CN109370180A - A kind of degradable PLA biomaterial of suction pipe manufacture and preparation method thereof - Google Patents
A kind of degradable PLA biomaterial of suction pipe manufacture and preparation method thereof Download PDFInfo
- Publication number
- CN109370180A CN109370180A CN201811193921.9A CN201811193921A CN109370180A CN 109370180 A CN109370180 A CN 109370180A CN 201811193921 A CN201811193921 A CN 201811193921A CN 109370180 A CN109370180 A CN 109370180A
- Authority
- CN
- China
- Prior art keywords
- pla
- biomaterial
- raw material
- suction pipe
- machine
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to technical field of material, and disclose a kind of degradable PLA biomaterial and preparation method thereof of suction pipe manufacture, which uses the raw material of following parts by weight: the molecular weight of polylactic acid PLA is 5-40 ten thousand;The molecular weight of polyethylene and ethylene copolymers is 2-25 ten thousand;The molecular weight of organo-metallic compound is 0.05-5 ten thousand;The molecular weight of function additive is 0.2-1 ten thousand;The molecular weight of bamboo fibre is 8-55 ten thousand, step 1: chooses raw material, step 2: raw material mixing, step 3: raw material refining, step 4: extruding pelletization and step 5: packing and storing.Degradable PLA biomaterial of the suction pipe manufacture and preparation method thereof can produce the high PLA biomaterial of shock resistance, thus the suction pipe made of PLA biomaterial have stronger shock resistance can, greatly improve its application.
Description
Technical field
The present invention relates to technical field of material, the degradable PLA biomaterial of specially a kind of suction pipe manufacture and
Preparation method.
Background technique
Polylactic acid (PLA) is a kind of biodegradable polyester material.The material acid of synthesizing polylactic acid is from jade
The natural crops such as rice, product can be degraded into water and carbon dioxide in the natural environment after discarded, therefore polylactic acid has life
Object degradability, recyclability, furthermore its good biocompatibility, good mechanical performance.But also having property is crisp for polylactic acid, impact strength
Low disadvantage.The toughness for improving polylactic acid can widen the application field of polylactic acid.Polylactic acid PLA be it is a kind of it is nontoxic can biology completely
The novel high polymer material of degradation, with the improvement of synthesis technology in recent years, it is production-scale expand, the decline of cost and
The rise of oil price, polylactic acid are going into more general plastics market extensively, partially instead of polyethylene, polyester and poly-
The plastics such as styrene alleviate conventional plastic pollution on the environment, it is therefore contemplated that it leads in high molecular material Related product
The application in domain will be fast-developing.
Polyethylene (polyethylene, abbreviation PE) is a kind of aggregated thermoplastic resin obtained of ethylene.Industrially,
It also include the copolymer of ethylene and a small amount of alpha-olefin.Polyethylene is odorless, nontoxic, feel ceraceous, has excellent resistance to low temperature,
Chemical stability is good, is resistant to the erosion of most of soda acids (intolerant to the acid with oxidizing property).Common solvent is not dissolved under room temperature,
Water imbibition is small, and electrical insulating property is excellent.
At present since not only property is crisp for polylactic acid (PLA), but also shock resistance is also low, therefore existing using polylactic acid
(PLA) its performance of suction pipe made of is all poor, significantly limits its popularization and application.For this purpose, the invention proposes a kind of suctions
Degradable PLA biomaterial of pipe manufacture and preparation method thereof.
Summary of the invention
(1) the technical issues of solving
In view of the deficiencies of the prior art, the present invention provides a kind of degradable PLA biomaterial of suction pipe manufacture and its
Preparation method, the high PLA biomaterial of shock resistance can be produced by having, to be inhaled made of PLA biomaterial
Pipe have stronger shock resistance can, the advantages that greatly improving its application, solves existing using polylactic acid
(PLA) the problem of its performance of suction pipe made of is all poor, significantly limits its popularization and application.
(2) technical solution
In order to achieve the above object, the invention provides the following technical scheme: a kind of degradable PLA biology of suction pipe manufacture
Material, the PLA biomaterial include that polylactic acid PLA, polyethylene and ethylene copolymers, organo-metallic compound, function additive and bamboo are fine
The mixing of dimension, bamboo fibre and polylactic acid PLA, polyethylene and ethylene copolymers, organo-metallic compound increases original PLA biomaterial
Toughness, to increase the shock resistance of PLA biomaterial, which uses the raw material of following parts by weight:
The molecular weight of polylactic acid PLA is 5-40 ten thousand;
The molecular weight of polyethylene and ethylene copolymers is 2-25 ten thousand;
The molecular weight of organo-metallic compound is 0.05-5 ten thousand;
The molecular weight of function additive is 0.2-1 ten thousand;
The molecular weight of bamboo fibre is 8-55 ten thousand.
