CN1092793A - High-bright cold enamel paint - Google Patents
High-bright cold enamel paint Download PDFInfo
- Publication number
- CN1092793A CN1092793A CN 93102668 CN93102668A CN1092793A CN 1092793 A CN1092793 A CN 1092793A CN 93102668 CN93102668 CN 93102668 CN 93102668 A CN93102668 A CN 93102668A CN 1092793 A CN1092793 A CN 1092793A
- Authority
- CN
- China
- Prior art keywords
- parts
- resins
- solvent
- ethyl ketone
- epoxy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
High-bright cold enamel paint is a kind of senior porcelain-imitated coating of development newly, by synthetic resins, and colored filler, the bottom of solidifying agent and solvent composition and surface layer are formed, and its construction is simple, and has acid and alkali-resistance, water-fast washing, high rigidity and coating beautiful in colour are the desired decoration materials of modern architecture interior wall.
Description
The present invention relates to a kind of coating technology, be specially adapted to the decoration of inner wall of building.
Porcelain-imitated coating is better than general coating in performances such as hardness, glossiness and moisture-proof wipings, but compares with porcelain, and its hardness, glossiness and water-fast, corrosion resistance nature also differ bigger, and therefore to have the coating of porcelain performance be pressing for of building coating market in development.
A kind of building decorative coating of providing in order to realize having the coating of porcelain performance is provided.
The objective of the invention is to realize by following approach.A kind of high-bright cold enamel paint, by synthetic resins, colored filler, solidifying agent, the priming paint of solvent composition reaches by synthetic resins, the investment precoat of colored filler and solvent composition is formed, the synthetic resins that it is characterized in that priming paint is Resins, epoxy, aminoresin, colored filler is a titanium dioxide, zinc sulfide white, process white and talcum powder, solidifying agent is the T31 solidifying agent, butanols and dimethylbenzene, solvent is the ring ethyl ketone, the synthetic resins of investment precoat is Resins, epoxy, alkyd resin, aminoresin, colored filler is a titanium dioxide, solvent is the ring ethyl ketone, and each becomes proportioning to be:
The priming paint proportioning:
Resins, epoxy: 16 parts
Aminoresin: 3 parts
Titanium dioxide: 7 parts
Zinc sulfide white: 20 parts
Process white: 6 parts
Talcum powder: 10 parts
T31 solidifying agent: 40 parts
Butanols: 20 parts
Dimethylbenzene: 40 parts
Ring ethyl ketone: 38 parts
The investment precoat proportioning:
Resins, epoxy: 19 parts
Vibrin: 9 parts
Aminoresin: 2 parts
Titanium dioxide: 36 parts
Solvent: 34 parts
In order to reduce the cost of coating, the solvent of investment precoat is ring ethyl ketone and dimethylbenzene, and its ratio is ring ethyl ketone 40%, dimethylbenzene 60%.With the ring ethyl ketone, its performance can be better as all.
Embodiment: the Resins, epoxy of priming paint selects 601
#With 604
#, its ratio is respectively 25% and 75%; The Resins, epoxy of investment precoat also selects 601
#With 604
#, its ratio is respectively 33% and 67%, and other compositions and proportioning are with aforementioned.
The present invention compares with imitation porcelain coating, and its hardness, glossiness is water-fastness and acid-alkali-resistant degree all is better than imitation porcelain coating greatly, reach with the close degree of porcelain, and be desirable decorative paint.
Claims (2)
1, a kind of high-bright cold enamel paint, by synthetic resins, colored filler, solidifying agent, the priming paint of solvent composition reaches by synthetic resins, the investment precoat of colored filler and solvent composition is formed, the synthetic resins that it is characterized in that priming paint is Resins, epoxy, aminoresin, colored filler is a titanium dioxide, zinc sulfide white, process white and talcum powder, solidifying agent is the T31 solidifying agent, butanols and dimethylbenzene, solvent is the ring ethyl ketone, the synthetic resins of investment precoat is Resins, epoxy, alkyd resin, aminoresin, colored filler is a titanium dioxide, solvent is the ring ethyl ketone, and each composition proportion is:
The priming paint proportioning:
Resins, epoxy: 16 parts
Aminoresin: 3 parts
Titanium dioxide: 7 parts
Zinc sulfide white: 20 parts
Process white: 6 parts
Talcum powder: 10 parts
T31 solidifying agent: 40 parts
Butanols: 20 parts
Dimethylbenzene: 40 parts
Ring ethyl ketone: 38 parts
The investment precoat proportioning:
Resins, epoxy: 19 parts
Vibrin: 9 parts
Aminoresin: 2 parts
Titanium dioxide: 36 parts
Solvent: 34 parts
2, high-bright cold enamel paint according to claim 1 is characterized in that the solvent of described investment precoat is ring ethyl ketone and dimethylbenzene composition, and its ratio is ring ethyl ketone 40%, dimethylbenzene 60%.