CN109337351A - A kind of pump valve pipeline and preparation method thereof with heat insulation function - Google Patents
A kind of pump valve pipeline and preparation method thereof with heat insulation function Download PDFInfo
- Publication number
- CN109337351A CN109337351A CN201811134976.2A CN201811134976A CN109337351A CN 109337351 A CN109337351 A CN 109337351A CN 201811134976 A CN201811134976 A CN 201811134976A CN 109337351 A CN109337351 A CN 109337351A
- Authority
- CN
- China
- Prior art keywords
- clamping ring
- tube
- inner tube
- heat insulation
- pipeline
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of pump valve pipeline with heat insulation function, including pipeline body, the pipeline body includes the inner tube being arranged from the inside to the outside, insulating tube and outer tube, the both ends of the pipeline body have been connected by screw to flange connection, the flange connection includes ring flange, the middle side edge of the ring flange is equipped with interior clamping ring and outer clamping ring, the outer clamping ring is plugged in the gap between outer tube and inner tube, and the inner tube is plugged in the inserting groove between interior clamping ring and outer clamping ring.Inventive pipeline ontology includes the inner tube being arranged from the inside to the outside, insulating tube and outer tube, and wherein the packed density of insulating tube is greater than the polyurethane insulation coating density of design, and density is larger after foaming curing, and compressive strength is good, meets the bearing capacity to pipeline body;The preferable dimensional stability of insulating tube also has preferable flexibility, and heat insulation effect is good, and high temperature resistance is good, long service life.
Description
Technical field
The invention belongs to pump valve pipe technology fields, and in particular to a kind of pump valve pipeline and its preparation with heat insulation function
Method.
Background technique
Pump valve pipeline is widely used in the production such as chemical industry, food and drug, with to production efficiency and quality
Requirement it is higher and higher, pump valve pipeline in addition to being attached to the new functions such as heat preservation, degerming, cooling in existing translocation,
But existing pump valve pipeline is generally fabricated using single metal or plastics, heat insulation effect is poor.Plastic conduit
Manufacturing cost it is lower, but its physical property is poor, is often easy to happen cracking, needs to check in time and replacement.
For this purpose, it is proposed that a kind of pump valve pipeline and preparation method thereof with heat insulation function, to solve above-mentioned background skill
The problem of being mentioned in art.
Summary of the invention
The purpose of the present invention is to provide a kind of pump valve pipeline and preparation method thereof with heat insulation function, it is above-mentioned to solve
The problem of being proposed in background technique.
To achieve the above object, the invention provides the following technical scheme: a kind of pump valve pipeline with heat insulation function, including
Pipeline body, the pipeline body include the inner tube being arranged from the inside to the outside, insulating tube and outer tube, and the two of the pipeline body
End has been connected by screw to flange connection, and the flange connection includes ring flange, in the side of the ring flange
Portion is equipped with interior clamping ring and outer clamping ring, and the outer clamping ring is plugged in the gap between outer tube and inner tube, described interior
Layer pipe is plugged in the inserting groove between interior clamping ring and outer clamping ring.
Preferably, the ring flange is integrally formed with interior clamping ring and outer clamping ring, the interior clamping ring and outer connection
Axle center is enclosed on same straight line, and interior clamping ring is located inside outer clamping ring.
Preferably, the screw sequentially passes through outer tube, outer clamping ring, inner tube and is finally bolted in interior clamping ring, and
Screw is placed equidistant with the circle in outer tube.
Preferably, mass fraction shared by the constituent of the insulating tube and each ingredient is respectively as follows: PET resin 58~70
Part, 15~25 parts of polyvinylidene fluoride, 13~22 parts of polymethyl methacrylate, 16-23 parts of combined polyether glycol, foam stabilizer
2~3 parts, 1~3 part of foaming agent and 100~130 parts of polyisocyanates.
The preparation method of the present invention also provides a kind of pump valve pipeline with heat insulation function, specifically includes the following steps:
S1, by load weighted PET resin, polyvinylidene fluoride, polymethyl methacrylate, combined polyether glycol, foam stabilizer,
In foaming agent and polyisocyanates investment mixing kettle, 30~60min of stirring to acquisition mixture A after mixing;
S2, mixture A is heated to 25~28 DEG C, is filled between outer tube and inner tube after mixing through high pressure foaming machine
Gap in, so that mixture A is carried out the foaming of free pressure in closed space, formation insulating tube, thus completed pipe
Road ontology;
S3, outer clamping ring is plugged in the gap between outer tube and inner tube, while inner tube is made to be plugged in interior connection
In inserting groove between circle and outer clamping ring, then screw sequentially passes through outer tube, outer clamping ring, inner tube and is finally bolted in
Interior clamping ring, the combination for completing pipeline body and flange connection are installed.
