CN109198784A - High resiliency running shoe and its manufacture craft - Google Patents
High resiliency running shoe and its manufacture craft Download PDFInfo
- Publication number
- CN109198784A CN109198784A CN201811045133.5A CN201811045133A CN109198784A CN 109198784 A CN109198784 A CN 109198784A CN 201811045133 A CN201811045133 A CN 201811045133A CN 109198784 A CN109198784 A CN 109198784A
- Authority
- CN
- China
- Prior art keywords
- high resiliency
- shoe
- running shoe
- mold
- bottom plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of high resiliency running shoes, including the bottom plate with shoe tack, the upper surface pressing of the bottom plate with shoe tack has middle bottom, the upper surface pressing of middle bottom has upper layer, the upper end on the upper layer is circumferentially sewed with vamp, the upper surface of said midsole layer, which offers, to join end to end to form the groove of irregular annular, and the lower end surface on the upper layer offers the card slot with groove shapes in mirror symmetry, and the groove and card slot, which are formed by cavity, is equipped with high resiliency circle.It can be enhanced the wear-resisting water repelling property of shoes, protection shoes make it more resistant to wearing;So that during running more easily.
Description
Technical field
The present invention relates to running shoe correlative technology fields, specially high resiliency running shoe and its manufacture craft.
Background technique
Present people increasingly pay attention to health, and running becomes one of key activities of body-building, current many runnings
More stringent requirements are proposed for elasticity with sports fan to shoes, and the insole sold currently on the market mainly or with comparing passes
The hard bottom footwear material of system, traditional hard bottom footwear material poor flexibility cannot play the role of to bodily protection, while the hard bottom footwear material of tradition is saturating
Gas is poor, is not easy foot health, and therefore, urgent need solves the problems, such as existing footwear material poor flexibility, for this purpose, it is proposed that a kind of high
Elastic running shoe and its manufacture craft.
Summary of the invention
The purpose of the present invention is to provide a kind of antibacterial insoles and preparation method thereof, to solve to propose in above-mentioned background technique
The problem of.
To achieve the above object, the invention provides the following technical scheme:
High resiliency running shoe, including the bottom plate with shoe tack, the upper surface pressing of the bottom plate with shoe tack has middle bottom, middle bottom
Upper surface pressing have a upper layer, the upper end on the upper layer is circumferentially sewed with vamp, and the upper surface of said midsole layer offers head and the tail
It is connected to form the groove of irregular annular, the lower end surface on the upper layer offers the card slot with groove shapes in mirror symmetry, institute
It states groove and card slot is formed by cavity and is equipped with high resiliency circle.
Preferably, the bottom plate with shoe tack is pressed after high-temperature fusion by TPU material.
Preferably, said midsole layer is pressed after high-temperature fusion by EVA material.
Preferably, the upper layer is made of high elastic rubber skin.
Preferably, the high resiliency circle is made of following raw material according to parts by weight:
100-120 parts of polyurethane elastomer, 8-12 parts of lecithin, 30-40 parts of high concrete face rock-fill dam, silicone master batch 2-5
Part, 3-5 parts of foaming agent, 0.5-1 parts of catalyst.
Preferably, the foaming agent is lauryl sodium sulfate;The catalyst is the mixing of bis ether and triethylene diamine
Object.
