CN109161260A - A kind of production technology for road mark paint - Google Patents
A kind of production technology for road mark paint Download PDFInfo
- Publication number
- CN109161260A CN109161260A CN201811030886.9A CN201811030886A CN109161260A CN 109161260 A CN109161260 A CN 109161260A CN 201811030886 A CN201811030886 A CN 201811030886A CN 109161260 A CN109161260 A CN 109161260A
- Authority
- CN
- China
- Prior art keywords
- parts
- added
- production technology
- agent
- road mark
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of production technologies for road mark paint, the following steps are included: 1) stirring, 2) be added filler, 3) grinding, 4) be added mill base, 5) be added drier, 6) filtering, 7) it is canned, the present invention is directed to bulky grain diameter polymer emulsion poor water resistance, the disadvantage of Corrosion Protection difference, select a kind of partial size in 100nm nanometer polymer emulsion once as base-material, using the step method of above-mentioned production technology, the coating of a kind of chemical property and the preferable roadmarking of physical property is obtained.
Description
Technical field
The present invention relates to a kind of production technologies for road mark paint.
Background technique
Road mark paint is a kind of coating that can be used specific construction method to be coated on pavement of road, by solidifying energy
Successional film is formed, and mark action can be played to the road surface applied by film, however in existing production technology,
It is relatively simple due to technical flow design, so the physical and chemical performance of coating is poor, it is easy to be worn away, be corroded, used
Service life is shorter.
Summary of the invention
The technical problem to be solved by the present invention is for overcome the deficiencies in the prior art, providing a kind of for roadmarking
The production technology of coating.
The technical solution adopted by the present invention to solve the technical problems is: the following steps are included:
1) stir: be added in mash vessel the water of formula ratio, wetting agent, dispersing agent, defoaming agent, preservative, mould inhibitor,
PH regulator, improved wood bonding agent, thickener, propyl benzene lotion, corrosion inhibiter, triethanolamine, mica powder, barite and sterilization
Agent is stirred 10-12 minutes, and revolving speed is 400 revs/min;
2) filler is added: the filler of formula ratio is added, stirs 8-10 minutes, revolving speed is 800 revs/min;
3) grind: during the grinding process, temperature control is at 30 DEG C hereinafter, mixed material is ground to fineness less than 30 μm;
4) mill base is added: the mill base and nanometer polymer emulsion of formula ratio being added in a reservoir, stirs 10-12 minutes, turns
Speed is 900 revs/min;
5) drier is added: drier is added in consistent, persistently stirs 8-10 minutes after adding drier, revolving speed is
1050 revs/min;
6) it filters: being filtered with the sieve of 100 mesh, repeat filtering three times;
7) canned: finished product to be carried out canned.
Preferably, in terms of quality proportioning, water has 6-8 parts, wetting agent has 7-11 parts, dispersing agent has 1-3 parts, defoaming agent has
2-3 parts, preservative have 3-8 parts, mould inhibitor have 7-11 parts, PH regulator have 0.5-1 parts, improved wood bonding agent have 6-12 parts,
Thickener have 4-8 parts, propyl benzene lotion have 5-8 parts, corrosion inhibiter have 4-8 parts, triethanolamine have 9-12 parts, mica powder have 6-8 parts, again
Spar has 6-8 parts to have 12-13 parts with fungicide.
Preferably, mash vessel is reaction kettle in step 1).
Preferably, the filler in step 2) is tetrafluoro filler.
Preferably, the mill base in step 4) is aqueous color paste.
Preferably, the nanometer polymer emulsion in step 4) is fluorine ketone Hydroxylated acrylic resin lotion.
Preferably, the drier in step 5) is organic acid soap drier.
The invention has the advantages that the present invention is directed to bulky grain diameter polymer emulsion poor water resistance, Corrosion Protection is poor
The shortcomings that, select a kind of partial size in 100nm nanometer polymer emulsion once as base-material, the step of using above-mentioned production technology
Method obtains the coating of a kind of chemical property and the preferable roadmarking of physical property.
Specific embodiment
A kind of production technology for road mark paint, comprising the following steps:
1) stir: be added in mash vessel the water of formula ratio, wetting agent, dispersing agent, defoaming agent, preservative, mould inhibitor,
PH regulator, improved wood bonding agent, thickener, propyl benzene lotion, corrosion inhibiter, triethanolamine, mica powder, barite and sterilization
Agent is stirred 10-12 minutes, and revolving speed is 400 revs/min;
2) filler is added: the filler of formula ratio is added, stirs 8-10 minutes, revolving speed is 800 revs/min;
3) grind: during the grinding process, temperature control is at 30 DEG C hereinafter, mixed material is ground to fineness less than 30 μm;
4) mill base is added: the mill base and nanometer polymer emulsion of formula ratio being added in a reservoir, stirs 10-12 minutes, turns
Speed is 900 revs/min;
5) drier is added: drier is added in consistent, persistently stirs 8-10 minutes after adding drier, revolving speed is
1050 revs/min;
6) it filters: being filtered with the sieve of 100 mesh, repeat filtering three times;
7) canned: finished product to be carried out canned.
