CN109161271A - A kind of household electrical appliances coating and preparation method thereof - Google Patents
A kind of household electrical appliances coating and preparation method thereof Download PDFInfo
- Publication number
- CN109161271A CN109161271A CN201811019984.2A CN201811019984A CN109161271A CN 109161271 A CN109161271 A CN 109161271A CN 201811019984 A CN201811019984 A CN 201811019984A CN 109161271 A CN109161271 A CN 109161271A
- Authority
- CN
- China
- Prior art keywords
- parts
- household electrical
- electrical appliances
- agent
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention belongs to fields of home appliance technology, more particularly to a kind of household electrical appliances coating and preparation method thereof, household electrical appliances of the invention are made of with coating the raw material of following parts by weight: 60-80 parts of resin aqueous emulsion, 0.8-1.2 parts of carbon nanotubes, 4-6 parts of modified carbon fiber, 0.6-1 parts of coupling agent, 0.3-0.5 parts of thickener, 1-3 parts of defoaming agent and 0.6-1 parts of coalescing agent;Household electrical appliances of the invention are comprised the steps of with preparation method for coating: (1) weighing raw material by corresponding parts by weight;(2) carbon nanotubes is put into dense H2SO4In HNO3 mixed liquor, handled 2-4 hours under supersonic oscillations and mechanical agitation, and be washed with deionized to neutrality;(3) resin aqueous emulsion is added in reaction kettle, coupling agent, thickener, defoaming agent and coalescing agent is added and is uniformly dispersed, obtains mixed liquor A;(4) modified carbon fiber and step (2) resulting carbon nanotubes are added into mixed liquor A, is uniformly dispersed.Household electrical appliances of the invention have good radiation protection and antistatic property with coating.
Description
Technical field
The invention belongs to fields of home appliance technology, and in particular to a kind of household electrical appliances coating and preparation method thereof.
Background technique
The development of science and technology is that people bring the life of high quality, and various domestic electric appliances are brought to people's lives
While convenient, a dangerous stealthy pollution sources-electromagnetic radiation invades also quietly and penetrates into the side of people's life
Our health is gradually endangered in aspect face.Know from physics common sense, any electric appliance be electrified stream will generate electromagnetic field or
Common air-conditioning, television set, computer, micro-wave oven, humidifier, air cleaner, electric blanket are arrived greatly in electromagnetic radiation;It is small to arrive daylight
The household electrical appliance such as lamp, hair dryer, mobile phone, charger even power outlet, switchboard, wiring insert row can all generate electromagnetic radiation.
Even if the electromagnetic field least to attract attention may also cause the symptoms such as stress, headache, depression and insomnia, lead to immunity degradation,
Greatly improve the disease incidence of various diseases.Therefore, a kind of radiation shielding coating of household electrical appliance is developed to reduce or slow down radiation
Influence to human health is this field technical issues that need to address.The Chinese invention of Publication No. CN104789004A is special
Benefit, discloses a kind of radiation shielding coating for electric appliance, in the raw material of the coating and is not added with to have and is obviously improved anti-radiation performance
The ingredient of energy.
Due to the effect of phase mutual friction between household electrical appliance and other objects, it is easy to produce accumulation of static electricity, electrostatic hazard occurs,
The normal use of household electrical appliance is such as influenced, can discharge generate spark in severe cases, is set off an explosion and fire.So opening
The antistatic coating for sending out household electrical appliance a kind of is this field technical issues that need to address.Antistatic coating be divided into Intrinsical and
Addition type two major classes, Intrinsical antistatic coating technology is still immature, and the antistatic coating largely used at present is addition type painting
Material.Addition type coating is the function of adding certain conductive coating in nonconducting binder resin to realize static conductive, only
The degree that the volume fraction of conductive filler reaches certain could form conductive network or access, embody conductive property.At present
Common conductive filler has: Carbon materials (carbon black, graphite etc.), metal powder (silver powder, copper powder), metal oxide semiconductor
(tin oxide, iron oxide, zinc oxide), conducting nanoparticles and antistatic auxiliary agent etc..Wherein metal powder density is big, is formed conductive
Access needs biggish volume fraction, and surface layer is oxidizable, electric conductivity, and poor corrosion resistance can be reduced or even lose, thus shadow
Other performances of coating are rung, therefore metal powder is subject to certain restrictions as the application of conductive filler;It is antistatic agent temperature tolerance, resistance to
Aqueous, oil resistivity, corrosion resistance, durability are poor, and antistatic property is unstable;Early stage antistatic coating generally uses Carbon materials
As conductive filler, black conductive graphite and carbon black dispersion are poor, and product color is black, it is not easy to be modulated to other shallower face
Color;With the development of science and technology, having gradually appeared the novel conductive fillers such as metal oxide semiconductor and nanometer conductive powder, and anti-
It is applied in electrostatic figure layer, this kind of material color is shallow, is easy to mix colours, and enriches the colour system of antistatic coating, but this kind of
Additive amount is big when coating is used alone, and dispersion stabilization is poor, will affect the performance of coating.Publication No. CN106221501A's
Chinese invention patent discloses a kind of electric fan antistatic coating, and the antistatic property of the coating is not obviously improved.