The manufacture craft of high resiliency running shoe, comprising the following steps:
S1, TPU material is put into the mold of bottom plate of the production with shoe tack after high-temperature smelting pot melts, is formed after mold presses
Bottom plate with shoe tack;EVA material is put into production in the mold of bottom after high-temperature smelting pot melts, is formed after mold presses
With reeded middle bottom;By high elastic rubber skin be cut into the matched upper layer of middle bottom, upper layer through skiving formed with
The card slot of matching grooves;
S2, polyurethane elastomer, lecithin, high concrete face rock-fill dam, silicone master batch, foaming agent and catalyst are mixed
It is even, it is subsequently placed in mold, strikes off, blow bubble, cover mold off, mode locking cures demoulding, is opened, and stands, and polishing obtains high resiliency
Circle;
S3, the bottom plate with shoe tack pressed in step S1, middle bottom and upper layer are sequentially placed on shoes mould, while by step S
Obtained in high resiliency circle be put into the cavity that groove and card slot are formed, successively coat one layer of glue on the contact surface, then pass through
Mold pressing and forming, cooling and demolding obtain the sole of high resiliency running shoe;
S4, the lower end that sole obtained in step S3 is placed on to shoe tree suture gum shoes surfacing material along shoe tree is circumferential with sole,
Obtain semi-finished product running shoe;
S5, semi-finished product running shoe obtained in step S4 is polished, is painted, obtaining high resiliency running shoe finished product.
Preferably, keeping mould temperature in the step S3 in sole bonding processes is 55-65 DEG C, after pressing and forming 10-15min
Die sinking is taken out.
Compared with prior art, the beneficial effects of the present invention are:
1, the bottom plate as made from TPU material with shoe tack is as the contact surface with ground, the bearing capacity of TPU product, shock resistance
Property and damping performance it is prominent, oil resistant, water-fast, resistance to mould can be enhanced the wear-resisting water repelling property of shoes, protection shoes make its more resistant to
It wears;
2, middle bottom is made using EVA material, and having characteristics, the upper layers such as flexibility is good, shockproof, anti-skidding, anti-stress is strong is height
Elastic rubber skin is made, and also has the characteristics that flexibility is good, shockproof, is installed in the cavity that groove is formed with card slot high-elastic
Property circle, enhance the elasticity of shoes so that during running more easily.
Detailed description of the invention
Fig. 1 is schematic structural view of the invention.
In figure: bottom plate 1, middle bottom 2, groove 21, upper layer 3, vamp 4, high resiliency circle 5 with shoe tack.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.It is based on
Embodiment in the present invention, it is obtained by those of ordinary skill in the art without making creative efforts every other
Embodiment shall fall within the protection scope of the present invention.
Referring to Fig. 1, the invention provides the following technical scheme:
Embodiment 1
High resiliency running shoe, including the bottom plate 1 with shoe tack, the upper surface pressing of the bottom plate 1 with shoe tack has middle bottom 2, middle bottom 2
Upper surface pressing have upper layer 3, the upper end on upper layer 3 is circumferentially sewed with vamp 4, and the upper surface of middle bottom 2, which offers, to join end to end
The groove 21 of irregular annular is formed, the lower end surface on upper layer 3 offers the card slot with 21 shape of groove in mirror symmetry, groove 21
High resiliency circle 5 is installed in the cavity formed with card slot.
Specifically, the bottom plate 1 with shoe tack is pressed after high-temperature fusion by TPU material.
Specifically, middle bottom 2 is pressed after high-temperature fusion by EVA material.
Specifically, upper layer 3 is made of high elastic rubber skin.
Specifically, high resiliency circle 5 is made of following raw material according to parts by weight:
100 parts of polyurethane elastomer, 8 parts of lecithin, 30 parts of high concrete face rock-fill dam, 2 parts of silicone master batch, 3 parts of foaming agent,
0.5 part of catalyst.
Specifically, foaming agent is lauryl sodium sulfate;Catalyst is the mixture of bis ether and triethylene diamine.
