CN109232017A - A kind of inorganic powder thermal insulation mortar - Google Patents
A kind of inorganic powder thermal insulation mortar Download PDFInfo
- Publication number
- CN109232017A CN109232017A CN201811320587.9A CN201811320587A CN109232017A CN 109232017 A CN109232017 A CN 109232017A CN 201811320587 A CN201811320587 A CN 201811320587A CN 109232017 A CN109232017 A CN 109232017A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- thermal insulation
- inorganic
- insulation mortar
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of inorganic powder thermal insulation mortars, raw material including following parts by weight: 30-50 parts of inorganic coagulation material, 25-30 parts of modified and light aggregate powder, 5-10 parts of diatom ooze, 4-6 parts of foamed ceramic particle, 6-10 parts of polystyrene particle, 2-4 parts of brucite fiber, 2-3 parts of ground pumice and 6-7 parts of additive, and additive includes retarder, water-retaining agent, thickener, adhesive and foaming agent.The present invention increases diatom ooze, foamed ceramic particle, polystyrene particle, brucite fiber and ground pumice on the basis of original, under the cooperation of additive, so that the thermal insulation property of inorganic powder mortar is greatly improved, is conducive to the use of people.
Description
Technical field
The present invention relates to field of mortar more particularly to a kind of inorganic powder thermal insulation mortars.
Background technique
Inorganic powder mortar refer to modified and light aggregate, inorganic coagulation material and additive through dry screening process etc. by
Certain proportion carries out a kind of graininess made of physical mixed or powdery, passes through the material that can be used directly after adding water to mix and stir;
Inorganic powder mortar is also referred to as dry mortar powder, dry blend, dry mixing powder.But the thermal insulation property of existing inorganic powder mortar
Difference, therefore we have proposed a kind of inorganic powder thermal insulation mortars for solving the above problems.
Summary of the invention
Technical problems based on background technology, the invention proposes a kind of inorganic powder thermal insulation mortars.
A kind of inorganic powder thermal insulation mortar proposed by the present invention, the raw material including following parts by weight: inorganic coagulation material 30-
50 parts, 25-30 parts of modified and light aggregate powder, 5-10 parts of diatom ooze, 4-6 parts of foamed ceramic particle, polystyrene particle 6-10
Part, 2-4 parts of brucite fiber, 2-3 parts of ground pumice and 6-7 parts of additive, and additive include retarder, water-retaining agent, thickener,
Adhesive and foaming agent.
Preferably, the raw material including following parts by weight: 35-45 parts of inorganic coagulation material, modified and light aggregate powder 27-28
Part, is floated at 7-8 parts of diatom ooze, 4.5-5.5 parts of foamed ceramic particle, 7-9 parts of polystyrene particle, 2.5-3.5 parts of brucite fiber
2.2-2.8 parts and additive 6.2-6.8 parts of mountain flour, and additive includes retarder, water-retaining agent, thickener, adhesive and gets angry
Agent.
Preferably, the raw material including following parts by weight: 40 parts of inorganic coagulation material, 27.5 parts of modified and light aggregate powder,
7.5 parts of diatom ooze, 5 parts of foamed ceramic particle, 8 parts of polystyrene particle, 3 parts of brucite fiber, 2.5 parts of ground pumice and additive
6.5 parts, and additive includes retarder, water-retaining agent, thickener, adhesive and foaming agent.
Preferably, the retarder is the mixture of hydroxycarboxylic acid and organic phospho acid.
Preferably, the water-retaining agent is the mixture of methylcellulose and hydroxy propyl cellulose according to 2:8 ratio.
Preferably, the thickener is gypsum, ethoxylated alkyl vulcanized sodium, dodecyl sodium sulfate and water-reducing agent group
At.
Preferably, the adhesive is phenolic resin.
Preferably, the foaming agent is aluminium powder.
Preferably, the inorganic coagulation material is the mixture of coal dust and desulfurized gypsum.
