CN109225785A - A kind of vacuum cup - Google Patents
A kind of vacuum cup Download PDFInfo
- Publication number
- CN109225785A CN109225785A CN201810971768.1A CN201810971768A CN109225785A CN 109225785 A CN109225785 A CN 109225785A CN 201810971768 A CN201810971768 A CN 201810971768A CN 109225785 A CN109225785 A CN 109225785A
- Authority
- CN
- China
- Prior art keywords
- parts
- cup body
- cup
- coating
- vacuum cup
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of vacuum cups comprising: cup body is provided with macromolecule material coating in the cup body, and the macromolecule material coating is sprayed in cup body;Manufacture craft of the present invention is simple, suitable for the macromolecule material coating of metal material cup, has stronger adhesive force, which has anion and inhibit bacterium, highly beneficial to human health.
Description
Technical field
The present invention relates to a kind of vacuum cups, belong to technical field of living goods.
Background technique
With the development and the improvement of people's living standards of society, requirement of the people to the quality of life is higher and higher, right
The requirement of cup is also increasingly paid attention to, and general vacuum cup is made of stainless steel metal material, uses vacuum cup in long-time
In the process, the bacteria breed inside vacuum cup is more, currently, the antimicrobial coating of traditional vacuum cup is clear in high-temperature heating and repeatedly
It washes down and be easy to cause breakage and fall off, low to the adhesive force of metal material, the ability without antibacterial can not be prevented effectively
Bacterial reproduction, it is low using degree of safety, it is very unfavorable to human health.
Summary of the invention
(1) technical problems to be solved
To solve the above problems, the present invention provides the macromolecule that a kind of manufacture craft is simple, suitable for metal material cup
Material coating has stronger adhesive force, which has anion and inhibit bacterium, very favorable to human health
Vacuum cup.
(2) technical solution
A kind of vacuum cup of the invention, it is characterised in that: cup body is provided with macromolecule material coating in the cup body,
The macromolecule material coating is sprayed in cup body.
Further, the material of the cup body is set as metal material.
Further, the composition and manufacturing process of the macromolecule material coating are as follows: 10 parts of organosilicon by weight ratio
~30 parts, 0 part~25 parts of silica 1 and 15 parts~20 parts of titanium dioxide pass through 25 parts~45 parts of water, 10 parts~15 parts of alcohol
With 5 parts~10 parts high speed dispersion grindings of adhesive, molecular weight reaches 10 nanoscales, merges it completely, forms coating.
Further, including following implementation steps:
Step 1): the inner surface of cup body is subjected to shock processing using granularity for 35 mesh~55 mesh steel sand, then to cup
The inner surface of body carries out ultrasonic clean processing, and dries;
Step 2): preheating 15min~25min is carried out to the inner surface of cup body, high molecular material is placed in spray gun and is passed through
High pressure painting is to cup body inner wall;
Step 3): the cup sprayed being put into tunnel oven and is toasted, and drying time is 20min~40min,
Ensure that coating is fully cured.
Further, the condition of the processing of ultrasonic clean described in step 1 is 1000W ultrasonic wave.
Further, preheating temperature described in step 2 is 30 DEG C~60 DEG C and the spray gun is 3~5, spray gun
Movement speed is 1.5m/min~2.5m/min, and spray gun pressure is 0.5MPa~0.8MPa, the coating layer thickness of spraying is 10 μm~
30μm。
Further, baking temperature described in step 3 is 200 DEG C~300 DEG C.
(3) beneficial effect
The present invention compared with prior art, has the advantages that manufacture craft of the present invention is simple, is suitable for gold
Belong to the macromolecule material coating of material cup, there is stronger adhesive force, which has anion and inhibit bacterium, right
Human health is highly beneficial.
Detailed description of the invention
Fig. 1 is structural schematic diagram of the invention.
1- cup body;2- macromolecule material coating.
Specific embodiment
Embodiment 1
A kind of formula and preparation process of refined steel ladles micro-porous permeable brick, it is characterised in that: described including cup body 1
Macromolecule material coating 2 is provided in cup body 1, the macromolecule material coating 2 is sprayed in cup body 1;
Wherein, the material of the cup body 1 is set as metal material;
The composition and manufacturing process of the macromolecule material coating 2 are as follows: 10 parts of organosilicon, silica by weight ratio
10 parts and 15 parts of titanium dioxide, by 5 parts of 25 parts of water, 10 parts of alcohol and adhesive part high speed dispersion grindings, molecular weight reaches 10
Nanoscale merges it completely, forms coating;
Including following implementation steps:
Step 1): the inner surface of cup body 1 is subjected to shock processing using the steel sand that granularity is 35 mesh, then in cup body
Surface carries out ultrasonic clean processing, and dries;
Step 2): preheating 15min is carried out to the inner surface of cup body 1, high molecular material is placed in spray gun and passes through high pressure spray
It is coated onto cup body inner wall;
Step 3): the cup sprayed being put into tunnel oven and is toasted, drying time 20min, it is ensured that is applied
Layer is fully cured;
The condition of the processing of ultrasonic clean described in step 1 is 1000W ultrasonic wave;
Preheating temperature described in step 2 is 30 DEG C and the spray gun is 3, and spray gun movement speed is 1.5m/min, spray
Rifle pressure is 0.5MPa, and the coating layer thickness of spraying is 10 μm;
Baking temperature described in step 3 is 200 DEG C.
