CN109367186A - A kind of corrugated board - Google Patents
A kind of corrugated board Download PDFInfo
- Publication number
- CN109367186A CN109367186A CN201811109551.6A CN201811109551A CN109367186A CN 109367186 A CN109367186 A CN 109367186A CN 201811109551 A CN201811109551 A CN 201811109551A CN 109367186 A CN109367186 A CN 109367186A
- Authority
- CN
- China
- Prior art keywords
- parts
- thermoplastic elastomer
- tpe
- cardboard
- corrugated board
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of corrugated boards, including cardboard matrix, in terms of the component of parts by weight, the cardboard matrix include 100 parts of paper pulp, 4-6 parts of polyglycolic acid, 2-3 parts of cationic polyacrylamide, 5-10 parts of oxidation of alkyl amine polyoxyethylene ether, 1-2 parts of chitosan, 1-2 parts of thickener, 20-30 parts of deionized water;The cardboard matrix surface is equipped with thermoplastic elastomer (TPE), the thermoplastic elastomer (TPE) is equipped with nano titanic oxide sol layer, the thermoplastic elastomer (TPE) is compounded in cardboard matrix by pressing technology while hot, and the thermoplastic elastomer (TPE) and nano titanic oxide sol layer are bonded by PU glue.
Description
Technical field
The present invention relates to board applications, and in particular to a kind of corrugated board.
Background technique
Corrugated board is to process the waveform plate object formed by liner board and by corrugated roller, is generally divided into single corrugation
Two class of cardboard and double-layer corrugated cardboard, is divided into: A, five seed type of B, C, E, F according to the size of corrugation.The invention and application of corrugated paper
There is more than 100 years history, at low cost, light weight, processing is easy, intensity is big, printing adaptability sample is excellent, storage convenient in carrying
The advantages that.
Packaging material is one of the major function of packaging to the protectiveness of built-in amount of substance, and inner packing is even more to protect to commodity
Shield property plays the role of vital.
Corrugated board is the adherend of a multilayer, it is at least made of one layer of waveform core layer and a layer paperboard.Corrugation
Cardboard has very high mechanical strength, can to being fallen by the collision in cargo handling process and falling, mainly for the manufacture of carton and
The outer packing of delicate articles.
Currently, corrugated board is mainly made of fibrous web, it is easy the shadow by external environmental factors such as humidity, temperature
It rings.In the higher environment of some temperature, corrugated board is easy to conduct the heat of absorption to packaging article, indirectly
Reduce the quality of article;And when corrugated board directly meets with open fire, then it is easy to happen combustion phenomena, directly destroys institute
The article of packaging, brings economic loss.
Summary of the invention
Goal of the invention: in order to overcome the deficiencies in the prior art, a kind of corrugated board is provided.
Technical solution: to achieve the above object, the present invention provides a kind of corrugated board, including cardboard matrix, with parts by weight
Component meter, the cardboard matrix include 100 parts of paper pulp, 4-6 parts of polyglycolic acid, 2-3 parts of cationic polyacrylamide, aoxidize alkane
5-10 parts of base amine polyoxyethylene ether, 1-2 parts of chitosan, 1-2 parts of thickener, 20-30 parts of deionized water;The cardboard matrix surface
Equipped with thermoplastic elastomer (TPE), the thermoplastic elastomer (TPE) is equipped with nano titanic oxide sol layer, and the thermoplastic elastomer (TPE) is logical
It is compounded in cardboard matrix after pressing technology while hot, the thermoplastic elastomer (TPE) and nano titanic oxide sol layer pass through PU glue
Bonding.
Be further improved, the thermoplastic elastomer by 50 DEG C of -60 DEG C of melt extrusions of vulcanization screw rod, direct membrane at
Type presses molding thermoplastic elastomer by knurling rolls and rubber rollers with cardboard matrix while hot, then cooling through chill roll,
Winding obtains semi-finished product.
It being further improved, the cardboard matrix include 100 parts of paper pulp, and 5 parts of polyglycolic acid, cationic polyacrylamide 2.5
Part, 7.5 parts of oxidation of alkyl amine polyoxyethylene ether, 1.5 parts of chitosan, 1.5 parts of thickener, 25 parts of deionized water.
It being further improved, the cardboard matrix include 100 parts of paper pulp, and 4 parts of polyglycolic acid, 2 parts of cationic polyacrylamide,
5 parts of oxidation of alkyl amine polyoxyethylene ether, 1 part of chitosan, 1 part of thickener, 20 parts of deionized water.
