CN109181629A - A kind of calcium carbonate whisker binding paper box glue and preparation method thereof - Google Patents
A kind of calcium carbonate whisker binding paper box glue and preparation method thereof Download PDFInfo
- Publication number
- CN109181629A CN109181629A CN201810783231.2A CN201810783231A CN109181629A CN 109181629 A CN109181629 A CN 109181629A CN 201810783231 A CN201810783231 A CN 201810783231A CN 109181629 A CN109181629 A CN 109181629A
- Authority
- CN
- China
- Prior art keywords
- calcium carbonate
- whisker
- added
- preparation
- paper box
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a kind of calcium carbonate whisker binding paper box glue and preparation method thereof, the binding paper box glue adhesive strength with higher of preparation and excellent water resistance, meanwhile, production cost is low, simple process;Steam explosion is handled after rice straw is carried out spray lye, the fluffy degree and dispersion degree of rice straw is improved, while increasing its toughness, to improve the adhesive strength of adhesive glue;The calcium carbonate crystal whisker of rigidity is combined with rice straw flexible, acts synergistically, significantly enhances the adhesive strength of adhesive glue;In calcium carbonate crystal whisker area load nano silica, the intensity of calcium carbonate crystal whisker is not only increased, further increases adhesive strength, on the other hand also improves the water resistance of adhesive glue, keeps its water resistance excellent.
Description
Technical field
The invention belongs to binding paper box glue technical fields, and in particular to a kind of calcium carbonate whisker binding paper box glue and its system
Preparation Method.
Background technique
Corrugated board in entire wrapping paper container material in occupation of particularly important status, this is because corrugated case is not
But moulding is changeable, is suitble to automatization high speed production, looking display works well, and commodity, price can also be effectively protected
It is cheap, it is easy to be recycled, it not can also cause environmental pollution, be environmental-friend packing material.In China, current almost all of corrugation
Production all uses starch adhesive, although amylum adhesive has source wide, resourceful, nontoxic and pollution-free, at low cost
The advantages that, but it is influenced very big by temperature, constituent, and performance is unstable, and it is easily thinning during recycling, production
Corrugated board easily get damp feel like jelly and the adhesion strength of cardboard caused to reduce, water resistance it is bad.
Summary of the invention
In view of the above-mentioned problems, the present invention is intended to provide a kind of adhesive strength is high, the binding paper box glue and its system of water-tolerant
Preparation Method.
The invention is realized by the following technical scheme:
A kind of calcium carbonate whisker binding paper box glue, which is characterized in that be made of raw material from the following weight:
Rice straw 5-10, poly-vinyl alcohol solution 10-20, calcium carbonate crystal whisker 4-8, sodium silicate aqueous solution 20-40, silane coupling agent
Ethanol solution 30-60, VAE resin emulsion 20-25, soyabean protein powder 40-60, glutinous rice flour 20-30, carboxymethyl cellulose 5-
10, dilute hydrochloric acid solution 3-8;
The VAE resin emulsion solid content is 30-40%.
Further, preparation method includes the following steps:
(1) rice straw is shredded to the segment of 1-2cm, is placed in blender, under 200-300rpm revolving speed, while stirring to
The poly-vinyl alcohol solution for wherein spraying 4-6% is put into steam-explosion jar, being passed through steam to pressure is when moisture content is in 35-45%
1.2-1.3MPa lets out rapidly valve blowing, gains is dried to moisture in 70-80 DEG C of vacuum oven after keeping 3-5min
Content is 5-8%, and being crushed to partial size is 50-500 μm;
(2) calcium carbonate crystal whisker is modified using sodium silicate aqueous solution, obtains modified calcium carbonate whisker;
(3) calcium carbonate crystal whisker of package silica obtained by step (2) is added in the ethanol solution of silane coupling agent, is utilized
Microwave treatment 1-3min is added rice straw obtained by step (1) and is added after stirring 20-30min under 600-800rpm after cooling
VAE resin emulsion, is transferred in reaction kettle, and 10-12h is reacted at 70-75 DEG C, is then cooled down, and filters and dries at 100-120 DEG C
It is dry.
(4) soyabean protein powder is added in the sodium hydroxide solution of 3%-6% of 10-20 times of its volume, 500-1000rpm
Lower stirring is added glutinous rice flour, carboxymethyl cellulose, is warming up to 90-95 DEG C to being completely dispersed, and continues to stir 2-3h, then be added
Step (3) gains stir 1-2h.
Further, step (2) the modified calcium carbonate whisker the preparation method comprises the following steps:
Calcium carbonate crystal whisker is added in the distilled water of 20-30 times of its volume, 40-50min is ultrasonically treated at 40-50 DEG C, so
After sodium silicate aqueous solution is added, be warming up to 70-80 DEG C, and be slowly added to the dilute of 5-10% under the stirring of the revolving speed of 300-400rpm
Hydrochloric acid solution continues after being stirred to react 30-60min, stands 5-8h, using spray drying, obtains package nano silica
Calcium carbonate crystal whisker.