Compared with prior art, the beneficial effects of the present invention are: a kind of pump valve with heat insulation function provided by the invention
Pipeline and preparation method thereof, inventive pipeline ontology includes the inner tube being arranged from the inside to the outside, insulating tube and outer tube, wherein protecting
Mass fraction shared by the constituent of warm pipe and each ingredient is respectively as follows: PET resin, polyvinylidene fluoride, polymethylacrylic acid
Methyl esters, combined polyether glycol, foam stabilizer, foaming agent and polyisocyanates, the packed density of insulating tube are greater than the poly- ammonia of design
Ester insulating layer density, density is larger after foaming curing, and compressive strength is good, meets the bearing capacity to pipeline body;
The preferable dimensional stability of insulating tube also has preferable flexibility, and heat insulation effect is good, and high temperature resistance is good, uses the longevity
Life length;
Outer clamping ring is plugged in the gap between outer tube and inner tube, at the same make inner tube be plugged in interior clamping ring and
In inserting groove between outer clamping ring, then screw sequentially passes through outer tube, outer clamping ring, inner tube and is finally bolted in interior company
Adapter ring, in this way, the combination installation of pipeline body and flange connection is simple.
Detailed description of the invention
Fig. 1 is that pipeline body of the invention connects schematic cross-sectional view with flange connection;
Fig. 2 is pipeline body schematic diagram of internal structure of the invention;
Fig. 3 is flange connection structural schematic diagram of the invention.
In figure: 1 outer tube, 2 insulating tubes, 3 inner tubes, 4 pipeline bodies, 5 ring flanges, 6 outer clamping rings, clamping ring, 8 in 7
Screw, 9 flange connections, 10 inserting grooves.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts every other
Embodiment shall fall within the protection scope of the present invention.
Embodiment 1
The present invention provides a kind of pump valve pipeline with heat insulation function of such as Fig. 1-3, including pipeline body 4, the pipeline sheets
Body 4 includes inner tube 3, insulating tube 2 and the outer tube 1 being arranged from the inside to the outside, and the both ends of the pipeline body 4 are connected by screw 8
It is connected to flange connection 9, the flange connection 9 includes ring flange 5, and the middle side edge of the ring flange 5 is equipped with interior
Clamping ring 7 and outer clamping ring 6, the outer clamping ring 6 are plugged in the gap between outer tube 1 and inner tube 3, the inner tube
3 are plugged in the inserting groove 10 between interior clamping ring 7 and outer clamping ring 6.
Specifically, the ring flange 5 is integrally formed with interior clamping ring 7 and outer clamping ring 6, the interior clamping ring 7 with it is outer
6 axle center of clamping ring is on same straight line, and interior clamping ring 7 is located inside outer clamping ring 6.
Specifically, the screw 8 sequentially passes through outer tube 1, outer clamping ring 6, inner tube 3 and is finally bolted in interior clamping ring
7, and screw 8 is placed equidistant with the circle in outer tube 1.
Specifically, mass fraction shared by the constituent of the insulating tube 2 and each ingredient be respectively as follows: 58 parts of PET resin,
25 parts of polyvinylidene fluoride, 22 parts of polymethyl methacrylate, 16 parts of combined polyether glycol, 3 parts of foam stabilizer, 2 parts of foaming agent
With 100 parts of polyisocyanates.
The preparation method of the present invention also provides a kind of pump valve pipeline with heat insulation function, specifically includes the following steps:
S1, by load weighted PET resin, polyvinylidene fluoride, polymethyl methacrylate, combined polyether glycol, foam stabilizer,
In foaming agent and polyisocyanates investment mixing kettle, stirring 50min to acquisition mixture A after mixing;
S2, mixture A is heated to 28 DEG C, is filled between outer tube 1 and inner tube 3 after mixing through high pressure foaming machine
In gap, so that mixture A is carried out free pressure foaming in closed space, form insulating tube 2, thus completed pipeline
Ontology 4;
S3, outer clamping ring 6 is plugged in the gap between outer tube 1 and inner tube 3, while it is interior that inner tube 3 is plugged in
In inserting groove 10 between clamping ring 7 and outer clamping ring 6, then screw 8 sequentially passes through outer tube 1, outer clamping ring 6, inner tube 3
And it is finally bolted in interior clamping ring 7, the combination for completing pipeline body 4 and flange connection 9 is installed.
