CN109130354A - A kind of composite non woven cloth fabric and preparation method thereof of the dust-proof anti-UV of new waterproof - Google Patents
A kind of composite non woven cloth fabric and preparation method thereof of the dust-proof anti-UV of new waterproof Download PDFInfo
- Publication number
- CN109130354A CN109130354A CN201810761497.7A CN201810761497A CN109130354A CN 109130354 A CN109130354 A CN 109130354A CN 201810761497 A CN201810761497 A CN 201810761497A CN 109130354 A CN109130354 A CN 109130354A
- Authority
- CN
- China
- Prior art keywords
- parts
- dust
- surface layer
- preparation
- woven cloth
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses the composite non woven cloth fabrics and preparation method thereof of the dust-proof anti-UV of new waterproof a kind of, including PET fiber layer and LDPE surface layer；Preparation method the following steps are included: S1, LDPE surface layer production: weigh raw material, it is sufficiently mixed after raw material is clayed into power, make it in molten condition using screw rod heating plasticizing in injection molding machine in mixed powder, obtains LDPE surface layer after the linear extrusion of flat-mould head die orifice；The production of S2, PET fiber layer: by high pressure fine water flow jet to 100% polyester slice, so that 100% polyester slice is mutually intertwined, PET fiber layer is prepared；S3, the side of LDPE surface layer is sticked on PET fiber layer using adhesive glue, carries out heating compacting reaction, is taken out after the cooling of its natural cooling and obtain the composite non woven cloth fabric of the anti-UV of water proof and dust proof.The present invention in LDPE surface layer by being added to the combined material of anti-UV, so that the compound nonwoven cloth being prepared has the effect of the anti-UV of better water proof and dust proof.
Description
Technical field
The present invention relates to compound nonwoven cloth technical field more particularly to the compound nonwoven cloths of the dust-proof anti-UV of new waterproof a kind of
Fabric and preparation method thereof.
Background technique
Non-woven fabrics is also known as nonwoven fabric, is made of fiber orient or random, is the environment-friendly materials of a new generation, is had anti-
It is damp, ventilative, flexible, light, not combustion-supporting, easy to decompose, is nontoxic nonirritant, rich in color, cheap and recyclable
The features such as, mostly using polypropylene granules is raw material, through high-temperature fusion, spinneret, paving guiding principle, hot pressing crimp continuous generations production and
At, it is called cloth because of the appearance and certain performances with cloth, because being a kind of fabric for not needing spinning and weaving and being formed,
It is to be oriented textile fabric or long filament or randomizing, forms fibre net structure, then uses physical mechanical (spun lacing or needle
Thorn), it is hot sticky or the methods of chemical reinforce.Non-woven fabrics is not knitted together by yarns interwoven one by one, but will
Fiber is bonded together by the method for direct physics, so, non-woven fabrics is not no the end of a thread.Non-woven fabrics breaks through traditional prevention and treatment
The features such as principle, and have process flow short, throughput rate is fast, and yield is high, at low cost, and purposes is wide, and raw material sources are more, with nothing
The application range of woven fabric constantly expands, and requirement of the people to non-woven fabrics is also continuously improved, and therefore, compound nonwoven cloth comes into being.
With being continuously increased for compound nonwoven cloth application demand, the characteristic of the water proof and dust proof uv blocking of non-woven fabrics is also increasingly by people's
Pay attention to, still, the compound nonwoven cloth that conventional method is worked it out at present, performance is poor, wants in the performance to the anti-UV of water proof and dust proof
High outdoor field use is asked to be severely limited.
Summary of the invention
The purpose of the present invention is to solve disadvantages existing in the prior art, and a kind of new waterproof proposed is dust-proof anti-
Composite non woven cloth fabric of UV and preparation method thereof.
