CN1091694A - High strength colour transparent compound board and method for making thereof - Google Patents
High strength colour transparent compound board and method for making thereof Download PDFInfo
- Publication number
- CN1091694A CN1091694A CN 93101978 CN93101978A CN1091694A CN 1091694 A CN1091694 A CN 1091694A CN 93101978 CN93101978 CN 93101978 CN 93101978 A CN93101978 A CN 93101978A CN 1091694 A CN1091694 A CN 1091694A
- Authority
- CN
- China
- Prior art keywords
- mylar
- promoter
- curing agent
- alkali
- high strength
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to high strength colour transparent compound board and method for making thereof.Composite plate of the present invention by one deck as alkali in the calico of colored intensive or colour picture and one deck and two layers or alkali-free glass fiber cloth through adding curing agent, the SR ' of promoter-922
#Mylar soaks into to solidify and forms.Composite plate of the present invention adopts curing process in the two layers polyester film, and product surface is smooth, and is beautiful in colour, and product can be used as building board, billboard etc., and technology is simple, and production cost is low.
Description
The present invention relates to the shade or the baffle plate field of usefulness such as greenhouse, particularly high strength colour transparent compound board and method for making thereof.
The construction material that is used for greenhouse at present is a kind of light transmission film, and this material is soaked into to solidify to alkali-free glass fiber cloth by unsaturated polyester resin and forms, but easy firing is easily aging, easy crisp and frangibility, and not attractive in appearance again, the cost height can't be repaired after wearing and tearing.
The objective of the invention is to: a kind of high strength colour transparent compound board and method for making thereof are provided, and this composite plate is nonflammable, and is in light weight, anti-aging, not crisp, and stronger bendability is arranged.
The objective of the invention is to reach like this: said composite plate is soaked into to solidify as alkali in the calico of colored enhancement Layer or colour picture and one deck or two layers or the SR-922# mylar of alkali-free glass fiber cloth through adding curing agent, promoter by one deck and is formed.
The present invention is described in detail below in conjunction with embodiment.
Composite plate of the present invention is soaked into to solidify as alkali in the calico of colored enhancement Layer or colour picture and one deck or two layers or the SR-922# mylar of alkali-free glass fiber cloth after adding curing agent, promoter by one deck and is formed.Gained composite plate intensity is about 2000kg/cm, and is nonflammable, and also over-emitting black exhaust not during combustion is anti-aging, not crisp, bend resistance.
The inventive method is as follows:
A) on workbench that polyester film or nylon film is smooth fixing;
B) with super-dry processing with adding curing agent, calico that the SR-922# mylar of promoter soaks into or do not soak into or colour picture are sandwiched in or are topped in middle alkali or alkali-free glass fiber cloth or on it;
C) preparation mylar: used mylar is the curing agent of SR-922# mylar (Tianjin synthetic material factory product, trace Lin Zhuan industrial area, eastern suburb, Tianjin), the dressing that is used as, promoter such as following table:
| Auxiliary material | Content's index | ProductName | Factory |
| Cyclohexanone peroxide peroxide phenylacetyl cobalt naphthenate dimethylaniline | ≥4.5% ≥4.5% 0.8-1% 10％ | No. 2 promoter of No. 2 curing agent of No. 1 promoter of No. 1 curing agent | Be all Tianjin synthetic material factory product |
Compound method is that per 100 parts of SR-922# mylar are allocated 2～4 parts of a kind of or two kinds of above-mentioned curing agent and 0.5～4 part of a kind of or two kinds of above-mentioned promoter into;
D) after being spread in uniform in the mylar for preparing on the machining object, cover another strata ester film or nylon film again, with the roll extrusion repeatedly thereon of rubber roll, mylar is fully soaked into equably, the preparation of polyester and infiltration temperature are more than 13 ℃;
E) after the curing, upper and lower two strata ester films or nylon film are separated, promptly get this high strength colour transparent compound board.
This composite plate is a planar structure, be easy to bonding with construction material commonly used, the totally-enclosed installation of large tracts of land can be saved a large amount of glass, fiberglass, steel, owing to use the SR-922# mylar, itself has had fire-proof function, must not add to be coated with fire resistant coating, thereby technology is simple again, in addition, this composite plate also has waterproof, acid-proof, alkali prevention, anti-low temperature, advantage anti-aging, crisp, not easy to break.Composite plate with calico is mainly used in the architectural of frame formula structure and not only has above-mentioned advantage as greenhouse, greenhouse etc., goes back light-permeable, intensity height, and the pattern of figured cloth is arranged, and is bright in luster.
Can be used as the material of billboard, picture poster board with picture as this composite plate of colored enhancement Layer, except that above-mentioned advantage is arranged, after wearing and tearing, also can repair, can select required picture pattern arbitrarily.
The inventive method adopts curing process in the two layers polyester film, smooth surface, and cost is low, and operation is simple, does not need special installation, can finish by hand basically.
Embodiment 1:
The used colored enhancement Layer of this composite plate is a calico, it is middle to use two layers of neutral and alkali glass fabric that this calico is sandwiched in, use 100 parts in SR-922# mylar, 3 parts of 4 parts, No. 1 promoter of No. 1 curing agent are fully soaked into this calico and glass fabric and to be torn upper and lower two strata ester films after the curing off.This composite plate made from this technology can replace roof of the courtyard that glass is used for large-scale hotel, the cool Room, roof, country trade market, movable dwellings, greenhouse etc.
Embodiment 2:
The used colored enhancement Layer of this composite plate is a colour picture, after using one deck alkali-free glass fiber cloth and this colour picture one to reinstate 1 part in 100 parts in SR-922# mylar, 2 parts, No. 2 promoter of No. 2 curing agent this glass fabric and colour picture are fully soaked into curing, tear behind upper and lower two layers of nylon film dry solidification off, this composite plate made from this technology is used for advertising board, picture lamp box and archives preservation etc.
Claims (2)
1, high strength colour transparent compound board is characterized in that, as alkali or alkali-free glass fiber cloth in the seal cloth of colored enhancement Layer or colour picture and one deck or two layers, the SR-922# mylar through allocating curing agent and promoter into soaks into to solidify and forms by one deck.
2, the method for making of high strength colour transparent compound board is characterized in that following operation:
A) on workbench that polyester film or nylon film is smooth fixing;
B) super-dry is handled and is added curing agent through using, and calico that the SR-922# mylar of promoter soaks into or do not soak into or colour picture are sandwiched in or are topped in middle alkali or alkali-free glass fiber cloth or on it;
C) preparation mylar: used mylar is the product SR-922# mylar of Tianjin synthetic material factory, curing agent and promoter that used dressing has Tianjin synthetic material factory to produce, wherein, No. 1 curing agent contains 〉=4.5% cyclohexanone peroxide, and No. 2 curing agent contains 0.8～1% cobalt naphthenate; No. 1 promoter is contained 〉=4.5% peroxide phenylacetyl; No. 2 promoter is contained 10% dimethylaniline, and per 100 parts of SR-922# mylar are allocated 2～4 parts of a kind of or two kinds of above-mentioned curing agent and 0.5～4 part of a kind of or two kinds of above-mentioned promoter into, and the preparation temperature is more than 13 ℃;
D) after being spread in uniform in the mylar for preparing on the machining object, cover another strata ester film or nylon film again, with the roll extrusion repeatedly thereon of rubber roll, mylar is fully soaked into equably, the infiltration temperature of polyester is more than 13 ℃;
E) after the curing, upper and lower two strata ester films or nylon film are separated, promptly get this high strength colour transparent compound board.