Further, step (3) microwave treatment conditions are 800-1000W.
Further, the ethanol solution mass concentration of step (3) described silane coupling agent is 3-7%, the silane coupling agent
For silane resin acceptor kh-550, Silane coupling reagent KH-570.
Further, the sodium silicate aqueous solution mass concentration is 40-44%.
Beneficial effects of the present invention: binding paper box glue prepared by the present invention adhesive strength with higher and excellent water-fast
Performance, meanwhile, production cost is low, simple process;Steam explosion is handled after rice straw is carried out spray lye, improves rice straw
Fluffy degree and dispersion degree, while increasing its toughness, to improve the adhesive strength of adhesive glue;By rigidity calcium carbonate crystal whisker with it is soft
Property rice straw combine, act synergistically, significantly enhance the adhesive strength of adhesive glue;It is received in calcium carbonate crystal whisker area load
Rice silica, not only increases the intensity of calcium carbonate crystal whisker, further increases adhesive strength, on the other hand also improve bonding
The water resistance of glue keeps its water resistance excellent.
Specific embodiment
Illustrate the present invention with specific embodiment below, but is not limitation of the present invention.
Embodiment 1
A kind of calcium carbonate whisker binding paper box glue, which is characterized in that be made of raw material from the following weight:
Rice straw 5, poly-vinyl alcohol solution 10, calcium carbonate crystal whisker 4, sodium silicate aqueous solution 20, the ethanol solution of silane coupling agent
30, VAE resin emulsions 20, soyabean protein powder 40, glutinous rice flour 20, carboxymethyl cellulose 5, dilute hydrochloric acid solution 3;
The VAE resin emulsion solid content is 30%.
Further, preparation method includes the following steps:
(1) rice straw is shredded to the segment of 1cm, is placed in blender, under 200rpm revolving speed, sprayed thereto while stirring
The poly-vinyl alcohol solution for spilling 4% is put into steam-explosion jar when moisture content is 35%, and being passed through steam to pressure is 1.2MPa, keeps
After 3min, valve blowing is let out rapidly, and it is 5% that gains are dried to moisture content in 70 DEG C of vacuum oven, and being crushed to partial size is
50μm;
(2) calcium carbonate crystal whisker is modified using sodium silicate aqueous solution, obtains modified calcium carbonate whisker;
(3) calcium carbonate crystal whisker of package silica obtained by step (2) is added in the ethanol solution of silane coupling agent, is utilized
Rice straw obtained by step (1) is added in microwave treatment 1min after cooling, after stirring 20min under 600rpm, VAE resin cream is added
Liquid is transferred in reaction kettle, and 10h is reacted at 70 DEG C, is then cooled down, and is filtered and is dried at 100 DEG C.
(4) soyabean protein powder is added in 3% sodium hydroxide solution of 10 times of its volume, is stirred under 500rpm to complete
Full dispersion, is added glutinous rice flour, carboxymethyl cellulose, is warming up to 90 DEG C, continues to stir 2h, step (3) gains are then added,
Stir 1h.
Further, step (2) the modified calcium carbonate whisker the preparation method comprises the following steps:
Calcium carbonate crystal whisker is added in the distilled water of 20 times of its volume, 40min is ultrasonically treated at 40 DEG C, silicic acid is then added
Sodium water solution is warming up to 70 DEG C, and 5% dilute hydrochloric acid solution is slowly added under the stirring of the revolving speed of 300rpm, continues to be stirred to react
After 30min, 5h is stood, using spray drying, obtains the calcium carbonate crystal whisker of package nano silica.
Further, step (3) microwave treatment conditions are 800W.
Further, the ethanol solution mass concentration of step (3) described silane coupling agent is 3%, and the silane coupling agent is
Silane resin acceptor kh-550, Silane coupling reagent KH-570.
Further, the sodium silicate aqueous solution mass concentration is 40%.
Embodiment 2
A kind of calcium carbonate whisker binding paper box glue, which is characterized in that be made of raw material from the following weight:
Rice straw 7, poly-vinyl alcohol solution 15, calcium carbonate crystal whisker 5, sodium silicate aqueous solution 30, the ethanol solution of silane coupling agent
40, VAE resin emulsions 22, soyabean protein powder 50, glutinous rice flour 25, carboxymethyl cellulose 8, dilute hydrochloric acid solution 5;
The VAE resin emulsion solid content is 35%.
