CN109367150A - A kind of high-performance transfer paper and preparation method thereof - Google Patents
A kind of high-performance transfer paper and preparation method thereof Download PDFInfo
- Publication number
- CN109367150A CN109367150A CN201811265451.2A CN201811265451A CN109367150A CN 109367150 A CN109367150 A CN 109367150A CN 201811265451 A CN201811265451 A CN 201811265451A CN 109367150 A CN109367150 A CN 109367150A
- Authority
- CN
- China
- Prior art keywords
- layer
- transfer
- radium
- mucigel
- transfer paper
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to field of packaging material, especially a kind of high-performance transfer paper, including ground paper layer, the side of ground paper layer is equipped with mucigel, mucigel is bonded with radium-shine layer far from the side of ground paper layer, radium-shine layer is fixed with transfer layer far from the side of mucigel, and transfer layer is equipped with layer of varnish far from the side of radium-shine layer.The present invention also provides a kind of preparation methods of high-performance transfer paper.The present invention passes through resin, viscose is that water paint environmental-protecting performance is excellent, aqueous viscose makes each combined material inter-layer bonding force of transfer paper strong, hardening agent is added in transfer paper, after transfer paper molding, increase radium-shine layer, the small stability for maintaining material of fluctuation of breathing freely during aperture improves the yield and efficiency of punching product, the configuration of the present invention is simple is worthy to be popularized.
Description
Technical field
The present invention relates to field of packaging material more particularly to a kind of high-performance transfer papers.
Background technique
Wrapping paper refer to the paper intensity for packaging is high, moisture content is low, gas permeability is small, corrosion-free effect, with certain anti-
It is aqueous use it is also very beautiful.For packing the paper of extensive stock goods and materials.General physical strength with higher and certain
Water-resistance.The characteristics of according to commodity, wrapping paper have in corresponding property wrapping paper, and maximum dosage is that packaging is large
Granular industrial or agricultural raw material, this wrapping paper major requirement intensity height, resistance to heavy duty, shock resistance, and have air permeability appropriate.At present
In packaging industry, transfer paper is because it is in glossiness, smoothness, flexibility, the feature of environmental protection, printing adaptability and beautiful antifalse effect
Etc. there is preferable performance, be widely used in the packaging of the high-grade goods such as cigarette, wine, tea and cosmetics, especially tobacco
The packaging of product.The research and development focus of some large size coating manufacturers is focused on using water as main dispersing medium, has obvious ring
Come on the water paint direction of guarantor's advantage.(radium-shine) the holographic transfer paper of laser is to be coated with one layer of resin on a pet film, using special
Moulding press, special laser holographic pattern is copied on resin, then the caudacoria and paper is compound, removing of aluminizing, with radium-shine complete
It is laser holographic transfer paper on paper that the resin and aluminium layer for ceasing pattern, which are transferred to,.
Industry is increasingly stringenter the environmental requirement of material now, it is expected that developing aqueous combination of materials laser transfer paper, city
Temporarily without mature holographic aqueous transfer coating investment sale on field, part manufacturer newly researches and develops aqueous transfer coating in levelability, nickel version
Industry requirement, the development of environment-friendly laser transfer paper is not achieved in continuous mould pressing, anti-fall photosensitiveness etc..
In existing transfer paper, during aperture, biggish fluctuation is generated, influences the quality and aperture of aperture product
Efficiency.
Summary of the invention
The purpose of the present invention is to solve a kind of high property that aperture exists in the prior art to fluctuate big disadvantage, and proposes
It can transfer paper.
To achieve the goals above, present invention employs following technical solutions:
A kind of high-performance transfer paper, including ground paper layer are designed, the side of the ground paper layer is equipped with mucigel, and the mucigel is separate
The side of the ground paper layer is bonded with radium-shine layer, and the radium-shine layer is fixed with transfer layer far from the side of the mucigel, institute
It states transfer layer and is equipped with layer of varnish far from the side of the radium-shine layer.
Preferably, the ground paper layer is the base stock plate of any color.
