Background technique
Currently, with the rapid development of our country's economy, Process of Urbanization Construction needs a large amount of building cementing material product, water
Cement concrete is 21st century most important construction material.China annual new building about 16-21m2, such as high speed public affairs
The infrastructure constructions such as road, high-speed railway, bridge, tunnel, subway are larger.Large-scale construction needs a large amount of cement mixed
Solidifying soil material, and manufacture of cement will consume a large amount of natural non-renewable resources and the energy, 1 ton of portland cement of every production are ripe
Material needs to consume 1.5 tons of fat lime stone, clay resource, consumes 0.15 ton of coal, co is discharged into atmosphere2And so2About 1.6 tons of gas
Equal pernicious gases, cause global warming problem by the common concern of whole world various countries.The cement industry of height consumption, high pollution
Aggravate the pressure of the energy resource and environment to society.And thermal power plants are after being generated electricity using a large amount of energy coal at present
A large amount of waste residue clinker is discharged, and pile up like a mountain, only makees general maintenance road etc. and uses, attached value is low, dosage is low, the benefit less than 20%
With rate.So the present invention produces a kind of cementitious material product using advanced technical matters, directly substitutes cement products and be used in
There is the processing method of concrete utilization rate to be up to 100%, and attached value is high, have a kind of energy-saving and environment-friendly utilization Industry Waste slag hearth
The method that slag produces novel gelled material is that the present invention to be solved the problems, such as to economize on resources and the energy and environmental pollution.
Summary of the invention
To the above problem of the prior art, Novel glue is produced using industrial residue clinker the object of the present invention is to provide a kind of
The processing method of gel material product has advanced technical matters, and low energy consumption, and attached value is high, using clinker 100%, without secondary dirt
The characteristics of dye, the protection for being conducive to economize on resources with the energy and environment.
The technical solution adopted by the present invention is that: the processing method of novel gelled material of the present invention, processing method
Include the following steps:
1, it stocks up: using the industrial residue clinker being discharged after the power generation of power plant's coal, adding auxiliary material tailing rejectable waste and make
Paper plant's waste residue calcium lignosulfonate;
2, ingredient: being 100% by industrial residue clinker count by weight percentage, and the tailing for being subject to total weight calculation outside, which is got a foothold, to give up
Expect 1-2% and waste residue calcium lignosulfonate 0.5-1%;
3, grinding: the mixture prepared feeding flour mill be finely ground into specific surface area up to 450-700m2The novel gelling of/kg
Material, abbreviation cementitious material;
4, cementitious material purposes and dosage and technical indicator;By the direct 100% substitution cement products of the novel gelled material being finely ground into
Industry and civilian equal architectural engineerings construction materials are widely used in for concrete batching.Technical indicator reaches following standard: comparing table
Area >=450-700m2/ kg, compatibility >=180mm, pre-hardening work >=45 minute, final set≤480 minute, sulfur trioxide≤4.0%,
Chloride ion≤0.06%, 32.5,42.5,52.5 grades of intensity values are distinguished flexural strength 3 days are as follows: 3.5mpa, 4.0mpa, 4.5mpa, 28
It are as follows: 6.0mpa, 6.5mpa, 7.0mpa;It is anti-to suppress intensity 3 days are as follows: 16.0mpa, 19.0mpa, 22.0mpa, to be within 28 days
32.5mpa、42.5mpa、52.5mpa。
The effect that the present invention obtains is:
1, novel gelled material product produced by the invention, can direct 100% substitution cement products to be used in concrete batching extensive
Materials are built for industry and civilian equal architectural engineerings, effect is better than the quality requirement of same cement products, improves concrete
The features such as service performance, compatibility is big, and water requirement is few, and intensity is high, economizes on electricity, the useless rate 100% of benefit, production cost is low;
2, product of the present invention is that the industrial residue clinker being discharged using power plant solves outlet, provides a new technology wound
New product protects environment not by secondary pollution, has saved natural resources lime stone, clay and coal for cement production enterprise 100%;
3, product of the present invention exploitation prospect is vast;
4, product of the present invention can be activated in 100% waste residue clinker using additional 1-2% tailing rejectable waste and 0.5-1% waste residue calcium lignosulfonate
Mineral composition, decomposition rate is fast, induction crystalline polymeric precipitability accelerate, and reduce dissolution in ion concentration increase than table
Grain rate of dispersion, so as to form the mineral composition ingredient of the cement cementitious material equal with cement products.Be conducive to Novel glue
The advanced hydration reaction of gel material.
Embodiment 2
Novel gelled material product preparation method is raw material using the industrial residue clinker being discharged after the power generation of power plant coal,
It is count by weight percentage 100%, additional tailing rejectable waste is calculated as 2% by total weight percent, additional paper mill sludge
Calcium lignosulfonate is calculated as 1% by total weight percent, is sent into flour mill through mixing and carries out being finely ground into specific surface area >=450-700m2/kg
Novel gelled material, direct 100% substitution cement products configuration concrete uses for industry and civilian equal architectural engineerings construction
Material, through detecting cementitious material quality index are as follows: specific surface area 705m2/ kg, compatibility 315mm, initial set 125 minutes, final set 209
Minute, sulfur trioxide 2.92%, chloride ion 0.016%, 3 days 5.6mpa of flexural strength, 28 days 8.8mpa, compression strength 3 days
25.2mpa, 28 days 55.1mpa.
Embodiment described above only technical thought and feature to illustrate the invention, its object is to be familiar with personnel of the invention
It will appreciate that its content and pay in implementation, the protection scope of the technology of the present invention, all technologies according to the present invention etc. can not be limited with this
It imitates system or modification is all covered in the protection scope of the technology of the present invention.