Preferably, preparation method includes the following steps:
S1: the diatom ooze of selection is crushed using ultrasonic grind equipment, and grinding time is set as 20-30min,
It recycles sieve to be sieved, obtains diatom ooze powder, for use;
S2: the foamed ceramic particle of selection is ground using grinder, is recycled sieve to be sieved, is foamed
Ceramic powders, for use;
S3: the brucite fiber of selection is crushed using ultrasonic grind equipment, grinding time is set as 15-
20min recycles sieve to be sieved, obtains brucite fiber powder, for use;
S4: by the diatom ooze powder in inorganic coagulation material, modified and light aggregate powder, polystyrene particle, ground pumice, S1
The brucite fiber powder in foamed ceramic powder and S3 in end, S2 is proportionally added sequentially to carry out in high-speed mixer
Mixing, the internal temperature of high-speed mixer is set as 80-120 DEG C, and incorporation time is set as 50-80 minutes;
S5: the high-speed mixer in the S4 during mixing, then successively by retarder, water-retaining agent, thickener,
Adhesive and foaming agent are successively added in high-speed mixer in sequence, finally obtain inorganic powder thermal insulation mortar.
The beneficial effects of the present invention are: increasing diatom ooze, foamed ceramic particle, polystyrene grain on the basis of original
Son, brucite fiber and ground pumice, under the cooperation of additive, so that the thermal insulation property of inorganic powder mortar is greatly mentioned
Height is conducive to the use of people.
Specific embodiment
Combined with specific embodiments below the present invention is made further to explain.
Embodiment one
The invention proposes a kind of inorganic powder thermal insulation mortar, the raw material including following parts by weight: inorganic coagulation material 30
Part, 30 parts of modified and light aggregate powder, 10 parts of diatom ooze, 6 parts of foamed ceramic particle, 10 parts of polystyrene particle, shepardite are fine
4 parts of dimension, 3 parts of ground pumice and 7 parts of additive, and additive includes retarder, water-retaining agent, thickener, adhesive and foaming agent, is delayed
Solidifying agent is the mixture of hydroxycarboxylic acid and organic phospho acid, and water-retaining agent is methylcellulose and hydroxy propyl cellulose according to 2:8 ratio
Mixture, thickener are that gypsum, ethoxylated alkyl vulcanized sodium, dodecyl sodium sulfate and water-reducing agent composition, adhesive are
Phenolic resin, foaming agent are aluminium powder, and inorganic coagulation material is the mixture of coal dust and desulfurized gypsum;
Preparation method includes the following steps:
S1: the diatom ooze of selection is crushed using ultrasonic grind equipment, and grinding time is set as 20min, then
It is sieved using sieve, obtains diatom ooze powder, for use;
S2: the foamed ceramic particle of selection is ground using grinder, is recycled sieve to be sieved, is foamed
Ceramic powders, for use;
S3: the brucite fiber of selection is crushed using ultrasonic grind equipment, grinding time is set as
15min recycles sieve to be sieved, obtains brucite fiber powder, for use;
S4: by the diatom ooze powder in inorganic coagulation material, modified and light aggregate powder, polystyrene particle, ground pumice, S1
The brucite fiber powder in foamed ceramic powder and S3 in end, S2 is proportionally added sequentially to carry out in high-speed mixer
Mixing, the internal temperature of high-speed mixer is set as 80 DEG C, and incorporation time is set as 50 minutes;
S5: the high-speed mixer in the S4 during mixing, then successively by retarder, water-retaining agent, thickener,
Adhesive and foaming agent are successively added in high-speed mixer in sequence, finally obtain inorganic powder thermal insulation mortar.