Preferably, the material preparation method of the mucigel is that water quantitatively is added in flask, is warming up to 70 DEG C, starts
Then blender is added at one time polyvinyl alcohol, polyacrylamide, emulsifier, thickener and tap water, it is continuously heating to 90~
95 DEG C, temperature 1h or more is kept, until polyvinyl alcohol all dissolves, after polyvinyl alcohol all dissolution, is cooled to 69~71 DEG C,
3/4 potassium peroxydisulfate is added, and vinyl acetate is slowly added dropwise；Kept for 69~71 DEG C of temperature, temperature is risen to 85 by reaction 6h or so
~90 DEG C, remaining 1/4 potassium peroxydisulfate, reaction 0.5h or so is added, is cooled to 75 DEG C or so, cornstarch is added, reacts 1h
Left and right, is cooled to 55 DEG C or so, is added dibutyl phthalate and ethylene glycol, stirring 0.5h or so, cold Kui room temperature, filtering,
Discharging.
Preferably, the mucigel with a thickness of 8-10 microns.
Preferably, the radium-shine layer is picture and text layer.
Preferably, the preparation method of the transfer layer is by raw cellulose resin, polyvinyl acetate, polyaniline, four
Stannic chloride, acetone, hardening agent and solvent are successively orderly in proportion to be put into the container with agitating device, then raw material will be housed
Container be put into water bath heating device, the temperature of water bath heating device is adjusted to 30-40 DEG C, temperature rise during,
Start agitating device, solution is sufficiently stirred, after stirring 30-40 minutes, the solid material in solution is all dissolved in molten
In liquid, container is taken out from heating device, and sufficient solution will be stirred and poured into another container, that is, transfer coatings are made,
Then start coating machine, coating machine is coated with transfer coatings in PET film, and transfer coatings are uniformly coated in PET film, through applying
PET film after cloth, which enters in oven drying, to be solidified, and is adjusted the drying temperature inside oven between 110-145 DEG C, is being passed through
After 8-10 minutes, transfer coatings film-forming forms transfer coated.
Preferably, the layer of varnish is by polylol abietate and drying oil, water 100:(8-10 in mass ratio): (10-12)
It is obtained after the coating of preparation is cured.
A kind of preparation method of high-performance transfer paper proposed by the present invention, includes the following steps:
S1: configured transfer coating notch board is coated on basement membrane, then the basement membrane for being coated with transfer coating is put into baking oven
Drying film forming obtains transfer layer；
S2: in the case where keeping the height condition of high temperature, to transfer layer plus silver material coloring, making it cover transfer layer, radium-shine on the transfer layer
Picture and text；
S3: viscose coating is sprayed in the side of transfer layer, the transfer layer for being coated with viscose is bonded on base stock；
S4: stripping basement membrane, forms layer of varnish on the transfer layer up to transfer paper.
A kind of high-performance transfer paper proposed by the present invention, beneficial effect are: the present invention is aqueous by resin, viscose
Coating, environmental-protecting performance is excellent, and aqueous viscose makes each combined material inter-layer bonding force of transfer paper strong, and hardening is added in transfer paper
Agent increases radium-shine layer after transfer paper molding, and the small stability for maintaining material of fluctuation of breathing freely during aperture, which improves, beats
The yield and efficiency of hole product, the configuration of the present invention is simple are worthy to be popularized.
Detailed description of the invention
Fig. 1 is a kind of schematic cross-sectional view of high-performance transfer paper proposed by the present invention.
In figure: ground paper layer 1, mucigel 2, radium-shine layer 3, transfer layer 4, layer of varnish 5.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.
Embodiment 1
Referring to Fig.1, a kind of high-performance transfer paper, including ground paper layer 1, ground paper layer 1 are the base stock plate of any color, ground paper layer 1
Side is equipped with mucigel 2, mucigel 2 with a thickness of 8 microns, the material preparation method of mucigel 2 is that water quantitatively is added to burn
Bottle in, be warming up to 70 DEG C, start blender, be then added at one time polyvinyl alcohol, polyacrylamide, emulsifier, thickener and
Tap water is continuously heating to 90 DEG C, keeps temperature 1h or more, until polyvinyl alcohol all dissolves, all dissolves to polyvinyl alcohol
Afterwards, 6971 DEG C are cooled to, 3/4 potassium peroxydisulfate is added, and vinyl acetate is slowly added dropwise；Kept for 69 DEG C of temperature, reaction 6h or so,
Temperature is risen to 85 DEG C, remaining 1/4 potassium peroxydisulfate, reaction 0.5h or so is added, is cooled to 75 DEG C or so, corn is added and forms sediment
Powder, reaction 1h or so, is cooled to 55 DEG C or so, and dibutyl phthalate and ethylene glycol, stirring 0.5h or so, cold Kui room is added
Temperature, filtering, discharging, the transfer layer 4 for being coated with viscose is bonded on ground paper layer 1.
