CN109294352A - A kind of automatically cleaning water-based fluorocarbon building coating and preparation method - Google Patents
A kind of automatically cleaning water-based fluorocarbon building coating and preparation method Download PDFInfo
- Publication number
- CN109294352A CN109294352A CN201811104595.XA CN201811104595A CN109294352A CN 109294352 A CN109294352 A CN 109294352A CN 201811104595 A CN201811104595 A CN 201811104595A CN 109294352 A CN109294352 A CN 109294352A
- Authority
- CN
- China
- Prior art keywords
- weight
- parts
- water
- agent
- solution
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The present invention provides a kind of automatically cleaning water-based fluorocarbon building coating and preparation methods.Nano silica glue liquid, silane coupling agent, alcohol, surfactant, alumine hydroxide colloid are mixed to prepare nano silica latex A, by hydroxyethyl cellulose obtained solution B soluble in water, wetting dispersing agent, latex A are mixed to prepare solution C, inorganic filler is added after solution B, solution C, inorganic pigment and water are mixed, slurry D is made, it is finally uniformly mixed with wetting dispersing agent, defoaming agent, fungicide, water-base fluorocarbon emulsion, coalescing agent, thickener, water, automatically cleaning water-based fluorocarbon building coating is made.This method is dispersed in water and coating hydrophobic type particle with surfactant, is combined with aqueous fluorocarbon coating, is greatly improved the optical property, anti-aging property and washing fastness of fluorocarbon coating, good hydrophilic property has excellent self-cleaning.
Description
Technical field
The present invention relates to paint fields, and in particular to the preparation of water paint, more particularly to a kind of aqueous fluorine of automatically cleaning
Carbon building coating and preparation method.
Background technique
Traditional solvent type coating contains a large amount of organic volatile (abbreviation VOC) during its manufacture and use, gives ring
Border brings more or less pollution and destruction, causes damage to human body.The development of coating is constantly improving human material's life
While production, life requirement, also deteriorate environment rapidly.Resin used in water paint is synthesized by carrier of water, at present
It is widely applied to have water-borne acrylic coatings, aqueous polyurethane coating etc..Compared with solvent based coating, it the biggest advantage is to
VOC content is lower, free from extraneous odour, does not burn and toxicity is low, but its there is also water resistances and poor solvent resistance, hardness low, gloss and
The disadvantages of richness difference and slow drying speed and weak substrate adhesive force.
In recent years, fluorocarbon coating be widely used in building, anti-corrosion, highway, railroad bridge, vehicular traffic, ship and
The fields such as ocean engineering facility have great application value.Fluorocarbon coating is primarily referred to as with pure fluororesin or by modified
Fluororesin be main film forming substance the coating with specific function, show brilliant pair thin property, weatherability, durability,
Resistance to acid and alkali, rotproofness, insulating properties and non-adhesive etc. are a kind of outstanding new special coating.
Chinese invention patent application number 201610954435.9 discloses a kind of preparation side of automatically cleaning aqueous fluorocarbon coating
Method belongs to technical field of paint preparation.The invention is first with butyl titanate, acetylacetone,2,4-pentanedione ethanol solution, ethyl orthosilicate etc.
It is mixed to prepare colloidal sol, is then aged filtering, gained filter residue is made through drying, grinding, calcining through SiO2Modifying titanium dioxide
Nano-powder, then double thinization processing are carried out to it by tridecafluoro-n-octyltriethoxysilane, finally by water-base fluorocarbon emulsion tree
Rouge, talcum powder, double thinization processing modifying titanium dioxides and auxiliary agent are uniformly mixed, that is, are available from clean water fluorocarbon coating.
Chinese invention patent application number 200610029160.4 discloses a kind of lotus leaf effect self cleaning fluorocarbon paint.It should be certainly
Fluorocarbon coating is cleaned mainly by organic-silicon-modified fluorocarbon resin, curing agent, hydrophobic particles, pigment, filler, auxiliary agent and solvent group
At.The weight ratio of each component is organic-silicon-modified fluororesin: curing agent: hydrophobic particles: pigment: filler: auxiliary agent: mixed solvent=
1:0.1~0.3:0.03~0.1:0~0.35:0~0.1:0.01~0.05:0.1~0.3。
Chinese invention patent application number 201710977587.5 discloses a kind of preparation method of self-cleaning fluorocarbon paint.The hair
The silicon fluoride of bright middle hydrolysis is mixed with titanium dioxide and high speed dispersion, obtains the modified titania nanoparticles in surface, then
Varnish mixes with carbon nanotubes dispersion liquid, micro- solidification obtains self-cleaning fluorocarbon paint, and silicon fluoride is by titanium dioxide granule and fluorine carbon tree
The combination of rouge increases, and silicon fluoride molecule hydrolyzes in acid condition, and due to hydrogen bond action, the silicon fluoride molecule after hydrolysis is inhaled
Be attached to titania nanoparticles surface, the carbochain in silicon fluoride molecule due to the protection by fluorine original physical barrier effect, other
Atom is not easy to invade, so silicon fluoride has good chemical stability and low surface free energy, silicon fluoride surface coating layer subtracts
Small TiO2Effect of the nano particle to the Van der Waals force and hydrogen bond of water greatly increases the contact angle of surface of the paint film, to show
Super-hydrophobicity out can significantly improve stain resistant, have a extensive future.
