CN109367142A - A kind of more base fabric glass fibre needle felts resistant to high temperature - Google Patents
A kind of more base fabric glass fibre needle felts resistant to high temperature Download PDFInfo
- Publication number
- CN109367142A CN109367142A CN201811414899.6A CN201811414899A CN109367142A CN 109367142 A CN109367142 A CN 109367142A CN 201811414899 A CN201811414899 A CN 201811414899A CN 109367142 A CN109367142 A CN 109367142A
- Authority
- CN
- China
- Prior art keywords
- layer
- reinforcing rib
- resistant
- high temperature
- base fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of more base fabric glass fibre needle felts resistant to high temperature, including base cloth layer, the two sides of base cloth layer are respectively equipped with the first reinforcing rib layer and the second reinforcing rib layer, first reinforcing rib layer and the second reinforcing rib layer are symmetrically distributed in the two sides up and down of base cloth layer, base cloth layer is all connected in first reinforcing rib layer and the second reinforcing rib layer equipped with ventilation pipe, the lower surface of first reinforcing rib layer is stained with carbon fiber layer, the lower surface of carbon fiber layer is stained with stainless steel fibre layer, the upper surface of second reinforcing rib layer is equipped with Zirconium oxide fibre layer, the upper surface of Zirconium oxide fibre layer, which is stained with, meets dirt composite layer, two side external surfaces for meeting dirt composite layer and stainless steel fibre layer are connected separately with the first anti oxidation layer and the second anti oxidation layer, reinforcing is mutually linked by needle thorn between base cloth layer and the first reinforcing rib layer and the second reinforcing rib layer to be integrated, of the invention one Kind more base fabric glass fibre needle felts resistant to high temperature, structure is simple, has high temperature resistant, good permeability, the high feature of pliability.
Description
Technical field
The present invention relates to a kind of Nomex apparatus field, in particular to a kind of more base fabric glass fibre needle thorns resistant to high temperature
Felt.
Background technique
Fiberglass needled mat is a kind of structurally reasonable, better performances materials, while it is also with glass fibre for original
Material, manufactured felted non-woven fabric material, glass fiber single filament is unordered staggeredly interspersed, is in omnidirectional three-dimensional micropore structure, gap
Small, gap rule is big, has good sound-absorbing, damping, corrosion-resistant, insulation, high temperature resistant, fire-retardant performance.Fiberglass needled mat
Be mainly used in automobile, noise eliminator of motorcycle inner core and engine boot, car door, roof liner thermal insulation layer or need keep the temperature,
Heat-insulated, fire prevention, sound-absorbing, insulation occasion.
But the high-temperature resistance of fiberglass needled mat is poor, glass fibre becomes fragile in the case of a high temperature, resistance to compression
Ability substantially reduces, and the internal break of fiberglass needled mat is be easy to cause to damage, and influences normally making for fiberglass needled mat
With, and Nomex currently on the market is various in style, and due to being chronically exposed under high temperature and air, is easy to produce oxidation, and
And since structure material is soft, wear in addition, so that Nomex consumption is fast, manufacturing cost is increased, wasting manpower and material resources.
Summary of the invention
The technical problem to be solved by the present invention is to overcome the defects of the prior art, provide a kind of more base fabric glass resistant to high temperature
Fiber needled felt.
In order to solve the above-mentioned technical problems, the present invention provides the following technical solutions:
One kind more base fabric glass fibre needle felts resistant to high temperature of the invention, including base cloth layer, the two sides of the base cloth layer
It is respectively equipped with the first reinforcing rib layer and the second reinforcing rib layer, the first reinforcing rib layer and the second reinforcing rib layer are symmetrically distributed in base
It is all connected with base cloth layer in the two sides up and down of layer of cloth, the first reinforcing rib layer and the second reinforcing rib layer and is equipped with ventilation pipe, it is described
The lower surface of first reinforcing rib layer is stained with carbon fiber layer, and the lower surface of the carbon fiber layer is stained with stainless steel fibre layer, institute
The upper surface for stating the second reinforcing rib layer is equipped with Zirconium oxide fibre layer, and the upper surface of the Zirconium oxide fibre layer is stained with that meet dirt compound
Layer, two side external surfaces for meeting dirt composite layer and stainless steel fibre layer are connected separately with the first anti oxidation layer and second anti-oxidant
Layer mutually links reinforcing by needle thorn between the base cloth layer and the first reinforcing rib layer and the second reinforcing rib layer and is integrated.
As a preferred technical solution of the present invention, it is described meet dirt composite layer with a thickness of 1.5-2 millimeters, it is described to meet dirt
Composite layer, the dirt composite layer of meeting is thin polyphenylene sulfide fibre.
As a preferred technical solution of the present invention, the base cloth layer with a thickness of 0.4.-0.8 millimeters.
As a preferred technical solution of the present invention, first anti oxidation layer and the second anti oxidation layer with a thickness of 2-
4 millimeters.
As a preferred technical solution of the present invention, the thickness of the first reinforcing rib layer and the second reinforcing rib layer is
5-8 millimeters.
It include metal material in the first reinforcing rib layer (8) as a preferred technical solution of the present invention.