Mucigel 2 is bonded with radium-shine layer 3 far from the side of ground paper layer 1, and radium-shine layer 3 is set far from the side fixation of mucigel 2
There is transfer layer 4, the preparation for shifting coating is by raw cellulose resin, polyvinyl acetate, polyaniline, tin tetrachloride, third
Ketone, hardening agent and solvent are successively orderly to be put into the container with agitating device, then the container equipped with raw material is put into water-bath
In heating device, the temperature of water bath heating device is adjusted to 30 DEG C, during temperature rises, starts agitating device, to molten
Liquid is sufficiently stirred, after stirring 30 minutes, solid material in solution all dissolution in the solution, by container from heating device
Middle taking-up, and sufficient solution will be stirred and poured into another container, that is, transfer coatings are made, then start coating machine, coating machine
Transfer coatings are coated in PET film, transfer coatings are uniformly coated in PET film, it is coated after PET film enter baking oven
Solidify in drying, adjusting the drying temperature inside oven is 110 DEG C, after by 8 minutes, transfer coatings film-forming, that is, shape
At transfer coated.
Transfer layer 4 is equipped with layer of varnish 5 far from the side of radium-shine layer 3, and layer of varnish 5 is by polylol abietate and drying oil, water
It is obtained after the coating of the preparation of 100:8:10 in mass ratio is cured.
The present invention proposes a kind of preparation method of high-performance transfer paper, includes the following steps:
S1: configured transfer coating notch board is coated on basement membrane, then the basement membrane for being coated with transfer coating is put into baking oven
Drying film forming obtains transfer layer；
S2: in the case where keeping the height condition of high temperature, to transfer layer plus silver material coloring, making it cover transfer layer, radium-shine on the transfer layer
Picture and text；
S3: viscose coating is sprayed in the side of transfer layer, the transfer layer for being coated with viscose is bonded on base stock；
S4: stripping basement membrane, forms layer of varnish on the transfer layer up to transfer paper.
Embodiment 2
Referring to Fig.1, a kind of high-performance transfer paper, including ground paper layer 1, ground paper layer 1 are the base stock plate of any color, ground paper layer 1
Side is equipped with mucigel 2, mucigel 2 with a thickness of 9 microns, the material preparation method of mucigel 2 is that water quantitatively is added to burn
Bottle in, be warming up to 70 DEG C, start blender, be then added at one time polyvinyl alcohol, polyacrylamide, emulsifier, thickener and
Tap water is continuously heating to 93 DEG C, keeps temperature 1h or more, until polyvinyl alcohol all dissolves, all dissolves to polyvinyl alcohol
Afterwards, 70 DEG C are cooled to, 3/4 potassium peroxydisulfate is added, and vinyl acetate is slowly added dropwise；Temperature 70 C, reaction 6h or so are kept, it will
Temperature rises to 87 DEG C, and remaining 1/4 potassium peroxydisulfate, reaction 0.5h or so is added, is cooled to 75 DEG C or so, cornstarch is added,
1h or so is reacted, is cooled to 55 DEG C or so, is added dibutyl phthalate and ethylene glycol, stirring 0.5h or so, cold Kui room temperature,
Filtering, discharging, the transfer layer 4 for being coated with viscose is bonded on ground paper layer 1.
Mucigel 2 is bonded with radium-shine layer 3 far from the side of ground paper layer 1, and radium-shine layer 3 is set far from the side fixation of mucigel 2
There is transfer layer 4, the preparation for shifting coating is by raw cellulose resin, polyvinyl acetate, polyaniline, tin tetrachloride, third
Ketone, hardening agent and solvent are successively orderly to be put into the container with agitating device, then the container equipped with raw material is put into water-bath
In heating device, the temperature of water bath heating device is adjusted to 35 DEG C, during temperature rises, starts agitating device, to molten
Liquid is sufficiently stirred, after stirring 35 minutes, solid material in solution all dissolution in the solution, by container from heating device
Middle taking-up, and sufficient solution will be stirred and poured into another container, that is, transfer coatings are made, then start coating machine, coating machine
Transfer coatings are coated in PET film, transfer coatings are uniformly coated in PET film, it is coated after PET film enter baking oven
Solidify in drying, adjusts the drying temperature inside oven between 130 DEG C, after by 9 minutes, transfer coatings film-forming
It is formed transfer coated.