Chinese invention patent application number 200610029163.8 discloses a kind of self cleaning fluorocarbon resin paint and its preparation
Method.Key step includes: that diisocyanate is first reacted to the polyethyleneglycol for adding metering to a certain extent with trihydroxylic alcohol
Ether react the diisocyanate of obtained branched modification, then reacts modifying diisocyanates with fluorocarbon resin, in fluorine carbon
Hydrophilic molecules group is introduced on resin, obtains a kind of self cleaning fluorocarbon resin.The self cleaning fluorocarbon resin is matched according to a conventional method
Coating is made, hydrophilic molecules group is migrated to coating surface after construction, makes film coated surface hydrophiling, to have automatically cleaning
Function;Fluorocarbon resin forms fine and close film in coating bottom simultaneously, prevents pollutant from entering inside film with rainwater and is formed permanently
Pollution.
According to above-mentioned, the fluorocarbon coating in existing scheme is based on solvent type, containing toluene in coating, dimethylbenzene and ethylbenzene
The substance that equal organic solvents and free vulcabond etc. are harmful to the human body, product is in production and transport and storage process
Fire protection requirement is very strict, and the man power and material of investment is higher, and such coating self-cleaning function is poor.
Summary of the invention
Do not have self-cleaning function for the wider aqueous fluorocarbon coating of current application, resistance to soiling and antibiotic property are poor, shape
It is poor at paint film wearability, and the toxic solvent contained in coating at branch to the hurtful defect of human body environment, the present invention
A kind of automatically cleaning water-based fluorocarbon building coating and preparation method are proposed, to significantly improve the optical property of fluorocarbon coating, anti-
While ageing properties, washability, and there is excellent self-cleaning function.
Specific technical solution of the present invention is as follows:
A kind of preparation method of automatically cleaning water-based fluorocarbon building coating, comprising the following steps:
(1) nano silica is dispersed in water, glue is made, water-soluble alcohol is then added, added silane coupled
Then surfactant, alumine hydroxide colloid is added at hydrophobic particulate in dosage form, form coating film, and nano silica cream is made
Liquid A;
(2) hydroxyethyl cellulose is soluble in water, obtained solution B;
(3) wetting dispersing agent, latex A are uniformly mixed, obtained solution C;
(4) solution B, solution C, inorganic pigment and water are uniformly mixed at room temperature, slurry is made in the inorganic filler after grinding is added
Expect D;
(5) under stirring, wetting dispersing agent is added again into slurry D, and newborn with defoaming agent, fungicide, water-based fluorocarbon
Liquid, coalescing agent, thickener, water are uniformly mixed, and automatically cleaning water-based fluorocarbon building coating is made.
Preferably, in step (1) the nano silica latex A, 15 ~ 20 parts by weight of nano silica, water 47 ~ 62
Parts by weight, 5 ~ 8 parts by weight of water-soluble alcohol, 3 ~ 5 parts by weight of silane coupling agent, 3 ~ 5 parts by weight of surfactant, aluminium hydroxide
12 ~ 15 parts by weight of colloid.
Preferably, in step (2) described solution B, 20 ~ 30 parts by weight of hydroxyethyl cellulose, 70 ~ 80 parts by weight of water.
Preferably, in step (3) described solution C, 2 ~ 5 parts by weight of wetting dispersing agent, nano silica latex A 75 ~ 93
Parts by weight.
Preferably, in step (4) the slurry D, 10 ~ 20 parts by weight of solution B, 25 ~ 35 parts by weight of solution C, inorganic face
Expect 2 ~ 4 parts by weight, 31 ~ 58 parts by weight of water, 5 ~ 10 parts by weight of inorganic filler.