Summary of the invention
In view of the deficiencies of the prior art, the purpose of the present invention is to provide one kind to have good radiation protection and antistatic property
Coating and preparation method thereof.
To achieve the above object, the present invention adopts the following technical scheme:
The present invention provides a kind of household electrical appliances coating, are made of the raw material of following parts by weight: 60-80 parts of resin aqueous emulsion is received
Rice 0.8-1.2 parts of carbon pipe, 4-6 parts of modified carbon fiber, 0.6-1 parts of coupling agent, 0.3-0.5 parts of thickener, 1-3 parts of defoaming agent and at
0.6-1 parts of film auxiliary agent.
Preferably, household electrical appliances coating of the invention, is made of the raw material of following parts by weight: 70 parts of resin aqueous emulsion is received
1 part of rice carbon pipe, 5 parts of modified carbon fiber, 0.8 part of coupling agent, 0.4 part of thickener, 2 parts of defoaming agent and 0.8 part of coalescing agent.
Preferably, the resin aqueous emulsion by weight ratio is the water-based acrylic resin of 4:1 and aqueous acrylic modified
Resin composition, the aqueous acrylic modified resin are the water-based acrylic resin and CoatOSi12287 for being 40:1 by weight ratio
The mixing of aqueous latex paint auxiliary agent, is stirred 30 minutes under the stirring condition of 500-600r/min, then is stored 48 hours and be made.
Preferably, the modified carbon fiber is the Ni-based carbon fiber prepared by chemical plating method, the nickel of surface covering
Layer is with a thickness of 0.3-0.5 μm.
Preferably, the draw ratio of the carbon nanotubes is 250.
Preferably, the coupling agent is metatitanic acid value coupling agent YB-401.
Preferably, the thickener is hydroxymethyl cellulose or hydroxypropyl cellulose.
Preferably, the defoaming agent is polypropylene glycol or polyethylene glycol.
Preferably, the coalescing agent is Lauryl Alcohol ester.
The present invention also provides the preparation methods of the household electrical appliances coating, are made of following preparation step:
(1) resin aqueous emulsion is weighed according to corresponding parts by weight, carbon nanotubes, modified carbon fiber, coupling agent, thickener, disappear
Infusion and coalescing agent;
(2) carbon nanotubes is put into the dense H that volume ratio is 3:12SO4 In HNO3 mixed liquor, stirred in supersonic oscillations and machinery
It mixes under effect, handles 2-4 hours, then washed with a large amount of deionized waters to neutrality;
(3) resin aqueous emulsion is added in reaction kettle, revolving speed 500-600r/min is set, coupling agent, thickener, defoaming is added
Agent and coalescing agent are uniformly dispersed, and obtain mixed liquor A;
(4) modified carbon fiber and step (2) resulting carbon nanotubes are added into mixed liquor A, revolving speed 600-800r/min is set,
Disperse 60-80min to get household electrical appliances coating.
The invention has the following beneficial effects:
(1) raw material of coating of the present invention uses draw ratio as 250 carbon nanotubes, is obtained by test data, works as carbon nanotubes
Draw ratio be greater than 250 when, obtained coating electric conductivity reduces with the increase of draw ratio, when the draw ratio of carbon nanotube
When less than 250, obtained coating electric conductivity increases with the increase of draw ratio, thus carbon nanotubes as conductive coating most
Good draw ratio is 250.The weight ratio of carbon nanotube and resin aqueous emulsion that raw material of the present invention uses is 0.8-1.5:1, this hair
It is bright to be obtained by test data, when carbon nanotube and the weight ratio of resin aqueous emulsion within this range when, carbon nanotube is in water
Dispersion effect is preferable in property resin emulsion, and obtained coating antistatic property is preferable.