To achieve the goals above, present invention employs following technical solutions:
A kind of composite non woven cloth fabric and preparation method thereof of the dust-proof anti-UV of new waterproof, including PET fiber layer and LDPE surface layer,
The LDPE surface layer includes the raw material of following parts by weight: 100-120 parts of LDPE particle, 16-18 parts of epoxy resin, and nanometer boron fibre
5-7 parts, 8-14 parts of butylated urea-formaldehyde resin, 2-5 parts of zinc stearate, 4-6 parts and dicyandiamide 1-2 parts of cellulose derivative；
The preparation method comprises the following steps:
The production of S1, LDPE surface layer: weighing raw material, is sufficiently mixed after raw material is clayed into power, by mixed powder in injection molding machine
It is interior to make it in molten condition using screw rod heating plasticizing, LDPE surface layer is obtained after the linear extrusion of flat-mould head die orifice；
The production of S2, PET fiber layer: 100 % polyester slice phases on the fine water flow jet of high pressure to 100 % polyester slices, will be made
It is mutually intertwined, PET fiber layer is prepared；
S3, the side of LDPE surface layer is sticked on PET fiber layer using adhesive glue, heating compacting reaction is carried out, to its nature
It is taken out after cooling and obtains the composite non woven cloth fabric of the anti-UV of water proof and dust proof.
Preferably, the LDPE surface layer includes the raw material of following parts by weight: 110 parts of LDPE particle, 17 parts of epoxy resin, being received
6 parts of boron fibre of rice, 11 parts of butylated urea-formaldehyde resin, 3 parts of zinc stearate, 5 parts and 2 parts of dicyandiamide of cellulose derivative.
Preferably, the cellulose derivative be cellulose nitrate, cellulose ethanoate, cellulose acetate butyrate and
Cellulose xanthate, carboxymethyl cellulose, hydroxyethyl cellulose, cyanethyl cellulose, hydroxypropyl cellulose and hydroxypropyl methyl
One of cellulose.
Preferably, the additive is benzophenone, benzotriazole, triazine, substitution acrylonitrile, salicyclic acid derivatives, benzene
Formic acid derivates, cinnamic acid derivative, chalcone derivative, dypnone derivative, crotonic acid derivates, acrylic acid hexichol
One or more of ester.
Preferably, the feeding inlet temperature of the injection molding machine is set as 200 DEG C, and the temperature of flat-mould head die orifice is set as 500
DEG C, the feeding inlet of injection molding machine is to flat-mould head die orifice 20 DEG C incremented by successively every a distance temperature.
Preferably, the laminating temperature of the heating compacting reaction is 170 DEG C -180 DEG C, the lamination pressure of heating compacting reaction
It is by force 16 kgf/cm2-18 kgf/cm2, the time of the heat-insulation pressure keeping of heating compacting reaction is 45 min-60 min, heating pressure
The release temperature reacted in fact is at 60 DEG C or less.
Preferably, stating adhesive is epoxy type adhesive or modified epoxy type adhesive.
Preferably, the upper end glue connection of the PET fiber layer is connected to LDPE surface layer.
The beneficial effects of the present invention are: the present invention is in LDPE surface layer by being added to the combined material of anti-UV, so that system
Standby obtained compound nonwoven cloth has the effect of the anti-UV of better water proof and dust proof.
Detailed description of the invention
Fig. 1 is a kind of knot of composite non woven cloth fabric of the dust-proof anti-UV of new waterproof proposed by the present invention and preparation method thereof
Structure schematic diagram.
In figure: 1 PET fiber layer, 2 LDPE surface layers.
Specific embodiment
Following will be combined with the drawings in the embodiments of the present invention, and technical solution in the embodiment of the present invention carries out clear, complete
Site preparation description, it is clear that described embodiments are only a part of the embodiments of the present invention, instead of all the embodiments.