Preferably, in step (5) described building coating, 30 ~ 40 parts by weight of slurry D, disappear at 1 ~ 2 parts by weight of wetting dispersing agent
1 ~ 2 parts by weight of infusion, 1 ~ 3 parts by weight of fungicide, 3 ~ 8 parts by weight of water-base fluorocarbon emulsion, 1 ~ 2 parts by weight of coalescing agent, thickener 1
~ 2 parts by weight, 36 ~ 60 parts by weight of water.The mass concentration of the water-base fluorocarbon emulsion is 15%.
Preferably, water-soluble alcohol is at least one of methanol, ethyl alcohol, propyl alcohol.
Preferably, the silane coupling agent be gamma-aminopropyl-triethoxy-silane, γ-aminopropyltrimethoxysilane,
At least one of γ-mercaptopropyl trimethoxysilane, γ-methacryloxypropyl trimethoxy silane.
Preferably, the surfactant is sodium alkyl sulfonate, sodium alkyl benzene sulfonate, at least one in Negel
Kind.
Preferably, the wetting dispersing agent is sodium methylene bis-naphthalene sulfonate, dispersing agent MF, polyethylene glycol
At least one of.
Preferably, the inorganic pigment is at least one of rutile titanium white, iron oxide yellow, iron oxide red.
Preferably, the inorganic filler is at least one of sericite in powder, kaolin, powdered whiting.
Preferably, the defoaming agent is polyoxyethylene polyoxypropylene pentaerythrite ether, polyoxyethylene polyoxy propyl alcohol amidogen ether, gathers
At least one of oxypropylene glycerin ether.
Preferably, the fungicide be ambam, sulfonat, ziram, zineb, Mancozeb, in thiram extremely
Few one kind.
Preferably, the coalescing agent is ethylene glycol ether, ethylene glycol monobutyl ether, diethylene glycol monomethyl ether, diethyl two
Alcohol list ether, triethylene glycol monomethyl ether, propylene glycol monopropyl ether, propylene glycol spy butyl ether, tripropylene glycol dimethyl ether, ethylene glycol phenyl ether,
At least one of propylene glycol phenylate.
Preferably, the thickener is methylcellulose, hydroxypropyl methyl cellulose, sodium carboxymethylcellulose, ethoxy
At least one of cellulose.
The present invention also provides a kind of automatically cleaning water-based fluorocarbon building coatings that above-mentioned preparation method is prepared.In nanometer two
Water-soluble alcohol is added in the colloidal solution of silica in water, adds with the silane coupled of hydrophilic and oleophilic both sexes structure
The group of agent, molecule one end can react to form firm chemical bond with the silanol group of nano silicon dioxide, another group
Then there is lipophilicity.Nano silica and silane coupling agent is set to be combined into a kind of hydrophobic particulate, adding is suitable for producing water
The surfactant and alumine hydroxide colloid of packet fat liquor, make lipophilic group one end of surfactant be adsorbed on it is silane coupled
On the hydrophobic nano nano silicon dioxide particles that agent reaction generates, a coating film is formed, can be preferably scattered in aqueous
In solvent, nano silica latex A is made;Then hydroxyethyl cellulose and water mixed dissolution are obtained into solution B;By wetting and dispersing
Agent and above-mentioned nano silica latex A are uniformly mixed obtained solution C;By solution B, solution C, inorganic pigment, filler and water in
It is uniformly mixed at room temperature, and slurry D is made in the inorganic filler being added after grinding;Finally under stirring, in slurry D again
Wetting dispersing agent, defoaming agent and fungicide, water-base fluorocarbon emulsion, coalescing agent, thickener, water is added, is mixed evenly, obtains
To product.
The present invention provides a kind of automatically cleaning water-based fluorocarbon building coating and preparation methods, compared with prior art, dash forward
Out the characteristics of and excellent effect are:
1, it proposes to form the method that hydrophobic type particle prepares automatically cleaning water-based fluorocarbon building coating.
2, by alumine hydroxide colloid being further added, makes nanometer with silane coupler modified nanometer titanium dioxide silicon emulsion
Nano silica and the silane coupling agent are combined into a kind of hydrophobic type particle, then by hydrophobic type particle surfactant packet
Cover and be dispersed in water, combined with aqueous fluorocarbon coating, greatly improve the optical property of fluorocarbon coating, anti-aging property and
Washing fastness.
3, water-based fluorocarbon building coating produced by the present invention has excellent self-cleaning.
