CN109130678A - A kind of production method of aluminium sheet decoration painting - Google Patents
A kind of production method of aluminium sheet decoration painting Download PDFInfo
- Publication number
- CN109130678A CN109130678A CN201811009933.1A CN201811009933A CN109130678A CN 109130678 A CN109130678 A CN 109130678A CN 201811009933 A CN201811009933 A CN 201811009933A CN 109130678 A CN109130678 A CN 109130678A
- Authority
- CN
- China
- Prior art keywords
- aluminium sheet
- glaze layer
- parts
- firing
- aluminum plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The present invention relates to a kind of production method of aluminium sheet decoration painting, including aluminium sheet is chosen, transition glaze layer is prepared, mixing, spraying transition glaze layer, preliminary firings, sprayed surface glaze layer, secondary firing, cools.The method of the present invention reasonable, transition glaze layer and aluminium sheet and cover coat are tightly combined, it is beautiful and generous to fire product, etching surfacing is wrinkle resistant, it is sturdy and durable, it can save for a long time, the existing spray painting cloth fugitive color of existing building decoration of exterior wall picture is solved to fall off, spray painting cloth service life is short, it cannot save for a long time, it replaces time-consuming and laborious, increased costs, surface of aluminum plate oxidation film is not easy to bind directly with glaze layer, influence surface glaze layer colouring, easily aluminium sheet is caused to melt when firing, it can not glazing, aluminium sheet cools down suddenly after firing, it is easy to cause surface of aluminum plate arching deformation, influencing quality influences the technical problems such as product quality and enterprise's productivity effect, for the prior art, it has good market prospects and development space.
Description
Technical field
The present invention relates to metallic enamel technical fields, and in particular to a kind of production method of aluminium sheet decoration painting.
Background technique
Recently as the aggravation of market competition, many enterprises use the publicity mode advertised on billboard outdoors,
Especially near some eye-catching buildings, long-term advertisement field, is pasted onto using spray painting cloth in some outdoor billboards etc.
Glass plate or iron plate surface, although temporarily looking at beauty in this way, but there is problems in that one, spray painting cloth exposure for a long time
Outside, it easily fades and falls off, it is beautiful to influence building；Two, spray painting cloth service life is short, cannot save for a long time, many heavy constructions
Billboard often just needs replacing gummed paper two to three moons by object especially expressway, not only operational hazards, but also time-consuming and laborious；
Three, frequently replacement causes increased costs, especially worker to dismount cost, influences Business Economic Benefit.There are also some building constructions
Exterior wall begins to use decoration painting, and common decoration is decorated with mural painting and plate is drawn, and plate, which is drawn, is generally glass plate picture or iron plate picture, and plate picture is
Product made of glass quality enamel layer is formed in the matrix surface being made of glass or iron plate.
Use iron plate enamel etching mostly currently on the market, due to iron plate price, weight weight, transport is inconvenient,
Therefore it can not promote on a large scale, some enterprise's trials aluminium sheet makes aluminium sheet and draws, and there is also following thorny problems: one, aluminium sheet
There is one layer of fine and close oxidation film on surface, and oxidation film is not easy to bind directly with glaze layer, influences the colouring of sequent surface glaze layer；Two, aluminium
Fusing point is lower, and aluminium sheet supplied materials thickness is different, and when firing once grasps bad temperature, easily aluminium sheet is caused to melt, can not glazing；
Two, when aluminium sheet is fired, the time is not grasped, is cooled down suddenly after firing, surface of aluminum plate arching deformation is easy to cause, influences quality.
Especially under the prior art, can not be successfully on the oxide of surface of aluminum plate in conjunction with transition glaze layer be in industry it is urgently to be resolved great
Problem.
How to design a kind of ingenious in design, method reasonable, ground glaze layer and aluminium sheet and cover coat are tightly combined, and are fired and are produced
Product are beautiful and generous, and etching surfacing is wrinkle resistant, sturdy and durable, and the production method for the aluminium sheet decoration painting that can be saved for a long time is current
Problem to be solved.
