CN109267366A - A kind of tent cloth and preparation method - Google Patents
A kind of tent cloth and preparation method Download PDFInfo
- Publication number
- CN109267366A CN109267366A CN201811151794.6A CN201811151794A CN109267366A CN 109267366 A CN109267366 A CN 109267366A CN 201811151794 A CN201811151794 A CN 201811151794A CN 109267366 A CN109267366 A CN 109267366A
- Authority
- CN
- China
- Prior art keywords
- coating
- tent cloth
- sleeping
- drying
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a kind of tent cloths, including base fabric, be successively arranged vertical coating, sleeping coating and finishing coat on the base fabric two sides, the vertical coating with a thickness of 0.25-0.3mm, the sleeping coating with a thickness of 0.3-0.4mm, the finishing coat with a thickness of 0.4-0.5mm；The vertical painting is identical as coating used in sleeping apply, raw material including following parts by weight: resin 90-110, plasticizer 60-80, stabilizer 2-3, adhesive 4-6, calcium carbonate 40-60, halogen phosphatide based flame retardant 8-10, described adhesive is by mix monomer, polyvinyl alcohol, azo-bis-isobutyl cyanide, ethyl acetate (20-25) in mass ratio: (1-2): (0.4-0.7): (2-3) hybrid reaction forms；The face applies the raw material that coating used includes following parts by weight: resin 90-100, plasticizer 50-60, stabilizer 2-3, calcium carbonate 15-25, boride fire retardant 6-10, mould inhibitor 3-5, pure-acrylic emulsion 10-16.The invention also discloses the preparation methods of the tent cloth.It is an advantage of the current invention that the tent cloth has flame retardant effect, it is suitable for various weather, can effectively prolongs the service life.
Description
Technical field
The invention belongs to functional Compound Fabric field of material technology, and in particular to a kind of tent cloth and preparation method.
Background technique
Outdoor camping, tent are to must be provided with.Tent is needed with the multiple family such as sunshade, ventilation, radix saposhnikoviae, rain-proof, warming
Outer function, outdoor tent must adapt to various weather environments, and when ambient weather is for the rainy day or by strong wind, people outdoor can not be cooked
It prepares food food.Existing tent is all combustibles, once touching open fire can burn quickly, therefore can not also be cooked in tent
It prepares food, this has the people to camp certain difficulty.
Summary of the invention
Technical problem to be solved by the present invention lies in: how to produce one kind and not only meets the multiple outdoor function of tent, but also tool
There is the tent cloth of fire retardancy.
The present invention solves above-mentioned technical problem using following technical scheme:
A kind of tent cloth, including base fabric are successively arranged vertical coating, sleeping coating and finishing coat, institute on the base fabric two sides
State vertical coating with a thickness of 0.25-0.3mm, the sleeping coating with a thickness of 0.3-0.4mm, the finishing coat with a thickness of 0.4-
0.5mm；
The vertical painting is identical as coating used in sleeping apply, the raw material including following parts by weight: resin 90-110, plasticizer 60-
80, stabilizer 2-3, adhesive 4-6, calcium carbonate 40-60, halogen phosphatide based flame retardant 8-10, wherein described adhesive is by mixing
Monomer, polyvinyl alcohol, azo-bis-isobutyl cyanide, ethyl acetate (20-25) in mass ratio: (1-2): (0.4-0.7): (2-3) mixing
It reacts；
The face applies the raw material that coating used includes following parts by weight: resin 90-100, plasticizer 50-60, stabilizer 2-
3, calcium carbonate 15-25, boride fire retardant 6-10, mould inhibitor 3-5, pure-acrylic emulsion 10-16.
Preferably, a kind of tent cloth of the present invention, the vertical painting is identical as coating used in sleeping apply, including following weight
The raw material of part: resin 100, plasticizer 70, stabilizer 2.5, adhesive 5, calcium carbonate 50, halogen phosphatide based flame retardant 10, wherein
Described adhesive is by mix monomer, polyvinyl alcohol, azo-bis-isobutyl cyanide, ethyl acetate 22:1:0.6:2 hybrid reaction in mass ratio
It forms；
The face applies the raw material that coating used includes following parts by weight: resin 100, plasticizer 55, stabilizer 2.5, carbonic acid
Calcium 20, boride fire retardant 8, mould inhibitor 4, pure-acrylic emulsion 13.
