CN109354763A - PP composite material and preparation method thereof - Google Patents
PP composite material and preparation method thereof Download PDFInfo
- Publication number
- CN109354763A CN109354763A CN201811043576.0A CN201811043576A CN109354763A CN 109354763 A CN109354763 A CN 109354763A CN 201811043576 A CN201811043576 A CN 201811043576A CN 109354763 A CN109354763 A CN 109354763A
- Authority
- CN
- China
- Prior art keywords
- composite material
- parts
- preparation
- barium sulfate
- retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to field of material technology, and in particular to a kind of PP composite material and preparation method thereof.The PP composite material includes the component of following parts by weight: 70-90 parts of acrylic resin;1-10 parts of wolframic acid lutetium;6-20 parts of barium sulfate;2-8 parts of fire retardant;1-4 parts of synergistic flame retardant;0.1-2 parts of coupling agent;0.2-0.5 parts of antioxidant;0.1-0.5 parts of lubricant;0.2-1 parts of nucleating agent.The PP composite material have high gloss, low-shrinkage, mechanical performance equilibrium characteristic, and the cost of material is low, with considerable economic benefit, the demand of the industries such as automobile, the household electrical appliances and electronic apparatus PP composite material fire-retardant for high-performance excellent appearance can satisfy.
Description
Technical field
The invention belongs to field of material technology, and in particular to a kind of PP composite material and preparation method thereof.
Background technique
Polypropylene (Polypropylene, PP) material is a kind of translucent colorless solid, odorless nontoxic macromolecule material
Material, compound with regular structure are easy crystallization, and fusing point is up to 168 DEG C, and heat-resisting, corrosion-resistant, density is small, is most light general-purpose plastics;But
Its low-temperature impact resistance is poor, and shrinking percentage is big, easy to aging.
The method for being usually used in reducing polypropylene material shrinking percentage at present has: 1) adding the fillers such as talcum powder, calcium carbonate, mica
Or increase its dosage;2) glass fibre is added;3) increase the content of toughener.1) the shortcomings that above-mentioned three kinds of methods, which is respectively as follows:, to be added
Amount that is filled or increasing filler declines toughness of material;2) after adding glass fibre, the apparent mass of polypropylene material is just
It is decreased obviously and the impact resistance of material also shows slightly insufficient;3) content for increasing toughener can bring increased costs and modulus to drop
Low problem.
As electric, household electrical appliances, auto parts and components, electromechanical equipment develop to high-performance microization, to PP material, especially
Be environmental-protection flame-retardant PP material demand it is more and more.Fire-retardant PP material is presently mainly that bromo- antimony is compound, and it is swollen that there are also P-N types
Swollen type.The characteristics of these fire-retardant PP materials is that fire retardant additive amount is big, fire retardant is easily precipitated, and toughness of material is poor, and specific gravity is high, size
Stability is poor, and when burning can generate a large amount of smog and pollute environment.
Summary of the invention
It is an object of the invention to overcome the above-mentioned deficiency of the prior art, a kind of PP composite material and its preparation are provided
Method, it is intended to solve existing PP Material shrinkage performance, the technical issues of fire-retardant and environment protecting cannot be taken into account.
For achieving the above object, The technical solution adopted by the invention is as follows:
One aspect of the present invention provides a kind of PP composite material, the component including following parts by weight:
In PP composite material provided by the invention, acrylic resin as basic resin, by select wolframic acid lutetium and
Barium sulfate compounding be used as auxiliary packing, not only can reinforced polypropylene compound material rigidity again make its surface have high gloss spy
Point can reduce composite material shrinking percentage to guarantee that its heat resistance is stablized but also improved to product size;And fire retardant and synergistic
Fire retardant can make the fire-retardant rank of composite material reach V2 grades, while nucleating agent makes the mechanical performance of composite material, heat resistance
It can further be promoted with low-shrinkage.In the formula of PP composite material of the invention, each ingredient and content pass through collaboration
Effect so that the PP composite material have high gloss, low-shrinkage, mechanical performance equilibrium characteristic, and material at
This is low, has considerable economic benefit, can satisfy the industries such as automobile, household electrical appliances and electronic apparatus and high-performance excellent appearance is hindered
The demand of the PP composite material of combustion.
Another aspect of the present invention provides a kind of preparation method of PP composite material, includes the following steps:
Each component materials are weighed respectively by ingredient contained by above-mentioned PP composite material of the invention and its content;
The acrylic resin, wolframic acid lutetium, barium sulfate, fire retardant, synergistic flame retardant, coupling agent, antioxidant, lubricant and
Nucleating agent carries out mixed processing, obtains mixed material;
The mixed material is subjected to melting extrusion granulation.
