CN109201633A - A kind of Environmental-protecting dust-removing device metal fittings dedusting cleaning process - Google Patents
A kind of Environmental-protecting dust-removing device metal fittings dedusting cleaning process Download PDFInfo
- Publication number
- CN109201633A CN109201633A CN201811191758.2A CN201811191758A CN109201633A CN 109201633 A CN109201633 A CN 109201633A CN 201811191758 A CN201811191758 A CN 201811191758A CN 109201633 A CN109201633 A CN 109201633A
- Authority
- CN
- China
- Prior art keywords
- metal fittings
- parts
- cleaning
- stainless steel
- dedusting
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to Environmental-protecting dust-removing device metal fittings working process technical fields, and in particular to a kind of Environmental-protecting dust-removing device metal fittings dedusting cleaning process;The following steps are included: (1) dedusting;(2) prerinse;(3) depth is cleaned;(4) surface preparation;(5) alkali cleaning;(6) it washes;(7) it dries;A kind of Environmental-protecting dust-removing device metal fittings dedusting cleaning process provided by the invention, the treatment process is dusted processing to metal fittings first, the dust on metal fittings surface is purged, it is cleaned using prerinse and depth, it is rolled by the stainless steel hexagonal cylinder to the metal fittings after prerinse, cleaning agent is added simultaneously, further improves the effect of cleaning;Technique provided by the invention can carry out metal fittings surface thoroughly and adequately cleaning, accomplishing metal fittings more beautiful and more added with texture, meeting the use in market, at the same have the advantages that simple process, handle it is high-quality.
Description
Technical field
The present invention relates to Environmental-protecting dust-removing device metal fittings working process technical fields, and in particular to a kind of Environmental-protecting dust-removing device
With metal fittings dedusting cleaning process.
Background technique
The equipment that dust is separated from flue gas is deduster or cleaner.The performance of deduster is with accessible
Drag losses and efficiency of dust collection when gas flow, gas are by deduster are expressed.Meanwhile price, operation and the dimension of deduster
The difficulty or ease of shield expense, service life length and operational administrative are also an important factor for considering its performance.Deduster is boiler and work
Common facility in industry production.
Cleaning refers to the liquid and solid pollutant for removing workpiece surface, and workpiece surface is made to reach certain cleanliness.Clearly
Washing is also one of very important intermediate auxiliary process in heat treatment production process.It is all add through machine, be heat-treated before workpiece all
Should carry out.Otherwise, the greasy dirt etc. being heat-treated on forward and backward workpiece surface is directly entered heating volatilization and burning in furnace, be easy to cause
Workshop air pollution, workpieces surface condition is also bad, or even influences thermal treatment quality, especially to thermo-chemical treatment and vacuum
Heat treatment.Heat treatment production efficiency and thermal treatment quality can be improved in cleaning, and the related environmental protection with heat treatment, cleaning belongs to cleaning
It is heat-treated scope.
As the Chinese invention patent of Publication No. CN105369270A discloses a kind of metalwork dedusting cleaning process, step
It include: (1) prerinse;(2) dedusting;(3) ultrasonic cleaning;(4) it air-dries;(5) alkali cleaning;(6) it rinses;(7) it dries, by metalwork
Dedusting and cleaning procedure be combined together, and can be dusted during cleaning, be cleaned again than first dedusting
Technique saves time and technical process, is pre-processed using dust removal operation to metalwork, it is possible to prevente effectively from dust meets aqueous fusion
Change, then just sticking not only can remove the dust on metalwork surface in dust removal operation on the surface of metalwork and can also remove
The moisture on metalwork surface avoids and has an impact to the concentration and ingredient of the post-processing liquid of metalwork, influences metalwork
The service life of post-processing liquid, make the solution that makes of alkali cleaning when processing will not be because of ultrasonic cleaning when clear water generate shadow
It rings, improves the effect of cleaning, save time and water resource.
The metalwork dedusting cleaning process of foregoing invention, although saving time and work than the technique that first dedusting is cleaned again
Skill process avoids and has an impact to the concentration and ingredient of the post-processing liquid of metalwork, influences the post-processing liquid of metalwork
Service life, but cannot ensure that metal fittings clean thorough situation, and be not suitable for profiled metal accessory and batch accessory
Cleaning, therefore, there is an urgent need to research and develop a kind of Environmental-protecting dust-removing device to meet city with metal fittings dedusting cleaning process at present
The demand of field.