Embodiment one: referring to Fig.1, a kind of composite non woven cloth fabric and preparation method thereof of the dust-proof anti-UV of new waterproof, packet
PET fiber layer 1 and LDPE surface layer 2 are included, the upper end glue connection of PET fiber layer 1 is connected to LDPE surface layer 2, and LDPE surface layer 2 includes following heavy
The raw material of amount part: 100 parts of LDPE particle, 16 parts of epoxy resin, 5 parts of nanometer boron fibre, 8 parts of butylated urea-formaldehyde resin, stearic acid
2 parts of zinc, 4 parts of cellulose acetate butyrate, 1 part and 1 part of salicyclic acid derivatives of dicyandiamide；
Preparation method the following steps are included:
The production of S1, LDPE surface layer 2: weighing raw material, is sufficiently mixed after raw material is clayed into power, by mixed powder in injection molding machine
The feeding inlet temperature of injection molding machine is set as 200 DEG C, and the temperature of flat-mould head die orifice is set as 500 DEG C, and the feeding inlet of injection molding machine arrives
Flat-mould head die orifice using screw rod heating plasticizing in 20 DEG C incremented by successively of a distance temperature every making it in molten condition, through flat
LDPE surface layer is obtained after the linear extrusion of die head die orifice；
The production of S2, PET fiber layer 1: 100 % polyester slice phases on the fine water flow jet of high pressure to 100 % polyester slices, will be made
It is mutually intertwined, PET fiber layer 1 is prepared；
S3, the side of LDPE surface layer 2 is sticked on PET fiber layer 1 using epoxy type adhesive glue, carries out heating compacting reaction and adds
The laminating temperature of warm compaction reaction is 170 DEG C, and the lamination pressure of heating compacting reaction is 16 kgf/cm2, heating compacting reaction
Heat-insulation pressure keeping time be 45 min, heating compacting reaction release temperature at 60 DEG C hereinafter, after its natural cooling cooling after
Taking-up obtains the composite non woven cloth fabric of the anti-UV of water proof and dust proof.
Embodiment two: referring to Fig.1, a kind of composite non woven cloth fabric and preparation method thereof of the dust-proof anti-UV of new waterproof, packet
PET fiber layer 1 and LDPE surface layer 2 are included, the upper end glue connection of PET fiber layer 1 is connected to LDPE surface layer 2, and LDPE surface layer 2 includes following heavy
The raw material of amount part: 110 parts of LDPE particle, 17 parts of epoxy resin, 6 parts of nanometer boron fibre, 11 parts of butylated urea-formaldehyde resin, stearic acid
3 parts of zinc, 5 parts of hydroxyethyl cellulose, 2 parts and 1 part of cinnamic acid derivative of dicyandiamide；
Preparation method the following steps are included:
The production of S1, LDPE surface layer 2: weighing raw material, is sufficiently mixed after raw material is clayed into power, by mixed powder in injection molding machine
The feeding inlet temperature of injection molding machine is set as 200 DEG C, and the temperature of flat-mould head die orifice is set as 500 DEG C, and the feeding inlet of injection molding machine arrives
Flat-mould head die orifice using screw rod heating plasticizing in 20 DEG C incremented by successively of a distance temperature every making it in molten condition, through flat
LDPE surface layer is obtained after the linear extrusion of die head die orifice；
The production of S2, PET fiber layer 1: 100 % polyester slice phases on the fine water flow jet of high pressure to 100 % polyester slices, will be made
It is mutually intertwined, PET fiber layer 1 is prepared；
S3, the side of LDPE surface layer 2 is sticked on PET fiber layer 1 using modified epoxy type adhesive glue, it is anti-carries out heating compacting
The laminating temperature that compacting reaction should be heated is 1180 DEG C, and the lamination pressure of heating compacting reaction is 18 kgf/cm2, heating compacting
The time of the heat-insulation pressure keeping of reaction is 60 min, and the release temperature of heating compacting reaction is at 60 DEG C hereinafter, dropping to its natural cooling
It is taken out after temperature and obtains the composite non woven cloth fabric of the anti-UV of water proof and dust proof.