A kind of preparation method of the degradable PLA biomaterial of suction pipe manufacture, the specific steps are as follows:
Step 1: choosing raw material, chooses 25 parts of polylactic acid PLA, 20 parts of polyethylene and ethylene copolymers, 5 parts of organo-metallic compound
And 1 part of function additive, and the raw material of selection is subjected to of short duration storage respectively and is placed;
Step 2: raw material mixing mixes the plurality of raw materials chosen in step 1 while being put into hybrid machine
Uniformly, polylactic acid PLA, polyethylene and ethylene copolymers and organo-metallic compound are put into hybrid machine first, then again by function
Energy auxiliary agent is put into hybrid machine, batcher is used when function additive is put into, so that polylactic acid PLA, polyethylene and ethylene copolymers
With organo-metallic compound while being sufficiently mixed, function additive is put into the inside of hybrid machine, in order to enable function helps
The significantly more efficient involvement of agent is to the inside of polylactic acid PLA, polyethylene and ethylene copolymers and organo-metallic compound;
Step 3: raw material refining;The mixed solution that step 2 is obtained is added into refining machine and refines, and solution is refining
When refining in machine processed, the temperature change inside refining machine is broadly divided into three phases: the first stage: 25 degrees Celsius -45 degrees Celsius;
Second stage: 45 degrees Celsius -60 degrees Celsius;Phase III: 60 degrees Celsius -120 degrees Celsius, wherein first stage and second stage
Between critical-temperature when need to stop heating 10 minutes, need when second stage and phase III critical-temperature to stop 15 points of heating
Clock when phase III temperature reaches 80 degrees Celsius, stops heating refining 20 minutes and keeps the temperature-resistant of refining device;
Step 4: extruding pelletization;The raw material that step 3 is obtained is passed through to being granulated in machine, and PLA biomaterial is made, makes
The discharge outlet of grain machine is provided with cooling device, higher since PLA biomaterial temperature is made, and is easy to cause staff
Scald;
Step 5: packing and storing;Step 4 PLA biomaterial after cooling is transported to packaging machine by conveyer belt
In, and by packaging machine by the inside of raw material loading Article holding box, finally pass through transport vehicle again for packaged PLA biomaterial
It is stored in warehouse.
Preferably, the inside of the hybrid machine is put into mixing water in advance.
Preferably, the raw material that the raw material is mixed to get is put into the inside of refining machine, if contained in mixed raw material
Micro impurity, then need mixed raw material being put into exclusion device and clean.
Preferably, the cooling device being granulated in machine mainly uses water cooling.
Preferably, the Article holding box is made of metal material.
Preferably, the temperature in the warehouse is maintained at 25 degrees Celsius.
(3) beneficial effect
Compared with prior art, the present invention provides a kind of degradable PLA biomaterial of suction pipe manufacture and its preparations
Method, have it is following the utility model has the advantages that
1, the preparation method of the degradable PLA biomaterial of the suction pipe manufacture by bamboo fibre and polylactic acid PLA, is gathered
The mixing of ethylene copolymer, organo-metallic compound increases the toughness of original PLA biomaterial, so that it is raw to increase PLA
The shock resistance of object material passes through step 1: choosing raw material, step 2: raw material mixing, step 3: raw material refining, step
Four: extruding pelletization and step 5: packing and storing can produce the high PLA biomaterial of shock resistance, to pass through
Suction pipe made of PLA biomaterial have stronger shock resistance can, greatly improve its application.
2, the preparation method of the degradable PLA biomaterial of the suction pipe manufacture, passes through the function in raw material mixing step
Energy auxiliary agent will use batcher when being put into, in order to enable the significantly more efficient involvement of function additive is total to polylactic acid PLA, polyethylene
The inside of polymers and organo-metallic compound, by raw material refine in refining machine inside temperature change be broadly divided into three ranks
Section: first stage: 25 degrees Celsius -45 degrees Celsius;Second stage: 45 degrees Celsius -60 degrees Celsius;Phase III: 60 degrees Celsius-
120 degrees Celsius, mixed raw material is enabled to preferably to be refined, to increase the intensity of PLA biomaterial, passes through pelletizer
The discharge outlet of device is provided with cooling device, higher since PLA biomaterial temperature is made, and is easy to cause to scald to staff
Wound, while the cooling velocity of PLA biomaterial is also accelerated, to improve the production efficiency of PLA biomaterial, be conducive to look forward to
The benefit of industry is made of metal material by Article holding box and is maintained at 25 degrees Celsius with the temperature in warehouse, can be avoided obtained
In the inside of Article holding box the variation of property occurs for PLA biomaterial long-time storage.