(2) raw material of coating of the present invention uses the Ni-based carbon fiber prepared by chemical plating method, and Ni-based carbon fiber exists
There are stable dispersibility and good compatibility in base-material resin aqueous emulsion, it is logical stable conduction can be formed in coating surface
Road increases coating to the absorption loss of electromagnetic wave, the reflection loss to electromagnetic wave is reduced, to reduce electromagnetic wave to environment
Caused by secondary pollution.
(3) coalescing agent of coating of the present invention uses Lauryl Alcohol ester, and Lauryl Alcohol ester is practically insoluble in water, Bu Huisui
The variation of ambient humidity the phenomenon that generating whiting, and small toxicity, nonflammable, hydrolytic stability is good, and volatility is lower, can have
Effect reduces the film-forming temperature of resin aqueous emulsion.
(4) coupling agent of coating of the present invention uses metatitanic acid value coupling agent YB-401, since the present invention is using aqueous
For resin emulsion as substrate, solvent is few, and lubricity is low, thus adhesive force is weaker, forms bridge between metatitanic acid value coupling agent and ground
Key is improved due to introducing polar group in coupling agent with the compatibility of ground, thus adhesive force is obviously improved.
Specific embodiment
Present invention will be further explained below with reference to specific examples, and embodiment is merely to illustrate the present invention rather than limit
The scope of the present invention processed.
Embodiment 1
A kind of household electrical appliances coating is present embodiments provided, is made of the raw material of following parts by weight: resin aqueous emulsion 60 part, nanometer
0.8 part of carbon pipe, 4 parts of modified carbon fiber, 0.6 part of coupling agent, 0.3 part of thickener, 1 part of defoaming agent and 0.6 part of coalescing agent.
The water-based acrylic resin and aqueous acrylic modified resin that the present embodiment resin aqueous emulsion is 4:1 by weight ratio
Composition, the aqueous acrylic modified resin are that weight ratio is aqueous for the water-based acrylic resin and CoatOSi12287 of 40:1
The mixing of emulsion paint auxiliary agent, is stirred 30 minutes under the stirring condition of 500r/min, then is stored 48 hours and be made.
The present embodiment modified carbon fiber is the Ni-based carbon fiber prepared by chemical plating method, and the nickel layer of surface covering is thick
Degree is 0.3 μm.
The draw ratio of the present embodiment carbon nanotubes is 250.
The coupling agent of the present embodiment is metatitanic acid value coupling agent YB-401.
The thickener of the present embodiment is hydroxymethyl cellulose.
The defoaming agent of the present embodiment is polypropylene glycol.
The coalescing agent of the present embodiment is Lauryl Alcohol ester.
The present invention also provides the preparation methods of the household electrical appliances coating, are made of following preparation step:
(1) resin aqueous emulsion is weighed according to corresponding parts by weight, carbon nanotubes, modified carbon fiber, coupling agent, thickener, disappear
Infusion and coalescing agent;
(2) carbon nanotubes is put into the dense H that volume ratio is 3:12SO4 In HNO3 mixed liquor, stirred in supersonic oscillations and machinery
It mixes under effect, handles 2 hours, then washed with a large amount of deionized waters to neutrality;
(3) will resin aqueous emulsion be added reaction kettle in, be arranged revolving speed 500r/min, be added coupling agent, thickener, defoaming agent and
Coalescing agent is uniformly dispersed, and obtains mixed liquor A;
(4) modified carbon fiber and step (2) resulting carbon nanotubes are added into mixed liquor A, revolving speed 600r/min, dispersion are set
60min is to get household electrical appliances coating.
Embodiment 2
The household electrical appliances coating of the present embodiment, is made of the raw material of following parts by weight: 70 parts of resin aqueous emulsion, 1 part of carbon nanotubes,
5 parts of modified carbon fiber, 0.8 part of coupling agent, 0.4 part of thickener, 2 parts of defoaming agent and 0.8 part of coalescing agent.
The resin aqueous emulsion of the present embodiment is by the water-based acrylic resin that weight ratio is 4:1 and aqueous acrylic modified tree
Rouge composition, the aqueous acrylic modified resin are the water-based acrylic resin and CoatOSi12287 water for being 40:1 by weight ratio
Property the mixing of emulsion paint auxiliary agent, stir 30 minutes under the stirring condition of 550r/min, then store 48 hours it is obtained.