Summary of the invention
In view of the deficiencies of the prior art, the present invention provides a kind of Environmental-protecting dust-removing device metal fittings dedusting cleaning process,
Metal fittings surface can be carried out thoroughly and adequately cleaning, accomplishing metal fittings more beautiful and more added with texture, completely
The foot use in market, while having the advantages that simple process, processing are high-quality.
In order to achieve the above object, the present invention is achieved by the following technical programs:
A kind of Environmental-protecting dust-removing device metal fittings dedusting cleaning process, comprising the following steps:
(1) it dedusting: is purged by dust of the electrostatic cleaner to metal fittings surface;
(2) prerinse: the metal fittings after dedusting are put into stainless steel hexagonal cylinder, and is put into service sink and is rushed
It washes, rinses 20-50min;
(3) depth is cleaned: it is 50-80 DEG C that the stainless steel hexagonal cylinder with the metal fittings after prerinse, which is put into temperature,
In warm water, at the same simultaneously thereto be added 5-8g cleaning agent, stainless steel hexagonal cylinder tumbling rate be 5-10r/min under conditions of into
Row slowly rolls, and carries out immersion 50-80min again after the 20-50min that rolls;
(4) surface preparation: the stainless steel hexagonal cylinder with the metal fittings after depth cleaning is immersed in degreasing agent, leaching
Bubble degreasing 5-10min is then immersed in rust remover controlled at 25-55 DEG C and impregnates 5-10min;
(5) alkali cleaning;
(6) it washes: the stainless steel hexagonal cylinder of the metal fittings after alkali cleaning being immersed in the clear water that temperature is 55-65 DEG C and is carried out
Cleaning, scavenging period 5-10min;
(7) it dries: the metal fittings after washing is subjected to drying and processing, drying time 10-15min.
Cleaning agent in step (3) is by parts by weight meter, including following components: 10-15 parts of sodium carbonate, sodium citrate 12-18
Part, 10-20 parts of neopelex, 3-5 parts of alkyl phosphate and 30-50 parts of deionized water.
Degreasing agent in step (4) is by parts by weight meter, including following components: 20-35 parts of hydrochloric acid, 8-12 parts of acetic acid, sulfuric acid
5-8 parts of ammonium, 2-6 parts of sodium citrate, 2-5 parts of sodium nitrate, 1-4 parts of glycerine, 3-7 parts of cyclohexanol, 6-12 parts of emulsifier and go from
Sub- water 25-40 parts.
Alkali cleaning in step (5) the following steps are included:
Under room temperature, the stainless steel hexagonal cylinder of the metal fittings after surface preparation is immersed in sodium hydroxide solution, it is stainless
Steel hexagonal cylinder is slowly rolled under conditions of tumbling rate is 5r/min, carries out immersion 10min again after the 20min that rolls, so
After transfer them in rinse bath, immersion treatment at normal temperature.
The mass fraction of sodium hydroxide solution is 10-15%.
The temperature dried in step (7) is 50-65 DEG C.
The utility model has the advantages that
A kind of Environmental-protecting dust-removing device metal fittings dedusting cleaning process provided by the invention, the treatment process is first to metal
Accessory is dusted processing, is purged to the dust on metal fittings surface, cleans using prerinse and depth, by pre-
The stainless steel hexagonal cylinder of metal fittings after cleaning rolls, while cleaning agent is added, and further improves the effect of cleaning
Fruit;Surface preparation is carried out to metal fittings by increasing, the grease on metal fittings surface can be not only purged, but also
The layer that gets rusty on metal fittings surface can be purged, keep metal fittings long-term bright as new;Finally by alkali cleaning, washing
And drying and processing, each process is all linked with one another, and efficiency is very high, and it is energy-saving, and clean thorough.
The present invention carries out the working process of links process by being placed on metal fittings in stainless steel hexagonal cylinder, and
And by carrying out continuous rolling cleaning in the warm water that cleaning agent is added to stainless steel hexagonal cylinder, conventional ultrasound cleaning is avoided
Mode, improve the completeness of its cleaning, to improve cleaning effect, and pass through the setting of stainless steel hexagonal cylinder, can
To be suitble to the cleaning of profiled metal accessory, while the batch cleaning of metal fittings can be carried out, further increase its cleaning
Efficiency saves scavenging period.
