CN109370720A - Low-noise lubricating grease and preparation method thereof - Google Patents
Low-noise lubricating grease and preparation method thereof Download PDFInfo
- Publication number
- CN109370720A CN109370720A CN201811273974.1A CN201811273974A CN109370720A CN 109370720 A CN109370720 A CN 109370720A CN 201811273974 A CN201811273974 A CN 201811273974A CN 109370720 A CN109370720 A CN 109370720A
- Authority
- CN
- China
- Prior art keywords
- oil
- organic amine
- diisocyanate
- low
- lubricating grease
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of low-noise lubricating grease and preparation method thereof, the low-noise lubricating grease includes following weight percentage components: base oil 40-50%;Thickening agent 30-35%;Vibration damping agent 20-25%;Antiwear additive 1-5%;Extreme-pressure antiwear compound additive for lubricating oil 1-2%;The base oil is polyester;The preparation method of the low-noise lubricating grease: it comprises the steps of: A, be added to organic amine in 1/2 base oil, be heated to organic amine and dissolve completely;B, diisocyanate is added in remaining base oil again, is heated to dissolving;C, then being added in organic amine oil to be sufficiently stirred by diisocyanate ester oil reacts organic amine completely with diisocyanate, temperature of charge is increased to 100-120 DEG C at this time, stirring simultaneously constant temperature 30 minutes at this temperature, are added vibration damping agent, antiwear additive and extreme-pressure antiwear compound additive for lubricating oil after being cooled to 30 DEG C;The present invention can be biodegradable, good environmental protection;The preparation method of low-noise lubricating grease of the present invention is simple, practical.
Description
Technical field
The present invention relates to a kind of improvement of low-noise lubricating grease, and in particular to it is a kind of with excellent bass performance, it is excellent
Bearing sound quality cover performance, excellent high temperature and cryogenic property, good mechanical stability, colloid stability and anti-oxidant peace
Qualitative, excellent greasy property, Corrosion Protection and long service life, while can be biodegradable, the low noise of good environmental protection
Sound lubricating grease and preparation method thereof.
Background technique
Current existing low noise bearing is moistened in lubricating grease kind with lithium base grease, complex lithium grease and polyureas
Based on consistent lubricant.In terms of the vibration performance of sealing bearing, the initiation value of lithium base grease is lower, can reach in a very short period of time
Stationary value the starting quietness of lithium base grease and operates mute better performances after special processing, but high temperature resistance, cuts
Cut stability, water-resistance can not meet the development of bearing technology.Complex lithium grease improves anti-softening ability when high temperature,
But fiber is caused to enhance the constraint ability of base oil simultaneously, static colloid point oil is lower, corresponding oily smaller, the molecule of dynamic point
Internal friction increases when mutually moving, and the apparent viscosity under identical rate of shear increases, and causes in the lubricated of Sealed Rolling Bearing with Low Noise
Starved Lubrication aggravates in journey, and bearing noise performance is not good enough.Polyurea grease has using temperature height, and the service life is long, good fluidity
The advantages that, but production technology is complicated, acoustic property is unstable, and product quality is difficult to control, and higher cost, meanwhile, it is existing low
Noise lubricating grease cannot be biodegradable, and environmental-protecting performance is poor.
For this purpose, we have developed a kind of bearing sound quality cover performance, excellent height with excellent bass performance, excellent
Temperature and cryogenic property, good mechanical stability, colloid stability and anti-oxidative stability, excellent greasy property, anticorrosion
Performance and long service life, while can be biodegradable, low-noise lubricating grease of good environmental protection and preparation method thereof.
Summary of the invention
It is covered in order to solve the above technical problems, the present invention provides a kind of bearing sound quality with excellent bass performance, excellent
It is lid performance, excellent high temperature and cryogenic property, good mechanical stability, colloid stability and anti-oxidative stability, excellent
Greasy property, Corrosion Protection and long service life, at the same can biodegrade, the low-noise lubricating grease of good environmental protection and its
Preparation method.
Low-noise lubricating grease of the present invention, including following weight percentage components:
The base oil is polyester;
The thickening agent is organic amine and diisocyanate;
The vibration damping agent is pentaerythritol fatty acid ester (PE1, 40 DEG C of viscosity 14.67mm2/ s) or trihydroxymethylpropanyl ester (TMP1,40℃
Viscosity 16.8mm2/s);
The antiwear additive is sulfide isobutene extreme pressure anti-wear additives, tricresyl phosphate extreme pressure anti-wear additives or phosphorous di-n-butyl extreme pressure
One of antiwear additive is a variety of.