The modified carbon fiber of the present embodiment is the Ni-based carbon fiber prepared by chemical plating method, the nickel layer of surface covering
With a thickness of 0.4 μm.
The draw ratio of the carbon nanotubes of the present embodiment is 250.
The coupling agent of the present embodiment is metatitanic acid value coupling agent YB-401.
The thickener of the present embodiment is hydroxypropyl cellulose.
The defoaming agent of the present embodiment is polyethylene glycol.
The coalescing agent of the present embodiment is Lauryl Alcohol ester.
The present invention also provides the preparation methods of the household electrical appliances coating, are made of following preparation step:
(1) resin aqueous emulsion is weighed according to corresponding parts by weight, carbon nanotubes, modified carbon fiber, coupling agent, thickener, disappear
Infusion and coalescing agent;
(2) carbon nanotubes is put into the dense H that volume ratio is 3:12SO4 In HNO3 mixed liquor, stirred in supersonic oscillations and machinery
It mixes under effect, handles 3 hours, then washed with a large amount of deionized waters to neutrality;
(3) will resin aqueous emulsion be added reaction kettle in, be arranged revolving speed 550r/min, be added coupling agent, thickener, defoaming agent and
Coalescing agent is uniformly dispersed, and obtains mixed liquor A;
(4) modified carbon fiber and step (2) resulting carbon nanotubes are added into mixed liquor A, revolving speed 700r/min, dispersion are set
70min is to get household electrical appliances coating.
Embodiment 3
The household electrical appliances coating of the present embodiment, is made of the raw material of following parts by weight: 80 parts of resin aqueous emulsion, carbon nanotubes 1.2
Part, 6 parts of modified carbon fiber, 1 part of coupling agent, 0.5 part of thickener, 3 parts of defoaming agent and 1 part of coalescing agent.
The resin aqueous emulsion of the present embodiment is by the water-based acrylic resin that weight ratio is 4:1 and aqueous acrylic modified tree
Rouge composition, the aqueous acrylic modified resin are the water-based acrylic resin and CoatOSi12287 water for being 40:1 by weight ratio
Property the mixing of emulsion paint auxiliary agent, stir 30 minutes under the stirring condition of 600r/min, then store 48 hours it is obtained.
The modified carbon fiber of the present embodiment is the Ni-based carbon fiber prepared by chemical plating method, the nickel layer of surface covering
With a thickness of 0.5 μm.
The draw ratio of the carbon nanotubes of the present embodiment is 250.
The coupling agent of the present embodiment is metatitanic acid value coupling agent YB-401.
The thickener of the present embodiment is hydroxymethyl cellulose.
The defoaming agent of the present embodiment is polypropylene glycol.
The coalescing agent of the present embodiment is Lauryl Alcohol ester.
The present invention also provides the preparation methods of the household electrical appliances coating, are made of following preparation step:
(1) resin aqueous emulsion is weighed according to corresponding parts by weight, carbon nanotubes, modified carbon fiber, coupling agent, thickener, disappear
Infusion and coalescing agent;
(2) carbon nanotubes is put into the dense H that volume ratio is 3:12SO4 In HNO3 mixed liquor, stirred in supersonic oscillations and machinery
It mixes under effect, handles 4 hours, then washed with a large amount of deionized waters to neutrality;
(3) will resin aqueous emulsion be added reaction kettle in, be arranged revolving speed 600r/min, be added coupling agent, thickener, defoaming agent and
Coalescing agent is uniformly dispersed, and obtains mixed liquor A;
(4) modified carbon fiber and step (2) resulting carbon nanotubes are added into mixed liquor A, revolving speed 800r/min, dispersion are set
80min is to get household electrical appliances coating.