The preparation method of PP composite material provided by the invention is simple for process, at low cost, final obtained poly-
In acrylic composite, by selecting wolframic acid lutetium and barium sulfate compounding as auxiliary packing and other auxiliary agents by acting synergistically,
So that the PP composite material have high gloss, low-shrinkage, mechanical performance equilibrium characteristic, can satisfy automobile, family
The demand of the industries PP composite material fire-retardant for high-performance excellent appearance such as electricity and electronic apparatus.
Specific embodiment
In order to which technical problems, technical solutions and advantageous effects to be solved by the present invention are more clearly understood, below in conjunction with
Embodiment, the present invention will be described in further detail.It should be appreciated that specific embodiment described herein is only used to explain
The present invention is not intended to limit the present invention.
On the one hand, the embodiment of the invention provides a kind of PP composite material, the component including following parts by weight:
In PP composite material provided in an embodiment of the present invention, acrylic resin is as basic resin, by selecting tungsten
Sour lutetium and barium sulfate compounding are used as auxiliary packing, not only can the rigidity of reinforced polypropylene compound material make its surface with high glaze again
Degree feature can reduce composite material shrinking percentage to guarantee that its heat resistance is stablized but also improved to product size;And fire retardant and
Synergistic flame retardant can make the fire-retardant rank of composite material reach V2 grades, while nucleating agent makes the mechanical performance, resistance to of composite material
Hot property and low-shrinkage can be promoted further.In the formula of the PP composite material of the embodiment of the present invention, each ingredient and contain
Amount by synergistic effect so that the PP composite material have high gloss, low-shrinkage, mechanical performance equilibrium characteristic,
And the cost of material is low, has considerable economic benefit, can satisfy the industries such as automobile, household electrical appliances and electronic apparatus for high-performance
The demand of the fire-retardant PP composite material of excellent appearance.
Further, in PP composite material provided in an embodiment of the present invention, the acrylic resin includes that homopolymerization is poly-
At least one of propylene, copolymer polypropylene and random polypropylene.The embodiment of the present invention selects homopolypropylene and copolymerization poly- third
Alkene compounding had both combined the rigidity of homopolypropylene and the toughness of copolymer polypropylene to assign the mechanicalness of material equilibrium in this way
Can, at the same only need to add on a small quantity nucleating agent allow for the mechanical property of materials, heat resistance and low-shrinkage can be more excellent.It is preferred that
Ground selects the melt flow rate (MFR) of homopolypropylene and copolymer polypropylene to be not less than 20g/ under the conditions of 230 DEG C/2.16Kg
10min carries out mixing compounding, and the homopolypropylene and copolymer polypropylene in above-mentioned specification limit are used to prepare polypropylene composite materials
Material can be better suited for the injection molding technique of blending extrusion.In the embodiment of the present invention, the parts by weight of acrylic resin are
70-90 parts, concretely 70 parts, 74 parts, 75 parts, 80 parts, 85 parts, 90 parts etc., it is preferable that select homopolypropylene and copolymerization poly-
Propylene equal proportion compounding effect more preferably, such as 37.5 parts of homopolypropylene and 37.5 parts of copolymer polypropylene.
Further, in PP composite material provided in an embodiment of the present invention, the wolframic acid lutetium chemical formula is Lu2
(WO4)3Or Lu2W3O12, wolframic acid lutetium is orthorhombic system type wolframic acid lutetium in the embodiment of the present invention, i.e. the negative heat of orthorhombic forms anisotropy
Expanding material, the wolframic acid lutetium along one or certain two axis is shunk and is expanded along other axis, make material with the raising crystal inside of temperature
The bulk expansion performance of material is negative expansion, can reduce the internal stress of material to greatest extent, increase the dimensionally stable of material
Property;Lu2W3O12There is negative expansion performance at -127 DEG C~627 DEG C, average thermal linear expansion coefficient is -6.8 × 10-6K-1;Wolframic acid
The preferred nanoscale wolframic acid lutetium of lutetium, specific partial size can be 30-300nm.The barium sulfate is it is also preferred that nanoscale barium sulfate, specifically
The partial size of barium sulfate is 30-300nm, nanoscale wolframic acid lutetium and nanoscale barium sulfate compounding, better effect.Further
Ground preferably carries out the modified barium sulfate in surface through aluminium oxide and/or polysiloxanes, and barium sulfate powder after modified is in polypropylene
It is easier to disperse in the matrix of composite material, it is closer in conjunction with matrix resin, the performance of composite material is influenced smaller.This hair
In bright embodiment, the parts by weight of wolframic acid lutetium are 1-10 parts, concretely 1 part, 2 parts, 5 parts, 8 parts, 10 parts etc., the weight of barium sulfate
Part is 6-20 parts, concretely 6 parts, 12 parts, 15 parts, 18 parts, 20 parts etc..