The manufacture craft of high resiliency running shoe, comprising the following steps:
S1, TPU material is put into after high-temperature smelting pot melts in the mold of bottom plate 1 of the production with shoe tack, the shape after mold presses
At the bottom plate 1 with shoe tack;EVA material is put into after high-temperature smelting pot melts in production in the mold of bottom 2, after mold presses
Form the middle bottom 2 with fluted 21;High elastic rubber skin is cut into and is passed through with the matched upper layer 3 of middle bottom 2, upper layer 3
Skiving is formed and the matched card slot of groove 21;
S2, polyurethane elastomer, lecithin, high concrete face rock-fill dam, silicone master batch, foaming agent and catalyst are mixed
It is even, it is subsequently placed in mold, strikes off, blow bubble, cover mold off, mode locking cures demoulding, is opened, and stands, and polishing obtains high resiliency
Circle 5;
S3, the bottom plate 1 with shoe tack, middle bottom 2 and the upper layer 3 that have pressed in step S1 are sequentially placed on shoes mould, while will step
High resiliency circle 5 obtained in rapid S2 is put into the cavity that groove 21 and card slot are formed, and successively coats one layer of glue on the contact surface, so
Afterwards by mold pressing and forming, cooling and demolding obtains the sole of high resiliency running shoe;
S4, the lower end that sole obtained in step S3 is placed on to shoe tree suture gum shoes surfacing material along shoe tree is circumferential with sole,
Obtain semi-finished product running shoe;
S5, semi-finished product running shoe obtained in step S4 is polished, is painted, obtaining high resiliency running shoe finished product.
Specifically, keeping mould temperature in step S3 in sole bonding processes is 55 DEG C, it is opened and takes out after pressing and forming 10min.
Embodiment 2
High resiliency running shoe, including the bottom plate 1 with shoe tack, the upper surface pressing of the bottom plate 1 with shoe tack has middle bottom 2, middle bottom 2
Upper surface pressing have upper layer 3, the upper end on upper layer 3 is circumferentially sewed with vamp 4, and the upper surface of middle bottom 2, which offers, to join end to end
The groove 21 of irregular annular is formed, the lower end surface on upper layer 3 offers the card slot with 21 shape of groove in mirror symmetry, groove 21
High resiliency circle 5 is installed in the cavity formed with card slot.
Specifically, the bottom plate 1 with shoe tack is pressed after high-temperature fusion by TPU material.
Specifically, middle bottom 2 is pressed after high-temperature fusion by EVA material.
Specifically, upper layer 3 is made of high elastic rubber skin.
Specifically, high resiliency circle 5 is made of following raw material according to parts by weight:
110 parts of polyurethane elastomer, 10 parts of lecithin, 35 parts of high concrete face rock-fill dam, 3 parts of silicone master batch, foaming agent 4
Part, 0.8 part of catalyst.
Specifically, foaming agent is lauryl sodium sulfate;Catalyst is the mixture of bis ether and triethylene diamine.
The manufacture craft of high resiliency running shoe, comprising the following steps:
S1, TPU material is put into after high-temperature smelting pot melts in the mold of bottom plate 1 of the production with shoe tack, the shape after mold presses
At the bottom plate 1 with shoe tack;EVA material is put into after high-temperature smelting pot melts in production in the mold of bottom 2, after mold presses
Form the middle bottom 2 with fluted 21;High elastic rubber skin is cut into and is passed through with the matched upper layer 3 of middle bottom 2, upper layer 3
Skiving is formed and the matched card slot of groove 21;
S2, polyurethane elastomer, lecithin, high concrete face rock-fill dam, silicone master batch, foaming agent and catalyst are mixed
It is even, it is subsequently placed in mold, strikes off, blow bubble, cover mold off, mode locking cures demoulding, is opened, and stands, and polishing obtains high resiliency
Circle 5;
S3, the bottom plate 1 with shoe tack, middle bottom 2 and the upper layer 3 that have pressed in step S1 are sequentially placed on shoes mould, while will step
High resiliency circle 5 obtained in rapid S2 is put into the cavity that groove 21 and card slot are formed, and successively coats one layer of glue on the contact surface, so
Afterwards by mold pressing and forming, cooling and demolding obtains the sole of high resiliency running shoe;
S4, the lower end that sole obtained in step S3 is placed on to shoe tree suture gum shoes surfacing material along shoe tree is circumferential with sole,
Obtain semi-finished product running shoe;
S5, semi-finished product running shoe obtained in step S4 is polished, is painted, obtaining high resiliency running shoe finished product.