Summary of the invention
It falls off to solve the existing spray painting cloth fugitive color of existing building decoration of exterior wall picture, influences building beauty, air brushing
Cloth service life is short, cannot save for a long time, and replacement operation is dangerous, time-consuming and laborious, increased costs, and aluminium sheet is drawn in production and application
Existing surface of aluminum plate has one layer of fine and close oxidation film, and oxidation film is not easy to bind directly with glaze layer, influences the colouring of sequent surface glaze layer,
Once grasp bad temperature when firing, easily aluminium sheet caused to melt, can not glazing, aluminium sheet fire after cool down suddenly, be easy to cause
Surface of aluminum plate arching deformation, influencing quality influences the technical problems such as product quality and enterprise's productivity effect, and the present invention provides one kind
The production method of aluminium sheet decoration painting, method reasonable ingenious in design to realize, ground glaze layer and aluminium sheet and cover coat combine tight
Close, firing product is beautiful and generous, and etching surfacing is wrinkle resistant, sturdy and durable, the purpose that can be saved for a long time.
Used technical solution is the present invention to solve above-mentioned technical problem: a kind of production method of aluminium sheet decoration painting,
The following steps are included:
Step 1 chooses fresh aluminium sheet, is derusted using physical method or chemical method to surface of aluminum plate, oil removal processing；
Step 2 prepares transition glaze layer, each component quality proportioning of the transition glaze layer are as follows: and 20-30 parts of metallic aluminium powder, aluminium silicon
30-60 parts of hydrochlorate mineral dust, 20-30 parts of low temperature frit powder, 10-30 parts of potassium oxide, 60-70 parts of water；
Step 3 uniformly mixes each component described in step 2, stirs 30-60 minutes, stands 10-30 minutes；
Step 4 erects aluminium sheet vertically, and the prepared transition glaze layer of step 3 is sprayed to aluminium sheet process face using spray gun；
Step 5 is fired mode using glass tempering furnace level and is tentatively fired to the aluminium sheet for having sprayed transition glaze layer, aluminium sheet
Bottom is provided with backing plate, 680-700 DEG C of firing temperature, firing time 1-10min, cooling after having fired；
Step 6 prepares surface glaze layer, each group distribution ratio of the surface glaze layer are as follows: and 5-10 parts of titanium dioxide powder, silica
60-70 parts of powder, 20-30 parts of low temperature frit powder, 60-70 parts of water；
Step 7 uniformly mixes each component described in step 6, stirs 30-60 minutes, stands 10-30 minutes；
Aluminium sheet after preliminary fire is horizontally arranged on glazing production line conveyer belt, utilizes reciprocal automatic spray gun pair by step 8
Surface of aluminum plate carries out even application surface glaze layer；
Step 9 carries out the printing of high definition pattern using aluminium sheet of the nano ceramics printer to sprayed surface glaze layer；
Step 10, the aluminium sheet level after high definition is printed, which is put into glass tempering furnace, carries out secondary rolling firing, firing temperature
It 550-650 DEG C, firing time 5-20min, is cooled using Dual-layer air grid to aluminium sheet after having fired；
Physical method used in the step 1 is that sandblasting dust removal machine carries out derusting by sandblasting to surface of aluminum plate.
The diamond dust mesh number that the sandblasting dust removal machine uses is 200-400 mesh.
Chemical method used in the step 1 is base extraction surface of aluminum plate.
The backing plate material that aluminium sheet bottom is arranged in the step 5 is heat-resisting material.
Compared with prior art, the beneficial effects of the present invention are:
1) derusting by sandblasting, the gold of sandblasting dust removal machine are carried out to surface of aluminum plate using sandblasting dust removal machine in physics derusting method of the present invention
Emery mesh number is 200-400 mesh, and when diamond dust mesh number is 200-400 in experiment, diamond dust can be effectively in high-velocity spray process
In surface derusting is carried out to surface of aluminum plate, carry out place mat for transition glaze layer in subsequent surface of aluminum plate；
2) it prepares and uses metallic aluminium powder and aluminium silicate mineral powder in transition glaze layer, since the fusing point of metallic aluminium is lower,
Under lower temperature, aluminium and aluminium silicate mineral issue biochemical reaction, table in the catalytic action of low temperature frit powder and potassium oxide
Face forms the transition glaze layer combined closely with aluminium sheet to be solved in favor of the smooth combination of sequent surface glaze layer and transition glaze layer
There is problem for a long time in industry；
3) when low temperature frit, i.e. preparation glaze, by the water-soluble material of sodium carbonate, potassium carbonate, borax, boric acid etc and quartz or
Other silicates are mixed in a certain ratio, manufactured frit, and frit and photoghraphic coupler are put together melting in proportion, make photoghraphic coupler
It is uniformly distributed, adds a certain amount of clay to be mixed and finely ground again after cooling, mixed well with water or other liquid as fritted glaze, can be made water-soluble
Property substance become insoluble, increase stability, suspension and the tackness with carcass of glaze, reduce bubble, to prevent these raw materials
It dissolves when preparing glaze slip in water, is easily absorbed by green body during glazing；
4) when preliminary firing, aluminium sheet bottom is provided with backing plate, backing plate material is heat-resisting material, and the effect of backing plate is in order to anti-
Only for aluminium sheet when high temperature is fired, there is a phenomenon where melt transition glaze layer caused by flowing not combining closely with aluminium sheet；
5) printing of high definition pattern, the printing of nano ceramics printer are carried out using aluminium sheet of the nano ceramics printer to spraying white glaze layer
Clearly, error is small, and easily operated control guarantees the beautiful and generous of pattern；
6) it is fired using novel reciprocating glass tempering furnace, firing temperature and firing time are easily controllable, and it is beautiful to fire product
Generous, aluminium sheet picture surfacing is wrinkle resistant, sturdy and durable, reduces subsequent board with enamel panel layer in the prior art and flattens process, saves
Cost of labor improves the performance of enterprises.