Further, in PP composite material provided in an embodiment of the present invention, the fire retardant includes eight bromo ether, eight bromines
At least one of thioether, hexabromocyclododecane and three (2,3- dibromopropyl) fulminuric acid esters;The synergistic flame retardant packet
Include at least one of antimony oxide, antimony pentoxide and zinc borate.Pass through preferred efficient bromo- antimony flame-retardant system, addition
Amount is few, but can control burning fuming amount well and reduce the corrosion to mold, can effectively reduce material cost, has more considerable
Economic benefit.In the embodiment of the present invention, the parts by weight of fire retardant are 2-8 parts, concretely 2 parts, 3 parts, 4 parts, 6 parts, 8 parts
Parts by weight Deng, synergistic flame retardant are 1-4 parts, concretely 1 part, 2 parts, 4 parts etc..
Further, in PP composite material provided in an embodiment of the present invention, the coupling agent is three second of γ-aminopropyl
Oxysilane (KH-550), the splicing which can effectively improve in PP composite material between each ingredient are strong
Degree;The antioxidant includes four [β-(3,5- di-tert-butyl-hydroxy phenyl) propionic acid] pentaerythritol esters (1010) and three [2,4-
At least one of di-tert-butyl-phenyl] phosphite ester (168), which can effectively improve PP composite material
Antioxygenic property.The lubricant is calcium stearate CaSt2, lubricant can drop the frictional resistance of low friction pair, improve compound
The processing performance of material;The nucleating agent is α type-nucleating agent, and preferably phosphate class nucleating agent, the nucleating agent is as polypropylene tree
The modified additive of rouge crystallization, can make PP composite material have good processing performance and service performance.
In the embodiment of the present invention, the parts by weight of coupling agent are 0.1-2 parts, concretely 0.1 part, 0.2 part, 1 part, 2 parts etc.,
The parts by weight of antioxidant are 0.2-0.5 parts, concretely 0.2 part, 0.3 part, 0.5 part etc..The parts by weight of lubricant are 0.1-0.5
Part, concretely 0.2 part, 0.3 part, 0.5 part etc.;The parts by weight of nucleating agent agent be 0.2-1 parts, concretely 0.2 part, 0.3 part,
1 part etc..
On the other hand, the embodiment of the invention also provides a kind of preparation methods of PP composite material, including walk as follows
It is rapid:
S01: ingredient contained by the above-mentioned PP composite material by the embodiment of the present invention and its content weigh respectively it is each at
Divide raw material;
S02: the acrylic resin, wolframic acid lutetium, barium sulfate, fire retardant, synergistic flame retardant, coupling agent, antioxidant, lubrication
Agent and nucleating agent carry out mixed processing, obtain mixed material;
S03: the mixed material is subjected to melting extrusion granulation.
The preparation method of PP composite material provided in an embodiment of the present invention is simple for process, at low cost, final to make
In the PP composite material obtained, by selecting wolframic acid lutetium and barium sulfate compounding to pass through association as auxiliary packing and other auxiliary agents
Same-action so that the PP composite material have high gloss, low-shrinkage, mechanical performance equilibrium characteristic, can satisfy
The demand of the industries such as automobile, the household electrical appliances and electronic apparatus PP composite material fire-retardant for high-performance excellent appearance.It is real with the present invention
The PP composite material product of an injection molding is applied due to possessing good appearance and flame retardant property, usually may not need spraying
It is directly used on all kinds of household electrical appliances, auto parts and components, electromechanical equipment or electric equipment products shell.
Further, the temperature that the melting extrusion is granulated is 160-200 DEG C.160 DEG C to 200 DEG C be one it is good plus
Work temperature range, this processing temperature can prevent the decomposition of the fire retardant of low decomposition temperature, while avoid PP resin too fast
Thermo-oxidative ageing.In the embodiment of the present invention, melting extrusion granulation is carried out by double screw extruder, which should be equipped with
Weightlessness claims, and can effectively control the ratio of functional filler in composite material in this way.Specifically, the barrel of double screw extruder
For ten section cylinders, first segment cylinder connects main drawing-in device, Section of six cylinder exhaust, and Section of nine cylinder vacuumizes;Barrel temperature
Setting are as follows: first segment cylinder does not heat, the second 180 ± 5 DEG C of section cylinder, 180 ± 5 DEG C of third section cylinder, Section of four cylinder 180 ±
5 DEG C, Section five 180 ± 5 DEG C of cylinder, Section six 170 ± 5 DEG C of cylinder, Section seven 170 ± 5 DEG C of cylinder, Section of eight cylinder 170 ± 5
DEG C, Section nine 170 ± 5 DEG C of cylinder, 170 ± 5 DEG C of protelum cylinder, 200 ± 5 DEG C of head.