Preferably, the organic amine is the mixture of C12-C18 alkylamine Yu C6-C8 arylamine, and the mass ratio of the two is 10:
1 to 1:16;It is preferred that 6.5:1 is to the preferred lauryl amine of 1:1.08. alkylamine and octadecylamine, the preferred aniline of arylamine and para-totuidine.
Preferably, the diisocyanate is toluene di-isocyanate(TDI) or 4,4 '-diisocyanate diphenyl-methanes.
Preferably, the extreme-pressure antiwear compound additive for lubricating oil is by HVI350 base oil, chloralkane, dialkyl disulfides
In mass ratio for carbaminate, dialkyl group phenol, ethylene-propylene copolymer, Acidic phosphates ammonium, 2% dimethicone kerosin
Are as follows: (25-30): (25-30): (20-25): (0.1-0.3): (2.5-3.0): (0.2-0.3): made after (0.25-0.30) mixing
At.
Preferably, it the preparation method of the low-noise lubricating grease: comprises the steps of:
A, organic amine is added in 1/2 base oil, is heated to organic amine and dissolves completely;
B, diisocyanate is added in remaining base oil again, is heated to dissolving;
C, then being added in organic amine oil to be sufficiently stirred by diisocyanate ester oil reacts organic amine completely with diisocyanate, this
When temperature of charge be increased to 100-120 DEG C, at this temperature stirring and constant temperature 30 minutes, after being cooled to 30 DEG C be added vibration damping agent,
Antiwear additive and extreme-pressure antiwear compound additive for lubricating oil are ground uniform on triple-roller mill.
Due to the application of the above technical scheme, compared with the prior art, the invention has the following advantages:
Low-noise lubricating grease of the present invention use polyester based on oil, the dual property with synthetic ester and PAO with compared with
High lubricity has significant load-carrying ability and extreme pressure property with wear-resistant and extruding agent compatibility.Ester group's molecule has certain pole
Property, therefore it has good affinity to metal.With PAO or mineral oil compatibility, there are a kind of unique property, i.e., low thickening effect
It answers, there is good high shear performance resistant to high temperatures, thus be widely used in I. C. engine oil and gear oil;Applicable temperature range :-
It is 35-+250 DEG C, short-term up to 300 DEG C;Low-noise lubricating grease of the present invention has excellent bass performance, excellent bearing
Sound quality cover performance, excellent high temperature and cryogenic property, good mechanical stability, colloid stability and anti-oxidative stability,
Excellent greasy property, Corrosion Protection and long service life, while can be biodegradable, good environmental protection;It is of the present invention
Low-noise lubricating grease preparation method it is simple, it is practical.
Specific embodiment
Embodiment 1
Low-noise lubricating grease, including following weight percentage components:
The base oil is polyester;The thickening agent is organic amine and diisocyanate;The vibration damping agent is pentaerythritol fatty acid ester
(PE1, 40 DEG C of viscosity 14.67mm2/s);The antiwear additive is sulfide isobutene extreme pressure anti-wear additives;The organic amine is C12-C18
The mixture of alkylamine and C6-C8 arylamine, the mass ratio of the two are 10:1 to 1:16;It is preferred that 6.5:1 is excellent to 1:1.08. alkylamine
Select lauryl amine and octadecylamine, the preferred aniline of arylamine and para-totuidine;The diisocyanate is toluene di-isocyanate(TDI);The profit
Lubricating oil extreme-pressure antiwear compound additive is by HVI350 base oil, chloralkane, dialkyl dithiocarbamate, dialkyl benzene
Phenol, ethylene-propylene copolymer, Acidic phosphates ammonium, 2% dimethicone kerosin are in mass ratio are as follows: 26:28:24:0.15:2.8:
It is made after 0.25:0.26 mixing.
The preparation method of the low-noise lubricating grease: it comprises the steps of:
A, organic amine is added in 1/2 base oil, is heated to organic amine and dissolves completely;
B, diisocyanate is added in remaining base oil again, is heated to dissolving;
C, then being added in organic amine oil to be sufficiently stirred by diisocyanate ester oil reacts organic amine completely with diisocyanate, this
When temperature of charge be increased to 100-120 DEG C, at this temperature stirring and constant temperature 30 minutes, after being cooled to 30 DEG C be added vibration damping agent,
Antiwear additive and extreme-pressure antiwear compound additive for lubricating oil are ground uniform on triple-roller mill.