Embodiment three: referring to Fig.1, a kind of composite non woven cloth fabric and preparation method thereof of the dust-proof anti-UV of new waterproof, packet
PET fiber layer 1 and LDPE surface layer 2 are included, the upper end glue connection of PET fiber layer 1 is connected to LDPE surface layer 2, and LDPE surface layer 2 includes following heavy
The raw material of amount part: 120 parts of LDPE particle, 18 parts of epoxy resin, 7 parts of nanometer boron fibre, 14 parts of butylated urea-formaldehyde resin, stearic acid
5 parts of zinc, 6 parts of hydroxypropyl methyl cellulose, 2 parts of dicyandiamide and, 2 parts of dypnone derivative；
Preparation method the following steps are included:
The production of S1, LDPE surface layer 2: weighing raw material, is sufficiently mixed after raw material is clayed into power, by mixed powder in injection molding machine
The feeding inlet temperature of injection molding machine is set as 200 DEG C, and the temperature of flat-mould head die orifice is set as 500 DEG C, and the feeding inlet of injection molding machine arrives
Flat-mould head die orifice using screw rod heating plasticizing in 20 DEG C incremented by successively of a distance temperature every making it in molten condition, through flat
LDPE surface layer is obtained after the linear extrusion of die head die orifice；
The production of S2, PET fiber layer 1: 100 % polyester slice phases on the fine water flow jet of high pressure to 100 % polyester slices, will be made
It is mutually intertwined, PET fiber layer 1 is prepared；
S3, the side of LDPE surface layer 2 is sticked on PET fiber layer 1 using epoxy type adhesive glue, carries out heating compacting reaction and adds
The laminating temperature of warm compaction reaction is 180 DEG C, and the lamination pressure of heating compacting reaction is 18 kgf/cm2, heating compacting reaction
Heat-insulation pressure keeping time be 45 min, heating compacting reaction release temperature at 60 DEG C hereinafter, after its natural cooling cooling after
Taking-up obtains the composite non woven cloth fabric of the anti-UV of water proof and dust proof.
By embodiment one, the composite non woven cloth fabric of the anti-UV of water proof and dust proof made of embodiment two and embodiment three is from removing
Intensity, chemical resistance, four aspects of hygroscopicity and tensile strength are detected, and testing result is as follows:
| Embodiment one | Embodiment two | Embodiment three | |
| Peel strength (Kgf/cm) | 1.36 | 1.42 | 1.41 |
| Chemical resistance (%) | 92 | 93 | 93 |
| Hygroscopicity (%) | 3.6 | 3.6 | 3.8 |
| Tensile strength (MPa) | 130 | 132 | 132 |
To testing result it is found that the compound nonwoven cloth of the anti-UV of water proof and dust proof made of embodiment one, embodiment two and embodiment three
Fabric peel strength is big, and chemical resistance is good, and hygroscopicity is poor, and tensile strength is big, therefore the anti-UV of water proof and dust proof made of the present invention
Composite non woven cloth fabric properties are excellent, and the composite non woven cloth fabric of the anti-UV of water proof and dust proof made of embodiment two is than implementing
The composite non woven cloth fabric of the anti-UV of water proof and dust proof made of example one and embodiment three is more preferable.Therefore, embodiment is second is that of the invention
Most preferred embodiment.
The foregoing is only a preferred embodiment of the present invention, but scope of protection of the present invention is not limited thereto,
Anyone skilled in the art in the technical scope disclosed by the present invention, according to the technique and scheme of the present invention and its
Inventive concept is subject to equivalent substitution or change, should be covered by the protection scope of the present invention.
