CN109222620A - A kind of cookware and preparation method thereof - Google Patents
A kind of cookware and preparation method thereof Download PDFInfo
- Publication number
- CN109222620A CN109222620A CN201811104448.2A CN201811104448A CN109222620A CN 109222620 A CN109222620 A CN 109222620A CN 201811104448 A CN201811104448 A CN 201811104448A CN 109222620 A CN109222620 A CN 109222620A
- Authority
- CN
- China
- Prior art keywords
- decorative pattern
- iron block
- cookware
- embossing
- aluminium flake
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of preparation methods of cookware, the following steps are included: the forge die of production embossing: preparing one piece of iron block, 49 degree are quenched after turnery processing is good, rough decorative pattern is carved in the iron block plane quenched again, using engraving machine in the rough decorative pattern of iron block surface engraving, hereinafter, the width of decorative pattern controls within 0.6MM, the spacing of decorative pattern controls within 0.6MM decorative pattern height 0.6MM；The embossing iron made is packaged on great tonnage hydraulic machine (3000T~5000T)；The common aluminium flake of buying back is carried out large-tonnage cold pressing to aluminum flake surface with knurling mould, common aluminum flake surface can be made to form cellular decorative pattern, and keep the molecular structure of aluminium flake even closer and be hardened.The invention has the advantages that pot body obtains significant stiffened, because of the stiffened of substrate, keep the durability of cookware more preferable；The convex-concave surface formed after embossing can be such that the service life of coating at least doubles.
Description
Technical field
The present invention relates to kitchen article, more precisely a kind of aluminium stretches cookware.
Background technique
Food, which refers to, can satisfy body normal physiological and biochemical energy requirement, and can continue the substance of ordinary life, right
For human body, it can satisfy the normal life activity need of people and be referred to as food conducive to service life extended substance, food is usual
It is made of carbohydrate, fat, protein, water, the substance of nutrition can be provided by feeding or drinking for the mankind or biology,
The source of food can be the biology of plant, animal or his boundary, for example, fungi or fermented product seem alcohol, the mankind by
Many different modes such as acquisition, cultivation, herding, hunting, fishing and hunting obtain food, common, in order to enable food is more palatable
It is tasty, it needs to process food, for example, enabling to food more may be used food process by the way of heating
Mouth is delicious.
Existing stretching aluminum pot, be first aluminium ingot heating and melting pass through again profession equipment aluminum water is pressed into aluminium sheet, then
After aluminium sheet is punched into disk, pot type required for aluminium flake is drawn by stretching-machine and drawing die；Manufactured by this technique
Cookware pot body it is soft easily-deformable.
Summary of the invention
The object of the present invention is to provide a kind of cookwares and preparation method thereof, and it is too soft to can solve material in the prior art
The shortcomings that being easily deformed.
The invention adopts the following technical scheme:
A kind of preparation method of cookware, comprising the following steps: make the forge die of embossing: prepare one piece of iron block, turning
49 degree are quenched after processing, then carves rough decorative pattern in the iron block plane quenched, using engraving machine in iron block table
Rough decorative pattern is carved in face, and decorative pattern height 0.6MM is hereinafter, the width of decorative pattern controls the spacing control of decorative pattern within 0.6MM
System is within 0.6MM；
Packaged on great tonnage hydraulic machine, 3000T~5000T the embossing iron made；
The common aluminium flake of buying back is carried out large-tonnage cold pressing to aluminum flake surface with knurling mould, common aluminium flake table can be made
Face forms cellular decorative pattern, and keeps the molecular structure of aluminium flake even closer and be hardened.
The invention has the advantages that present invention cookware made of the technique of this stiffened embossing forging and stamping, has following two points good
Place 1, pot body obtain significant stiffened, because of the stiffened of substrate, keep the durability of cookware more preferable；2, the concave-convex table formed after being embossed
After spraying non-sticky coating the service life of coating can at least doubled in face.
Detailed description of the invention
Below with reference to embodiment and attached drawing, the present invention is described in detail, in which:
Fig. 1 is the appearance diagram of the aluminium flake of the prior art.
Fig. 2 is the appearance diagram of the aluminium flake after forging and stamping.
Fig. 3 is common stretching pot abrasion resistance testing device figure.
Fig. 4 is common stretching pot wear-resisting test result figure.
Fig. 5 is that the present invention stretches pot abrasion resistance testing device figure.
Fig. 6 is that the present invention stretches a pot abrasion resistance testing device figure.
Specific embodiment
The specific embodiment that present invention is further explained below:
As shown in Figure 1, a kind of preparation method of cookware, comprising the following steps: make the forge die of embossing: preparing one piece
Iron block quenches 49 degree, then carves rough decorative pattern in the iron block plane quenched after turnery processing is good；What is made
Embossing iron is packaged on great tonnage hydraulic machine (3000T~5000T)；
The common aluminium flake of buying back is carried out large-tonnage cold pressing to aluminum flake surface with knurling mould, common aluminium flake table can be made
Face forms cellular decorative pattern, and keeps the molecular structure of aluminium flake even closer and be hardened.
Present invention cookware made of the technique of this stiffened embossing forging and stamping, has following two points benefit 1, pot body to obtain significantly
Stiffened keep the durability of cookware more preferable because of the stiffened of substrate；2, the convex-concave surface formed after being embossed, is spraying non-sticky painting
The service life of coating can be made at least to double after layer.
The test of ordinary pan is as follows:
Common to stretch pot wear-resisting test 10,000 times, the show-through situation of substrate is as shown in Figure 3,4.
Test of the invention is as follows:
Honeycomb sample pot wear-resisting test 10,000 times, the show-through situation of substrate, as shown in Figure 5,6.
The foregoing is merely illustrative of the preferred embodiments of the present invention, is not intended to limit the invention, all in essence of the invention
Made any modifications, equivalent replacements, and improvements etc., should all be included in the protection scope of the present invention within mind and principle.
Claims (2)
1. a kind of preparation method of cookware, which comprises the following steps: make the forge die of embossing: preparing one piece
Iron block quenches 49 degree, then carves rough decorative pattern in the iron block plane quenched after turnery processing is good, utilize engraving machine
In the rough decorative pattern of iron block surface engraving, decorative pattern height 0.6MM is hereinafter, the width of decorative pattern controls the decorative pattern within 0.6MM
Spacing control within 0.6MM；
Packaged on great tonnage hydraulic machine, 3000T~5000T the embossing iron made；
The common aluminium flake of buying back is carried out large-tonnage cold pressing to aluminum flake surface with knurling mould, common aluminum flake surface shape can be made
At cellular decorative pattern, and keeps the molecular structure of aluminium flake even closer and be hardened.
2. a kind of cookware, which is characterized in that it is prepared by the above method.