Preferably, a kind of tent cloth of the present invention, the resin are polyethylene.
Preferably, a kind of tent cloth of the present invention, the plasticizer are ditridecyl phthalate.
Preferably, a kind of tent cloth of the present invention, the stabilizer are barium zinc stabilizer or calcium zinc stabilizer.
Preferably, a kind of tent cloth of the present invention, the mix monomer are acrylonitrile, methyl acrylate, methyl-prop
At least two in e pioic acid methyl ester.
Preferably, a kind of tent cloth of the present invention, the base fabric are warp knitting cloth.
The present invention also provides a kind of preparation methods of above-mentioned tent cloth, comprising the following steps:
(1) painting and sleeping painting coating are found in preparation: first mix monomer, initiator are mixed, add dispersing agent, react, filter,
After washing, drying, then it is dissolved in ethyl acetate；It is stated in system then up and other raw materials is added, stirred in dispersion cylinder,
Dispersion, controlling its viscosity is 5800-6200cp；
(2) it prepares painting coating: weighing raw material, raw material is placed in flask, with the speed of revolving speed 70-90r/min under room temperature
Degree stirring to viscosity is 5600-6000cp；
(3) stand and apply starching and drying: in the uniform starching in the front and back sides of base fabric, slurry covers cloth cover, without open-work, then by it
Put in a drying box drying；
(4) substrate that step (3) obtains is subjected to sleeping painting starching, slurry covers cloth cover, without open-work, then dries；
(5) the substrate front and back sides face for obtaining step (4) applies starching, is then dried to obtain tent cloth.
Preferably, the preparation method of a kind of tent cloth of the present invention, the dry temperature in the step (3), step (4)
Degree is 165-190 DEG C；The drying temperature of the step (5) is 170-190 DEG C.
Preferably, the preparation method of a kind of tent cloth of the present invention, drying used in the step (3), step (4)
Case is Two stage dryer case, and the drying temperature of first segment is 165-175 DEG C, and the drying temperature of second segment is 180-190 DEG C；It is described
Drying box used is five sections of drying boxes in step (5), and the drying temperature of first segment is 170-175 DEG C, the drying temperature of second segment
Be 175-185 DEG C, third section, the 4th section and the 5th section drying temperature be 185-190 DEG C.
The technology of the present invention the utility model has the advantages that
The tent cloth of technical solution of the present invention preparation has both multiple outdoor function, and can be effectively fire-retardant, is adapted to various days
Outdoor camping activity under gas；Also it can effectively prevent tent cloth that dieseling occurs because ambient temperature is excessively high in fine day simultaneously；
By the regulation to coating raw material and proportion, improves tent cloth surface roughness, reduce its diffusing reflection to light, improving it makes
Use the service life.
Specific embodiment
For convenient for those skilled in the art understand that technical solution of the present invention, now in conjunction with specific embodiment to the technology of the present invention side
Case is described further.
Embodiment one
The present embodiment provides a kind of tent cloths, including the base fabric that warp knitting cloth is constituted, are successively arranged on the base fabric two sides
Vertical coating, sleeping coating and finishing coat, the vertical coating with a thickness of 0.28mm, the sleeping coating with a thickness of 0.35mm, it is described
Finishing coat with a thickness of 0.45mm；Its preparation process is as follows:
(1) coating is prepared
A, painting, sleeping painting coating preparation are stood.The vertical painting is identical as coating used in sleeping apply, the original including following parts by weight
Material: resin 100, plasticizer 70, stabilizer 2.5, adhesive 5, calcium carbonate 50, halogen phosphatide based flame retardant 10, wherein described viscous
Mixture is formed by mix monomer, polyvinyl alcohol, azo-bis-isobutyl cyanide, ethyl acetate 22:1:0.6:2 hybrid reaction in mass ratio；
Its specific preparation method: first mixing mix monomer, azo-bis-isobutyl cyanide, adds polyvinyl alcohol, reaction, mistake
After filter, washing, drying, then it is dissolved in ethyl acetate；It is stated in system then up and other raw materials is added, stirred in dispersion cylinder
It mixes, disperse, controlling its viscosity is 5800-6200cp.