Specifically, keeping mould temperature in step S3 in sole bonding processes is 60 DEG C, it is opened and takes out after pressing and forming 12min.
Embodiment 3
High resiliency running shoe, including the bottom plate 1 with shoe tack, the upper surface pressing of the bottom plate 1 with shoe tack has middle bottom 2, middle bottom 2
Upper surface pressing have upper layer 3, the upper end on upper layer 3 is circumferentially sewed with vamp 4, and the upper surface of middle bottom 2, which offers, to join end to end
The groove 21 of irregular annular is formed, the lower end surface on upper layer 3 offers the card slot with 21 shape of groove in mirror symmetry, groove 21
High resiliency circle 5 is installed in the cavity formed with card slot.
Specifically, the bottom plate 1 with shoe tack is pressed after high-temperature fusion by TPU material.
Specifically, middle bottom 2 is pressed after high-temperature fusion by EVA material.
Specifically, upper layer 3 is made of high elastic rubber skin.
Specifically, high resiliency circle 5 is made of following raw material according to parts by weight:
120 parts of polyurethane elastomer, 12 parts of lecithin, 40 parts of high concrete face rock-fill dam, 5 parts of silicone master batch, foaming agent 5
Part, 1 part of catalyst.
Specifically, foaming agent is lauryl sodium sulfate;Catalyst is the mixture of bis ether and triethylene diamine.
The manufacture craft of high resiliency running shoe, comprising the following steps:
S1, TPU material is put into after high-temperature smelting pot melts in the mold of bottom plate 1 of the production with shoe tack, the shape after mold presses
At the bottom plate 1 with shoe tack;EVA material is put into after high-temperature smelting pot melts in production in the mold of bottom 2, after mold presses
Form the middle bottom 2 with fluted 21;High elastic rubber skin is cut into and is passed through with the matched upper layer 3 of middle bottom 2, upper layer 3
Skiving is formed and the matched card slot of groove 21;
S2, polyurethane elastomer, lecithin, high concrete face rock-fill dam, silicone master batch, foaming agent and catalyst are mixed
It is even, it is subsequently placed in mold, strikes off, blow bubble, cover mold off, mode locking cures demoulding, is opened, and stands, and polishing obtains high resiliency
Circle 5;
S3, the bottom plate 1 with shoe tack, middle bottom 2 and the upper layer 3 that have pressed in step S1 are sequentially placed on shoes mould, while will step
High resiliency circle 5 obtained in rapid S2 is put into the cavity that groove 21 and card slot are formed, and successively coats one layer of glue on the contact surface, so
Afterwards by mold pressing and forming, cooling and demolding obtains the sole of high resiliency running shoe;
S4, the lower end that sole obtained in step S3 is placed on to shoe tree suture gum shoes surfacing material along shoe tree is circumferential with sole,
Obtain semi-finished product running shoe;
S5, semi-finished product running shoe obtained in step S4 is polished, is painted, obtaining high resiliency running shoe finished product.
Specifically, keeping mould temperature in step S3 in sole bonding processes is 65 DEG C, it is opened and takes out after pressing and forming 15min.
In this case, the bottom plate 1 as made from TPU material with shoe tack is as the contact surface with ground, the carrying energy of TPU product
Power, impact resistance and damping performance are prominent, and oil resistant, water-fast, resistance to mould can be enhanced the wear-resisting water repelling property of shoes, protect shoes
Son makes it more resistant to wearing;
Middle bottom 2 is made using EVA material, and having characteristics, the upper layers 3 such as flexibility is good, shockproof, anti-skidding, anti-stress is strong is height
Elastic rubber skin is made, and also has the characteristics that flexibility is good, shockproof, is installed with height in the cavity that groove 21 and card slot are formed
Elastic ring 5 enhances the elasticity of shoes, mitigates the physical demands of human body starting, so that during running more easily.