In conclusion compared with prior art, inventive pipeline ontology 4 includes the inner tube 3 being arranged from the inside to the outside, heat preservation
Pipe 2 and outer tube 1, wherein mass fraction shared by the constituent of insulating tube 2 and each ingredient is respectively as follows: PET resin, gathers inclined two
Vinyl fluoride, polymethyl methacrylate, combined polyether glycol, foam stabilizer, foaming agent and polyisocyanates, insulating tube 2 are filled out
The polyurethane insulation coating density that density is greater than design is filled, density is larger after foaming curing, and compressive strength is good, meets to pipeline body
4 bearing capacity;
The preferable dimensional stability of insulating tube 2 also has preferable flexibility, and heat insulation effect is good, and high temperature resistance is good, uses the longevity
Life length;
Outer clamping ring 6 is plugged in the gap between outer tube 1 and inner tube 3, while inner tube 3 being made to be plugged in interior connection
In inserting groove 10 between circle 7 and outer clamping ring 6, then screw 8 sequentially passes through outer tube 1, outer clamping ring 6, inner tube 3 and most
It is bolted in interior clamping ring 7 eventually, in this way, the combination installation of pipeline body 4 and flange connection 9 is simple.
Finally, it should be noted that the foregoing is only a preferred embodiment of the present invention, it is not intended to restrict the invention,
Although the present invention is described in detail referring to the foregoing embodiments, for those skilled in the art, still may be used
To modify the technical solutions described in the foregoing embodiments or equivalent replacement of some of the technical features,
All within the spirits and principles of the present invention, any modification, equivalent replacement, improvement and so on should be included in of the invention
Within protection scope.
Claims (5)
1. a kind of pump valve pipeline with heat insulation function, including pipeline body (4), it is characterised in that: pipeline body (4) packet
The inner tube (3) being arranged from the inside to the outside, insulating tube (2) and outer tube (1) are included, the both ends of the pipeline body (4) pass through screw
(8) it is connected with flange connection (9), the flange connection (9) includes ring flange (5), the side of the ring flange (5)
Interior clamping ring (7) and outer clamping ring (6) are equipped in the middle part of side, the outer clamping ring (6) is plugged in outer tube (1) and inner tube (3)
Between gap in, the inner tube (3) is plugged in the inserting groove (10) between interior clamping ring (7) and outer clamping ring (6).
2. a kind of pump valve pipeline with heat insulation function according to claim 1, it is characterised in that: the ring flange (5)
It is integrally formed with interior clamping ring (7) and outer clamping ring (6), the interior clamping ring (7) and outer clamping ring (6) axle center are in same
On straight line, and interior clamping ring (7) is located at outer clamping ring (6) inside.
3. a kind of pump valve pipeline with heat insulation function according to claim 1, it is characterised in that: the screw (8) according to
It is secondary to run through outer tube (1), outer clamping ring (6), inner tube (3) and be finally bolted in interior clamping ring (7), and screw (8) is equidistantly set
It is placed in a circle of outer tube (1).
4. a kind of pump valve pipeline with heat insulation function according to claim 1, it is characterised in that: the insulating tube (2)
Constituent and each ingredient shared by mass fraction be respectively as follows: 58~70 parts of PET resin, 15~25 parts of polyvinylidene fluoride,
13~22 parts of polymethyl methacrylate, 16-23 parts of combined polyether glycol, 2~3 parts of foam stabilizer, 1~3 part of foaming agent and more
100~130 parts of isocyanates.
5. a kind of preparation method of the pump valve pipeline described in claim 1 with heat insulation function, it is characterised in that: specifically include
Following steps:
S1, by load weighted PET resin, polyvinylidene fluoride, polymethyl methacrylate, combined polyether glycol, foam stabilizer,
In foaming agent and polyisocyanates investment mixing kettle, 30~60min of stirring to acquisition mixture A after mixing;
S2, mixture A is heated to 25~28 DEG C, is filled into outer tube (1) and inner tube after mixing through high pressure foaming machine
(3) in the gap between, so that mixture A is carried out free pressure foaming in closed space, formed insulating tube (2), thus made
Complete pipeline body (4);
S3, outer clamping ring (6) is plugged in the gap between outer tube (1) and inner tube (3), while makes inner tube (3)
It is plugged in the inserting groove (10) between interior clamping ring (7) and outer clamping ring (6), then screw (8) sequentially passes through outer tube
(1), it outer clamping ring (6), inner tube (3) and is finally bolted in interior clamping ring (7), completes pipeline body (4) and flanged joint knot
The combination of structure (9) is installed.