CN109266160A - A kind of single-component water-based paint and preparation method thereof with high anti-corrosive properties - Google Patents
A kind of single-component water-based paint and preparation method thereof with high anti-corrosive properties Download PDFInfo
- Publication number
- CN109266160A CN109266160A CN201810738198.1A CN201810738198A CN109266160A CN 109266160 A CN109266160 A CN 109266160A CN 201810738198 A CN201810738198 A CN 201810738198A CN 109266160 A CN109266160 A CN 109266160A
- Authority
- CN
- China
- Prior art keywords
- parts
- high anti
- corrosive properties
- based paint
- component water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to technical field of coatings, specifically disclose a kind of single-component water-based paint and preparation method thereof with high anti-corrosive properties.The single-component water-based paint with high anti-corrosive properties, according to parts by weight, including following component: epoxy ester resin: 30-50 parts, 1-5 parts of filler, pigment: 16-20 parts, aqueous drier: 5-7 parts, neutralizer: 0.1-0.4 parts, defoaming agent: 0.1-0.3 parts, wetting dispersing agent: 0.3-0.5 parts, substrate wetting agents: 0.3-0.5 parts, deionized water: 2-5 parts, cosolvent: 3-5 parts, zinc oxide: 3-5 parts, amino resins: 3-5 parts.The salt fog resistance of single-component water-based paint prepared by the present invention with high anti-corrosive properties is up to 140h, and water resistance reaches 140h, and hardness is high, and impact resistance is strong, while acidproof, alkaline-resisting, resistance to machine oil is had excellent performance.
Description
Technical field
The present invention relates to technical field of coatings more particularly to a kind of with the single-component water-based paint of high anti-corrosive properties and its preparation
Method.
Background technique
With the continuous development of modern industry, transmission yield is growing, and automobile chassis local environment is various.Cause
This, is just particularly important effective protective coating of transmission shaft.Transmission shaft coating requires have excellent adhesive force, flexible
Property, shock resistance and good hardness.Because driveshaft applications field is extensive, institute's contact environment is relatively complicated, so outside it
Shell coating need to have good antiseptic property and good chemical-resistant again.
Overwhelming majority transmission shaft mainly uses solvent type industrial coating at present.With people to environment and health increasingly
Pay attention to, water paint has been more and more widely used, and traditional solvent type coating is discharged in the production and use process
Volatile organic substance (VolatileOrganic Compounds, VOC) generate pollution, at present become come automobile it
City primary pollution source afterwards, constantly improve and perfect with Environmental Protection in China laws and regulations, forced use environment-friendly type industry
Coating has become trend of the times.And prior development direction one of of the aqueous industrial coating as environment-friendly type coating, in garage
Application in industry has boundless market.But that there are the not high enough feels of hardness of paint film is poor, is easy for traditional water paint
Scratch, chemical resistance are poor, contain the disadvantages of low, film thickness is thin, drying property is poor, price is high admittedly.For response country environmental protection act and
The Policy Conditions of energy-saving and emission-reduction develop a low VOC (VOC) and discharge, is good for the coating specification of transmission shaft
The aqueous industrial coating of antiseptic property is significant.
Summary of the invention
For the problem that existing water paint hardness of paint film is low, chemical resistance is poor, resistance to saltfog can be poor, the present invention provides one kind
Single-component water-based paint with high anti-corrosive properties.
And a kind of preparation method of the single-component water-based paint with high anti-corrosive properties.
To achieve the above object of the invention, the embodiment of the present invention uses the following technical solution:
A kind of single-component water-based paint with high anti-corrosive properties, according to parts by weight, including following component: in parts by weight
Meter, including following component: epoxy ester resin: 30-50 parts, 1-5 parts of filler, pigment: 16-20 parts, aqueous drier: 5-7 parts, in
And agent: it 0.1-0.4 parts, defoaming agent: 0.1-0.3 parts, wetting dispersing agent: 0.3-0.5 parts, substrate wetting agents: 0.3-0.5 parts, goes
Ionized water: 2-5 parts, cosolvent: 3-5 parts, zinc oxide: 3-5 parts, amino resins: 3-5 parts.