Embodiment 2
Low-noise lubricating grease, including following weight percentage components:
The base oil is polyester;The thickening agent is organic amine and diisocyanate;The vibration damping agent is trimethylolpropane
Ester (TMP1, 40 DEG C of viscosity 16.8mm2/s);The antiwear additive is tricresyl phosphate extreme pressure anti-wear additives;The organic amine is C12-
The mixture of C18 alkylamine and C6-C8 arylamine, the mass ratio of the two are 10:1 to 1:16;It is preferred that 6.5:1 is to 1:1.08. alkyl
The preferred lauryl amine of amine and octadecylamine, the preferred aniline of arylamine and para-totuidine;The diisocyanate is 4,4 '-diisocyanate two
Phenylmethane;The extreme-pressure antiwear compound additive for lubricating oil is by HVI350 base oil, chloralkane, dialkyl dithio amino first
Hydrochlorate, dialkyl group phenol, ethylene-propylene copolymer, Acidic phosphates ammonium, 2% dimethicone kerosin are in mass ratio are as follows: 25:
25:20:0.3:3.0:0.3:0.30 being made after mixing.
The preparation method of the low-noise lubricating grease: it comprises the steps of:
A, organic amine is added in 1/2 base oil, is heated to organic amine and dissolves completely;
B, diisocyanate is added in remaining base oil again, is heated to dissolving;
C, then being added in organic amine oil to be sufficiently stirred by diisocyanate ester oil reacts organic amine completely with diisocyanate, this
When temperature of charge be increased to 100-120 DEG C, at this temperature stirring and constant temperature 30 minutes, after being cooled to 30 DEG C be added vibration damping agent,
Antiwear additive and extreme-pressure antiwear compound additive for lubricating oil are ground uniform on triple-roller mill.
Embodiment 3
Low-noise lubricating grease, including following weight percentage components:
The base oil is polyester;The thickening agent is organic amine and diisocyanate;
The vibration damping agent is pentaerythritol fatty acid ester (PE1, 40 DEG C of viscosity 14.67mm2/ s) and trihydroxymethylpropanyl ester (TMP1,40℃
Viscosity 16.8mm2/ s), 50% is respectively accounted for by weight percentage;
The antiwear additive is phosphorous di-n-butyl extreme pressure anti-wear additives;
The organic amine is the mixture of C12-C18 alkylamine Yu C6-C8 arylamine, and the mass ratio of the two is 10:1 to 1:16;It is excellent
Select 6.5:1 to the preferred lauryl amine of 1:1.08. alkylamine and octadecylamine, the preferred aniline of arylamine and para-totuidine;
The diisocyanate is toluene di-isocyanate(TDI) and 4, and 4 '-diisocyanate diphenyl-methanes respectively account for by weight percentage
50%;
The extreme-pressure antiwear compound additive for lubricating oil is by HVI350 base oil, chloralkane, dialkyldithiocarbamacompositions
Salt, dialkyl group phenol, ethylene-propylene copolymer, Acidic phosphates ammonium, 2% dimethicone kerosin are in mass ratio are as follows: 28:25:
It is made after 20:0.1:3.0:0.3:0.25 mixing.
The preparation method of the low-noise lubricating grease: it comprises the steps of:
A, organic amine is added in 1/2 base oil, is heated to organic amine and dissolves completely;
B, diisocyanate is added in remaining base oil again, is heated to dissolving;
C, then being added in organic amine oil to be sufficiently stirred by diisocyanate ester oil reacts organic amine completely with diisocyanate, this
When temperature of charge be increased to 100-120 DEG C, at this temperature stirring and constant temperature 30 minutes, after being cooled to 30 DEG C be added vibration damping agent,
Antiwear additive and extreme-pressure antiwear compound additive for lubricating oil are ground uniform on triple-roller mill.
Embodiment 4
Low-noise lubricating grease, including following weight percentage components:
The base oil is polyester;The thickening agent is organic amine and diisocyanate;The vibration damping agent is pentaerythritol fatty acid ester
(PE1, 40 DEG C of viscosity 14.67mm2/ s) and trihydroxymethylpropanyl ester (TMP1, 40 DEG C of viscosity 16.8mm2/ s), by weight percentage
Respectively account for 50%;
The antiwear additive is sulfide isobutene extreme pressure anti-wear additives and tricresyl phosphate extreme pressure anti-wear additives and phosphorous di-n-butyl pole
Antiwear additive is pressed, respectively accounts for one third by weight percentage;
The organic amine is the mixture of C12-C18 alkylamine Yu C6-C8 arylamine, and the mass ratio of the two is 10:1 to 1:16;It is excellent
Select 6.5:1 to the preferred lauryl amine of 1:1.08. alkylamine and octadecylamine, the preferred aniline of arylamine and para-totuidine;
The diisocyanate is toluene di-isocyanate(TDI) and 4, and 4 '-diisocyanate diphenyl-methanes respectively account for by weight percentage
50%;
The extreme-pressure antiwear compound additive for lubricating oil is by HVI350 base oil, chloralkane, dialkyldithiocarbamacompositions
Salt, dialkyl group phenol, ethylene-propylene copolymer, Acidic phosphates ammonium, 2% dimethicone kerosin are in mass ratio are as follows: 30:30:
It is made after 25:0.2:2.5:0.3:0.25 mixing.