B, face applies the preparation for using coating.The face applies the raw material that coating used includes following parts by weight: resin 100, plasticising
Agent 55, stabilizer 2.5, calcium carbonate 20, boride fire retardant 8, mould inhibitor 4, pure-acrylic emulsion 13.Raw material is weighed according to the ratio, it will be former
Material is placed in flask, is stirred to viscosity with the speed of revolving speed 70-90r/min as 5600-6000cp under room temperature；
Above-mentioned resin is polyethylene；The plasticizer is ditridecyl phthalate；The stabilizer is barium zinc stabilizer；
The mix monomer is mixed by acrylonitrile, methyl acrylate, methyl methacrylate.
(2) stand and apply starching and drying: in the uniform starching in the front and back sides of base fabric, slurry covers cloth cover, without open-work, then by it
Put in a drying box drying；The drying box is two-part drying box, and the drying temperature of first segment is set as 170 DEG C, when dry
Between 20min, the temperature of second segment is 180 DEG C, drying time 10min.
(3) substrate that step (2) obtains is subjected to sleeping painting starching, slurry covers cloth cover, without open-work, then dries；The step
Suddenly it is dried using two-part drying box, the drying temperature of first segment is 170 DEG C, drying time 30min, the dry temperature of second segment
Degree is 180 DEG C, drying time 30min.
(4) the substrate front and back sides face for obtaining step (3) applies starching, is then dried to obtain tent cloth.The step uses five
Segmentation drying box is dried, and the drying temperature of first segment is 170 DEG C, and the drying temperature of second segment is 180 DEG C, third section, the
Four sections and the 5th section of temperature is 185 DEG C.
Embodiment two
The present embodiment provides a kind of tent cloths, including the base fabric that warp knitting cloth is constituted, are successively arranged on the base fabric two sides
Vertical coating, sleeping coating and finishing coat, the vertical coating with a thickness of 0.25mm, the sleeping coating with a thickness of 0.3mm, the face
Coating with a thickness of 0.4mm；Its preparation process is as follows:
(1) coating is prepared
A, painting, sleeping painting coating preparation are stood.The vertical painting is identical as coating used in sleeping apply, the original including following parts by weight
Material: resin 90, plasticizer 60, stabilizer 2, adhesive 4, calcium carbonate 40, halogen phosphatide based flame retardant 8, wherein described adhesive
It is formed by mix monomer, polyvinyl alcohol, azo-bis-isobutyl cyanide, ethyl acetate 25:1:0.7:2 hybrid reaction in mass ratio；
Its specific preparation method: first mixing mix monomer, azo-bis-isobutyl cyanide, adds polyvinyl alcohol, reaction, mistake
After filter, washing, drying, then it is dissolved in ethyl acetate；It is stated in system then up and other raw materials is added, stirred in dispersion cylinder
It mixes, disperse, controlling its viscosity is 6100cp.
B, face applies the preparation for using coating.The face applies the raw material that coating used includes following parts by weight: resin 100, plasticising
Agent 60, stabilizer 3, calcium carbonate 20, boride fire retardant 10, mould inhibitor 5, pure-acrylic emulsion 16.Raw material is weighed according to the ratio, by raw material
It is placed in flask, is stirred to viscosity with the speed of revolving speed 70-90r/min as 6000cp under room temperature；
Above-mentioned resin is polyethylene；The plasticizer is ditridecyl phthalate；The stabilizer is barium zinc stabilizer；
The mix monomer is mixed by acrylonitrile, methyl methacrylate.
(2) stand and apply starching and drying: in the uniform starching in the front and back sides of base fabric, slurry covers cloth cover, without open-work, then by it
Put in a drying box drying；The drying box is two-part drying box, and the drying temperature of first segment is set as 165 DEG C, when dry
Between 25min, the temperature of second segment is 185 DEG C, drying time 15min.