Compared with the existing technology, the single-component water-based paint provided by the invention with high anti-corrosive properties, using epoxy ester resin
For film forming matter, select amino resins for curing agent, epoxy resin energy fast reaction after curing agent contact, while in its molecule
Containing hydrophilic hydroxyl and ehter bond, Quick cross-linking (keeping higher reactivity) polymerization dense mess can be formed at normal temperature
Shape structure, interacting between molecule permeate solvent can not effectively, to use for a long time in complexity molten without occurring
Solution falls off, and guarantees that coating has excellent adhesive force and hardness, obtains low temperature baking vanish that can be dry with 80 DEG C of bakings, while epoxy
Ester resin, amino resins, zinc oxide mutually cooperate with, and improve the resistance to saltfog energy of water paint, and using the auxiliary agent of environmental protection, reduce
The content of VOC.
Specifically, it is preferable that the amino resins is Amino resin.
Preferably, the neutralizer is at least one of dimethylethanolamine or 2-amino-2-methyl-1-propanol.
Dimethylethanolamine is a kind of efficient amine neutralizer, effective regulation system pH value, for coating have low smell,
The advantages of low volatility, and can assign system good pH stability, have it is good help pigment-dispersing, can promote paint film light
Pool show and the raising of covering power.
2-amino-2-methyl-1-propanol (AMP-95) is a kind of multifunction amine auxiliary agent, adjusts the pH value of lotion adhesive very
Stablize, there are also the effects of wet dispersion, meanwhile, also there is outstanding base strength, efficient pigment dispersion and enhanced
Scrub resistance.
Preferably, the pigment includes titanium dioxide and rust resisting pigment, wherein the mass ratio of the titanium dioxide and rust resisting pigment
For 5:(3-5).
Preferably, the defoaming agent is at least one in polyether siloxane copolymer class defoaming agent or polysiloxane defoaming agent
Kind.
Polyether siloxane copolymer combines the advantages of both polyether antifoam agent and organic silicon defoamer, and antifoaming speed is fast,
Stability is good, and in its molecule, siloxanes section is lipophilic group, and polyethers section is hydrophilic group, and in polyether segment, polycyclic oxygen second
Alkane chain link provides hydrophilicity and frothing capacity, and polypropylene oxide chain link provides hydrophobic performance and penetration, to reduce
Surface tension.
Preferably, it is (0.8-1.1): polycarboxylic acid salt's dispersing agent of (0.8-1.1) that the wetting dispersing agent, which is mass ratio,
With the mixture of nonionic surfactant.
Preferably, the substrate wetting agents are the wetting agent of Siloxane-Oxyalkylene Copolymers class, can improve the flowing of solution
Property, and can make paint film that there is slippery feel, while also there is high-compatibility, it can be compatible well with unclassified stores.
Further, it the present invention also provides a kind of preparation method of single-component water-based paint with high anti-corrosive properties, at least wraps
Include following steps:
Step a, each component is weighed according to above-mentioned raw material proportioning；
Step b, by the epoxy ester resin, pigments and fillers, rust resisting pigment, aqueous drier, neutralizer, defoaming agent, wetting
Dispersing agent, substrate wetting agents, deionized water, cosolvent, zinc oxide, amino resins carry out mixing treatment, obtain mixture；
Step c, the mixture is ground, fineness obtains described with high anti-corrosive properties less than 25 microns
Single-component water-based paint.
Compared with the existing technology, preparation method provided by the invention is simple, and process is easy to control, and is suitable for industrial metaplasia
It produces.Fineness of grind is controlled simultaneously no more than 25 microns, is to guarantee pigments and fillers fineness of grind no more than 25 microns, and in coating
Degree of scatter is high, is conducive to the stability of system.And the overlong time of dispersion or grinding causes solvent volatilization serious, can make viscosity
It is obviously improved, therefore fineness of grind is selected to be not more than 25 microns.
Specifically, it is preferable that the condition of mixing treatment in the step b are as follows: 10- is stirred with the speed of 400-600rpm
20min。
Selection 400-600rpm's stirs at low speed, and since system medium viscosity is larger, stirs at low speed and is not easy to stir into bubble
System is readily incorporated bubble if speed is too high, and when viscosity is big, bubble is not easy to be precipitated, and will affect filming performance.