Embodiment two
The invention proposes a kind of inorganic powder thermal insulation mortar, the raw material including following parts by weight: inorganic coagulation material 35
Part, 28 parts of modified and light aggregate powder, 8 parts of diatom ooze, 5.5 parts of foamed ceramic particle, 9 parts of polystyrene particle, shepardite are fine
3.5 parts of dimension, 2.8 parts of ground pumice and 6.8 parts of additive, and additive includes retarder, water-retaining agent, thickener, adhesive and hair
Gas agent, retarder are the mixture of hydroxycarboxylic acid and organic phospho acid, and water-retaining agent is methylcellulose and hydroxy propyl cellulose according to 2:8
The mixture of ratio, thickener are gypsum, ethoxylated alkyl vulcanized sodium, dodecyl sodium sulfate and water-reducing agent composition, glue
Glutinous agent is phenolic resin, and foaming agent is aluminium powder, and inorganic coagulation material is the mixture of coal dust and desulfurized gypsum;
Preparation method includes the following steps:
S1: the diatom ooze of selection is crushed using ultrasonic grind equipment, and grinding time is set as 20min, then
It is sieved using sieve, obtains diatom ooze powder, for use;
S2: the foamed ceramic particle of selection is ground using grinder, is recycled sieve to be sieved, is foamed
Ceramic powders, for use;
S3: the brucite fiber of selection is crushed using ultrasonic grind equipment, grinding time is set as
15min recycles sieve to be sieved, obtains brucite fiber powder, for use;
S4: by the diatom ooze powder in inorganic coagulation material, modified and light aggregate powder, polystyrene particle, ground pumice, S1
The brucite fiber powder in foamed ceramic powder and S3 in end, S2 is proportionally added sequentially to carry out in high-speed mixer
Mixing, the internal temperature of high-speed mixer is set as 80 DEG C, and incorporation time is set as 50 minutes;
S5: the high-speed mixer in the S4 during mixing, then successively by retarder, water-retaining agent, thickener,
Adhesive and foaming agent are successively added in high-speed mixer in sequence, finally obtain inorganic powder thermal insulation mortar.
Embodiment three
The invention proposes a kind of inorganic powder thermal insulation mortar, the raw material including following parts by weight: inorganic coagulation material 40
Part, 27.5 parts of modified and light aggregate powder, 7.5 parts of diatom ooze, 5 parts of foamed ceramic particle, 8 parts of polystyrene particle, shepardite
3 parts of fiber, 2.5 parts of ground pumice and 6.5 parts of additive, and additive includes retarder, water-retaining agent, thickener, adhesive and hair
Gas agent, retarder are the mixture of hydroxycarboxylic acid and organic phospho acid, and water-retaining agent is methylcellulose and hydroxy propyl cellulose according to 2:8
The mixture of ratio, thickener are gypsum, ethoxylated alkyl vulcanized sodium, dodecyl sodium sulfate and water-reducing agent composition, glue
Glutinous agent is phenolic resin, and foaming agent is aluminium powder, and inorganic coagulation material is the mixture of coal dust and desulfurized gypsum;
Preparation method includes the following steps:
S1: the diatom ooze of selection is crushed using ultrasonic grind equipment, and grinding time is set as 25min, then
It is sieved using sieve, obtains diatom ooze powder, for use;
S2: the foamed ceramic particle of selection is ground using grinder, is recycled sieve to be sieved, is foamed
Ceramic powders, for use;
S3: the brucite fiber of selection is crushed using ultrasonic grind equipment, grinding time is set as
18min recycles sieve to be sieved, obtains brucite fiber powder, for use;
S4: by the diatom ooze powder in inorganic coagulation material, modified and light aggregate powder, polystyrene particle, ground pumice, S1
The brucite fiber powder in foamed ceramic powder and S3 in end, S2 is proportionally added sequentially to carry out in high-speed mixer
Mixing, the internal temperature of high-speed mixer is set as 100 DEG C, and incorporation time is set as 65 minutes;
S5: the high-speed mixer in the S4 during mixing, then successively by retarder, water-retaining agent, thickener,
Adhesive and foaming agent are successively added in high-speed mixer in sequence, finally obtain inorganic powder thermal insulation mortar.