Although having been shown and having retouched the embodiment of the present invention, for the ordinary skill in the art, Ke Yili
Solution without departing from the principles and spirit of the present invention can to these embodiments carry out it is a variety of variation, modification, replacement and
Modification, the scope of the present invention is defined by the appended.
Claims (8)
1. high resiliency running shoe, including the bottom plate (1) with shoe tack, it is characterised in that: the upper surface of the bottom plate (1) with shoe tack
Pressing has middle bottom (2), and the upper surface pressing of middle bottom (2) has upper layer (3), and the upper end of the upper layer (3) is circumferentially sewed with shoes
Face (4), the upper surface of said midsole layer (2), which offers, to join end to end to form the groove (21) of irregular annular, the upper layer (3)
Lower end surface offer be in groove (21) shape mirror symmetry card slot, the groove (21) and card slot are formed by cavity
High resiliency circle (5) are installed.
2. high resiliency running shoe according to claim 1, it is characterised in that: the bottom plate (1) with shoe tack is by TPU material
Material presses after high-temperature fusion.
3. high resiliency running shoe according to claim 1, it is characterised in that: said midsole layer (2) is by EVA material through height
It is pressed after temperature melting.
4. high resiliency running shoe according to claim 1, it is characterised in that: the upper layer (3) is high elastic rubber leather
At.
5. high resiliency running shoe according to claim 1, it is characterised in that: the high resiliency circle (5) is pressed by following raw material
It is formed according to parts by weight:
100-120 parts of polyurethane elastomer, 8-12 parts of lecithin, 30-40 parts of high concrete face rock-fill dam, silicone master batch 2-5
Part, 3-5 parts of foaming agent, 0.5-1 parts of catalyst.
6. high resiliency running shoe according to claim 5, it is characterised in that: the foaming agent is lauryl sodium sulfate;
The catalyst is the mixture of bis ether and triethylene diamine.
7. the manufacture craft of high resiliency running shoe described in -6 according to claim 1, it is characterised in that: the following steps are included:
S1, TPU material is put into after high-temperature smelting pot melts in the mold of bottom plate (1) of the production with shoe tack, after mold presses
Form the bottom plate (1) with shoe tack;EVA material is put into after high-temperature smelting pot melts in production in the mold of bottom (2), through mold
The middle bottom (2) with fluted (21) is formed after pressing;By high elastic rubber skin be cut into middle bottom (2) it is matched on
Layer (3), upper layer (3) are formed and groove (21) matched card slot through skiving;
S2, polyurethane elastomer, lecithin, high concrete face rock-fill dam, silicone master batch, foaming agent and catalyst are mixed
It is even, it is subsequently placed in mold, strikes off, blow bubble, cover mold off, mode locking cures demoulding, is opened, and stands, and polishing obtains high resiliency
It encloses (5);
S3, the bottom plate (1) with shoe tack pressed in step S1, middle bottom (2) and upper layer (3) are sequentially placed on shoes mould, together
When high resiliency circle (5) obtained in step S2 is put into the cavity that groove (21) and card slot are formed, successively apply on the contact surface
One layer of glue is covered, then by mold pressing and forming, cooling and demolding obtains the sole of high resiliency running shoe;
S4, the lower end that sole obtained in step S3 is placed on to shoe tree suture gum shoes surfacing material along shoe tree is circumferential with sole,
Obtain semi-finished product running shoe;
S5, semi-finished product running shoe obtained in step S4 is polished, is painted, obtaining high resiliency running shoe finished product.
8. the manufacture craft of high resiliency running shoe according to claim 7, it is characterised in that: sole pressure in the step S3
It is 55-65 DEG C that mould temperature is kept during closing, and is opened and takes out after pressing and forming 10-15min.