Specific embodiment
In order to make the objectives, technical solutions, and advantages of the present invention clearer, with reference to embodiments, to the present invention
It is further elaborated.It should be appreciated that the specific embodiments described herein are merely illustrative of the present invention, it is not used to
Limit the present invention.
Embodiment provides in order to better illustrate the present invention, is illustrated below by embodiment is further.
Embodiment 1
The present embodiment provides a kind of single-component water-based paints with high anti-corrosive properties, according to parts by weight, including following component:
Epoxy ester resin: 30 parts, filler: 2.5 parts, titanium dioxide: 10 parts, rust resisting pigment: 6 parts, aqueous drier: 5 parts, neutralizer: 0.4
Part, defoaming agent: 0.3 part, wetting dispersing agent: 0.5 part, substrate wetting agents: 0.4 part, deionized water: 2 parts, cosolvent: 3 parts, oxygen
Change zinc: 4 parts, amino resins: 4 parts.
Above-mentioned epoxy ester resin uses the 5314 of brilliant same moral Chemical Co., Ltd. of Foshan City；Drier is with moral company
Aqueous drier 5003-1；Neutralizer is dimethylethanolamine；Defoaming agent is the Tego-902w and BYK-028 that mass ratio is 1:1
Mixture；Wetting dispersing agent be mass ratio be 1:1 hamming this FX600 and hamming this FX365 mixture；Substrate profit
Humectant is the Tego-245 of (Digao) TEGO；Amino resins is the 5717 of the wooden chemical industry in Jiangsu three；Zinc oxide is selected from Zibo sea along zinc
Industry, purity zinc oxide 99.7%.
The preparation method of the above-mentioned single-component water-based paint with high anti-corrosive properties, comprising the following steps:
Step a, each component is weighed according to above-mentioned raw material proportioning；
Step b, by the epoxy ester resin, pigments and fillers, rust resisting pigment, aqueous drier, neutralizer, defoaming agent, wetting
Dispersing agent, substrate wetting agents, deionized water, cosolvent, zinc oxide, amino resins stir 15min with the speed of 500rpm, obtain
First mixture；
Step c, first mixture is ground, fineness obtains described with high anti-corrosion less than 25 microns
The single-component water-based paint of property.
Embodiment 2
The present embodiment provides a kind of single-component water-based paints with high anti-corrosive properties, according to parts by weight, including following component:
Epoxy ester resin: 40 parts, filler: 1 part, titanium dioxide: 10 parts, rust resisting pigment: 10 parts, aqueous drier: 6 parts, neutralizer: 0.1
Part, defoaming agent: 0.2 part, wetting dispersing agent: 0.3 part, substrate wetting agents: 0.5 part, deionized water: 4 parts, cosolvent: 4 parts, oxygen
Change zinc: 5 parts, amino resins: 5 parts.
Above-mentioned epoxy ester resin uses the 5314 of brilliant same moral Chemical Co., Ltd. of Foshan City；Drier is with moral company
Aqueous drier 5003-1；Neutralizer is AMP-95；Defoaming agent is the mixing of Tego-902w and BYK-028 that mass ratio is 1:1
Object；Wetting dispersing agent be mass ratio be 0.8:1.1 hamming this FX600 and hamming this FX365 mixture；Substrate wetting
Agent is the Tego-270 of (Digao) TEGO；Amino resins is the 5717 of the wooden chemical industry in Jiangsu three；Zinc oxide is selected from Zibo sea along zinc industry,
Purity zinc oxide is 99.7%.
The preparation method of the above-mentioned single-component water-based paint with high anti-corrosive properties, comprising the following steps:
Step a, each component is weighed according to above-mentioned raw material proportioning；
Step b, by the epoxy ester resin, pigments and fillers, rust resisting pigment, aqueous drier, neutralizer, defoaming agent, wetting
Dispersing agent, substrate wetting agents, deionized water, cosolvent, zinc oxide, amino resins stir 20min with the speed of 400rpm, obtain
First mixture；
Step c, first mixture is ground, fineness obtains described with high anti-corrosion less than 25 microns
The single-component water-based paint of property.