Specific embodiment
Specific embodiments of the present invention will be described in further detail below.
Embodiment one,
A kind of production method of aluminium sheet decoration painting, comprising the following steps:
Step 1 chooses fresh aluminium sheet, is derusted using physical method or chemical method to surface of aluminum plate, oil removal processing；
Step 2 prepares transition glaze layer, each component quality proportioning of the transition glaze layer are as follows: and 20 parts of metallic aluminium powder, manosil AS
30 parts of salt mineral dust, 20 parts of low temperature frit powder, 10 parts of potassium oxide, 60 parts of water；
Step 3 uniformly mixes each component described in step 2, stirs 30 minutes, stands 10 minutes；
Step 4 erects aluminium sheet vertically, and the prepared transition glaze layer of step 3 is sprayed to aluminium sheet process face using spray gun；
Step 5 is fired mode using glass tempering furnace level and is tentatively fired to the aluminium sheet for having sprayed transition glaze layer, aluminium sheet
Bottom is provided with backing plate, 680 DEG C of firing temperature, firing time 1min, cooling after having fired；
Step 6 prepares surface glaze layer, each group distribution ratio of the surface glaze layer are as follows: and 5 parts of titanium dioxide powder, SiO 2 powder
60 parts, 20 parts of low temperature frit powder, 60 parts of water；
Step 7 uniformly mixes each component described in step 6, stirs 30 minutes, stands 10 minutes；
Aluminium sheet after preliminary fire is horizontally arranged on glazing production line conveyer belt, utilizes reciprocal automatic spray gun pair by step 8
Surface of aluminum plate carries out even application surface glaze layer；
Step 9 carries out the printing of high definition pattern using aluminium sheet of the nano ceramics printer to sprayed surface glaze layer；
Step 10, the aluminium sheet level after high definition is printed, which is put into glass tempering furnace, carries out secondary rolling firing, firing temperature 550
DEG C, firing time 5min cools to aluminium sheet using Dual-layer air grid after having fired；
The above are basic embodiments of the invention, further can be improved, improved and limited on the basis of above: as described in
Physical method used in step 1 is that sandblasting dust removal machine carries out derusting by sandblasting to surface of aluminum plate.
The above are basic embodiments of the invention, further can be improved, improved and limited on the basis of above: such as
The diamond dust mesh number that the sandblasting dust removal machine uses is 200 mesh.
The above are basic embodiments of the invention, further can be improved, improved and limited on the basis of above: such as
Chemical method used in the step 1 is base extraction surface of aluminum plate.
The above are basic embodiments of the invention, further can be improved, improved and limited on the basis of above: such as
The backing plate material that aluminium sheet bottom is arranged in the step 5 is heat-resisting material.
