiber filler material of high-hydroscopicity according to claim 8, it is characterized in that the needle pierces
Including two stages: pre-needling stage and main acupuncture stage, wherein the needle plate in pre-needling stage is 2200~2500/m2, main
The needle plate of acupuncture stage is 2800~3000/m2。
10. the production method of the bamboo fiber filler material of high-hydroscopicity according to claim 8, it is characterized in that the baking oven
Inside it is divided into heating and lower heating, wherein the temperature above heated is 110 DEG C, and the temperature of lower heating is 110 DEG C, and mixture is from upper
The past is conveyed between heating and lower heating.