CN109371323A - A kind of novel 51CrV4 special type steel alloy and its preparation process - Google Patents
A kind of novel 51CrV4 special type steel alloy and its preparation process Download PDFInfo
- Publication number
- CN109371323A CN109371323A CN201811380636.8A CN201811380636A CN109371323A CN 109371323 A CN109371323 A CN 109371323A CN 201811380636 A CN201811380636 A CN 201811380636A CN 109371323 A CN109371323 A CN 109371323A
- Authority
- CN
- China
- Prior art keywords
- steel alloy
- 51crv4
- novel
- special type
- preparation process
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of novel 51CrV4 special type steel alloy and its preparation processes, including being prepared by the chemical component of following weight percent: carbon 0.47~0.55%, silicon 0.15~0.4%, manganese 0.7~1.1%, phosphorus 0.001~0.025%, sulphur 0.001~0.025%, chromium 0.9~1.2%, molybdenum 0.001~0.40%, vanadium 0.10~0.25%, copper 0.001~0.40% and surplus are iron.The present invention in the ferrous alloy using iron as base by adding the metallic elements such as chromium, molybdenum, vanadium and copper, improve the overall structural strength of extraordinary steel alloy, by whole carbon containing raising, though losing the plasticity and impact of a part, but its tensile strength greatly improves, and in order to improve market competition, reduces cost, titanium is not added while improving carbon content, so that the overall structural strength of steel alloy is still relatively strong;By the way that amount of copper is added in component, steel alloy atmospheric corrosion resistance ability, and so more save the cost are improved, is also added as intensified element, plays the role of precipitation-hardening, allomeric function is perfect, practical.
Description
Technical field
The present invention relates to steel manufacturing technology fields, more specifically, it relates to a kind of novel 51CrV4 special type steel alloy
And its preparation process.
Background technique
Steel alloy, steel alloy are also special steel.One or more of alloying elements are appropriately added in carbon steel, make steel
Institutional framework changes, so that steel be made to have a variety of different properties.
With the constant growth of productivity, the use demand of industrial special type steel alloy is continuously improved, existing special steel
Alloy has been unable to satisfy the use demand in market gradually, and intensity is not high, and whole using effect is bad.Accordingly, the present invention proposes
A kind of novel 51CrV4 special type steel alloy and its preparation process.
Summary of the invention
It is an object of the invention to overcome the deficiencies in the prior art described above, a kind of novel 51CrV4 special type steel alloy is provided
And its preparation process.
In order to solve the above technical problems, the object of the present invention is achieved like this: one kind according to the present invention is novel
51CrV4 special type steel alloy and its preparation process, including being prepared by the chemical component of following weight percent:
Carbon 0.47~0.55%, silicon 0.15~0.4%, manganese 0.7~1.1%, phosphorus 0.001~0.025%, sulphur 0.001~
0.025%, chromium 0.9~1.2%, molybdenum 0.001~0.40%, vanadium 0.10~0.25%, copper 0.001~0.40% and surplus are
Iron.
The present invention is further arranged to: being included the following steps:
S1, carbon 0.47~0.55%, silicon 0.15~0.4%, manganese 0.7~1.1%, phosphorus 0.001~0.025%, sulphur are weighed
0.001~0.025%, chromium 0.9~1.2%, molybdenum 0.001~0.40%, vanadium 0.10~0.25%, 0.001~0.40% and of copper
Surplus is iron;
S2, continuous casting operation will be carried out on the placement conticaster of steel alloy blank obtained in step S1, obtains alloy steel profile;
S3, by the resulting alloy steel profile of step S1 after heat treatment, be heat-fed in roll mill, carry out hot rolling and fine
Hot-rolled manipulation obtains special steel alloy finished product;
S4, it after the resulting extraordinary steel alloy of step S3 is passed through annealing, is cooled to room temperature, by examining, packing
Storage.
The present invention is further arranged to: 1400~1600 DEG C of smelting temperature in the step S1, and smelting time is 1~3h,
Smelting furnace operating pressure is 0.05~0.12MPa.