Example IV
The invention proposes a kind of inorganic powder thermal insulation mortar, the raw material including following parts by weight: inorganic coagulation material 45
Part, 27 parts of modified and light aggregate powder, 7 parts of diatom ooze, 4.5 parts of foamed ceramic particle, 7 parts of polystyrene particle, shepardite are fine
2.5 parts of dimension, 2.2 parts of ground pumice and 6.2 parts of additive, and additive includes retarder, water-retaining agent, thickener, adhesive and hair
Gas agent, retarder are the mixture of hydroxycarboxylic acid and organic phospho acid, and water-retaining agent is methylcellulose and hydroxy propyl cellulose according to 2:8
The mixture of ratio, thickener are gypsum, ethoxylated alkyl vulcanized sodium, dodecyl sodium sulfate and water-reducing agent composition, glue
Glutinous agent is phenolic resin, and foaming agent is aluminium powder, and inorganic coagulation material is the mixture of coal dust and desulfurized gypsum;
Preparation method includes the following steps:
S1: the diatom ooze of selection is crushed using ultrasonic grind equipment, and grinding time is set as 30min, then
It is sieved using sieve, obtains diatom ooze powder, for use;
S2: the foamed ceramic particle of selection is ground using grinder, is recycled sieve to be sieved, is foamed
Ceramic powders, for use;
S3: the brucite fiber of selection is crushed using ultrasonic grind equipment, grinding time is set as
20min recycles sieve to be sieved, obtains brucite fiber powder, for use;
S4: by the diatom ooze powder in inorganic coagulation material, modified and light aggregate powder, polystyrene particle, ground pumice, S1
The brucite fiber powder in foamed ceramic powder and S3 in end, S2 is proportionally added sequentially to carry out in high-speed mixer
Mixing, the internal temperature of high-speed mixer is set as 120 DEG C, and incorporation time is set as 80 minutes;
S5: the high-speed mixer in the S4 during mixing, then successively by retarder, water-retaining agent, thickener,
Adhesive and foaming agent are successively added in high-speed mixer in sequence, finally obtain inorganic powder thermal insulation mortar.
Embodiment five
The invention proposes a kind of inorganic powder thermal insulation mortar, the raw material including following parts by weight: inorganic coagulation material 50
Part, 25 parts of modified and light aggregate powder, 5 parts of diatom ooze, 4 parts of foamed ceramic particle, 6 parts of polystyrene particle, brucite fiber 2
Part, 2 parts of ground pumice and 6 parts of additive, and additive includes retarder, water-retaining agent, thickener, adhesive and foaming agent, slow setting
Agent is the mixture of hydroxycarboxylic acid and organic phospho acid, and water-retaining agent is methylcellulose and hydroxy propyl cellulose according to the mixed of 2:8 ratio
Object is closed, thickener is gypsum, ethoxylated alkyl vulcanized sodium, dodecyl sodium sulfate and water-reducing agent composition, and adhesive is phenol
Urea formaldehyde, foaming agent are aluminium powder, and inorganic coagulation material is the mixture of coal dust and desulfurized gypsum;
Preparation method includes the following steps:
S1: the diatom ooze of selection is crushed using ultrasonic grind equipment, and grinding time is set as 30min, then
It is sieved using sieve, obtains diatom ooze powder, for use;
S2: the foamed ceramic particle of selection is ground using grinder, is recycled sieve to be sieved, is foamed
Ceramic powders, for use;
S3: the brucite fiber of selection is crushed using ultrasonic grind equipment, grinding time is set as
20min recycles sieve to be sieved, obtains brucite fiber powder, for use;
S4: by the diatom ooze powder in inorganic coagulation material, modified and light aggregate powder, polystyrene particle, ground pumice, S1
The brucite fiber powder in foamed ceramic powder and S3 in end, S2 is proportionally added sequentially to carry out in high-speed mixer
Mixing, the internal temperature of high-speed mixer is set as 120 DEG C, and incorporation time is set as 80 minutes;
S5: the high-speed mixer in the S4 during mixing, then successively by retarder, water-retaining agent, thickener,
Adhesive and foaming agent are successively added in high-speed mixer in sequence, finally obtain inorganic powder thermal insulation mortar.