Further, after the melting extrusion is granulated, further includes the steps that being dried processing, be dried removal
Moisture in final PP composite material, convenient for storage.Preferably, the temperature of the drying process is 70-90 DEG C;It is described dry
The time 2-4h of dry processing.Within the scope of the temperature and time, drying effect is best.
The present invention successively carried out test of many times, and it is further detailed as reference pair invention progress now to lift A partial experiment result
Thin description, is described in detail combined with specific embodiments below.
Embodiment 1
A kind of PP composite material is formulated the embodiment 1 being shown in Table in 1.The preparation side of the polycarbonate composite material
Method includes the following steps:
(1) each component is weighed according to the formula of embodiment 1 in table 1;
(2) recipe ingredient in addition to functional filler is used into high mixer mixing 3min, be added after mixing remaining
Functional filler continues to mix 5min, obtain uniform mixed material;
(3) mixed material is put into melting extrusion in double screw extruder, be granulated.
Embodiment 2
A kind of PP composite material is formulated the embodiment 2 being shown in Table in 1.The preparation side of the polycarbonate composite material
Method includes the following steps:
(1) each component is weighed according to the formula of embodiment 2 in table 1;
(2) recipe ingredient in addition to functional filler is used into high mixer mixing 3min, be added after mixing remaining
Functional filler continues to mix 5min, obtain uniform mixed material;
(3) mixed material is put into melting extrusion in double screw extruder, be granulated.
Embodiment 3
A kind of PP composite material is formulated the embodiment 3 being shown in Table in 1.The preparation side of the polycarbonate composite material
Method includes the following steps:
(1) each component is weighed according to the formula of embodiment 3 in table 1;
(2) recipe ingredient in addition to functional filler is used into high mixer mixing 3min, be added after mixing remaining
Functional filler continues to mix 5min, obtain uniform mixed material;
(3) mixed material is put into melting extrusion in double screw extruder, be granulated.
Embodiment 4
A kind of PP composite material is formulated the embodiment 4 being shown in Table in 1.The preparation side of the polycarbonate composite material
Method includes the following steps:
(1) each component is weighed according to the formula of embodiment 4 in table 1;
(2) recipe ingredient in addition to functional filler is used into high mixer mixing 3min, be added after mixing remaining
Functional filler continues to mix 5min, obtain uniform mixed material;
(3) mixed material is put into melting extrusion in double screw extruder, be granulated.
Embodiment 5
A kind of PP composite material is formulated the embodiment 5 being shown in Table in 1.The preparation side of the polycarbonate composite material
Method includes the following steps:
(1) each component is weighed according to the formula of embodiment 5 in table 1;
(2) recipe ingredient in addition to functional filler is used into high mixer mixing 3min, be added after mixing remaining
Functional filler continues to mix 5min, obtain uniform mixed material;
(3) mixed material is put into melting extrusion in double screw extruder, be granulated.
Embodiment 6
A kind of PP composite material is formulated the embodiment 6 being shown in Table in 1.The preparation side of the polycarbonate composite material
Method includes the following steps:
(1) each component is weighed according to the formula of embodiment 6 in table 1;
(2) recipe ingredient in addition to functional filler is used into high mixer mixing 3min, be added after mixing remaining
Functional filler continues to mix 5min, obtain uniform mixed material;
(3) mixed material is put into melting extrusion in double screw extruder, be granulated.
Table 1
In above-mentioned table 1,
A is PP resin, comprising: A1- homopolymerization PP resin (tensile strength 30MPa);A2- is copolymerized PP resin (impact strength
38KJ/m2)
B is functional filler, comprising: B1- nanoscale barium sulfate;B2-Lu2W3O12;
C is fire retardant: eight bromo ether;
D is synergistic flame retardant: antimony oxide;
E is coupling agent: KH-550;
F is antioxidant, including 1010:168=1:1;
G is lubricant: CaSt2;
H is nucleating agent: phosphoric acid salt nucleating agent.