It being further improved, the cardboard matrix include 100 parts of paper pulp, and 6 parts of polyglycolic acid, 3 parts of cationic polyacrylamide,
10 parts of oxidation of alkyl amine polyoxyethylene ether, 2 parts of chitosan, 2 parts of thickener, 30 parts of deionized water.
The beneficial effects of the present invention are:
It is strong by the tear-proof that fabric entirety on the one hand can be improved in double-deck overlay film of cardboard matrix surface progress in the present invention
Degree and crocking resistance, and the use of glue and plasticizer is reduced, Environmental Safety, on the other hand, the titanium dioxide of Nano grade
The coating of titanium sol layer enables the surface of fabric to have clean surfaces net work, it is possible to reduce wash number, while having preferably
Waterproofness;
Cardboard matrix are reinforced using composite construction, and there are the strong substrate base of crushing resistance compound thermoplastic elastomers again, just
In thermoplastic elastomer (TPE) stabilization be compounded on matrix, while thermoplastic elastomer (TPE) have stronger compressive property, elastic property, because
This further enhances corrugated board intensity and elasticity, ultimate strength Jing Xiang≤2500N, Wei Xiang≤2800N, tearing brute force through to
≤ 500N, Wei Xiang≤300N, waterproof performance are good.
Specific embodiment
Below with reference to embodiment, the present invention will be further explained.
Embodiment one:
A kind of corrugated board, including cardboard matrix, in terms of the component of parts by weight, the cardboard matrix include 100 parts of paper pulp, poly- second
4 parts of alkyd, 2 parts of cationic polyacrylamide, 5 parts of oxidation of alkyl amine polyoxyethylene ether, 1 part of chitosan, 1 part of polyacrylate,
20 parts of deionized water;The cardboard matrix surface is equipped with thermoplastic elastomer (TPE), and the thermoplastic elastomer (TPE) is equipped with nano-silica
Change titanium sol layer, the thermoplastic elastomer (TPE) is compounded in cardboard matrix by pressing technology while hot, the thermoplastic elastomer (TPE)
It is bonded with nano titanic oxide sol layer by PU glue;
The thermoplastic elastomer is formed by 50 DEG C of -60 DEG C of melt extrusions of vulcanization screw rod, direct membrane, by molding thermoplasticity
Elastomer layer is pressed with cardboard matrix while hot by knurling rolls and rubber rollers, then cooling through chill roll, and winding obtains semi-finished product, will
The thermoplastic elastomer surface of semi-finished product is rolled up outwardly on A cabinet frame, and PU glue and nano titanic oxide sol layer are mixed simultaneously
It stirs evenly, is coated by coating machine, and application temperature is maintained at 60 DEG C, the speed of coating machine is maintained at per minute 15
Code;After having coated one layer, drying and processing is carried out, is repeated 2 times;After drying, processing is carried out shaping, the speed of A cabinet frame is maintained at every
30 yards of minute, finished product rolls to form corrugated board through Corrugator roller;
Embodiment two:
A kind of corrugated board, including cardboard matrix, in terms of the component of parts by weight, the cardboard matrix include 100 parts of paper pulp, poly- second
5 parts of alkyd, 2.5 parts of cationic polyacrylamide, 7.5 parts of oxidation of alkyl amine polyoxyethylene ether, 1.5 parts of chitosan, thickener 1.5
Part, 25 parts of deionized water;The cardboard matrix surface is equipped with thermoplastic elastomer (TPE), and the thermoplastic elastomer (TPE) is equipped with nanometer two
Titanium oxide sol layer, the thermoplastic elastomer (TPE) are compounded in cardboard matrix by pressing technology while hot, the thermoplastic elastic
Body and nano titanic oxide sol layer are bonded by PU glue;
The thermoplastic elastomer is formed by 50 DEG C of -60 DEG C of melt extrusions of vulcanization screw rod, direct membrane, by molding thermoplasticity
Elastomer layer is pressed with cardboard matrix while hot by knurling rolls and rubber rollers, then cooling through chill roll, and winding obtains semi-finished product, will
The thermoplastic elastomer surface of semi-finished product is rolled up outwardly on A cabinet frame, and PU glue and nano titanic oxide sol layer are mixed simultaneously
It stirs evenly, is coated by coating machine, and application temperature is maintained at 60 DEG C, the speed of coating machine is maintained at per minute 15