To inorganic powder thermal insulation mortar made from embodiment one to five, conventional inorganic powder mortar, experimental data are compared
It is as shown in the table:
By above table it is found that it is proposed by the present invention have significantly improve, and implement three be most preferred embodiment.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (10)
1. a kind of inorganic powder thermal insulation mortar, which is characterized in that the raw material including following parts by weight: inorganic coagulation material 30-50
Part, 25-30 parts of modified and light aggregate powder, 5-10 parts of diatom ooze, 4-6 parts of foamed ceramic particle, 6-10 parts of polystyrene particle,
2-4 parts of brucite fiber, 2-3 parts of ground pumice and 6-7 parts of additive, and additive includes retarder, water-retaining agent, thickener, glue
Glutinous agent and foaming agent.
2. a kind of inorganic powder thermal insulation mortar according to claim 1, which is characterized in that the original including following parts by weight
Material: 35-45 parts of inorganic coagulation material, 27-28 parts of modified and light aggregate powder, 7-8 parts of diatom ooze, foamed ceramic particle 4.5-
5.5 parts, 7-9 parts of polystyrene particle, 2.5-3.5 parts of brucite fiber, 2.2-2.8 parts of ground pumice and 6.2-6.8 parts of additive,
And additive includes retarder, water-retaining agent, thickener, adhesive and foaming agent.
3. a kind of inorganic powder thermal insulation mortar according to claim 1, which is characterized in that the original including following parts by weight
Material: 40 parts of inorganic coagulation material, 27.5 parts of modified and light aggregate powder, 7.5 parts of diatom ooze, 5 parts of foamed ceramic particle, polyphenyl second
8 parts of alkene particle, 3 parts of brucite fiber, 2.5 parts of ground pumice and 6.5 parts of additive, and additive includes retarder, water-retaining agent, increasing
Thick dose, adhesive and foaming agent.
4. a kind of inorganic powder thermal insulation mortar according to claim 1, which is characterized in that the retarder is hydroxycarboxylic acid
With the mixture of organic phospho acid.
5. a kind of inorganic powder thermal insulation mortar according to claim 1, which is characterized in that the water-retaining agent is Methyl cellulose
Element and hydroxy propyl cellulose according to 2:8 ratio mixture.
6. a kind of inorganic powder thermal insulation mortar according to claim 1, which is characterized in that the thickener be gypsum,
Ethoxylated alkyl vulcanized sodium, dodecyl sodium sulfate and water-reducing agent composition.
7. a kind of inorganic powder thermal insulation mortar according to claim 1, which is characterized in that the adhesive is phenolic aldehyde tree
Rouge.
8. a kind of inorganic powder thermal insulation mortar according to claim 1, which is characterized in that the foaming agent is aluminium powder.
9. a kind of inorganic powder thermal insulation mortar according to claim 1, which is characterized in that the inorganic coagulation material is coal
The mixture of carbon powder and desulfurized gypsum.
10. a kind of inorganic powder thermal insulation mortar according to claim 1, which is characterized in that preparation method includes following
Step:
S1: the diatom ooze of selection is crushed using ultrasonic grind equipment, and grinding time is set as 20-30min, then benefit
It is sieved with sieve, obtains diatom ooze powder, for use;
S2: the foamed ceramic particle of selection is ground using grinder, is recycled sieve to be sieved, is obtained foamed ceramic
Powder, for use;
S3: the brucite fiber of selection is crushed using ultrasonic grind equipment, and grinding time is set as 15-20min,
It recycles sieve to be sieved, obtains brucite fiber powder, for use;
S4: by inorganic coagulation material, modified and light aggregate powder, polystyrene particle, ground pumice, S1 diatom ooze powder,
Foamed ceramic powder in S2 and the brucite fiber powder in S3 are proportionally added sequentially to be mixed in high-speed mixer
It closes, the internal temperature of high-speed mixer is set as 80-120 DEG C, and incorporation time is set as 50-80 minutes;
S5: the high-speed mixer in the S4 is during mixing, then successively by retarder, water-retaining agent, thickener, gluing
Agent and foaming agent are successively added in high-speed mixer in sequence, finally obtain inorganic powder thermal insulation mortar.