Specific embodiment
In the following, the present invention will be further described in detail by way of specific embodiments, but this should not be interpreted as to the present invention
Range be only limitted to example below.Without departing from the idea of the above method of the present invention, according to ordinary skill
The various replacements or change that knowledge and customary means are made, should be included in the scope of the present invention.
Embodiment 1
Preparation process are as follows:
(1) nano silica is dispersed in water, glue is made, water-soluble alcohol is then added, added silane coupled
Then surfactant, alumine hydroxide colloid is added at hydrophobic particulate in dosage form, form coating film, and nano silica cream is made
Liquid A;In nano silica latex A, 17 parts by weight of nano silica, 55 parts by weight of water, 7 parts by weight of water-soluble alcohol,
4 parts by weight of silane coupling agent, 4 parts by weight of surfactant, 13 parts by weight of alumine hydroxide colloid;
(2) hydroxyethyl cellulose is soluble in water, obtained solution B;In solution B, 26 parts by weight of hydroxyethyl cellulose, 74 weight of water
Part;
(3) wetting dispersing agent, nano silica latex A are uniformly mixed, obtained solution C;In solution C, 3 weight of wetting dispersing agent
Measure part, 86 parts by weight of nano silica latex A;
(4) solution B, solution C, inorganic pigment and water are uniformly mixed at room temperature, slurry is made in the inorganic filler after grinding is added
Expect D;In slurry D, 16 parts by weight of solution B, 29 parts by weight of solution C, 3 parts by weight of inorganic pigment, 45 parts by weight of water, inorganic filler
7 parts by weight;
(5) under stirring, wetting dispersing agent is added again into slurry D, and newborn with defoaming agent, fungicide, water-based fluorocarbon
Liquid, coalescing agent, thickener, water are uniformly mixed, and automatically cleaning water-based fluorocarbon building coating is made;In building coating, slurry D 36
Parts by weight, 1 parts by weight of wetting dispersing agent, 1 parts by weight of defoaming agent, 2 parts by weight of fungicide, 5 parts by weight of water-base fluorocarbon emulsion, film forming
1 parts by weight of auxiliary agent, 2 parts by weight of thickener, 49 parts by weight of water;The mass concentration of the water-base fluorocarbon emulsion is 15%.
Water-soluble alcohol is methanol;Silane coupling agent is gamma-aminopropyl-triethoxy-silane;Surfactant is alkyl
Sodium sulfonate;Wetting dispersing agent is sodium methylene bis-naphthalene sulfonate;Inorganic pigment is rutile titanium white;Inorganic filler is sericite in powder;
Defoaming agent is polyoxyethylene polyoxypropylene pentaerythrite ether;Fungicide is ambam;Coalescing agent is ethylene glycol ether;Thickening
Agent is methylcellulose.
Embodiment 2
Preparation process are as follows:
(1) nano silica is dispersed in water, glue is made, water-soluble alcohol is then added, added silane coupled
Then surfactant, alumine hydroxide colloid is added at hydrophobic particulate in dosage form, form coating film, and nano silica cream is made
Liquid A;In nano silica latex A, 15 parts by weight of nano silica, 62 parts by weight of water, 5 parts by weight of water-soluble alcohol,
3 parts by weight of silane coupling agent, 3 parts by weight of surfactant, 12 parts by weight of alumine hydroxide colloid;
(2) hydroxyethyl cellulose is soluble in water, obtained solution B;In solution B, 20 parts by weight of hydroxyethyl cellulose, 80 weight of water
Part;
(3) wetting dispersing agent, nano silica latex A are uniformly mixed, obtained solution C;In solution C, 2 weight of wetting dispersing agent
Measure part, 93 parts by weight of nano silica latex A;
(4) solution B, solution C, inorganic pigment and water are uniformly mixed at room temperature, slurry is made in the inorganic filler after grinding is added
Expect D;In slurry D, 10 parts by weight of solution B, 25 parts by weight of solution C, 2 parts by weight of inorganic pigment, 58 parts by weight of water, inorganic filler
5 parts by weight;
(5) under stirring, wetting dispersing agent is added again into slurry D, and newborn with defoaming agent, fungicide, water-based fluorocarbon
Liquid, coalescing agent, thickener, water are uniformly mixed, and automatically cleaning water-based fluorocarbon building coating is made;In building coating, slurry D 30
Parts by weight, 1 parts by weight of wetting dispersing agent, 1 parts by weight of defoaming agent, 1 parts by weight of fungicide, 3 parts by weight of water-base fluorocarbon emulsion, film forming
1 parts by weight of auxiliary agent, 1 parts by weight of thickener, 60 parts by weight of water;The mass concentration of the water-base fluorocarbon emulsion is 15%.