It include metal material in the second reinforcing rib layer (9) as a preferred technical solution of the present invention.
The beneficial effects obtained by the present invention are as follows being: one kind more base fabric glass fibre needle felts resistant to high temperature of the invention, knot
Structure is simple, has high temperature resistant, good permeability, the high feature of pliability, by the carbon fiber layer of setting, which is by carbon cloth
It constitutes, which has light weight, high intensity, high-modulus, high temperature resistant, corrosion-resistant characteristic, has excellent thermal conductivity, excellent
Thermal stability and chemical stability, the made finished product of carbon fiber pass through the zirconium oxide of setting with excellent physical and chemical properties
Fibrous layer has the characteristics that stable high temeperature chemistry property, corrosion-resistant, anti-oxidant, anti-thermal shock, non-volatile, free of contamination, in Nomex
Surface up and down be respectively equipped with the first anti oxidation layer and the second anti oxidation layer, ensure the promotion of antioxygenic property;Improve entirety
The stability of structure;Promote internal oxidation resistance;Using stainless steel fibre layer, stainless steel fibre layer can enhance Nomex
Intensity, and there is antistatic performance, it both ensure that higher flame retardant property and corrosion resistance, in the two sides up and down of base cloth layer point
Not She You the first reinforcing rib layer and the second reinforcing rib layer, can make Nomex have enough intensity, prevent from pullling deformation, setting
Ventilation pipe become base cloth layer inner air flow channel, improve glass Nomex gas permeability, also ensure Nomex
The dirt composite layer of meeting of flexibility, setting is thin polyphenylene sulfide fibre, fine and closely woven to meet dirt composite layer filtering surface and effectively filter powder
Dirt reduces the discharge of dust.
Detailed description of the invention
Attached drawing is used to provide further understanding of the present invention, and constitutes part of specification, with reality of the invention
It applies example to be used to explain the present invention together, not be construed as limiting the invention.In the accompanying drawings:
Fig. 1 is structural schematic diagram of the invention;
Fig. 2 is ventilation pipe structural schematic diagram of the invention.
In figure: 1, base cloth layer;2, carbon fiber layer;3, stainless steel fibre layer;4, the first anti oxidation layer;5, second is anti-oxidant
Layer;6, Zirconium oxide fibre layer;7, dirt composite layer is met;8, the first reinforcing rib layer;9, the second reinforcing rib layer;10, ventilation pipe.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts every other
Embodiment shall fall within the protection scope of the present invention.
In the description of the present invention, it should be noted that term " on ", "lower", "inner", "outside" " end ", " front end ",
The orientation or positional relationship of the instructions such as " rear end ", " both ends ", " one end ", " other end " is orientation based on the figure or position
Relationship is merely for convenience of description of the present invention and simplification of the description, rather than the device or element of indication or suggestion meaning must have
There is specific orientation, be constructed and operated in a specific orientation, therefore is not considered as limiting the invention.In addition, term " the
One ", " second " is used for descriptive purposes only and cannot be understood as indicating or suggesting relative importance.
In the description of the present invention, it should be noted that unless otherwise clearly defined and limited, term " installation " " is set
Set/offer ", " connection ", etc., shall be understood in a broad sense, such as " connection ", may be a fixed connection, be also possible to detachably connect
It connects, or is integrally connected;It can be mechanical connection, be also possible to be electrically connected;It can be directly connected, intermediate matchmaker can also be passed through
Jie is indirectly connected, and can be the connection inside two elements.It for the ordinary skill in the art, can be with concrete condition
Understand the concrete meaning of above-mentioned term in the present invention.
As shown in Figs. 1-2, a kind of more base fabric glass fibre needle felts resistant to high temperature, including base cloth layer 1, the two of base cloth layer 1
Side is respectively equipped with the first reinforcing rib layer 8 and the second reinforcing rib layer 9, and the first reinforcing rib layer 8 and the second reinforcing rib layer 9 are symmetrically distributed in
It is all connected with base cloth layer 1 in the two sides up and down of base cloth layer 1, the first reinforcing rib layer 8 and the second reinforcing rib layer 9 and is equipped with ventilation pipe 10,
The lower surface of first reinforcing rib layer 8 is stained with carbon fiber layer 2, and the lower surface of carbon fiber layer 2 is stained with stainless steel fibre layer 3, the
The upper surface of two reinforcing rib layers 9 is equipped with Zirconium oxide fibre layer 6, and the upper surface of Zirconium oxide fibre layer 6, which is stained with, meets dirt composite layer 7,
Two side external surfaces for meeting dirt composite layer 7 and stainless steel fibre layer 3 are connected separately with the first anti oxidation layer 4 and the second anti oxidation layer 5,
Reinforcing is mutually linked by needle thorn between base cloth layer 1 and the first reinforcing rib layer 8 and the second reinforcing rib layer 9 to be integrated.