Control group 1 and control group 2 are set, and control group 1 uses disclosed in the patent of invention of Publication No. CN104789004A
A kind of radiation shielding coating for electric appliance, control group 2 use one kind disclosed in the patent of invention of Publication No. CN106221501A
Antistatic coating, the coating that the coating and control group 1 and control group 2 prepare to embodiment 1, embodiment 2, embodiment 3 uses
Electromagnet shield effect and surface resistivity test are carried out, electromagnetic shielding effect is tested using coaxial line electromagnet shield effect method of testing
Can, using test specimens diagonal line electric resistivity method test surfaces resistivity, specimen size is 150mm × 150mm, test result such as table
1。
Table 1
Test item | Embodiment 1 | Embodiment 2 | Embodiment 3 | Control group 1 | Control group 2 |
Electromagnet shield effect (dB) | 57 | 59 | 58 | 38 | 32 |
Surface resistivity (Ω/cm2) | 0.44 | 0.43 | 0.42 | 0.52 | 0.55 |
As it can be seen from table 1 coating prepared by embodiment 1, embodiment 2 and embodiment 3, electromagnet shield effect compared to the control group 1
50%, 55.3% and 52.6% is improved respectively, 2 improves 78.1%, 84.3% and 81.2% respectively compared to the control group;Embodiment 1, reality
Apply coating prepared by example 2 and embodiment 3, resistivity 1 reduces 15.4%, 17.3% and 19.2% compared to the control group respectively, compared to pair
20%, 21.8% and 23.6% is reduced respectively according to group 2.It can analyze and obtain from above data, coating of the invention compares existing skill
Art has better anti-electromagnetic radiation performance and antistatic property.
Specific embodiments of the present invention are described above.It is to be appreciated that the invention is not limited to above-mentioned
Particular implementation, those skilled in the art can make various deformations or amendments within the scope of the claims, this not shadow
Ring substantive content of the invention.
Claims (10)
1. a kind of household electrical appliances coating, which is characterized in that be made of the raw material of following parts by weight: 60-80 parts of resin aqueous emulsion is received
Rice 0.8-1.2 parts of carbon pipe, 4-6 parts of modified carbon fiber, 0.6-1 parts of coupling agent, 0.3-0.5 parts of thickener, 1-3 parts of defoaming agent and at
0.6-1 parts of film auxiliary agent.
2. a kind of household electrical appliances coating according to claim 1, which is characterized in that be made of the raw material of following parts by weight: water
70 parts of resin emulsion of property, 1 part of carbon nanotubes, 5 parts of modified carbon fiber, 0.8 part of coupling agent, 0.4 part of thickener, 2 parts of defoaming agent and
0.8 part of coalescing agent.
3. a kind of household electrical appliances coating according to claim 1 or 2, it is characterised in that: the resin aqueous emulsion is by weight
Than the water-based acrylic resin and aqueous acrylic modified resin composition for 4:1, the aqueous acrylic modified resin is will to weigh
Amount is than the water-based acrylic resin for being 40:1 and the mixing of CoatOSi12287 aqueous latex paint auxiliary agent, in stirring for 500-600r/min
It is stirred 30 minutes under the conditions of mixing, then stores 48 hours and be made.
4. a kind of household electrical appliances coating according to claim 1 or 2, it is characterised in that: the modified carbon fiber is passing through
The Ni-based carbon fiber of electroplating method preparation is learned, the nickel layer thickness of surface covering is 0.3-0.5 μm.
5. a kind of household electrical appliances coating according to claim 1 or 2, it is characterised in that: the draw ratio of the carbon nanotubes is
250。
6. a kind of household electrical appliances coating according to claim 1 or 2, it is characterised in that: the coupling agent is the coupling of metatitanic acid value
Agent YB-401.
7. a kind of household electrical appliances coating according to claim 1 or 2, it is characterised in that: the thickener is hydroxylmethyl cellulose
Element or hydroxypropyl cellulose.
8. a kind of household electrical appliances coating according to claim 1 or 2, it is characterised in that: the defoaming agent be polypropylene glycol or
Polyethylene glycol.
9. a kind of household electrical appliances coating according to claim 1 or 2, it is characterised in that: the coalescing agent is Lauryl Alcohol
Ester.
10. a kind of preparation method of household electrical appliances coating according to claim 1 or claim 2, which is characterized in that by following preparation step
Composition:
(1) resin aqueous emulsion is weighed according to corresponding parts by weight, carbon nanotubes, modified carbon fiber, coupling agent, thickener, disappear
Infusion and coalescing agent;
(2) carbon nanotubes is put into the dense H that volume ratio is 3:12SO4 In HNO3 mixed liquor, stirred in supersonic oscillations and machinery
It mixes under effect, handles 2-4 hours, then washed with a large amount of deionized waters to neutrality;
(3) resin aqueous emulsion is added in reaction kettle, revolving speed 500-600r/min is set, coupling agent, thickener, defoaming is added
Agent and coalescing agent are uniformly dispersed, and obtain mixed liquor A;
(4) modified carbon fiber and step (2) resulting carbon nanotubes are added into mixed liquor A, revolving speed 600-800r/min is set,
Disperse 60-80min to get household electrical appliances coating.