Water-soluble alcohol is ethyl alcohol;Silane coupling agent is γ-aminopropyltrimethoxysilane;Surfactant is alkyl
Benzene sulfonic acid sodium salt;Wetting dispersing agent is dispersing agent MF;Inorganic pigment is iron oxide yellow;Inorganic filler is kaolinite
Soil;Defoaming agent is polyoxyethylene polyoxy propyl alcohol amidogen ether;Fungicide is sulfonat;Coalescing agent is ethylene glycol monobutyl ether;Thickener
For hydroxypropyl methyl cellulose.
Embodiment 3
Preparation process are as follows:
(1) nano silica is dispersed in water, glue is made, water-soluble alcohol is then added, added silane coupled
Then surfactant, alumine hydroxide colloid is added at hydrophobic particulate in dosage form, form coating film, and nano silica cream is made
Liquid A;In nano silica latex A, 20 parts by weight of nano silica, 47 parts by weight of water, 8 parts by weight of water-soluble alcohol,
5 parts by weight of silane coupling agent, 5 parts by weight of surfactant, 15 parts by weight of alumine hydroxide colloid;
(2) hydroxyethyl cellulose is soluble in water, obtained solution B;In solution B, 30 parts by weight of hydroxyethyl cellulose, 70 weight of water
Part;
(3) wetting dispersing agent, nano silica latex A are uniformly mixed, obtained solution C;In solution C, 5 weight of wetting dispersing agent
Measure part, 75 parts by weight of nano silica latex A;
(4) solution B, solution C, inorganic pigment and water are uniformly mixed at room temperature, slurry is made in the inorganic filler after grinding is added
Expect D;In slurry D, 20 parts by weight of solution B, 35 parts by weight of solution C, 4 parts by weight of inorganic pigment, 31 parts by weight of water, inorganic filler
10 parts by weight;
(5) under stirring, wetting dispersing agent is added again into slurry D, and newborn with defoaming agent, fungicide, water-based fluorocarbon
Liquid, coalescing agent, thickener, water are uniformly mixed, and automatically cleaning water-based fluorocarbon building coating is made;In building coating, slurry D 40
Parts by weight, 2 parts by weight of wetting dispersing agent, 2 parts by weight of defoaming agent, 3 parts by weight of fungicide, 8 parts by weight of water-base fluorocarbon emulsion, film forming
2 parts by weight of auxiliary agent, 2 parts by weight of thickener, 36 parts by weight of water;The mass concentration of the water-base fluorocarbon emulsion is 15%.
Water-soluble alcohol is propyl alcohol;Silane coupling agent is γ-mercaptopropyl trimethoxysilane;Surfactant is alkyl
Sodium naphthalene sulfonate;Wetting dispersing agent is polyethylene glycol;Inorganic pigment is iron oxide red;Inorganic filler is powdered whiting;Defoaming agent
For polypropylene glycerol aether;Fungicide is ziram;Coalescing agent is diethylene glycol monomethyl ether;Thickener is carboxymethyl cellulose
Sodium.
Embodiment 4
Preparation process are as follows:
(1) nano silica is dispersed in water, glue is made, water-soluble alcohol is then added, added silane coupled
Then surfactant, alumine hydroxide colloid is added at hydrophobic particulate in dosage form, form coating film, and nano silica cream is made
Liquid A;In nano silica latex A, 16 parts by weight of nano silica, 58 parts by weight of water, 6 parts by weight of water-soluble alcohol,
4 parts by weight of silane coupling agent, 3 parts by weight of surfactant, 13 parts by weight of alumine hydroxide colloid;
(2) hydroxyethyl cellulose is soluble in water, obtained solution B;In solution B, 22 parts by weight of hydroxyethyl cellulose, 78 weight of water
Part;
(3) wetting dispersing agent, nano silica latex A are uniformly mixed, obtained solution C;In solution C, 3 weight of wetting dispersing agent
Measure part, 87 parts by weight of nano silica latex A;
(4) solution B, solution C, inorganic pigment and water are uniformly mixed at room temperature, slurry is made in the inorganic filler after grinding is added
Expect D;In slurry D, 12 parts by weight of solution B, 27 parts by weight of solution C, 3 parts by weight of inorganic pigment, 52 parts by weight of water, inorganic filler
6 parts by weight;
(5) under stirring, wetting dispersing agent is added again into slurry D, and newborn with defoaming agent, fungicide, water-based fluorocarbon
Liquid, coalescing agent, thickener, water are uniformly mixed, and automatically cleaning water-based fluorocarbon building coating is made;In building coating, slurry D 32
Parts by weight, 1 parts by weight of wetting dispersing agent, 1 parts by weight of defoaming agent, 2 parts by weight of fungicide, 4 parts by weight of water-base fluorocarbon emulsion, film forming
1 parts by weight of auxiliary agent, 1 parts by weight of thickener, 55 parts by weight of water;The mass concentration of the water-base fluorocarbon emulsion is 15%.It is water-soluble
Alcohol be methanol;Silane coupling agent is γ-methacryloxypropyl trimethoxy silane;Surfactant is alkyl sulfonic acid
Sodium;Wetting dispersing agent is sodium methylene bis-naphthalene sulfonate;Inorganic pigment is rutile titanium white;Inorganic filler is sericite in powder;Defoaming
Agent is polyoxyethylene polyoxypropylene pentaerythrite ether;Fungicide is zineb;Coalescing agent is diethylene glycol monoethyl ether;Thickener
For hydroxyethyl cellulose.