Technique provided by the invention can carry out metal fittings surface thoroughly and adequately cleaning, and accomplish metal fittings
It is more beautiful and more added with texture, the use in market is met, while having the advantages that simple process, processing are high-quality.
Detailed description of the invention
Fig. 1 is process flow diagram of the invention.
Specific embodiment
In order to make the object, technical scheme and advantages of the embodiment of the invention clearer, below in conjunction with the embodiment of the present invention,
Technical scheme in the embodiment of the invention is clearly and completely described, it is clear that described embodiment is the present invention one
Divide embodiment, instead of all the embodiments.Based on the embodiments of the present invention, those of ordinary skill in the art are not making
Every other embodiment obtained, shall fall within the protection scope of the present invention under the premise of creative work.
Embodiment 1:
A kind of Environmental-protecting dust-removing device metal fittings dedusting cleaning process, comprising the following steps:
(1) it dedusting: is purged by dust of the electrostatic cleaner to metal fittings surface;
(2) prerinse: the metal fittings after dedusting are put into stainless steel hexagonal cylinder, and is put into service sink and is rushed
It washes, rinses 20min;
(3) depth is cleaned: the stainless steel hexagonal cylinder with the metal fittings after prerinse is put into the temperature that temperature is 50 DEG C
In water, while 5g cleaning agent being simultaneously added thereto, stainless steel hexagonal cylinder carries out slow under conditions of tumbling rate is 5r/min
It rolls, carries out immersion 50min again after the 20min that rolls;
(4) surface preparation: the stainless steel hexagonal cylinder with the metal fittings after depth cleaning is immersed in degreasing agent, leaching
Bubble degreasing 5min is then immersed in rust remover controlled at 25 DEG C and impregnates 5min;
(5) alkali cleaning;
(6) it washes: the stainless steel hexagonal cylinder of the metal fittings after alkali cleaning being immersed in the clear water that temperature is 55 DEG C and is carried out clearly
It washes, scavenging period 5min;
(7) it dries: the metal fittings after washing is subjected to drying and processing, drying time 10min.
Cleaning agent in step (3) is by parts by weight meter, including following components: 10 parts of sodium carbonate, 14 parts of sodium citrate, 12
10 parts of sodium alkyl benzene sulfonate, 4 parts of alkyl phosphate and 35 parts of deionized water.
Degreasing agent in step (4) is by parts by weight meter, including following components: 20 parts of hydrochloric acid, 10 parts of acetic acid, 5 parts of ammonium sulfate,
4 parts of sodium citrate, 2 parts of sodium nitrate, 2 parts of glycerine, 3 parts of cyclohexanol, 8 parts of emulsifier and 25 parts of deionized water.
Alkali cleaning in step (5) the following steps are included:
Under room temperature, the stainless steel hexagonal cylinder of the metal fittings after surface preparation is immersed in sodium hydroxide solution, it is stainless
Steel hexagonal cylinder is slowly rolled under conditions of tumbling rate is 5r/min, carries out immersion 10min again after the 20min that rolls, so
After transfer them in rinse bath, immersion treatment at normal temperature.
The mass fraction of sodium hydroxide solution is 10%.
The temperature dried in step (7) is 50 DEG C.
Embodiment 2:
A kind of Environmental-protecting dust-removing device metal fittings dedusting cleaning process, comprising the following steps:
(1) it dedusting: is purged by dust of the electrostatic cleaner to metal fittings surface;
(2) prerinse: the metal fittings after dedusting are put into stainless steel hexagonal cylinder, and is put into service sink and is rushed
It washes, rinses 25min;
(3) depth is cleaned: the stainless steel hexagonal cylinder with the metal fittings after prerinse is put into the temperature that temperature is 60 DEG C
In water, while 6g cleaning agent being simultaneously added thereto, stainless steel hexagonal cylinder carries out slow under conditions of tumbling rate is 6r/min
It rolls, carries out immersion 60min again after the 30min that rolls;
(4) surface preparation: the stainless steel hexagonal cylinder with the metal fittings after depth cleaning is immersed in degreasing agent, leaching
Bubble degreasing 7min is then immersed in rust remover controlled at 30 DEG C and impregnates 7min;
(5) alkali cleaning;
(6) it washes: the stainless steel hexagonal cylinder of the metal fittings after alkali cleaning being immersed in the clear water that temperature is 57 DEG C and is carried out clearly
It washes, scavenging period 7min;
(7) it dries: the metal fittings after washing is subjected to drying and processing, drying time 12min.