Embodiment two,
A kind of production method of aluminium sheet decoration painting, comprising the following steps:
Step 1 chooses fresh aluminium sheet, is derusted using physical method or chemical method to surface of aluminum plate, oil removal processing；
Step 2 prepares transition glaze layer, each component quality proportioning of the transition glaze layer are as follows: and 25 parts of metallic aluminium powder, manosil AS
40 parts of salt mineral dust, 25 parts of low temperature frit powder, 15 parts of potassium oxide, 65 parts of water；
Step 3 uniformly mixes each component described in step 2, stirs 40 minutes, stands 15 minutes；
Step 4 erects aluminium sheet vertically, and the prepared transition glaze layer of step 3 is sprayed to aluminium sheet process face using spray gun；
Step 5 is fired mode using glass tempering furnace level and is tentatively fired to the aluminium sheet for having sprayed transition glaze layer, aluminium sheet
Bottom is provided with backing plate, 690 DEG C of firing temperature, firing time 5min, cooling after having fired；
Step 6 prepares surface glaze layer, each group distribution ratio of the surface glaze layer are as follows: and 5 parts of titanium dioxide powder, SiO 2 powder
65 parts, 25 parts of low temperature frit powder, 65 parts of water；
Step 7 uniformly mixes each component described in step 6, stirs 45 minutes, stands 15 minutes；
Aluminium sheet after preliminary fire is horizontally arranged on glazing production line conveyer belt, utilizes reciprocal automatic spray gun pair by step 8
Surface of aluminum plate carries out even application surface glaze layer；
Step 9 carries out the printing of high definition pattern using aluminium sheet of the nano ceramics printer to sprayed surface glaze layer；
Step 10, the aluminium sheet level after high definition is printed, which is put into glass tempering furnace, carries out secondary rolling firing, firing temperature 600
DEG C, firing time 10min cools to aluminium sheet using Dual-layer air grid after having fired；
The above are basic embodiments of the invention, further can be improved, improved and limited on the basis of above: as described in
Physical method used in step 1 is that sandblasting dust removal machine carries out derusting by sandblasting to surface of aluminum plate.
The above are basic embodiments of the invention, further can be improved, improved and limited on the basis of above: such as
The diamond dust mesh number that the sandblasting dust removal machine uses is 300 mesh.
The above are basic embodiments of the invention, further can be improved, improved and limited on the basis of above: such as
Chemical method used in the step 1 is base extraction surface of aluminum plate.
The above are basic embodiments of the invention, further can be improved, improved and limited on the basis of above: such as
The backing plate material that aluminium sheet bottom is arranged in the step 5 is heat-resisting material.
Embodiment three,
A kind of production method of aluminium sheet decoration painting, comprising the following steps:
Step 1 chooses fresh aluminium sheet, is derusted using physical method or chemical method to surface of aluminum plate, oil removal processing；
Step 2 prepares transition glaze layer, each component quality proportioning of the transition glaze layer are as follows: and 30 parts of metallic aluminium powder, manosil AS
60 parts of salt mineral dust, 30 parts of low temperature frit powder, 30 parts of potassium oxide, 70 parts of water；
Step 3 uniformly mixes each component described in step 2, stirs 60 minutes, stands 30 minutes；
Step 4 erects aluminium sheet vertically, and the prepared transition glaze layer of step 3 is sprayed to aluminium sheet process face using spray gun；
Step 5 is fired mode using glass tempering furnace level and is tentatively fired to the aluminium sheet for having sprayed transition glaze layer, aluminium sheet
Bottom is provided with backing plate, 700 DEG C of firing temperature, firing time 10min, cooling after having fired；
Step 6 prepares surface glaze layer, each group distribution ratio of the surface glaze layer are as follows: and 10 parts of titanium dioxide powder, silicon dioxide powder
70 parts, 30 parts of low temperature frit powder, 70 parts of water of end；
Step 7 uniformly mixes each component described in step 6, stirs 60 minutes, stands 30 minutes；
Aluminium sheet after preliminary fire is horizontally arranged on glazing production line conveyer belt, utilizes reciprocal automatic spray gun pair by step 8
Surface of aluminum plate carries out even application surface glaze layer；
Step 9 carries out the printing of high definition pattern using aluminium sheet of the nano ceramics printer to sprayed surface glaze layer；
Step 10, the aluminium sheet level after high definition is printed, which is put into glass tempering furnace, carries out secondary rolling firing, firing temperature 650
DEG C, firing time 20min cools to aluminium sheet using Dual-layer air grid after having fired；
The above are basic embodiments of the invention, further can be improved, improved and limited on the basis of above: as described in
Physical method used in step 1 is that sandblasting dust removal machine carries out derusting by sandblasting to surface of aluminum plate.
The above are basic embodiments of the invention, further can be improved, improved and limited on the basis of above: such as
The diamond dust mesh number that the sandblasting dust removal machine uses is 400 mesh.
The above are basic embodiments of the invention, further can be improved, improved and limited on the basis of above: such as
Chemical method used in the step 1 is base extraction surface of aluminum plate.
The above are basic embodiments of the invention, further can be improved, improved and limited on the basis of above: such as
The backing plate material that aluminium sheet bottom is arranged in the step 5 is heat-resisting material.