The present invention is further arranged to: casting temperature is 500~700 DEG C in the step S2.
The present invention is further arranged to: hot-rolled temperature is 400 DEG C~700 DEG C in the step S3, and the time is 1~3h, essence
Thin hot-rolled temperature is 400 DEG C~600 DEG C, and the time is 1~2h.
The present invention is further arranged to: the step S4 annealing temperature is 400~500 DEG C, and then air is cooled to
Room temperature, annealing time 1h.
In conclusion the invention has the following advantages: novel 51CrV4 special type steel alloy according to the present invention and
Its preparation process improves special steel by adding the metallic elements such as chromium, molybdenum, vanadium and copper in the ferrous alloy using iron as base
The overall structural strength of alloy, by whole carbon containing raising, though the plasticity and impact of loss a part, its tensile strength are big
It is big to improve, and in order to improve market competition, cost is reduced, titanium is not added while improving carbon content, so that steel alloy
Overall structural strength is still relatively strong;By the way that amount of copper is added in component, steel alloy atmospheric corrosion resistance ability is improved, and so more
Save the cost is also added as intensified element, plays the role of precipitation-hardening, allomeric function is perfect, practical.
Specific embodiment
Below with reference to preferred embodiment, the present invention is further described.
A kind of novel 51CrV4 special type steel alloy and its preparation process involved in the present embodiment, including by following weight hundred
The chemical component of ratio is divided to be prepared:
Carbon 0.47~0.55%, silicon 0.15~0.4%, manganese 0.7~1.1%, phosphorus 0.001~0.025%, sulphur 0.001~
0.025%, chromium 0.9~1.2%, molybdenum 0.001~0.40%, vanadium 0.10~0.25%, copper 0.001~0.40% and surplus are
Iron.
A kind of novel 51CrV4 special type steel alloy and its preparation process, include the following steps:
S1, carbon 0.47~0.55%, silicon 0.15~0.4%, manganese 0.7~1.1%, phosphorus 0.001~0.025%, sulphur are weighed
0.001~0.025%, chromium 0.9~1.2%, molybdenum 0.001~0.40%, vanadium 0.10~0.25%, 0.001~0.40% and of copper
Surplus is iron;
S2, continuous casting operation will be carried out on the placement conticaster of steel alloy blank obtained in step S1, obtains alloy steel profile;
S3, by the resulting alloy steel profile of step S1 after heat treatment, be heat-fed in roll mill, carry out hot rolling and fine
Hot-rolled manipulation obtains special steel alloy finished product;
S4, it after the resulting extraordinary steel alloy of step S3 is passed through annealing, is cooled to room temperature, by examining, packing
Storage.
Further, 1400~1600 DEG C of smelting temperature in the step S1, smelting time is 1~3h, smelting furnace work
Pressure is 0.05~0.12MPa.
Further, casting temperature is 500~700 DEG C in the step S2.
Further, hot-rolled temperature is 400 DEG C~700 DEG C in the step S3, and the time is 1~3h, fine hot-rolled temperature
It is 400 DEG C~600 DEG C, the time is 1~2h.
Further, step S4 annealing temperature is 400~500 DEG C, and then air is cooled to room temperature, when annealing
Between 1h.
Embodiment 1:
S1, carbon 0.5%, silicon 0.3%, manganese 1.0%, phosphorus 0.018%, sulphur 0.02%, chromium 1.0%, molybdenum 0.3%, vanadium are weighed
0.20%, copper 0.25% and surplus are iron, are smelted in investment vacuum metling converter after mixing, obtain steel alloy blank;
S2, continuous casting operation will be carried out on the placement conticaster of steel alloy blank obtained in step S1, obtains alloy steel profile;
S3, by the resulting alloy steel profile of step S1 after heat treatment, be heat-fed in roll mill, carry out hot rolling and fine
Hot-rolled manipulation obtains special steel alloy finished product;
S4, it after the resulting extraordinary steel alloy of step S3 is passed through annealing, is cooled to room temperature, by examining, packing
Storage.