Further, preparation method includes the following steps:
(1) rice straw is shredded to the segment of 2cm, is placed in blender, under 250rpm revolving speed, sprayed thereto while stirring
The poly-vinyl alcohol solution for spilling 5% is put into steam-explosion jar when moisture content is 40%, and being passed through steam to pressure is 1.3MPa, keeps
After 4min, valve blowing is let out rapidly, and it is 6% that gains are dried to moisture content in 75 DEG C of vacuum oven, and being crushed to partial size is
100μm;
(2) calcium carbonate crystal whisker is modified using sodium silicate aqueous solution, obtains modified calcium carbonate whisker;
(3) calcium carbonate crystal whisker of package silica obtained by step (2) is added in the ethanol solution of silane coupling agent, is utilized
Rice straw obtained by step (1) is added in microwave treatment 2min after cooling, after stirring 25min under 700rpm, VAE resin cream is added
Liquid is transferred in reaction kettle, and 11h is reacted at 72 DEG C, is then cooled down, and is filtered and is dried at 110 DEG C.
(4) soyabean protein powder is added in 4% sodium hydroxide solution of 15 times of its volume, is stirred under 700rpm to complete
Full dispersion, is added glutinous rice flour, carboxymethyl cellulose, is warming up to 92 DEG C, continues to stir 3h, step (3) gains are then added,
Stir 2h.
Further, step (2) the modified calcium carbonate whisker the preparation method comprises the following steps:
Calcium carbonate crystal whisker is added in the distilled water of 25 times of its volume, 45min is ultrasonically treated at 45 DEG C, silicic acid is then added
Sodium water solution is warming up to 75 DEG C, and 6% dilute hydrochloric acid solution is slowly added under the stirring of the revolving speed of 350rpm, continues to be stirred to react
After 50min, 7h is stood, using spray drying, obtains the calcium carbonate crystal whisker of package nano silica.
Further, step (3) microwave treatment conditions are 900W.
Further, the ethanol solution mass concentration of step (3) described silane coupling agent is 6%, and the silane coupling agent is
Silane resin acceptor kh-550, Silane coupling reagent KH-570.
Further, the sodium silicate aqueous solution mass concentration is 42%.
Embodiment 3
A kind of calcium carbonate whisker binding paper box glue, which is characterized in that be made of raw material from the following weight:
Rice straw 10, poly-vinyl alcohol solution 20, calcium carbonate crystal whisker 8, sodium silicate aqueous solution 40, the ethanol solution of silane coupling agent
60, VAE resin emulsions 25, soyabean protein powder 60, glutinous rice flour 30, carboxymethyl cellulose 10, dilute hydrochloric acid solution 8;
The VAE resin emulsion solid content is 40%.
Further, preparation method includes the following steps:
(1) rice straw is shredded to the segment of 2cm, is placed in blender, under 300rpm revolving speed, sprayed thereto while stirring
The poly-vinyl alcohol solution for spilling 6% is put into steam-explosion jar when moisture content is 45%, and being passed through steam to pressure is 1.3MPa, keeps
After 5min, valve blowing is let out rapidly, and it is 8% that gains are dried to moisture content in 80 DEG C of vacuum oven, and being crushed to partial size is
500μm;
(2) calcium carbonate crystal whisker is modified using sodium silicate aqueous solution, obtains modified calcium carbonate whisker;
(3) calcium carbonate crystal whisker of package silica obtained by step (2) is added in the ethanol solution of silane coupling agent, is utilized
Rice straw obtained by step (1) is added in microwave treatment 3min after cooling, after stirring 30min under 800rpm, VAE resin cream is added
Liquid is transferred in reaction kettle, and 12h is reacted at 75 DEG C, is then cooled down, and is filtered and is dried at 120 DEG C.
(4) soyabean protein powder is added in 6% sodium hydroxide solution of 20 times of its volume, is stirred under 1000rpm to complete
Full dispersion, is added glutinous rice flour, carboxymethyl cellulose, is warming up to 95 DEG C, continues to stir 3h, step (3) gains are then added,
Stir 2h.
Further, step (2) the modified calcium carbonate whisker the preparation method comprises the following steps:
Calcium carbonate crystal whisker is added in the distilled water of 30 times of its volume, 50min is ultrasonically treated at 50 DEG C, silicic acid is then added
Sodium water solution is warming up to 80 DEG C, and 10% dilute hydrochloric acid solution is slowly added under the stirring of the revolving speed of 400rpm, and it is anti-to continue stirring
After answering 60min, 8h is stood, using spray drying, obtains the calcium carbonate crystal whisker of package nano silica.
Further, step (3) microwave treatment conditions are 1000W.
Further, the ethanol solution mass concentration of step (3) described silane coupling agent is 7%, and the silane coupling agent is
Silane resin acceptor kh-550, Silane coupling reagent KH-570.
Further, the sodium silicate aqueous solution mass concentration is 44%.