Claims (8)
1. a kind of composite non woven cloth fabric and preparation method thereof of the dust-proof anti-UV of new waterproof, including PET fiber layer (1) and LDPE
Surface layer (2), which is characterized in that the LDPE surface layer (2) includes the raw material of following parts by weight: 100-120 parts of LDPE particle, epoxy
16-18 parts of resin, 5-7 parts of nanometer boron fibre, 8-14 parts of butylated urea-formaldehyde resin, 2-5 parts of zinc stearate, cellulose derivative 4-
6 parts, 1-2 parts and additive 1-2 parts of dicyandiamide；
The preparation method comprises the following steps:
The production of S1, LDPE surface layer (2): weighing raw material, is sufficiently mixed after raw material is clayed into power, and mixed powder is being molded
Make it in molten condition using screw rod heating plasticizing in machine, obtains LDPE surface layer after the linear extrusion of flat-mould head die orifice；
The production of S2, PET fiber layer (1): by the fine water flow jet of high pressure to 100 % polyester slices, make 100 % polyester slices
It is mutually intertwined, PET fiber layer (1) is prepared；
S3, the side of LDPE surface layer (2) is sticked on PET fiber layer (1) using adhesive glue, carries out heating compacting reaction, to
It is taken out after the cooling of its natural cooling and obtains the composite non woven cloth fabric of the anti-UV of water proof and dust proof.
2. the composite non woven cloth fabric and preparation method thereof of the dust-proof anti-UV of new waterproof according to claim 1 a kind of,
It is characterized in that, the LDPE surface layer (2) includes the raw material of following parts by weight: 110 parts of LDPE particle, 17 parts of epoxy resin, nanometer
6 parts of boron fibre, 11 parts of butylated urea-formaldehyde resin, 3 parts of zinc stearate, 5 parts of cellulose derivative, 2 parts of dicyandiamide and additive 1
Part.
3. the composite non woven cloth fabric and preparation method thereof of the dust-proof anti-UV of new waterproof according to claim 1 a kind of,
It is characterized in that, the cellulose derivative is cellulose nitrate, cellulose ethanoate, cellulose acetate butyrate and cellulose
Xanthate acid, carboxymethyl cellulose, hydroxyethyl cellulose, cyanethyl cellulose, hydroxypropyl cellulose and hydroxypropyl methyl cellulose
One of.
4. the composite non woven cloth fabric and preparation method thereof of the dust-proof anti-UV of new waterproof according to claim 1 a kind of,
It is characterized in that, the additive is benzophenone, benzotriazole, and triazine replaces acrylonitrile, and salicyclic acid derivatives, benzoic acid spreads out
Biology, cinnamic acid derivative, chalcone derivative, dypnone derivative, crotonic acid derivates, in diphenylacrylate
It is one or more of.
5. the composite non woven cloth fabric and preparation method thereof of the dust-proof anti-UV of new waterproof according to claim 1 a kind of,
It is characterized in that, the feeding inlet temperature of the injection molding machine is set as 200 DEG C, and the temperature of flat-mould head die orifice is set as 500 DEG C, injection molding
The feeding inlet of machine is to flat-mould head die orifice 20 DEG C incremented by successively every a distance temperature.
6. the composite non woven cloth fabric and preparation method thereof of the dust-proof anti-UV of new waterproof according to claim 1 a kind of,
It is characterized in that, the laminating temperature of the heating compacting reaction is 170 DEG C -180 DEG C, and the lamination pressure of heating compacting reaction is 16
Kgf/cm2-18 kgf/cm2, the time of the heat-insulation pressure keeping of heating compacting reaction are 45 min-60 min, heating compacting reaction
Release temperature is at 60 DEG C or less.
7. the composite non woven cloth fabric and preparation method thereof of the dust-proof anti-UV of new waterproof according to claim 1 a kind of,
It is characterized in that, the adhesive is epoxy type adhesive or modified epoxy type adhesive.
8. the composite non woven cloth fabric and preparation method thereof of the dust-proof anti-UV of new waterproof according to claim 1 a kind of,
It is characterized in that, the upper end glue connection of the PET fiber layer (1) is connected to LDPE surface layer (2).