Cleaning agent in step (3) is by parts by weight meter, including following components: 14 parts of sodium carbonate, 12 parts of sodium citrate, 12
14 parts of sodium alkyl benzene sulfonate, 3 parts of alkyl phosphate and 30 parts of deionized water.
Degreasing agent in step (4) is by parts by weight meter, including following components: 25 parts of hydrochloric acid, 8 parts of acetic acid, 6 parts of ammonium sulfate,
2 parts of sodium citrate, 3 parts of sodium nitrate, 1 part of glycerine, 4 parts of cyclohexanol, 12 parts of emulsifier and 30 parts of deionized water.
Alkali cleaning in step (5) the following steps are included:
Under room temperature, the stainless steel hexagonal cylinder of the metal fittings after surface preparation is immersed in sodium hydroxide solution, it is stainless
Steel hexagonal cylinder is slowly rolled under conditions of tumbling rate is 5r/min, carries out immersion 10min again after the 20min that rolls, so
After transfer them in rinse bath, immersion treatment at normal temperature.
The mass fraction of sodium hydroxide solution is 12%.
The temperature dried in step (7) is 55 DEG C.
Embodiment 3:
A kind of Environmental-protecting dust-removing device metal fittings dedusting cleaning process, comprising the following steps:
(1) it dedusting: is purged by dust of the electrostatic cleaner to metal fittings surface;
(2) prerinse: the metal fittings after dedusting are put into stainless steel hexagonal cylinder, and is put into service sink and is rushed
It washes, rinses 40min;
(3) depth is cleaned: the stainless steel hexagonal cylinder with the metal fittings after prerinse is put into the temperature that temperature is 70 DEG C
In water, while 7g cleaning agent being simultaneously added thereto, stainless steel hexagonal cylinder carries out slow under conditions of tumbling rate is 8r/min
It rolls, carries out immersion 70min again after the 40min that rolls;
(4) surface preparation: the stainless steel hexagonal cylinder with the metal fittings after depth cleaning is immersed in degreasing agent, leaching
Bubble degreasing 8min is then immersed in rust remover controlled at 35 DEG C and impregnates 8min;
(5) alkali cleaning;
(6) it washes: the stainless steel hexagonal cylinder of the metal fittings after alkali cleaning being immersed in the clear water that temperature is 60 DEG C and is carried out clearly
It washes, scavenging period 8min;
(7) it dries: the metal fittings after washing is subjected to drying and processing, drying time 14min.
Cleaning agent in step (3) is by parts by weight meter, including following components: 12 parts of sodium carbonate, 18 parts of sodium citrate, 12
16 parts of sodium alkyl benzene sulfonate, 5 parts of alkyl phosphate and 45 parts of deionized water.
Degreasing agent in step (4) is by parts by weight meter, including following components: 30 parts of hydrochloric acid, 12 parts of acetic acid, 7 parts of ammonium sulfate,
6 parts of sodium citrate, 4 parts of sodium nitrate, 4 parts of glycerine, 5 parts of cyclohexanol, 10 parts of emulsifier and 35 parts of deionized water.
Alkali cleaning in step (5) the following steps are included:
Under room temperature, the stainless steel hexagonal cylinder of the metal fittings after surface preparation is immersed in sodium hydroxide solution, it is stainless
Steel hexagonal cylinder is slowly rolled under conditions of tumbling rate is 5r/min, carries out immersion 10min again after the 20min that rolls, so
After transfer them in rinse bath, immersion treatment at normal temperature.
The mass fraction of sodium hydroxide solution is 15%.
The temperature dried in step (7) is 60 DEG C.
