CN1092046A - A kind of slag cement compound method of promoting agent - Google Patents

A kind of slag cement compound method of promoting agent Download PDF

Info

Publication number
CN1092046A
CN1092046A CN94101331A CN94101331A CN1092046A CN 1092046 A CN1092046 A CN 1092046A CN 94101331 A CN94101331 A CN 94101331A CN 94101331 A CN94101331 A CN 94101331A CN 1092046 A CN1092046 A CN 1092046A
Authority
CN
China
Prior art keywords
slag
cement
tensio
active agent
compound method
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN94101331A
Other languages
Chinese (zh)
Other versions
CN1045580C (en
Inventor
田键
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN94101331A priority Critical patent/CN1045580C/en
Publication of CN1092046A publication Critical patent/CN1092046A/en
Application granted granted Critical
Publication of CN1045580C publication Critical patent/CN1045580C/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

The invention discloses a kind of slag cement compound method that has tensio-active agent of discharging waste material in the iron and steel smelting production of utilizing, it is characterized in that grog 22-42%, slag 50-70%, gypsum 5-8% and tensio-active agent (CH 2CH 2OH) 3N, sulphite yeast distiller's wort, sodium oxalate combination or wherein any combinations of substances, its total volume is 0.01-0.75 gram, through mixer mill to specific surface area 2500-4500cm 2/ g.This invented technology is simple, and is easy to control, and cost is low, and output can improve 2-3 times, the early strength height, and hydration heat is low, has remarkable economic and social benefit.

Description

A kind of slag cement compound method of promoting agent
The invention belongs to a kind of slag cement compound method that has tensio-active agent of discharging waste material in the iron and steel smelting production of utilizing, be applicable to ground and underground structure, the buildings of various concrete and Steel Concrete product, water conservancy project and marine structure, heat insulating and high-temperature workshop.
China's cement mark is a lot of at present; slag cement for example; the production process of slag cement is identical with ordinary Portland cement; with Portland clinker, gypsum is sent into common grinding in the mill by a certain percentage, according to cement clinker behind the granulation slag drying; scoriaceous quality; change grog and the scoriaceous cooperation grinding fineness of cement when, can produce the cement of different mark labels, its prescription is listed as follows:
Figure 941013316_IMG1
" Portland blast ", " gypsum slag cement ", " with other clinker-free cements of Iron And Steel Industry slag preparation " are disclosed in " cement technology " " blast-furnace slag and slag cement " literary composition in (institution of higher education's teaching material on probation in July, 1991), the problem that these cement exist is, at the bottom of the early strength, sclerosis is slow, and label descends.
Chinese patent by retrieval, application number is 89101567.1 " dross slag cements ", 87107956.9 " method for making steam curing cement ", 87107249.1 " low clinker phosphorous residue cement and processing method ", 88107684.8 " prescriptions of mixed cement material from phosphorus slag ", in these cement formulas, all do not add tensio-active agent, exist the problems referred to above equally, do not find that by retrieval a kind of slag cement of promoting agent is disclosed.
The slag cement compound method that the purpose of this invention is to provide a kind of promoting agent has solved and has mixed slag and make cement early strength height, hydration heat is low, label is high problem.
For realizing above-mentioned task, the technical scheme that the present invention solves is: the tensio-active agent that adopts slag, grog, gypsum, trace is as the cement component part.With the slag is major ingredient, slag quality coefficient (CaO+AC 2O 3+ MgO/SiO 2+ P 2O 5) must not be less than 1: 2.Grog and gypsum are the promoting agent exciting agent, and slag is played the dual excitation of alkalescence, vitriol, because produce hydrated calcium silicate after the grog aquation, hydrated products such as drated calcium aluminate produce pectisation.And the Calucium Silicate powder in the middle of them can be more stable in conjunction with generating crystal with gypsum.Generate the higher S+AL of intensity 3+→ AFt(ettringite).And tensio-active agent plays the activation slag, stops C 2S, C 3The too early aquation of S plays strong effect in later strength.The volume of tensio-active agent adapts to and can quicken scoriaceous active performance, improves cement intensity.Effective way is, do not improve or delays C 3S, C 2The hydration rate of S and accelerate C 3A, C 4The hydration rate of AF is at C 3A, C 4After AF forms ettringite, form the spatial skeleton of netted product, C 3S continues aquation again, makes the water mudrock structure densification, crosses the high-stability adverse consequences to eliminate fCaO, and intensity is improved.
Adopt the mechanism of surfactant to be: 1. softening slag, make vitreum generation more defects in the slag, slag has super-active; 2. depolymerization C 2The S mineral; 3. make C 3The S mineral crack stress corrosion, promote crack propagation, to weaken cohesive strength.Delay C simultaneously 3The S hydration can be quickened C 3A, C 4The hydration rate of AF utilizes gypsum can make C 3A, C 4The easier formation ettringite of AF forms finer and close water mudrock structure, and strength of cement increases substantially.
With the promoting agent combined grinding on Portland clinker, slag, gypsum, trace surface to specific surface area 2500-4500Cm 2/ g, the best is 2980-4000Cm 2/ g.Can produce the slag cement that has tensio-active agent.Used Portland clinker refers to the grog that existing each cement mill produces, gypsum major ingredient CaSO among the present invention 4, the main tensio-active agent (CH that adds in preparation 2CH 2OH) 3N, Na 2SO 4, C 10H 14N 2O 3Na 22H 2A kind of or any five kinds of following combinations of substances more than two kinds in O, sulphite yeast wine brewing wheat tooth juice, the sodium oxalate, its total volume is the 0.01-0.75 gram, the volume of gypsum is SO 33.5 the optimum mix amount is 5-8%, all meets GB through Physical Test.
Embodiment:
Raw materials used chemical ingredients is listed as follows:
Figure 941013316_IMG2
The slag cement prescription that the present invention has tensio-active agent is listed as follows:
The present invention is by ruggedness test, and existing antagonism folding, ultimate compression strength are listed as follows:
Figure 941013316_IMG4
The inventive method is easily gone, and technology is simple, and is easy to control, the slag consumption is big, and the grog consumption is few, has eliminated the pollution of slag to environment, drought period the intensity height, aquation is ripe low, label height, intensity stabilization, can make cement output improve 2~3 times, cost is low, adapts to suitability for industrialized production, has remarkable economical and social benefit.

Claims (1)

1, a kind of slag cement compound method of promoting agent is characterized in that tensio-active agent (CH 2CH 2OH) 3N, Na 2SO 4, C 10H 14N 2O 3Na 22H 2A kind of or any five kinds of following combinations of substances more than two kinds in O, sulphite yeast wine brewing wheat tooth juice, the sodium oxalate, its total volume are that 0.01-0.75 gram, slag 50-60%, grog 22-42%, gypsum 5-8% are prepared.
CN94101331A 1994-02-02 1994-02-02 Method for manufacture of slag cement containing activator Expired - Fee Related CN1045580C (en)