Comparative example 1
The addition of calcium carbonate crystal whisker is omitted compared to embodiment 1 in this comparative example, and method and step in addition to this is homogeneous
Together.
Comparative example 2
The modifying processing step of calcium carbonate crystal whisker is omitted compared to embodiment 1 in this comparative example, method step in addition to this
It is rapid all the same.
Comparative example 3
Compared to embodiment 1 the spray lye and steam explosion processing step of rice straw is omitted, in addition to this in this comparative example
Method and step is all the same.
Comparative example 4
The addition of rice straw is omitted compared to embodiment 1 in this comparative example, and method and step in addition to this is all the same.
Experiment:
Bond strength test: adhesive glue obtained by each group is glued applied to corrugated board, is glued with a thickness of 2mm, is dried at 90 DEG C
Dry 3min.Then by the adhesive strength of the method detection each group corrugated board in GB/T6548-2011.
Water resistance test: corrugated board being placed in 25 DEG C of water, indicates water resistance power with separation time.
Test result is as shown in table 1:
Table 1
As can be seen from Table 1, calcium carbonate crystal whisker and rice straw collaboration improve the adhesive strength of adhesive glue of the present invention, to the two
Modified and processing also improves its adhesive strength to a certain extent, is significantly improved using nano-silicon dioxide modified calcium carbonate crystal whisker
Its water resistance.
Claims (6)
1. a kind of calcium carbonate whisker binding paper box glue, which is characterized in that be made of raw material from the following weight:
Rice straw 5-10, poly-vinyl alcohol solution 10-20, calcium carbonate crystal whisker 4-8, sodium silicate aqueous solution 20-40, silane coupling agent
Ethanol solution 30-60, VAE resin emulsion 20-25, soyabean protein powder 40-60, glutinous rice flour 20-30, carboxymethyl cellulose 5-
10, dilute hydrochloric acid solution 3-8;
The VAE resin emulsion solid content is 30-40%.
2. a kind of calcium carbonate whisker binding paper box glue according to claim 1, which is characterized in that preparation method includes
Following steps:
(1) rice straw is shredded to the segment of 1-2cm, is placed in blender, under 200-300rpm revolving speed, while stirring to
The poly-vinyl alcohol solution for wherein spraying 4-6% is put into steam-explosion jar, being passed through steam to pressure is when moisture content is in 35-45%
1.2-1.3MPa lets out rapidly valve blowing, gains is dried to moisture in 70-80 DEG C of vacuum oven after keeping 3-5min
Content is 5-8%, and being crushed to partial size is 50-500 μm;
(2) calcium carbonate crystal whisker is modified using sodium silicate aqueous solution, obtains modified calcium carbonate whisker;
(3) calcium carbonate crystal whisker of package silica obtained by step (2) is added in the ethanol solution of silane coupling agent, is utilized
Microwave treatment 1-3min is added rice straw obtained by step (1) and is added after stirring 20-30min under 600-800rpm after cooling
VAE resin emulsion, is transferred in reaction kettle, and 10-12h is reacted at 70-75 DEG C, is then cooled down, and filters and dries at 100-120 DEG C
It is dry.
(4) soyabean protein powder is added in the sodium hydroxide solution of 3%-6% of 10-20 times of its volume, is stirred under 500-1000rpm
It mixes to being completely dispersed, glutinous rice flour, carboxymethyl cellulose is added, is warming up to 90-95 DEG C, continue to stir 2-3h, step is then added
(3) gains stir 1-2h.
3. a kind of calcium carbonate whisker binding paper box glue preparation method according to claim 2, which is characterized in that step
(2) the modified calcium carbonate whisker the preparation method comprises the following steps:
Calcium carbonate crystal whisker is added in the distilled water of 20-30 times of its volume, 40-50min is ultrasonically treated at 40-50 DEG C, so
After sodium silicate aqueous solution is added, be warming up to 70-80 DEG C, and be slowly added to the dilute of 5-10% under the stirring of the revolving speed of 300-400rpm
Hydrochloric acid solution continues after being stirred to react 30-60min, stands 5-8h, using spray drying, obtains package nano silica
Calcium carbonate crystal whisker.
4. a kind of calcium carbonate whisker binding paper box glue preparation method according to claim 2, which is characterized in that step
(3) microwave treatment conditions are 800-1000W.
5. a kind of calcium carbonate whisker binding paper box glue preparation method according to claim 2, which is characterized in that step
(3) the ethanol solution mass concentration of the silane coupling agent is 3-7%, and the silane coupling agent is silane resin acceptor kh-550, silicon
Alkane coupling agent kh-570.
6. the preparation method of modified calcium carbonate whisker according to claim 3, which is characterized in that the sodium silicate aqueous solution
Mass concentration is 40-44%.