Performance test
The enhancing PP composite material of mineral filler prepared by embodiment 1-6 and comparative example 1-3 is molded into mark according to national standard
Quasi- test bars carry out mechanical property dependence test.
Notch shock test reference national standard GB/T 1843 is carried out;Extension test is carried out with reference to national standard GB/T 1040;Bending
Test reference national standard GB/T 9341 is carried out;Thermal deformation (0.45MPa/6.4mm) test reference national standard GB/T1634 is carried out;It is fire-retardant
Performance is tested according to UL94 (1.6mm) flammability test standard;Shrinking percentage test reference national standard GB/T 15585 is carried out, choosing
With 150 × 100 × 3.2mm mold;Glossiness test reference national standard GB/T 9754 is carried out.Glossiness is to show that finished surface is thick
One index of rough degree, usually, the better product of glossiness, surface is more smooth, and appearance is better, therefore glossiness is normal
For characterizing the appearance quality of product surface.
The test result of embodiment 1-6 and comparative example 1-3 are as shown in table 2.
Table 2
As can be seen from Table 1 and Table 2, the composite material that 1-6 of the embodiment of the present invention is provided has good appearance, machine simultaneously
Tool performance, heat resistance and low-shrinkage are suitable for injection molding technique.Compared with Example 3, impact property is especially for comparative example 1
It is that dimensional stability has larger decline, this illustrates the PP and Lu of selection compounding2W3O12For the toughness and dimensional stability of material
There can be active influence.Compared with Example 3, rigidity and appearance have larger decline to comparative example 2, this is because in copolymerization PP resin
PE toughening containing 1%~5% declines material stiffness, Lu2W3O12For the opposite spherical junctions with barium sulfate of orthorhombic forms structure
There is structure stronger photoextinction appearance glossiness is decreased obviously, and its special anisotropy negative expansion performance assigns
The fabulous dimensional stability of material;Compared with Example 3, the curved impact property and glossiness of comparative example 3 are slightly higher for comparative example 3,
And other machinery performance, heat resistance, fire-retardant and dimensional stability are lower, this is because non-functional filler is to PP material knot
The destruction of brilliant process and the heterogeneous nucleating effect of nucleating agent make its glossiness and impact strength keep higher, and make other machinery
Performance, heat resistance and dimensional stability decline.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all in essence of the invention
Made any modifications, equivalent replacements, and improvements etc., should all be included in the protection scope of the present invention within mind and principle.
Claims (10)
1. a kind of PP composite material, which is characterized in that the component including following parts by weight:
2. PP composite material as described in claim 1, which is characterized in that the acrylic resin includes homopolymerization poly- third
At least one of alkene, copolymer polypropylene and random polypropylene.
3. PP composite material as described in claim 1, which is characterized in that the wolframic acid lutetium is orthorhombic system type wolframic acid
Lutetium;And/or
The barium sulfate is nanoscale barium sulfate.
4. PP composite material as described in claim 1, which is characterized in that the fire retardant includes eight bromo ether, eight bromine sulphur
At least one of ether, hexabromocyclododecane and three (2,3- dibromopropyl) fulminuric acid esters;And/or
The synergistic flame retardant includes at least one of antimony oxide, antimony pentoxide and zinc borate.
5. PP composite material as described in claim 1, which is characterized in that the coupling agent is three ethoxy of γ-aminopropyl
Base silane;And/or
The antioxidant includes four [β-(3,5- di-tert-butyl-hydroxy phenyl) propionic acid] pentaerythritol esters and three [bis- uncles of 2,4-
At least one of butyl phenyl] phosphite ester.
6. PP composite material as described in claim 1, which is characterized in that the lubricant is calcium stearate;And/or
The nucleating agent is phosphoric acid salt nucleating agent.
7. a kind of preparation method of PP composite material, which comprises the steps of:
It is former that each ingredient is weighed respectively by ingredient contained by PP composite material described in any one of claims 1-6 and its content
Material;
By the acrylic resin, wolframic acid lutetium, barium sulfate, fire retardant, synergistic flame retardant, coupling agent, antioxidant, lubricant and at
Core agent carries out mixed processing, obtains mixed material;
The mixed material is subjected to melting extrusion granulation.
8. preparation method as claimed in claim 7, which is characterized in that the temperature that the melting extrusion is granulated is 160-200 DEG C.
9. preparation method as claimed in claim 7, which is characterized in that further include drying after the melting extrusion is granulated
The step of processing processing.
10. preparation method as claimed in claim 9, which is characterized in that the temperature of the drying process is 70-90 DEG C;And/or
The time 2-4h of the drying process.