(3) substrate that step (2) obtains is subjected to sleeping painting starching, slurry covers cloth cover, without open-work, then dries；The step
Suddenly it is dried using two-part drying box, the drying temperature of first segment is 170 DEG C, drying time 30min, the dry temperature of second segment
Degree is 190 DEG C, drying time 20min.
(4) the substrate front and back sides face for obtaining step (3) applies starching, is then dried to obtain tent cloth.The step uses five
Segmentation drying box is dried, and the drying temperature of first segment is 175 DEG C, and the drying temperature of second segment is 180 DEG C, third section, the
Four sections and the 5th section of temperature is 190 DEG C.
Embodiment three
The present embodiment provides a kind of tent cloths, including the base fabric that warp knitting cloth is constituted, are successively arranged on the base fabric two sides
Vertical coating, sleeping coating and finishing coat, the vertical coating with a thickness of 0.3mm, the sleeping coating with a thickness of 0.3mm, the face
Coating with a thickness of 0.5mm；Its preparation process is as follows:
(1) coating is prepared
A, painting, sleeping painting coating preparation are stood.The vertical painting is identical as coating used in sleeping apply, the original including following parts by weight
Material: resin 110, plasticizer 80, stabilizer 3, adhesive 4, calcium carbonate 60, halogen phosphatide based flame retardant 10, wherein the bonding
Agent is formed by mix monomer, polyvinyl alcohol, azo-bis-isobutyl cyanide, ethyl acetate 20:1:0.4:1.8 hybrid reaction in mass ratio；
Its specific preparation method: first mixing mix monomer, azo-bis-isobutyl cyanide, adds polyvinyl alcohol, reaction, mistake
After filter, washing, drying, then it is dissolved in ethyl acetate；It is stated in system then up and other raw materials is added, stirred in dispersion cylinder
It mixes, disperse, controlling its viscosity is 6200cp.
B, face applies the preparation for using coating.The face applies the raw material that coating used includes following parts by weight: resin 95, plasticizer
50, stabilizer 3, calcium carbonate 23, boride fire retardant 10, mould inhibitor 3, pure-acrylic emulsion 10.Raw material is weighed according to the ratio, and raw material is set
In in flask, stirred to viscosity with the speed of revolving speed 70-90r/min as 5800cp under room temperature；
Above-mentioned resin is polyethylene；The plasticizer is ditridecyl phthalate；The stabilizer is barium zinc stabilizer；
The mix monomer is mixed by methyl acrylate, methyl methacrylate.
(2) stand and apply starching and drying: in the uniform starching in the front and back sides of base fabric, slurry covers cloth cover, without open-work, then by it
Put in a drying box drying；The drying box is two-part drying box, and the drying temperature of first segment is set as 165 DEG C, when dry
Between 25min, the temperature of second segment is 185 DEG C, drying time 15min.
(3) substrate that step (2) obtains is subjected to sleeping painting starching, slurry covers cloth cover, without open-work, then dries；The step
Suddenly it is dried using two-part drying box, the drying temperature of first segment is 175 DEG C, drying time 30min, the dry temperature of second segment
Degree is 180 DEG C, drying time 30min.
(4) the substrate front and back sides face for obtaining step (3) applies starching, is then dried to obtain tent cloth.The step uses five
Segmentation drying box is dried, and the drying temperature of first segment is 175 DEG C, and the drying temperature of second segment is 180 DEG C, third section, the
Four sections and the 5th section of temperature is 185 DEG C.
Technical solution of the present invention is exemplarily described invention above in conjunction with specific embodiment, it is clear that present invention tool
Body realization is not subject to the restrictions described above, as long as using the various non-realities that the inventive concept and technical scheme of the present invention carry out
Matter improve, or it is not improved the conception and technical scheme of invention are directly applied into other occasions, in guarantor of the invention
Within the scope of shield.