Embodiment 2
A kind of formula and preparation process of refined steel ladles micro-porous permeable brick, it is characterised in that: described including cup body 1
Macromolecule material coating 2 is provided in cup body 1, the macromolecule material coating 2 is sprayed in cup body 1;
Wherein, the material of the cup body 1 is set as metal material;
The composition and manufacturing process of the macromolecule material coating 2 are as follows: 20 parts of organosilicon, silica by weight ratio
15 parts and 17 parts of titanium dioxide, by 8 parts of 30 parts of water, 13 parts of alcohol and adhesive high speed dispersion grindings, molecular weight reaches 10 and receives
Meter level merges it completely, forms coating;
Including following implementation steps:
Step 1): the inner surface of cup body 1 is subjected to shock processing using the steel sand that granularity is 40 mesh, then to cup body 1
Inner surface carries out ultrasonic clean processing, and dries;
Step 2): preheating 20min is carried out to the inner surface of cup body 1, high molecular material is placed in spray gun and passes through high pressure spray
It is coated onto 1 inner wall of cup body;
Step 3): the cup sprayed being put into tunnel oven and is toasted, drying time 30min, it is ensured that is applied
Layer is fully cured;
The condition of the processing of ultrasonic clean described in step 1 is 1000W ultrasonic wave;
Preheating temperature described in step 2 is 45 DEG C and the spray gun is 4, and spray gun movement speed is 2m/min, spray gun
Pressure is 0.6MPa, and the coating layer thickness of spraying is 15 μm;
Baking temperature described in step 3 is 250 DEG C.
Embodiment 3
A kind of formula and preparation process of refined steel ladles micro-porous permeable brick, it is characterised in that: described including cup body 1
Macromolecule material coating 2 is provided in cup body 1, the macromolecule material coating 2 is sprayed in cup body 1;
Wherein, the material of the cup body 1 is set as metal material;
The composition and manufacturing process of the macromolecule material coating 2 are as follows: 30 parts of organosilicon, silica by weight ratio
25 parts and 20 parts of titanium dioxide, by 10 parts of 45 parts of water, 15 parts of alcohol and adhesive high speed dispersion grindings, molecular weight reaches 10 and receives
Meter level merges it completely, forms coating;
Including following implementation steps:
Step 1): the inner surface of cup body 1 is subjected to shock processing using the steel sand that granularity is 55 mesh, then to cup body 1
Inner surface carries out ultrasonic clean processing, and dries;
Step 2): preheating 25min is carried out to the inner surface of cup body 1, high molecular material is placed in spray gun and passes through high pressure spray
It is coated onto 1 inner wall of cup body;
Step 3): the cup sprayed being put into tunnel oven and is toasted, drying time 40min, it is ensured that is applied
Layer is fully cured;
The condition of the processing of ultrasonic clean described in step 1 is 1000W ultrasonic wave;
Preheating temperature described in step 2 is 60 DEG C and the spray gun is 5, and spray gun movement speed is 2.5m/min, spray
Rifle pressure is 0.8MPa, and the coating layer thickness of spraying is 30 μm;
Baking temperature described in step 3 is 300 DEG C.
Manufacture craft of the present invention is simple, suitable for the macromolecule material coating of metal material cup, has stronger attachment
Power, which has anion and inhibits bacterium, highly beneficial to human health.
The above-described embodiments are merely illustrative of preferred embodiments of the present invention, not to structure of the invention
Think and model point is enclosed and is defined.Without departing from the design concept of the invention, ordinary people in the field is to skill of the invention
The all variations and modifications that art scheme is made, should all drop into protection scope of the present invention, in the claimed technology of the present invention
Hold, is all described in the claims.
Claims (7)
1. a kind of vacuum cup, it is characterised in that: including cup body (1), be provided with macromolecule material coating in the cup body (1)
(2), the macromolecule material coating (2) is sprayed in cup body (1).
2. a kind of vacuum cup according to claim 1, it is characterised in that: the material of the cup body (1) is set as metal
Material.
3. a kind of vacuum cup according to claim 1, it is characterised in that: the composition of the macromolecule material coating (2)
And manufacturing process are as follows: 10 parts~30 parts of organosilicon, 0 part~25 parts of silica 1 and titanium dioxide 15 parts~20 by weight ratio
Part, by 5 parts~10 parts 25 parts~45 parts of water, 10 parts~15 parts of alcohol and adhesive high speed dispersion grindings, molecular weight reaches 10
Nanoscale merges it completely, forms coating.
4. a kind of vacuum cup according to claim 1, it is characterised in that: including following implementation steps:
Step 1): the inner surface of cup body (1) is subjected to shock processing using granularity for 35 mesh~55 mesh steel sand, then to cup body
(1) inner surface carries out ultrasonic clean processing, and dries;
Step 2): preheating 15min~25min is carried out to the inner surface of cup body (1), high molecular material is placed in spray gun and passes through height
Pressure sprays to cup body (1) inner wall;
Step 3): the cup sprayed being put into tunnel oven and is toasted, and drying time is 20min~40min, it is ensured that
Coating is fully cured.
5. a kind of vacuum cup according to claim 4, it is characterised in that: the condition of the processing of ultrasonic clean described in step 1
For 1000W ultrasonic wave.
6. a kind of vacuum cup according to claim 4, it is characterised in that: preheating temperature described in step 2 is 30 DEG C~60
DEG C and the spray gun be 3~5, spray gun movement speed is 1.5m/min~2.5m/min, spray gun pressure be 0.5MPa~
0.8MPa, the coating layer thickness of spraying are 10 μm~30 μm.
7. a kind of vacuum cup according to claim 4, it is characterised in that: baking temperature described in step 3 be 200 DEG C~
300℃。