Code;After having coated one layer, drying and processing is carried out, is repeated 2 times;After drying, processing is carried out shaping, the speed of A cabinet frame is maintained at every
30 yards of minute, finished product rolls to form corrugated board through Corrugator roller;
Embodiment three:
A kind of corrugated board, including cardboard matrix, in terms of the component of parts by weight, the cardboard matrix include 100 parts of paper pulp, poly- second
6 parts of alkyd, 3 parts of cationic polyacrylamide, 10 parts of oxidation of alkyl amine polyoxyethylene ether, 2 parts of chitosan, 2 parts of thickener, go from
30 parts of sub- water;The cardboard matrix surface is equipped with thermoplastic elastomer (TPE), and the thermoplastic elastomer (TPE) is equipped with nano-titanium dioxide
Sol layer, the thermoplastic elastomer (TPE) are compounded in cardboard matrix by pressing technology while hot, the thermoplastic elastomer (TPE) and are received
Rice TiO 2 sol layer is bonded by PU glue;
The thermoplastic elastomer is formed by 50 DEG C of -60 DEG C of melt extrusions of vulcanization screw rod, direct membrane, by molding thermoplasticity
Elastomer layer is pressed with cardboard matrix while hot by knurling rolls and rubber rollers, then cooling through chill roll, and winding obtains semi-finished product, will
The thermoplastic elastomer surface of semi-finished product is rolled up outwardly on A cabinet frame, and PU glue and nano titanic oxide sol layer are mixed simultaneously
It stirs evenly, is coated by coating machine, and application temperature is maintained at 60 DEG C, the speed of coating machine is maintained at per minute 15
Code;After having coated one layer, drying and processing is carried out, is repeated 3 times;After drying, processing is carried out shaping, the speed of A cabinet frame is maintained at every
It 30 yards of minute, rolls to form corrugated board through Corrugator roller.
The above is only a preferred embodiment of the present invention, it should be pointed out that: those skilled in the art are come
It says, various improvements and modifications may be made without departing from the principle of the present invention, these improvements and modifications also should be regarded as
Protection scope of the present invention.
Claims (5)
1. a kind of corrugated board, which is characterized in that including cardboard matrix, in terms of the component of parts by weight, the cardboard matrix include
100 parts of paper pulp, 4-6 parts of polyglycolic acid, 2-3 parts of cationic polyacrylamide, 5-10 parts of oxidation of alkyl amine polyoxyethylene ether, shell gathers
It is 1-2 parts sugared, 1-2 parts of thickener, 20-30 parts of deionized water;The cardboard matrix surface is equipped with thermoplastic elastomer (TPE), the thermoplastic
Property elastomer be equipped with nano titanic oxide sol layer, the thermoplastic elastomer (TPE) by while hot pressing technology be compounded in cardboard base
On body, the thermoplastic elastomer (TPE) and nano titanic oxide sol layer are bonded by PU glue.
2. the corrugated board according to claim 1, it is characterised in that: the thermoplastic elastomer is by vulcanization screw rod 50
DEG C -60 DEG C of melt extrusions, the molding of direct membrane, by molding thermoplastic elastomer by knurling rolls and rubber rollers while hot with paper
The pressing of plate matrix, then it is cooling through chill roll, winding obtains semi-finished product.
3. the corrugated board according to claim 1, it is characterised in that: the cardboard matrix include 100 parts of paper pulp, poly- second
5 parts of alkyd, 2.5 parts of cationic polyacrylamide, 7.5 parts of oxidation of alkyl amine polyoxyethylene ether, 1.5 parts of chitosan, thickener 1.5
Part, 25 parts of deionized water.
4. the corrugated board according to claim 1, it is characterised in that: the cardboard matrix include 100 parts of paper pulp, poly- second
4 parts of alkyd, 2 parts of cationic polyacrylamide, 5 parts of oxidation of alkyl amine polyoxyethylene ether, 1 part of chitosan, 1 part of thickener, go from
20 parts of sub- water.
5. the corrugated board according to claim 1, it is characterised in that: the cardboard matrix include 100 parts of paper pulp, poly- second
6 parts of alkyd, 3 parts of cationic polyacrylamide, 10 parts of oxidation of alkyl amine polyoxyethylene ether, 2 parts of chitosan, 2 parts of thickener, go from
30 parts of sub- water.