Embodiment 1:
Preferably, in terms of quality proportioning, water have 6 parts, wetting agent have 7 parts, dispersing agent have 1 part, defoaming agent have 2 parts, it is anti-
Rotten agent have 3 parts, mould inhibitor have 7 parts, PH regulator have 0.5 part, improved wood bonding agent have 6 parts, thickener have 4 parts, propyl benzene cream
Liquid has 5 parts, corrosion inhibiter has 4 parts, triethanolamine has 9 parts, mica powder has 6 parts, barite has 6 parts and fungicide has 12 parts.
Embodiment 2:
Preferably, in terms of quality proportioning, water have 7 parts, wetting agent have 9 parts, dispersing agent have 2 parts, defoaming agent have 2.5 parts,
Preservative have 6 parts, mould inhibitor have 9 parts, PH regulator have 0.75 part, improved wood bonding agent have 9 parts, thickener have 6 parts, propyl benzene
Lotion has 5.5 parts, corrosion inhibiter has 6 parts, triethanolamine has 10.5 parts, mica powder has 7 parts, barite has 7 parts and fungicide has
12.5 parts.
Embodiment 3:
Preferably, in terms of quality proportioning, water have 8 parts, wetting agent have 11 parts, dispersing agent have 3 parts, defoaming agent have 3 parts, it is anti-
Rotten agent have 8 parts, mould inhibitor have 11 parts, PH regulator have 1 part, improved wood bonding agent have 12 parts, thickener have 8 parts, propyl benzene cream
Liquid has 8 parts, corrosion inhibiter has 8 parts, triethanolamine has 12 parts, mica powder has 8 parts, barite has 8 parts and fungicide has 13 parts.
Preferably, mash vessel is reaction kettle in step 1).
Preferably, the filler in step 2) is tetrafluoro filler.
Preferably, the mill base in step 4) is aqueous color paste.
Preferably, the nanometer polymer emulsion in step 4) is fluorine ketone Hydroxylated acrylic resin lotion.
Preferably, the drier in step 5) is organic acid soap drier.
Compared with prior art, the present invention is directed to bulky grain diameter polymer emulsion poor water resistance, and Corrosion Protection difference lacks
Point selects a kind of partial size in 100nm nanometer polymer emulsion once as base-material, using above-mentioned production technology the step of side
Method obtains the coating of a kind of chemical property and the preferable roadmarking of physical property
Taking the above-mentioned ideal embodiment according to the present invention as inspiration, through the above description, relevant staff is complete
Various changes and amendments can be carried out without departing from the scope of the technological thought of the present invention' entirely.The technology of this invention
Property range is not limited to the contents of the specification, it is necessary to which the technical scope thereof is determined according to the scope of the claim.
Claims (7)
1. a kind of production technology for road mark paint, which comprises the following steps:
1) it stirs: water, wetting agent, dispersing agent, defoaming agent, preservative, mould inhibitor, the PH tune of formula ratio being added in mash vessel
Agent, improved wood bonding agent, thickener, propyl benzene lotion, corrosion inhibiter, triethanolamine, mica powder, barite and fungicide are saved, is stirred
It mixes 10-12 minutes, revolving speed is 400 revs/min;
2) filler is added: the filler of formula ratio is added, stirs 8-10 minutes, revolving speed is 800 revs/min;
3) grind: during the grinding process, temperature control is at 30 DEG C hereinafter, mixed material is ground to fineness less than 30 μm;
4) mill base is added: the mill base and nanometer polymer emulsion of formula ratio being added in a reservoir, stirs 10-12 minutes, revolving speed is
900 revs/min;
5) drier is added: drier is added in consistent, persistently stirs 8-10 minutes after adding drier, revolving speed 1050
Rev/min;
6) it filters: being filtered with the sieve of 100 mesh, repeat filtering three times;
7) canned: finished product to be carried out canned.
2. being used for the production technology of road mark paint as described in claim 1, which is characterized in that in terms of quality proportioning, water
Have 6-8 parts, wetting agent have 7-11 parts, dispersing agent have 1-3 parts, defoaming agent have 2-3 parts, preservative have 3-8 parts, mould inhibitor have 7-11
Part, PH regulator have 0.5-1 part, improved wood bonding agent have 6-12 parts, thickener have 4-8 parts, propyl benzene lotion have 5-8 parts, delay
Erosion agent has 4-8 parts, triethanolamine has 9-12 parts, mica powder has 6-8 parts, barite has 6-8 parts and fungicide has 12-13 parts.
3. being used for the production technology of road mark paint as described in claim 1, which is characterized in that in step 1), slurrying is held
Device is reaction kettle.
4. being used for the production technology of road mark paint as described in claim 1, which is characterized in that the filler in step 2) is
Tetrafluoro filler.
5. being used for the production technology of road mark paint as described in claim 1, which is characterized in that the mill base in step 4) is
Aqueous color paste.
6. being used for the production technology of road mark paint as described in claim 1, which is characterized in that the nanometer in step 4) is poly-
Conjunction object lotion is fluorine ketone Hydroxylated acrylic resin lotion.
7. being used for the production technology of road mark paint as described in claim 1, which is characterized in that the drier in step 5)
For organic acid soap drier.