Embodiment 3
The present embodiment provides a kind of single-component water-based paints with high anti-corrosive properties, according to parts by weight, including following component:
Epoxy ester resin: 50 parts, filler: 5 parts, titanium dioxide: 10 parts, rust resisting pigment: 8 parts, aqueous drier: 7 parts, neutralizer: 0.3
Part, defoaming agent: 0.1 part, wetting dispersing agent: 0.4 part, substrate wetting agents: 0.3 part, deionized water: 5 parts, cosolvent: 5 parts, oxygen
Change zinc: 3 parts, amino resins: 3 parts.
Above-mentioned epoxy ester resin uses the 5314 of brilliant same moral Chemical Co., Ltd. of Foshan City；Drier is with moral company
Aqueous drier 5003-1；Neutralizer is the dimethylethanolamine that mass ratio is 1:1 and the mixture of AMP-95；Defoaming agent is matter
Mixture of the amount than the Tego-902w and BYK-028 that are 1:1；Wetting dispersing agent be mass ratio be 1.1:0.8 hamming this
FX600 and hamming this FX365 mixture；Substrate wetting agents are the Tego-270 of (Digao) TEGO；Amino resins is Jiangsu
The 5717 of the three wooden chemical industry；Zinc oxide is selected from Zibo sea along zinc industry, purity zinc oxide 99.7%.
The preparation method of the above-mentioned single-component water-based paint with high anti-corrosive properties, comprising the following steps:
Step a, each component is weighed according to above-mentioned raw material proportioning；
Step b, by the epoxy ester resin, pigments and fillers, rust resisting pigment, aqueous drier, neutralizer, defoaming agent, wetting
Dispersing agent, substrate wetting agents, deionized water, cosolvent, zinc oxide, amino resins stir 10min with the speed of 600rpm, obtain
First mixture；
Step c, first mixture is ground, fineness obtains described with high anti-corrosion less than 25 microns
The single-component water-based paint of property.
Technical solution in order to better illustrate the present invention is done by comparative example and the embodiment of the present invention into one further below
The comparison of step.
Comparative example 1
This comparative example provides a kind of single-component water-based paint with high anti-corrosive properties, according to parts by weight, including following component:
Epoxy ester resin: 30 parts, filler: 2.5 parts, titanium dioxide: 10 parts, rust resisting pigment: 6 parts, aqueous drier: 5 parts, neutralizer: 0.4
Part, defoaming agent: 0.3 part, wetting dispersing agent: 0.5 part, substrate wetting agents: 0.4 part, deionized water: 2 parts, cosolvent: 3 parts, oxygen
Change copper: 4 parts, amino resins: 4 parts.
Above-mentioned epoxy ester resin uses the 5314 of brilliant same moral Chemical Co., Ltd. of Foshan City；Drier is with moral company
Aqueous drier 5003-1；Neutralizer is dimethylethanolamine；Defoaming agent is the Tego-902w and BYK-028 that mass ratio is 1:1
Mixture；Wetting dispersing agent be mass ratio be 1:1 hamming this FX600 and hamming this FX365 mixture；Substrate profit
Humectant is the Tego-245 of (Digao) TEGO；Amino resins is the 5717 of the wooden chemical industry in Jiangsu three.
The preparation method of the above-mentioned single-component water-based paint with high anti-corrosive properties is as described in Example 1, repeats no more.
Comparative example 2
This comparative example provides a kind of single-component water-based paint with high anti-corrosive properties, according to parts by weight, including following component:
Epoxy ester resin: 30 parts, filler: 2.5 parts, titanium dioxide: 10 parts, rust resisting pigment: 6 parts, aqueous drier: 5 parts, neutralizer: 0.4
Part, defoaming agent: 0.3 part, wetting dispersing agent: 0.5 part, substrate wetting agents: 0.4 part, deionized water: 2 parts, cosolvent: 3 parts, oxygen
Change zinc: 4 parts, fatty amines curing agent: 4 parts.