In practical operation, when step 1 chooses aluminium sheet, chemical method derusting also can be used, it is water-soluble for example, by using highly basic
Liquid removes surface of aluminum plate oxide；In step 5, using ceramic vertical furnace horizontal mode to the aluminium sheet for having sprayed transition glaze layer
It is tentatively fired, firing temperature and firing time are by depending on the aluminium plate thickness chosen, aluminium sheet is thinner, and the firing time is shorter, aluminium
Plate is thicker, and the firing time is longer.
In printing step, the printing dyestuff that the present invention uses is inorganic dyestuff, in printing and firing, will not generate
Machine exhaust gas, it is environmentally friendly, it is environmentally protective, meet enterprise Green developing direction.
The present invention is ingenious in design, and method reasonable, transition glaze layer and aluminium sheet and cover coat are tightly combined, and fires product beauty
To see generous, etching surfacing is wrinkle resistant, and it is sturdy and durable, it can save for a long time, solve existing building decoration of exterior wall and draw existing spray
It draws cloth fugitive color to fall off, influences building beauty, spray painting cloth service life is short, cannot save for a long time, and replacement operation is dangerous, time-consuming
Arduously, increased costs, aluminium sheet is drawn in produce and use in the surface of aluminum plate that occurs have one layer of fine and close oxidation film, oxidation film be not easy with
Glaze layer is bound directly, and influences the colouring of sequent surface glaze layer, and when firing once grasps bad temperature, easily aluminium sheet caused to melt, nothing
Method glazing, aluminium sheet cool down suddenly after firing, and are easy to cause surface of aluminum plate arching deformation, and influencing quality influences product quality and enterprise
The technical problems such as productivity effect have good market prospects and development space for the prior art.
The preferred embodiments of the disclosure and embodiment are explained in detail above, but the present invention is not limited to
The above-described embodiment and examples can also not depart from the present invention within the knowledge of those skilled in the art
Various changes can be made under the premise of design.
Claims (5)
1. a kind of production method of aluminium sheet decoration painting, it is characterised in that: the following steps are included:
Step 1 chooses fresh aluminium sheet, is derusted using physical method or chemical method to surface of aluminum plate, oil removal processing；
Step 2 prepares transition glaze layer, each component quality proportioning of the transition glaze layer are as follows: and 20-30 parts of metallic aluminium powder, aluminium silicon
30-60 parts of hydrochlorate mineral dust, 20-30 parts of low temperature frit powder, 10-30 parts of potassium oxide, 60-70 parts of water；
Step 3 uniformly mixes each component described in step 2, stirs 30-60 minutes, stands 10-30 minutes；
Step 4 erects aluminium sheet vertically, and the prepared transition glaze layer of step 3 is sprayed to aluminium sheet process face using spray gun；
Step 5 is fired mode using glass tempering furnace level and is tentatively fired to the aluminium sheet for having sprayed transition glaze layer, aluminium sheet
Bottom is provided with backing plate, 680-700 DEG C of firing temperature, firing time 1-10min, cooling after having fired；
Step 6 prepares surface glaze layer, each group distribution ratio of the surface glaze layer are as follows: and 5-10 parts of titanium dioxide powder, silica
60-70 parts of powder, 20-30 parts of low temperature frit powder, 60-70 parts of water；
Step 7 uniformly mixes each component described in step 6, stirs 30-60 minutes, stands 10-30 minutes；
Aluminium sheet after preliminary fire is horizontally arranged on glazing production line conveyer belt, utilizes reciprocal automatic spray gun pair by step 8
Surface of aluminum plate carries out even application surface glaze layer；
Step 9 carries out the printing of high definition pattern using aluminium sheet of the nano ceramics printer to sprayed surface glaze layer；
Step 10, the aluminium sheet level after high definition is printed, which is put into glass tempering furnace, carries out secondary rolling firing, firing temperature
It 550-650 DEG C, firing time 5-20min, is cooled using Dual-layer air grid to aluminium sheet after having fired.
2. a kind of production method of aluminium sheet decoration painting as described in claim 1, it is characterised in that: used in the step 1
Physical method is that sandblasting dust removal machine carries out derusting by sandblasting to surface of aluminum plate.
3. a kind of production method of aluminium sheet decoration painting as claimed in claim 2, it is characterised in that: the sandblasting dust removal machine makes
Diamond dust mesh number is 200-400 mesh.
4. a kind of production method of aluminium sheet decoration painting as described in claim 1, it is characterised in that: used in the step 1
Chemical method is base extraction surface of aluminum plate.
5. a kind of production method of aluminium sheet decoration painting as described in claim 1, it is characterised in that: aluminium sheet bottom in the step 5
The backing plate material of portion's setting is heat-resisting material.