Meet dirt composite layer 7 with a thickness of 1.5-2 millimeters, meeting dirt composite layer 7 is thin polyphenylene sulfide fibre, and fine and closely woven to meet dirt multiple
Dust can effectively be filtered by closing 7 filtering surface of layer, reduce the discharge of dust, base cloth layer 1 with a thickness of 0.4-0.8 millimeter, first resists
Oxide layer 4 and the second anti oxidation layer 5 with a thickness of 2-4 millimeters, delay the oxidation of material, while can increase the ventilation of Nomex
Property, the thickness of the first reinforcing rib layer 8 and the second reinforcing rib layer 9 is 5-8 millimeters, and it can make Nomex that there is enough intensity,
It prevents from pullling deformation.
Specifically, the layer is made of carbon cloth by the carbon fiber layer 2 of setting, which has light weight, high-strength
Degree, high-modulus, high temperature resistant, corrosion-resistant characteristic have excellent thermal conductivity, excellent thermal stability and chemical stability, carbon fiber
Made finished product is tieed up with excellent physical and chemical properties, has high temeperature chemistry property steady by the Zirconium oxide fibre layer 6 of setting
Fixed, corrosion-resistant, anti-oxidant, anti-thermal shock, non-volatile, free of contamination feature, it is anti-to be respectively equipped with first above and below the surface of Nomex
Oxide layer 4 and the second anti oxidation layer 5, ensure the promotion of antioxygenic property;Improve integrally-built stability;It is promoted internal anti-
Oxidability;Using stainless steel fibre layer 3, stainless steel fibre layer 3 can enhance the intensity of Nomex, and have static electricity resistance
Can, it both ensure that higher flame retardant property and corrosion resistance, and be respectively equipped with the first reinforcing rib layer in the two sides up and down of base cloth layer 1
8 and the second reinforcing rib layer 9, it can make Nomex that there is enough intensity, prevent from pullling deformation, the ventilation pipe 10 of setting becomes
The channel of 1 inner air flow of base cloth layer improves the gas permeability of glass Nomex, also ensures the flexibility of Nomex, setting
Meeting dirt composite layer 7 is thin polyphenylene sulfide fibre, and fine and closely woven 7 filtering surface of dirt composite layer of meeting can effectively filter dust, reduces dust
Discharge, one kind more base fabric glass fibre needle felts resistant to high temperature of the invention, structure is simple, there is high temperature resistant, good permeability,
The high feature of pliability.
Finally, it should be noted that the foregoing is only a preferred embodiment of the present invention, it is not intended to restrict the invention,
Although the present invention is described in detail referring to the foregoing embodiments, for those skilled in the art, still may be used
To modify the technical solutions described in the foregoing embodiments or equivalent replacement of some of the technical features.
All within the spirits and principles of the present invention, any modification, equivalent replacement, improvement and so on should be included in of the invention
Within protection scope.
Claims (7)
1. a kind of more base fabric glass fibre needle felts resistant to high temperature, including base cloth layer (1), which is characterized in that the base cloth layer (1)
Two sides be respectively equipped with the first reinforcing rib layer (8) and the second reinforcing rib layer (9), the first reinforcing rib layer (8) and second is reinforced
Muscle layer (9) is symmetrically distributed in the two sides up and down of base cloth layer (1), in the first reinforcing rib layer (8) and the second reinforcing rib layer (9)
It connects base cloth layer (1) and is equipped with ventilation pipe (10), the lower surface of the first reinforcing rib layer (8) is stained with carbon fiber layer (2), institute
The lower surface for stating carbon fiber layer (2) is stained with stainless steel fibre layer (3), and the upper surface of the second reinforcing rib layer (9) is equipped with oxygen
Change zirconium fibrous layer (6), the upper surface of the Zirconium oxide fibre layer (6), which is stained with, meets dirt composite layer (7), described to meet dirt composite layer
(7) and two side external surfaces of stainless steel fibre layer (3) are connected separately with the first anti oxidation layer (4) and the second anti oxidation layer (5), institute
It states and mutually links reinforcing by needle thorn between base cloth layer (1) and the first reinforcing rib layer (8) and the second reinforcing rib layer (9) and be integrated.
2. one kind more base fabric glass fibre needle felts resistant to high temperature according to claim 1, which is characterized in that described to meet dirt
Composite layer (7) with a thickness of 1.5-2 millimeters, it is described meet dirt composite layer (7) be thin polyphenylene sulfide fibre.
3. one kind more base fabric glass fibre needle felts resistant to high temperature according to claim 1, which is characterized in that the base fabric
Layer (1) with a thickness of 0.4-0.8 millimeters.
4. one kind more base fabric glass fibre needle felts resistant to high temperature according to claim 1, which is characterized in that described first
Anti oxidation layer (4) and the second anti oxidation layer (5) with a thickness of 2-4 millimeters.
5. one kind more base fabric glass fibre needle felts resistant to high temperature according to claim 1, which is characterized in that described first
The thickness of reinforcing rib layer (8) and the second reinforcing rib layer (9) is 5-8 millimeters.
6. one kind more base fabric glass fibre needle felts resistant to high temperature according to claim 1, which is characterized in that described first
It include metal material in reinforcing rib layer (8).
7. one kind more base fabric glass fibre needle felts resistant to high temperature according to claim 1, which is characterized in that described second
It include metal material in reinforcing rib layer (9).