Above-mentioned epoxy ester resin uses the 5314 of brilliant same moral Chemical Co., Ltd. of Foshan City；Drier is with moral company
Aqueous drier 5003-1；Neutralizer is dimethylethanolamine；Defoaming agent is the Tego-902w and BYK-028 that mass ratio is 1:1
Mixture；Wetting dispersing agent be mass ratio be 1:1 hamming this FX600 and hamming this FX365 mixture；Substrate profit
Humectant is the Tego-245 of (Digao) TEGO；Amino resins is the 5717 of the wooden chemical industry in Jiangsu three.
The preparation method of the above-mentioned single-component water-based paint with high anti-corrosive properties is as described in Example 1, repeats no more.
The characteristic for the single-component water-based paint with high anti-corrosive properties that embodiment provides in order to better illustrate the present invention, below
Single-component water-based paint with high anti-corrosive properties prepared by embodiment 1,2,3 and comparative example 1,2 is subjected to performance detection, detection knot
Fruit is as shown in table 1 below.
1 performance test results of table
From table 1, it is apparent that the salt fog resistance of the single-component water-based paint prepared by the present invention with high anti-corrosive properties is high
Up to 140h, water resistance reaches 140h, and hardness is high, and impact resistance is strong, while acidproof, alkaline-resisting, resistance to machine oil is had excellent performance.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all in essence of the invention
Made any modification, equivalent replacement or improvement etc., should all be included in the protection scope of the present invention within mind and principle.
Claims (9)
1. a kind of single-component water-based paint with high anti-corrosive properties, it is characterised in that: according to parts by weight, including following component: ring
Oxygen ester resin: 30-50 parts, 1-5 parts of filler, pigment: 16-20 parts, aqueous drier: 5-7 parts, neutralizer: 0.1-0.4 parts, disappear
Infusion: 0.1-0.3 parts, wetting dispersing agent: 0.3-0.5 parts, substrate wetting agents: 0.3-0.5 parts, deionized water: 2-5 parts, hydrotropy
Agent: 3-5 parts, zinc oxide: 3-5 parts, amino resins: 3-5 parts.
2. as described in claim 1 with the single-component water-based paint of high anti-corrosive properties, it is characterised in that: the amino resins is first
Etherified amino resins.
3. as described in claim 1 with the single-component water-based paint of high anti-corrosive properties, it is characterised in that: the neutralizer is diformazan
At least one of ethylethanolamine or 2-amino-2-methyl-1-propanol.
4. as described in claim 1 with the single-component water-based paint of high anti-corrosive properties, it is characterised in that: the pigment includes titanium white
Powder and rust resisting pigment, wherein the mass ratio of the titanium dioxide and rust resisting pigment is 5:(3-5).
5. as described in claim 1 with the single-component water-based paint of high anti-corrosive properties, it is characterised in that: the defoaming agent is polyethers
At least one of copolymeric siloxane species defoaming agent or polysiloxane defoaming agent.
6. as described in claim 1 with the single-component water-based paint of high anti-corrosive properties, it is characterised in that: the wetting dispersing agent is
Mass ratio is (0.8-1.1): polycarboxylic acid salt's dispersing agent of (0.8-1.1) and the mixture of nonionic surfactant.
7. as described in claim 1 with the single-component water-based paint of high anti-corrosive properties, it is characterised in that: the substrate wetting agents are
The wetting agent of Siloxane-Oxyalkylene Copolymers class.
8. a kind of preparation method of the single-component water-based paint with high anti-corrosive properties, it is characterised in that: at least include the following steps:
Step a, each component is weighed according to raw material proportioning as described in any one of claims 1 to 7；
Step b, by the epoxy ester resin, pigments and fillers, rust resisting pigment, aqueous drier, neutralizer, defoaming agent, wetting and dispersing
Agent, substrate wetting agents, deionized water, cosolvent, zinc oxide, amino resins carry out mixing treatment, obtain mixture；
Step c, the mixture is ground, fineness obtains the single group with high anti-corrosive properties less than 25 microns
Part water paint.
9. the preparation method of the single-component water-based paint with high anti-corrosive properties as claimed in claim 8, it is characterised in that: the step
The condition of mixing treatment in rapid b are as follows: 10-20min is stirred with the speed of 400-600rpm.