Specific embodiment
The following is a clear and complete description of the technical scheme in the embodiments of the invention, it is clear that described embodiment
Only a part of the embodiment of the present invention, instead of all the embodiments.Based on the embodiments of the present invention, the common skill in this field
Art personnel every other embodiment obtained without making creative work belongs to the model that the present invention protects
It encloses.
A kind of degradable PLA biomaterial of suction pipe manufacture, the PLA biomaterial include that polylactic acid PLA, polyethylene are total
Polymers, organo-metallic compound, function additive and bamboo fibre, the PLA biomaterial use the raw material of following parts by weight:
The molecular weight of polylactic acid PLA is 5-40 ten thousand;
The molecular weight of polyethylene and ethylene copolymers is 2-25 ten thousand;
The molecular weight of organo-metallic compound is 0.05-5 ten thousand;
The molecular weight of function additive is 0.2-1 ten thousand;
The molecular weight of bamboo fibre is 8-55 ten thousand.
A kind of preparation method of the degradable PLA biomaterial of suction pipe manufacture, the specific steps are as follows:
Step 1: choosing raw material, chooses 25 parts of polylactic acid PLA, 20 parts of polyethylene and ethylene copolymers, 5 parts of organo-metallic compound
And 1 part of function additive, and the raw material of selection is subjected to of short duration storage respectively and is placed;
Step 2: raw material mixing mixes the plurality of raw materials chosen in step 1 while being put into hybrid machine
Uniformly, polylactic acid PLA, polyethylene and ethylene copolymers and organo-metallic compound are put into hybrid machine first, then again by function
Energy auxiliary agent is put into hybrid machine, batcher is used when function additive is put into, so that polylactic acid PLA, polyethylene and ethylene copolymers
With organo-metallic compound while being sufficiently mixed, function additive is put into the inside of hybrid machine, in order to enable function helps
The significantly more efficient involvement of agent is to the inside of polylactic acid PLA, polyethylene and ethylene copolymers and organo-metallic compound;
Step 3: raw material refining;The mixed solution that step 2 is obtained is added into refining machine and refines, and solution is refining
When refining in machine processed, the temperature change inside refining machine is broadly divided into three phases: the first stage: 25 degrees Celsius -45 degrees Celsius;
Second stage: 45 degrees Celsius -60 degrees Celsius;Phase III: 60 degrees Celsius -120 degrees Celsius, wherein first stage and second stage
Between critical-temperature when need to stop heating 10 minutes, need when second stage and phase III critical-temperature to stop 15 points of heating
Clock when phase III temperature reaches 80 degrees Celsius, stops heating refining 20 minutes and keeps the temperature-resistant of refining device;
Step 4: extruding pelletization;The raw material that step 3 is obtained is passed through to being granulated in machine, and PLA biomaterial is made, makes
The discharge outlet of grain machine is provided with cooling device, higher since PLA biomaterial temperature is made, and is easy to cause staff
Scald;
Step 5: packing and storing;Step 4 PLA biomaterial after cooling is transported to packaging machine by conveyer belt
In, and by packaging machine by the inside of raw material loading Article holding box, finally pass through transport vehicle again for packaged PLA biomaterial
It is stored in warehouse.
The inside of hybrid machine is put into mixing water in advance, and the raw material that raw material is mixed to get is put into the inside of refining machine
Before, if containing micro impurity in mixed raw material, need mixed raw material being put into exclusion device and clean, is granulated machine
In cooling device mainly use water cooling, Article holding box is made of metal material, and the temperature in warehouse is maintained at 25 degrees Celsius.
In conclusion the preparation method of the degradable PLA biomaterial of the suction pipe manufacture, bamboo fibre and polylactic acid PLA,
The mixing of polyethylene and ethylene copolymers, organo-metallic compound increases the toughness of original PLA biomaterial, to increase PLA
The shock resistance of biomaterial passes through step 1: choosing raw material, step 2: raw material mixing, step 3: raw material refining, step
Four: extruding pelletization and step 5: packing and storing can produce the high PLA biomaterial of shock resistance, to pass through
Suction pipe made of PLA biomaterial have stronger shock resistance can, its application is greatly improved, by raw material
Function additive in mixing step will use batcher when being put into, in order to enable the significantly more efficient involvement of function additive is to poly- cream
The inside of sour PLA, polyethylene and ethylene copolymers and organo-metallic compound, by raw material refine in refining machine inside temperature change
It is broadly divided into three phases: the first stage: 25 degrees Celsius -45 degrees Celsius;Second stage: 45 degrees Celsius -60 degrees Celsius;Third rank
Section: 60 degrees Celsius -120 degrees Celsius, mixed raw material is enabled to preferably to be refined, to increase the strong of PLA biomaterial
Degree, the discharge outlet by being granulated machine is provided with cooling device, higher since PLA biomaterial temperature is made, and is easy to work
It causes to scald as personnel, while also accelerating the cooling velocity of PLA biomaterial, to improve the production of PLA biomaterial
Efficiency is conducive to the benefit of enterprise, is made of metal material by Article holding box and is maintained at 25 degrees Celsius with the temperature in warehouse,
It can be avoided obtained PLA biomaterial long-time storage and the variation of property occur in the inside of Article holding box.