Transfer layer 4 is equipped with layer of varnish 5 far from the side of radium-shine layer 3, and layer of varnish 5 is by polylol abietate and drying oil, water
It is obtained after the coating of the preparation of 100:9:11 in mass ratio is cured.
The present invention proposes a kind of preparation method of high-performance transfer paper, includes the following steps:
S1: configured transfer coating notch board is coated on basement membrane, then the basement membrane for being coated with transfer coating is put into baking oven
Drying film forming obtains transfer layer；
S2: in the case where keeping the height condition of high temperature, to transfer layer plus silver material coloring, making it cover transfer layer, radium-shine on the transfer layer
Picture and text；
S3: viscose coating is sprayed in the side of transfer layer, the transfer layer for being coated with viscose is bonded on base stock；
S4: stripping basement membrane, forms layer of varnish on the transfer layer up to transfer paper.
Embodiment 3
Referring to Fig.1, a kind of high-performance transfer paper, including ground paper layer 1, ground paper layer 1 are the base stock plate of any color, ground paper layer 1
Side is equipped with mucigel 2, mucigel 2 with a thickness of 10 microns, the material preparation method of mucigel 2 is that water quantitatively is added to burn
Bottle in, be warming up to 70 DEG C, start blender, be then added at one time polyvinyl alcohol, polyacrylamide, emulsifier, thickener and
Tap water is continuously heating to 95 DEG C, keeps temperature 1h or more, until polyvinyl alcohol all dissolves, all dissolves to polyvinyl alcohol
Afterwards, 71 DEG C are cooled to, 3/4 potassium peroxydisulfate is added, and vinyl acetate is slowly added dropwise；Kept for 71 DEG C of temperature, reaction 6h or so, it will
Temperature rises to 90 DEG C, and remaining 1/4 potassium peroxydisulfate, reaction 0.5h or so is added, is cooled to 75 DEG C or so, cornstarch is added,
1h or so is reacted, is cooled to 55 DEG C or so, is added dibutyl phthalate and ethylene glycol, stirring 0.5h or so, cold Kui room temperature,
Filtering, discharging, the transfer layer 4 for being coated with viscose is bonded on ground paper layer 1.
Mucigel 2 is bonded with radium-shine layer 3 far from the side of ground paper layer 1, and radium-shine layer 3 is set far from the side fixation of mucigel 2
There is transfer layer 4, the preparation for shifting coating is by raw cellulose resin, polyvinyl acetate, polyaniline, tin tetrachloride, third
Ketone, hardening agent and solvent are successively orderly to be put into the container with agitating device, then the container equipped with raw material is put into water-bath
In heating device, the temperature of water bath heating device is adjusted to 40 DEG C, during temperature rises, starts agitating device, to molten
Liquid is sufficiently stirred, stirring after forty minutes, solid material in solution all dissolution in the solution, by container from heating device
Middle taking-up, and sufficient solution will be stirred and poured into another container, that is, transfer coatings are made, then start coating machine, coating machine
Transfer coatings are coated in PET film, transfer coatings are uniformly coated in PET film, it is coated after PET film enter baking oven
Solidify in drying, adjusts the drying temperature inside oven between 145 DEG C, after by 10 minutes, transfer coatings are solidified into
Film forms transfer coated.
Transfer layer 4 is equipped with layer of varnish 5 far from the side of radium-shine layer 3, and layer of varnish 5 is by polylol abietate and drying oil, water
It is obtained after the coating of the preparation of 100:10:12 in mass ratio is cured.
