CN109137198A - A kind of high abrasion yarn - Google Patents
A kind of high abrasion yarn Download PDFInfo
- Publication number
- CN109137198A CN109137198A CN201811182998.6A CN201811182998A CN109137198A CN 109137198 A CN109137198 A CN 109137198A CN 201811182998 A CN201811182998 A CN 201811182998A CN 109137198 A CN109137198 A CN 109137198A
- Authority
- CN
- China
- Prior art keywords
- yarn
- fiber
- molecular weight
- weight polyethylene
- high molecular
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to yarn technical field, especially a kind of high abrasion yarn, it is made of ultra high molecular weight polyethylene fiber, polyester fiber, spandex fibre and cotton fiber, wherein the mass ratio of polyester fiber and spandex fibre is 1:1, the two passes through blended formation mixed yarn, by being twisted after doubling between the mixed yarn and fiber of formation, the twist is controlled at 100-200 twists/m, forms intermediate yarn;Two ultra high molecular weight polyethylene fibers are coated to Z-direction with S respectively in the outside of intermediate yarn, and S to the twist of the ultra high molecular weight polyethylene fiber on intermediate yarn be 240-300 twists/m, the twist of the ultra high molecular weight polyethylene fiber of Z-direction on intermediate yarn is 200-250 twists/m.A kind of obtained high abrasion yarn of the present invention, is designed by reasonable structure, can effectively promote the wear-resisting property of yarn, and after decoration cloth material processing, the service performance of bunting gets a promotion.
Description
Technical field
The present invention relates to yarn technical field, especially a kind of high abrasion yarn.
Background technique
In the prior art, the performances such as high abrasion are typically necessary for the yarn used on bunting, but current yarn
Its wear-resisting property of line all compare it is poor, be easy influence bunting service performance.
Summary of the invention
A kind of the purpose of the present invention is to solve the deficiencies of the above technologies and provide height that can effectively promote wear-resisting property
Abrasion resistant yarn.
In order to achieve the above object, a kind of high abrasion yarn designed by the present invention, it is by ultra-high molecular weight polyethylene fibre
Dimension, polyester fiber, spandex fibre and cotton fiber are constituted, and wherein the mass ratio of polyester fiber and spandex fibre is 1:1, and the two passes through
Blended formation mixed yarn, by being twisted after doubling between the mixed yarn and fiber of formation, twist control twists in 100-200/
Rice forms intermediate yarn;Two ultra high molecular weight polyethylene fibers, and S are coated to Z-direction with S respectively in the outside of intermediate yarn
To the twist of the ultra high molecular weight polyethylene fiber on intermediate yarn be 240-300 twists/m, the ultra-high molecular weight polyethylene of Z-direction
The twist of the fiber on intermediate yarn is 200-250 twists/m.
Yam surface after cladding coats one layer of TPU membrane, and the TPU membrane with a thickness of 0.1-0.2mm.
A kind of obtained high abrasion yarn of the present invention, is designed by reasonable structure, can effectively promote the resistance to of yarn
Performance is ground, after decoration cloth material processing, the service performance of bunting gets a promotion.
Specific embodiment
The present invention is further described by the following embodiment.
Embodiment 1:
The present embodiment description a kind of high abrasion yarn, it by ultra high molecular weight polyethylene fiber, polyester fiber, spandex fibre and
Cotton fiber is constituted, and wherein the mass ratio of polyester fiber and spandex fibre is 1:1, the two by blended formation mixed yarn, formation
By being twisted after doubling between mixed yarn and fiber, the twist is controlled at 100 twists/m, forms intermediate yarn;In the outer of intermediate yarn
Portion respectively with S to Z-direction coat two ultra high molecular weight polyethylene fibers, and S to ultra high molecular weight polyethylene fiber exist
The twist on intermediate yarn is 240 twists/m, and the twist of the ultra high molecular weight polyethylene fiber of Z-direction on intermediate yarn is 200 twists/m.
Yam surface after cladding coats one layer of TPU membrane, and the TPU membrane with a thickness of 0.1mm.
Embodiment 2:
The present embodiment description a kind of high abrasion yarn, it by ultra high molecular weight polyethylene fiber, polyester fiber, spandex fibre and
Cotton fiber is constituted, and wherein the mass ratio of polyester fiber and spandex fibre is 1:1, the two by blended formation mixed yarn, formation
By being twisted after doubling between mixed yarn and fiber, the twist is controlled at 200 twists/m, forms intermediate yarn;In the outer of intermediate yarn
Portion respectively with S to Z-direction coat two ultra high molecular weight polyethylene fibers, and S to ultra high molecular weight polyethylene fiber exist
The twist on intermediate yarn is 300 twists/m, and the twist of the ultra high molecular weight polyethylene fiber of Z-direction on intermediate yarn is 250 twists/m.
Yam surface after cladding coats one layer of TPU membrane, and the TPU membrane with a thickness of 0.2mm.
Embodiment 3:
The present embodiment description a kind of high abrasion yarn, it by ultra high molecular weight polyethylene fiber, polyester fiber, spandex fibre and
Cotton fiber is constituted, and wherein the mass ratio of polyester fiber and spandex fibre is 1:1, the two by blended formation mixed yarn, formation
By being twisted after doubling between mixed yarn and fiber, the twist is controlled at 150 twists/m, forms intermediate yarn;In the outer of intermediate yarn
Portion respectively with S to Z-direction coat two ultra high molecular weight polyethylene fibers, and S to ultra high molecular weight polyethylene fiber exist
The twist on intermediate yarn is 280 twists/m, and the twist of the ultra high molecular weight polyethylene fiber of Z-direction on intermediate yarn is 230 twists/m.
Yam surface after cladding coats one layer of TPU membrane, and the TPU membrane with a thickness of 0.1mm.
Claims (2)
1. a kind of high abrasion yarn, it is characterized in that: it is by ultra high molecular weight polyethylene fiber, polyester fiber, spandex fibre and cotton
Fiber is constituted, and wherein the mass ratio of polyester fiber and spandex fibre is 1:1, and the two is mixed by blended formation mixed yarn, formation
By being twisted after doubling between spinning and fiber, the twist is controlled at 100-200 twists/m, forms intermediate yarn;In intermediate yarn
It is external that two ultra high molecular weight polyethylene fibers are coated to Z-direction with S respectively, and S to ultra high molecular weight polyethylene fiber
The twist on intermediate yarn is 240-300 twists/m, and the twist of the ultra high molecular weight polyethylene fiber of Z-direction on intermediate yarn is
200-250 twists/m.
2. a kind of high abrasion yarn according to claim 1, it is characterized in that: the yam surface after cladding coats one layer
TPU membrane, and the TPU membrane with a thickness of 0.1-0.2mm.