Embodiment 5
Preparation process are as follows:
(1) nano silica is dispersed in water, glue is made, water-soluble alcohol is then added, added silane coupled
Then surfactant, alumine hydroxide colloid is added at hydrophobic particulate in dosage form, form coating film, and nano silica cream is made
Liquid A;In nano silica latex A, 18 parts by weight of nano silica, 52 parts by weight of water, 7 parts by weight of water-soluble alcohol,
5 parts by weight of silane coupling agent, 4 parts by weight of surfactant, 14 parts by weight of alumine hydroxide colloid;
(2) hydroxyethyl cellulose is soluble in water, obtained solution B;In solution B, 27 parts by weight of hydroxyethyl cellulose, 73 weight of water
Part;
(3) wetting dispersing agent, nano silica latex A are uniformly mixed, obtained solution C;In solution C, 4 weight of wetting dispersing agent
Measure part, 80 parts by weight of nano silica latex A;
(4) solution B, solution C, inorganic pigment and water are uniformly mixed at room temperature, slurry is made in the inorganic filler after grinding is added
Expect D;In slurry D, 17 parts by weight of solution B, 33 parts by weight of solution C, 4 parts by weight of inorganic pigment, 37 parts by weight of water, inorganic filler
9 parts by weight;
(5) under stirring, wetting dispersing agent is added again into slurry D, and newborn with defoaming agent, fungicide, water-based fluorocarbon
Liquid, coalescing agent, thickener, water are uniformly mixed, and automatically cleaning water-based fluorocarbon building coating is made;In building coating, slurry D 37
Parts by weight, 2 parts by weight of wetting dispersing agent, 2 parts by weight of defoaming agent, 2 parts by weight of fungicide, 7 parts by weight of water-base fluorocarbon emulsion, film forming
2 parts by weight of auxiliary agent, 2 parts by weight of thickener, 42 parts by weight of water;The mass concentration of the water-base fluorocarbon emulsion is 15%.
Water-soluble alcohol is ethyl alcohol;Silane coupling agent is γ-aminopropyltrimethoxysilane;Surfactant is alkyl
Benzene sulfonic acid sodium salt;Wetting dispersing agent is dispersing agent MF;Inorganic pigment is iron oxide yellow;Inorganic filler is kaolinite
Soil;Defoaming agent is polyoxyethylene polyoxy propyl alcohol amidogen ether;Fungicide is Mancozeb;Coalescing agent is triethylene glycol monomethyl ether;Increase
Thick dose is methylcellulose.
Embodiment 6
Preparation process are as follows:
(1) nano silica is dispersed in water, glue is made, water-soluble alcohol is then added, added silane coupled
Then surfactant, alumine hydroxide colloid is added at hydrophobic particulate in dosage form, form coating film, and nano silica cream is made
Liquid A;In nano silica latex A, 18 parts by weight of nano silica, 54 parts by weight of water, 6 parts by weight of water-soluble alcohol,
4 parts by weight of silane coupling agent, 4 parts by weight of surfactant, 14 parts by weight of alumine hydroxide colloid;
(2) hydroxyethyl cellulose is soluble in water, obtained solution B;In solution B, 25 parts by weight of hydroxyethyl cellulose, 75 weight of water
Part;
(3) wetting dispersing agent, nano silica latex A are uniformly mixed, obtained solution C;In solution C, 4 weight of wetting dispersing agent
Measure part, 84 parts by weight of nano silica latex A;
(4) solution B, solution C, inorganic pigment and water are uniformly mixed at room temperature, slurry is made in the inorganic filler after grinding is added
Expect D;In slurry D, 15 parts by weight of solution B, 30 parts by weight of solution C, 3 parts by weight of inorganic pigment, 44 parts by weight of water, inorganic filler
8 parts by weight;
(5) under stirring, wetting dispersing agent is added again into slurry D, and newborn with defoaming agent, fungicide, water-based fluorocarbon
Liquid, coalescing agent, thickener, water are uniformly mixed, and automatically cleaning water-based fluorocarbon building coating is made;In building coating, slurry D 35
Parts by weight, 1 parts by weight of wetting dispersing agent, 1 parts by weight of defoaming agent, 2 parts by weight of fungicide, 6 parts by weight of water-base fluorocarbon emulsion, film forming
1 parts by weight of auxiliary agent, 2 parts by weight of thickener, 48 parts by weight of water;The mass concentration of the water-base fluorocarbon emulsion is 15%.