Embodiment 4:
A kind of Environmental-protecting dust-removing device metal fittings dedusting cleaning process, comprising the following steps:
(1) it dedusting: is purged by dust of the electrostatic cleaner to metal fittings surface;
(2) prerinse: the metal fittings after dedusting are put into stainless steel hexagonal cylinder, and is put into service sink and is rushed
It washes, rinses 45min;
(3) depth is cleaned: the stainless steel hexagonal cylinder with the metal fittings after prerinse is put into the temperature that temperature is 75 DEG C
In water, while 7g cleaning agent being simultaneously added thereto, stainless steel hexagonal cylinder carries out slow under conditions of tumbling rate is 9r/min
It rolls, carries out immersion 75min again after the 45min that rolls;
(4) surface preparation: the stainless steel hexagonal cylinder with the metal fittings after depth cleaning is immersed in degreasing agent, leaching
Bubble degreasing 9min is then immersed in rust remover controlled at 50 DEG C and impregnates 9min;
(5) alkali cleaning;
(6) it washes: the stainless steel hexagonal cylinder of the metal fittings after alkali cleaning being immersed in the clear water that temperature is 60 DEG C and is carried out clearly
It washes, scavenging period 9min;
(7) it dries: the metal fittings after washing is subjected to drying and processing, drying time 14min.
Cleaning agent in step (3) is by parts by weight meter, including following components: 15 parts of sodium carbonate, 16 parts of sodium citrate, 12
18 parts of sodium alkyl benzene sulfonate, 4 parts of alkyl phosphate and 40 parts of deionized water.
Degreasing agent in step (4) is by parts by weight meter, including following components: 35 parts of hydrochloric acid, 10 parts of acetic acid, 8 parts of ammonium sulfate,
5 parts of sodium citrate, 5 parts of sodium nitrate, 3 parts of glycerine, 6 parts of cyclohexanol, 6 parts of emulsifier and 40 parts of deionized water.
Alkali cleaning in step (5) the following steps are included:
Under room temperature, the stainless steel hexagonal cylinder of the metal fittings after surface preparation is immersed in sodium hydroxide solution, it is stainless
Steel hexagonal cylinder is slowly rolled under conditions of tumbling rate is 5r/min, carries out immersion 10min again after the 20min that rolls, so
After transfer them in rinse bath, immersion treatment at normal temperature.
The mass fraction of sodium hydroxide solution is 14%.
The temperature dried in step (7) is 65 DEG C.
Embodiment 5:
A kind of Environmental-protecting dust-removing device metal fittings dedusting cleaning process, comprising the following steps:
(1) it dedusting: is purged by dust of the electrostatic cleaner to metal fittings surface;
(2) prerinse: the metal fittings after dedusting are put into stainless steel hexagonal cylinder, and is put into service sink and is rushed
It washes, rinses 50min;
(3) depth is cleaned: the stainless steel hexagonal cylinder with the metal fittings after prerinse is put into the temperature that temperature is 80 DEG C
In water, while 8g cleaning agent being simultaneously added thereto, stainless steel hexagonal cylinder carries out slow under conditions of tumbling rate is 10r/min
It rolls, carries out immersion 80min again after the 50min that rolls;
(4) surface preparation: the stainless steel hexagonal cylinder with the metal fittings after depth cleaning is immersed in degreasing agent, leaching
Bubble degreasing 10min is then immersed in rust remover controlled at 55 DEG C and impregnates 10min;
(5) alkali cleaning;
(6) it washes: the stainless steel hexagonal cylinder of the metal fittings after alkali cleaning being immersed in the clear water that temperature is 65 DEG C and is carried out clearly
It washes, scavenging period 10min;
(7) it dries: the metal fittings after washing is subjected to drying and processing, drying time 15min.
Cleaning agent in step (3) is by parts by weight meter, including following components: 13 parts of sodium carbonate, 15 parts of sodium citrate, 12
20 parts of sodium alkyl benzene sulfonate, 3 parts of alkyl phosphate and 50 parts of deionized water.
Degreasing agent in step (4) is by parts by weight meter, including following components: 30 parts of hydrochloric acid, 9 parts of acetic acid, 7 parts of ammonium sulfate,
3 parts of sodium citrate, 3 parts of sodium nitrate, 2 parts of glycerine, 7 parts of cyclohexanol, 9 parts of emulsifier and 35 parts of deionized water.
Alkali cleaning in step (5) the following steps are included:
Under room temperature, the stainless steel hexagonal cylinder of the metal fittings after surface preparation is immersed in sodium hydroxide solution, it is stainless
Steel hexagonal cylinder is slowly rolled under conditions of tumbling rate is 5r/min, carries out immersion 10min again after the 20min that rolls, so
After transfer them in rinse bath, immersion treatment at normal temperature.
The mass fraction of sodium hydroxide solution is 13%.