Claims (10)
1. a kind of tent cloth, including base fabric, which is characterized in that be successively arranged on the base fabric two sides vertical coating, sleeping coating and
Finishing coat, the vertical coating with a thickness of 0.25-0.3mm, the sleeping coating with a thickness of 0.3-0.4mm, the finishing coat
With a thickness of 0.4-0.5mm；
The vertical painting and sleeping identical, the raw material including following parts by weight that applies coating used: resin 90-110, plasticizer 60-80, surely
Determine agent 2-3, adhesive 4-6, calcium carbonate 40-60, halogen phosphatide based flame retardant 8-10, wherein described adhesive by mix monomer,
Polyvinyl alcohol, azo-bis-isobutyl cyanide, ethyl acetate (20-25) in mass ratio: (1-2): (0.4-0.7): (2-3) hybrid reaction and
At；
The face applies the raw material that coating used includes following parts by weight: resin 90-100, plasticizer 50-60, stabilizer 2-3, carbon
Sour calcium 15-25, boride fire retardant 6-10, mould inhibitor 3-5, pure-acrylic emulsion 10-16.
2. a kind of tent cloth according to claim 1, which is characterized in that the vertical painting is identical as coating used in sleeping apply, packet
Include the raw material of following parts by weight: resin 100, plasticizer 70, stabilizer 2.5, adhesive 5, calcium carbonate 50, halogen phospholipid are fire-retardant
Agent 10, wherein described adhesive is by mix monomer, polyvinyl alcohol, azo-bis-isobutyl cyanide, ethyl acetate 22:1:0.6 in mass ratio:
2 hybrid reactions form；
The face applies the raw material that coating used includes following parts by weight: resin 100, plasticizer 55, stabilizer 2.5, calcium carbonate 20,
Boride fire retardant 8, mould inhibitor 4, pure-acrylic emulsion 13.
3. a kind of tent cloth according to claim 1 or 2, which is characterized in that the resin is polyethylene.
4. a kind of tent cloth according to claim 1 or 2, which is characterized in that the plasticizer is ditridecyl phthalate.
5. a kind of tent cloth according to claim 1, which is characterized in that the stabilizer is that barium zinc stabilizer or calcium zinc are steady
Determine agent.
6. a kind of tent cloth according to claim 1, which is characterized in that the mix monomer is acrylonitrile, acrylic acid first
At least two in ester, methyl methacrylate.
7. a kind of tent cloth according to claim 1, which is characterized in that the base fabric is warp knitting cloth.
8. such as a kind of described in any item preparation methods of tent cloth of claim 1-7, which comprises the following steps:
(1) the vertical painting coating that applies and crouch of preparation: first mix monomer, initiator are mixed, add dispersing agent, reaction, filtering, water
After washing, drying, then it is dissolved in ethyl acetate；It is stated in system then up and other raw materials is added, stirred, divide in dispersion cylinder
It dissipates, controlling its viscosity is 5800-6200cp；
(2) it prepares painting coating: weighing raw material, raw material is placed in flask, stirred under room temperature with the speed of revolving speed 70-90r/min
Mixing to viscosity is 5600-6000cp；
(3) stand and apply starching and drying: in the uniform starching in the front and back sides of base fabric, slurry covers cloth cover, without open-work, then places it in
It is dry in drying box；
(4) substrate that step (3) obtains is subjected to sleeping painting starching, slurry covers cloth cover, without open-work, then dries；
(5) the substrate front and back sides face for obtaining step (4) applies starching, is then dried to obtain tent cloth.
9. a kind of preparation method of tent cloth according to claim 8, which is characterized in that the step (3), step (4)
In drying temperature be 165-190 DEG C；The drying temperature of the step (5) is 170-190 DEG C.
10. a kind of preparation method of tent cloth according to claim 9, which is characterized in that the step (3), step (4)
In drying box used be Two stage dryer case, the drying temperature of first segment is 165-175 DEG C, and the drying temperature of second segment is 180-
190℃；Drying box used is five sections of drying boxes in the step (5), and the drying temperature of first segment is 170-175 DEG C, second segment
Drying temperature be 175-185 DEG C, third section, the 4th section and the 5th section drying temperature be 185-190 DEG C.