The preparation method of the low-noise lubricating grease: it comprises the steps of:
A, organic amine is added in 1/2 base oil, is heated to organic amine and dissolves completely;
B, diisocyanate is added in remaining base oil again, is heated to dissolving;
C, then being added in organic amine oil to be sufficiently stirred by diisocyanate ester oil reacts organic amine completely with diisocyanate, this
When temperature of charge be increased to 100-120 DEG C, at this temperature stirring and constant temperature 30 minutes, after being cooled to 30 DEG C be added vibration damping agent,
Antiwear additive and extreme-pressure antiwear compound additive for lubricating oil are ground uniform on triple-roller mill.
Testing result:
Due to the application of the above technical scheme, compared with the prior art, the invention has the following advantages:
Low-noise lubricating grease of the present invention use polyester based on oil, the dual property with synthetic ester and PAO with compared with
High lubricity has significant load-carrying ability and extreme pressure property with wear-resistant and extruding agent compatibility.Ester group's molecule has certain pole
Property, therefore it has good affinity to metal.With PAO or mineral oil compatibility, there are a kind of unique property, i.e., low thickening effect
It answers, there is good high shear performance resistant to high temperatures, thus be widely used in I. C. engine oil and gear oil;Applicable temperature range :-
It is 35-+250 DEG C, short-term up to 300 DEG C;Low-noise lubricating grease of the present invention has excellent bass performance, excellent bearing
Sound quality cover performance, excellent high temperature and cryogenic property, good mechanical stability, colloid stability and anti-oxidative stability,
Excellent greasy property, Corrosion Protection and long service life, while can be biodegradable, good environmental protection;It is of the present invention
Low-noise lubricating grease preparation method it is simple, it is practical.
The above embodiments merely illustrate the technical concept and features of the present invention, and its object is to allow person skilled in the art
Scholar can understand the contents of the present invention and be implemented, and it is not intended to limit the scope of the present invention, it is all according to the present invention
Equivalent change or modification made by Spirit Essence, should be covered by the scope of protection of the present invention.
Claims (5)
1. low-noise lubricating grease, which is characterized in that including following weight percentage components:
Base oil 40-50%;
Thickening agent 30-35%;
Vibration damping agent 20-25%;
Antiwear additive 1-5%;
Extreme-pressure antiwear compound additive for lubricating oil 1-2%;
The base oil is polyester;
The thickening agent is organic amine and diisocyanate;
The vibration damping agent is pentaerythritol fatty acid ester (PE1, 40 DEG C of viscosity 14.67mm2/ s) or trihydroxymethylpropanyl ester (TMP1, 40
DEG C viscosity 16.8mm2/ s);
The antiwear additive is sulfide isobutene extreme pressure anti-wear additives, tricresyl phosphate extreme pressure anti-wear additives or phosphorous di-n-butyl extreme pressure
One of antiwear additive is a variety of.
2. low-noise lubricating grease according to claim 1, which is characterized in that the organic amine be C12-C18 alkylamine with
The mixture of C6-C8 arylamine, the mass ratio of the two are 10:1 to 1:16;It is preferred that 6.5:1 is to the preferred lauryl amine of 1:1.08. alkylamine
And octadecylamine, the preferred aniline of arylamine and para-totuidine.
3. low-noise lubricating grease according to claim 1, which is characterized in that the diisocyanate is toluene diisocynate
Ester or 4,4 '-diisocyanate diphenyl-methanes.
4. low-noise lubricating grease according to claim 1, which is characterized in that the extreme-pressure antiwear compound additive for lubricating oil
By HVI350 base oil, chloralkane, dialkyl dithiocarbamate, dialkyl group phenol, ethylene-propylene copolymer, dialkyl group phosphorus
Sour ammonium, 2% dimethicone kerosin are in mass ratio are as follows: (25-30): (25-30): (20-25): (0.1-0.3): (2.5-
3.0): (0.2-0.3): being made after (0.25-0.30) mixing.
5. the preparation method of low-noise lubricating grease according to claim 1 or 2 or 3 or 4: comprising the steps of:
A, organic amine is added in 1/2 base oil, is heated to organic amine and dissolves completely;
B, diisocyanate is added in remaining base oil again, is heated to dissolving;
C, then being added in organic amine oil to be sufficiently stirred by diisocyanate ester oil reacts organic amine completely with diisocyanate, this
When temperature of charge be increased to 100-120 DEG C, at this temperature stirring and constant temperature 30 minutes, after being cooled to 30 DEG C be added vibration damping agent,
Antiwear additive and extreme-pressure antiwear compound additive for lubricating oil are ground uniform on triple-roller mill.