It should be noted that the terms "include", "comprise" or its any other variant are intended to the packet of nonexcludability
Contain, so that the process, method, article or equipment for including a series of elements not only includes those elements, but also including
Other elements that are not explicitly listed, or further include for elements inherent to such a process, method, article, or device.
In the absence of more restrictions, the element limited by sentence "including a ...", it is not excluded that including the element
Process, method, article or equipment in there is also other identical elements.
It although an embodiment of the present invention has been shown and described, for the ordinary skill in the art, can be with
A variety of variations, modification, replacement can be carried out to these embodiments without departing from the principles and spirit of the present invention by understanding
And modification, the scope of the present invention is defined by the appended.
Claims (7)
1. a kind of degradable PLA biomaterial of suction pipe manufacture, the PLA biomaterial include polylactic acid PLA, polyethylene copolymer
Object, organo-metallic compound, function additive and bamboo fibre, the PLA biomaterial use the raw material of following parts by weight:
The molecular weight of polylactic acid PLA is 5-40 ten thousand;
The molecular weight of polyethylene and ethylene copolymers is 2-25 ten thousand;
The molecular weight of organo-metallic compound is 0.05-5 ten thousand;
The molecular weight of function additive is 0.2-1 ten thousand;
The molecular weight of bamboo fibre is 8-55 ten thousand.
2. a kind of preparation method of the degradable PLA biomaterial of suction pipe manufacture, the specific steps are as follows:
Step 1: choose raw material, choose 25 parts of polylactic acid PLA, 20 parts of polyethylene and ethylene copolymers, 5 parts of organo-metallic compound and
1 part of function additive, and the raw material of selection is subjected to of short duration storage respectively and is placed;
Step 2: raw material mixing, the plurality of raw materials chosen in step 1 while being put into hybrid machine is carried out it is uniformly mixed,
Polylactic acid PLA, polyethylene and ethylene copolymers and organo-metallic compound are put into hybrid machine first, then again by function additive
It is put into hybrid machine, batcher is used when function additive is put into, so that polylactic acid PLA, polyethylene and ethylene copolymers and organic
While being sufficiently mixed, function additive is put into the inside of hybrid machine metallic compound, in order to enable function additive is more
Add effective incorporate to the inside of polylactic acid PLA, polyethylene and ethylene copolymers and organo-metallic compound;
Step 3: raw material refining;The mixed solution that step 2 is obtained is added into refining machine and refines, and solution is in refining machine
When middle refining, the temperature change inside refining machine is broadly divided into three phases: the first stage: 25 degrees Celsius -45 degrees Celsius;Second
Stage: 45 degrees Celsius -60 degrees Celsius;Phase III: 60 degrees Celsius -120 degrees Celsius, wherein between first stage and second stage
It needs to stop heating 10 minutes when critical-temperature, needs when second stage and phase III critical-temperature to stop heating 15 minutes,
When phase III temperature reaches 80 degrees Celsius, stops heating refining 20 minutes and keep the temperature-resistant of refining device;
Step 4: extruding pelletization;The raw material that step 3 is obtained is passed through to being granulated in machine, and PLA biomaterial, pelletizer is made
The discharge outlet of device is provided with cooling device, higher since PLA biomaterial temperature is made, and is easy to cause to scald to staff
Wound;
Step 5: packing and storing;Step 4 PLA biomaterial after cooling is transported in packaging machine by conveyer belt, and
Raw material is packed into the inside of Article holding box by packaging machine, is finally again stored packaged PLA biomaterial by transport vehicle
In warehouse.
3. a kind of preparation method of the degradable PLA biomaterial of suction pipe manufacture according to claim 2, feature exist
In: the inside of the hybrid machine is put into mixing water in advance.
4. a kind of preparation method of the degradable PLA biomaterial of suction pipe manufacture according to claim 2, feature exist
In: the raw material that the raw material is mixed to get is put into the inside of refining machine, if containing micro impurity in mixed raw material,
It needs mixed raw material being put into exclusion device and clean.
5. a kind of preparation method of the degradable PLA biomaterial of suction pipe manufacture according to claim 2, feature exist
In: the cooling device being granulated in machine mainly uses water cooling.
6. a kind of preparation method of the degradable PLA biomaterial of suction pipe manufacture according to claim 2, feature exist
In: the Article holding box is made of metal material.
7. a kind of preparation method of the degradable PLA biomaterial of suction pipe manufacture according to claim 2, feature exist
In: the temperature in the warehouse is maintained at 25 degrees Celsius.