The present invention proposes a kind of preparation method of high-performance transfer paper, includes the following steps:
S1: configured transfer coating notch board is coated on basement membrane, then the basement membrane for being coated with transfer coating is put into baking oven
Drying film forming obtains transfer layer；
S2: in the case where keeping the height condition of high temperature, to transfer layer plus silver material coloring, making it cover transfer layer, radium-shine on the transfer layer
Picture and text；
S3: viscose coating is sprayed in the side of transfer layer, the transfer layer for being coated with viscose is bonded on base stock；
S4: stripping basement membrane, forms layer of varnish on the transfer layer up to transfer paper.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (8)
1. a kind of high-performance transfer paper, including ground paper layer (1), which is characterized in that the side of the ground paper layer (1) is equipped with mucigel
(2), the mucigel (2) is bonded with radium-shine layer (3) far from the side of the ground paper layer (1), and the radium-shine layer (3) is far from described
The side of mucigel (2) is fixed with transfer layer (4), and the transfer layer (4) is equipped with varnish far from the side of the radium-shine layer (3)
Layer (5).
2. a kind of high-performance transfer paper according to claim 1, which is characterized in that the ground paper layer (1) is any color
Base stock plate.
3. a kind of high-performance transfer paper according to claim 1, which is characterized in that prepared by the material of the mucigel (3)
Method is that water quantitatively is added in flask, is warming up to 70 DEG C, starts blender, is then added at one time polyvinyl alcohol, poly- third
Acrylamide, emulsifier, thickener and tap water are continuously heating to 90~95 DEG C, keep temperature 1h or more, until polyvinyl alcohol is complete
Portion's dissolution is cooled to 69~71 DEG C after polyvinyl alcohol all dissolution, 3/4 potassium peroxydisulfate is added, and vinyl acetate is slowly added dropwise
Ester；Kept for 69~71 DEG C of temperature, temperature is risen to 85~90 DEG C by reaction 6h or so, and remaining 1/4 potassium peroxydisulfate, reaction is added
0.5h or so is cooled to 75 DEG C or so, and cornstarch, reaction 1h or so is added, is cooled to 55 DEG C or so, phthalic acid is added
Dibutyl ester and ethylene glycol, stirring 0.5h or so, cold Kui room temperature, filtering, discharging.
4. a kind of high-performance transfer paper according to claim 1, which is characterized in that the mucigel (2) with a thickness of 8-
10 microns.
5. a kind of high-performance transfer paper according to claim 1, which is characterized in that the radium-shine layer (3) is picture and text layer.
6. a kind of high-performance transfer paper according to claim 1, which is characterized in that the preparation method of the transfer layer (4)
For raw cellulose resin, polyvinyl acetate, polyaniline, tin tetrachloride, acetone, hardening agent and solvent are successively had in proportion
Sequence is put into the container with agitating device, then the container equipped with raw material is put into water bath heating device, by heating water bath
The temperature of device is adjusted to 30-40 DEG C, during temperature rises, starts agitating device, solution is sufficiently stirred, stir
After 30-40 minutes, all in the solution, container is taken out the solid material in solution from heating device for dissolution, and will stirring
Sufficient solution pours into another container, that is, transfer coatings are made, then start coating machine, coating machine is coated in PET film
Transfer coatings, transfer coatings are uniformly coated in PET film, it is coated after PET film enter in oven drying and solidify, adjust
Drying temperature inside oven is between 110-145 DEG C, and after by 8-10 minutes, transfer coatings film-forming, which is formed, to be turned
Move coating.
7. a kind of high-performance transfer paper according to claim 1, which is characterized in that the layer of varnish (6) is by polyalcohol pine
Fragrant ester and drying oil, water 100:(8-10 in mass ratio): it is obtained after the coating of (10-12) preparation is cured.
8. the preparation method of high-performance transfer paper described in claim 1-7 any claim, which is characterized in that including walking as follows
It is rapid:
S1: configured transfer coating notch board is coated on basement membrane, then the basement membrane for being coated with transfer coating is put into baking oven
Drying film forming obtains transfer layer；
S2: in the case where keeping the height condition of high temperature, to transfer layer plus silver material coloring, making it cover transfer layer, radium-shine on the transfer layer
Picture and text；
S3: viscose coating is sprayed in the side of transfer layer, the transfer layer for being coated with viscose is bonded on base stock；
S4: stripping basement membrane, forms layer of varnish on the transfer layer up to transfer paper.