The temperature dried in step (7) is 60 DEG C.
It should be noted that, in this document, relational terms such as first and second and the like are used merely to a reality
Body or operation are distinguished with another entity or operation, are deposited without necessarily requiring or implying between these entities or operation
In any actual relationship or order or sequence.Moreover, the terms "include", "comprise" or its any other variant are intended to
Non-exclusive inclusion, so that the process, method, article or equipment including a series of elements is not only wanted including those
Element, but also including other elements that are not explicitly listed, or further include for this process, method, article or equipment
Intrinsic element.In the absence of more restrictions, the element limited by sentence "including a ...", it is not excluded that
There is also other identical elements in process, method, article or equipment including the element.
The above embodiments are merely illustrative of the technical solutions of the present invention, rather than its limitations;Although with reference to the foregoing embodiments
Invention is explained in detail, those skilled in the art should understand that: it still can be to aforementioned each implementation
Technical solution documented by example is modified or equivalent replacement of some of the technical features;And these modification or
Replacement, the spirit and scope for technical solution of various embodiments of the present invention that it does not separate the essence of the corresponding technical solution.
Claims (6)
1. a kind of Environmental-protecting dust-removing device metal fittings dedusting cleaning process, which comprises the following steps:
(1) it dedusting: is purged by dust of the electrostatic cleaner to metal fittings surface;
(2) prerinse: the metal fittings after dedusting being put into stainless steel hexagonal cylinder, and is put into service sink and is rinsed, punching
Wash 20-50min;
(3) depth is cleaned: the stainless steel hexagonal cylinder with the metal fittings after prerinse is put into the warm water that temperature is 50-80 DEG C
In, while 5-8g cleaning agent being simultaneously added thereto, stainless steel hexagonal cylinder is delayed under conditions of tumbling rate is 5-10r/min
It is slow to roll, immersion 50-80min is carried out again after the 20-50min that rolls;
(4) surface preparation: the stainless steel hexagonal cylinder with the metal fittings after depth cleaning is immersed in degreasing agent, is impregnated de-
Rouge 5-10min is then immersed in rust remover controlled at 25-55 DEG C and impregnates 5-10min;
(5) alkali cleaning;
(6) it washes: the stainless steel hexagonal cylinder of the metal fittings after alkali cleaning being immersed in the clear water that temperature is 55-65 DEG C and is carried out clearly
It washes, scavenging period 5-10min;
(7) it dries: the metal fittings after washing is subjected to drying and processing, drying time 10-15min.
2. a kind of Environmental-protecting dust-removing device metal fittings dedusting cleaning process according to claim 1, it is characterised in that: described
Cleaning agent in step (3) is by parts by weight meter, including following components: 10-15 parts of sodium carbonate, 12-18 parts of sodium citrate, dodecane
10-20 parts of base benzene sulfonic acid sodium salt, 3-5 parts of alkyl phosphate and 30-50 parts of deionized water.
3. a kind of Environmental-protecting dust-removing device metal fittings dedusting cleaning process according to claim 1, it is characterised in that: described
Degreasing agent in step (4) is by parts by weight meter, including following components: 20-35 parts of hydrochloric acid, 8-12 parts of acetic acid, 5-8 parts of ammonium sulfate,
2-6 parts of sodium citrate, 2-5 parts of sodium nitrate, 1-4 parts of glycerine, 3-7 parts of cyclohexanol, 6-12 parts of emulsifier and deionized water 25-40
Part.
4. a kind of Environmental-protecting dust-removing device metal fittings dedusting cleaning process according to claim 1, it is characterised in that: described
Alkali cleaning in step (5) the following steps are included:
Under room temperature, the stainless steel hexagonal cylinder of the metal fittings after surface preparation is immersed in sodium hydroxide solution, stainless steel six
Angle cylinder is slowly rolled under conditions of tumbling rate is 5r/min, carries out immersion 10min again after the 20min that rolls, and then will
It is transferred in rinse bath, at normal temperature immersion treatment.
5. a kind of Environmental-protecting dust-removing device metal fittings dedusting cleaning process according to claim 4, it is characterised in that: described
The mass fraction of sodium hydroxide solution is 10-15%.
6. a kind of Environmental-protecting dust-removing device metal fittings dedusting cleaning process according to claim 1, it is characterised in that: described
The temperature dried in step (7) is 50-65 DEG C.