Water-soluble alcohol is propyl alcohol;Silane coupling agent is γ-mercaptopropyl trimethoxysilane;Surfactant is alkyl
Sodium naphthalene sulfonate;Wetting dispersing agent is polyethylene glycol;Inorganic pigment is iron oxide red;Inorganic filler is powdered whiting;Defoaming agent
For polypropylene glycerol aether;Fungicide is thiram;Coalescing agent is propylene glycol spy butyl ether;Thickener is hydroxypropyl methyl fiber
Element.
Comparative example 1
Preparation process are as follows:
(1) nano silica is dispersed in water, glue is made, water-soluble alcohol is then added, added silane coupled
Then surfactant is added at hydrophobic particulate in dosage form, nano silica latex A is made;In nano silica latex A,
18 parts by weight of nano silica, 54 parts by weight of water, 6 parts by weight of water-soluble alcohol, 4 parts by weight of silane coupling agent, surface are living
Property 4 parts by weight of agent;
(2) hydroxyethyl cellulose is soluble in water, obtained solution B;In solution B, 25 parts by weight of hydroxyethyl cellulose, 75 weight of water
Part;
(3) wetting dispersing agent, nano silica latex A are uniformly mixed, obtained solution C;In solution C, 4 weight of wetting dispersing agent
Measure part, 84 parts by weight of nano silica latex A;
(4) solution B, solution C, inorganic pigment and water are uniformly mixed at room temperature, slurry is made in the inorganic filler after grinding is added
Expect D;In slurry D, 15 parts by weight of solution B, 30 parts by weight of solution C, 3 parts by weight of inorganic pigment, 44 parts by weight of water, inorganic filler
8 parts by weight;
(5) under stirring, wetting dispersing agent is added again into slurry D, and newborn with defoaming agent, fungicide, water-based fluorocarbon
Liquid, coalescing agent, thickener, water are uniformly mixed, and automatically cleaning water-based fluorocarbon building coating is made;In building coating, slurry D 35
Parts by weight, 1 parts by weight of wetting dispersing agent, 1 parts by weight of defoaming agent, 2 parts by weight of fungicide, 6 parts by weight of water-base fluorocarbon emulsion, film forming
1 parts by weight of auxiliary agent, 2 parts by weight of thickener, 48 parts by weight of water;The mass concentration of the water-base fluorocarbon emulsion is 15%.
Water-soluble alcohol is propyl alcohol;Silane coupling agent is γ-mercaptopropyl trimethoxysilane;Surfactant is alkyl
Sodium naphthalene sulfonate;Wetting dispersing agent is polyethylene glycol;Inorganic pigment is iron oxide red;Inorganic filler is powdered whiting;Defoaming agent
For polypropylene glycerol aether;Fungicide is thiram;Coalescing agent is propylene glycol spy butyl ether;Thickener is hydroxypropyl methyl fiber
Element.
Comparative example 1 does not handle nano silica using alumine hydroxide colloid.
Test method are as follows:
By coating even application made from embodiment 1-6, comparative example 1 in concrete surface, coating average thickness is 0.25mm, is adopted
Measure water contact angle and oily contact angle respectively with contact angle tester, then sample impregnates 8h in water, forced air drying after taking-up,
It is recycled as one, tests water contact angle and oily contact angle after circulation 10 times again.As shown in table 1.