Wherein, 1550 DEG C of smelting temperature, smelting time 2h in the step S1, smelting furnace operating pressure is 0.1MPa.
Wherein, casting temperature is 650 DEG C in the step S2.
Further, hot-rolled temperature is 500 DEG C, time 2.5h in the step S3, and fine hot-rolled temperature is 550 DEG C,
Time is 2h.
Further, the step S4 annealing temperature is 480 DEG C, and then air is cooled to room temperature, annealing time 1h.
Novel 51CrV4 special type steel alloy according to the present invention and its preparation process, by using iron as the iron-based conjunction of base
The metallic elements such as chromium, molybdenum, vanadium and copper are added in gold, improve the overall structural strength of extraordinary steel alloy, and carbon containing by entirety mentions
Height, though the plasticity and impact of loss a part, its tensile strength greatly improved, and in order to improve market competition, reduce at
This, titanium is not added while improving carbon content, so that the overall structural strength of steel alloy is still relatively strong;By adding in component
Enter amount of copper, improves steel alloy atmospheric corrosion resistance ability, and more save the cost plays also as intensified element addition in this way
The effect of precipitation-hardening, allomeric function is perfect, practical.
The preferred embodiment of the present invention has been described in detail above.It should be appreciated that those skilled in the art without
It needs creative work according to the present invention can conceive and makes many modifications and variations.Therefore, all technologies in the art
Personnel are available by logical analysis, reasoning, or a limited experiment on the basis of existing technology under this invention's idea
Technical solution, all should be within the scope of protection determined by the claims.
Claims (6)
1. a kind of novel 51CrV4 special type steel alloy and its preparation process, which is characterized in that including by following weight percent
Chemical component is prepared:
Carbon 0.47~0.55%, silicon 0.15~0.4%, manganese 0.7~1.1%, phosphorus 0.001~0.025%, sulphur 0.001~
0.025%, chromium 0.9~1.2%, molybdenum 0.001~0.40%, vanadium 0.10~0.25%, copper 0.001~0.40% and surplus are
Iron.
2. a kind of novel 51CrV4 special type steel alloy and its preparation process, which comprises the steps of:
S1, carbon 0.47~0.55%, silicon 0.15~0.4%, manganese 0.7~1.1%, phosphorus 0.001~0.025%, sulphur 0.001 are weighed
~0.025%, chromium 0.9~1.2%, molybdenum 0.001~0.40%, vanadium 0.10~0.25%, copper 0.001~0.40% and surplus are
Iron;
S2, continuous casting operation will be carried out on the placement conticaster of steel alloy blank obtained in step S1, obtains alloy steel profile;
S3, it after the resulting alloy steel profile of step S1 is passed through heat treatment, is heat-fed in roll mill, carries out hot rolling and fine hot rolling
Operation, obtains special steel alloy finished product;
S4, it after the resulting extraordinary steel alloy of step S3 is passed through annealing, is cooled to room temperature, by examining, being packed and stored.
3. novel 51CrV4 special type steel alloy according to claim 2 and its preparation process, which is characterized in that the step
1400~1600 DEG C of smelting temperature in S1, smelting time are 1~3h, and smelting furnace operating pressure is 0.05~0.12MPa.
4. novel 51CrV4 special type steel alloy according to claim 2 and its preparation process, which is characterized in that the step
Casting temperature is 500~700 DEG C in S2.
5. novel 51CrV4 special type steel alloy according to claim 2 and its preparation process, which is characterized in that the step
In S3 hot-rolled temperature be 400 DEG C~700 DEG C, the time be 1~3h, fine hot-rolled temperature be 400 DEG C~600 DEG C, the time be 1~
2h。
6. novel 51CrV4 special type steel alloy according to claim 2 and its preparation process, which is characterized in that the step
It is 400~500 DEG C that S4, which makes annealing treatment temperature, and then air is cooled to room temperature, annealing time 1h.