Table 1:
Claims (8)
1. a kind of preparation method of automatically cleaning water-based fluorocarbon building coating, which comprises the following steps:
(1) nano silica is dispersed in water, glue is made, water-soluble alcohol is then added, added silane coupled
Then surfactant, alumine hydroxide colloid is added at hydrophobic particulate in dosage form, form coating film, and nano silica cream is made
Liquid A;
(2) hydroxyethyl cellulose is soluble in water, obtained solution B;
(3) wetting dispersing agent, nano silica latex A are uniformly mixed, obtained solution C;
(4) solution B, solution C, inorganic pigment and water are uniformly mixed at room temperature, slurry is made in the inorganic filler after grinding is added
Expect D;
(5) under stirring, wetting dispersing agent is added again into slurry D, and newborn with defoaming agent, fungicide, water-based fluorocarbon
Liquid, coalescing agent, thickener, water are uniformly mixed, and automatically cleaning water-based fluorocarbon building coating is made.
2. a kind of preparation method of automatically cleaning water-based fluorocarbon building coating according to claim 1, it is characterised in that: step
(1) in the nano silica latex A, 15 ~ 20 parts by weight of nano silica, 47 ~ 62 parts by weight of water, water-soluble alcohol
5 ~ 8 parts by weight, 3 ~ 5 parts by weight of silane coupling agent, 3 ~ 5 parts by weight of surfactant, 12 ~ 15 parts by weight of alumine hydroxide colloid.
3. a kind of preparation method of automatically cleaning water-based fluorocarbon building coating according to claim 1, it is characterised in that: step
(2) in the solution B, 20 ~ 30 parts by weight of hydroxyethyl cellulose, 70 ~ 80 parts by weight of water.
4. a kind of preparation method of automatically cleaning water-based fluorocarbon building coating according to claim 1, it is characterised in that: step
(3) in the solution C, 2 ~ 5 parts by weight of wetting dispersing agent, 75 ~ 93 parts by weight of nano silica latex A.
5. a kind of preparation method of automatically cleaning water-based fluorocarbon building coating according to claim 1, it is characterised in that: step
(4) in the slurry D, 10 ~ 20 parts by weight of solution B, 25 ~ 35 parts by weight of solution C, 2 ~ 4 parts by weight of inorganic pigment, water 31 ~ 58
Parts by weight, 5 ~ 10 parts by weight of inorganic filler.
6. a kind of preparation method of automatically cleaning water-based fluorocarbon building coating according to claim 1, it is characterised in that: step
(5) in the building coating, 30 ~ 40 parts by weight of slurry D, 1 ~ 2 parts by weight of wetting dispersing agent, 1 ~ 2 parts by weight of defoaming agent, sterilization
1 ~ 3 parts by weight of agent, 3 ~ 8 parts by weight of water-base fluorocarbon emulsion, 1 ~ 2 parts by weight of coalescing agent, 1 ~ 2 parts by weight of thickener, 36 ~ 60 weight of water
Measure part.
7. a kind of any one preparation method of automatically cleaning water-based fluorocarbon building coating, feature exist according to claim 1~6
In:
Water-soluble alcohol is at least one of methanol, ethyl alcohol, propyl alcohol;
The silane coupling agent is gamma-aminopropyl-triethoxy-silane, γ-aminopropyltrimethoxysilane, γ-mercapto propyl front three
At least one of oxysilane, γ-methacryloxypropyl trimethoxy silane;
The surfactant is at least one of sodium alkyl sulfonate, sodium alkyl benzene sulfonate, Negel;
The wetting dispersing agent is sodium methylene bis-naphthalene sulfonate, dispersing agent MF, at least one in polyethylene glycol
Kind;
The inorganic pigment is at least one of rutile titanium white, iron oxide yellow, iron oxide red;
The inorganic filler is at least one of sericite in powder, kaolin, powdered whiting;
The defoaming agent is polyoxyethylene polyoxypropylene pentaerythrite ether, polyoxyethylene polyoxy propyl alcohol amidogen ether, polyoxypropylene glyceryl
At least one of ether;
The fungicide is at least one of ambam, sulfonat, ziram, zineb, Mancozeb, thiram;
The coalescing agent is ethylene glycol ether, ethylene glycol monobutyl ether, diethylene glycol monomethyl ether, diethylene glycol monoethyl ether, three
Glycol monoethyl ether, propylene glycol monopropyl ether, propylene glycol spy butyl ether, tripropylene glycol dimethyl ether, ethylene glycol phenyl ether, in propylene glycol phenylate
At least one;
The thickener be methylcellulose, hydroxypropyl methyl cellulose, sodium carboxymethylcellulose, in hydroxyethyl cellulose extremely
Few one kind.
8. a kind of automatically cleaning water-based fluorocarbon building coating that any one of claim 1 ~ 7 preparation method is prepared.