CN109130045A - A kind of light-type roller and its manufacturing method - Google Patents
A kind of light-type roller and its manufacturing method Download PDFInfo
- Publication number
- CN109130045A CN109130045A CN201811100592.9A CN201811100592A CN109130045A CN 109130045 A CN109130045 A CN 109130045A CN 201811100592 A CN201811100592 A CN 201811100592A CN 109130045 A CN109130045 A CN 109130045A
- Authority
- CN
- China
- Prior art keywords
- roller
- body portion
- main body
- metal parts
- light
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to a kind of light-type rollers and preparation method thereof, the light-type roller includes columnar roller main body portion, it is provided with metal parts on the periphery in the roller main body portion, coating is provided in the peripheral surface of the metal parts, the roller main body portion is carbon fiber-reinforced resin roller main body portion.The present invention solves the technical issues of easily-deformable existing roller and heavier mass, the light-type roller lighter weight, to keep rotary inertia smaller, easily turns round, to improve production efficiency, and elasticity is good for the light-type roller, is unlikely to deform.
Description
Technical field
The present invention relates to a kind of light-type roller and its manufacturing methods, belong to technology for coating field.
Background technique
In the production field of light polarizing film and other films, generallys use rolling method and produced, it is used in production at present
Metal roll it is more easily-deformable, and due to heavier mass, the rotary inertia of roller is larger, so that the acceleration and deceleration of the rotation of roller
Time increases, and greatly reduces rhythm of production, extends the production cycle, to reduce production efficiency.
Summary of the invention
The purpose of the present invention is to provide a kind of light-type roller and its manufacturing method, solve that existing roller is easily-deformable and matter
Heavier technical problem is measured, which easily turns round, to keep rotary inertia smaller to improve production
Efficiency, and elasticity is good for the light-type roller, is unlikely to deform.
In order to achieve the above objectives, the invention provides the following technical scheme:
On the one hand, the present invention provides a kind of light-type roller, including columnar roller main body portion, the periphery in the roller main body portion
On be provided with metal parts, be provided with coating in the peripheral surface of the metal parts, the roller main body portion is fibre reinforced
Resin roll main part.
Further, the metal parts with a thickness of 0.5-1.5mm.Make the lighter weight of roller, and reduces cost.
Further, the coating be chrome plating, the chrome plating with a thickness of 50-80 μm.Make any surface finish of roller, and
Keep roller corrosion-resistant and scratch resistant.
Further, the metal parts is stainless steel metal component or aluminum metal component.
Further, the peripheral surface in the roller main body portion polishes smooth setting.Conducive to the even closer patch of metal parts
Conjunction is set on the periphery in roller main body portion.
Further, the roller main body portion with a thickness of 8-30mm.
On the other hand, the present invention also provides a kind of manufacturing methods of above-mentioned light-type roller, comprising the following steps:
A, the metal parts is heated by heating device, the metal parts expanded；
B, the metal parts of obtained expansion is sheathed on the periphery in the roller main body portion, obtains being provided with metal parts
Roller main body portion；
C, coating is plated in the peripheral surface of the metal parts in the obtained roller main body portion for being provided with metal parts.
Further, the heating temperature of the heating device is 120-170 DEG C, and the heating time of the heating device is
30-60min.Under this condition, expand metal parts, to be sheathed on the periphery in roller main body portion.
Further, before to metal parts heating, the internal diameter of the metal parts is less than the outer of the roller main body portion
Diameter 0.05-0.15mm.Not only it may insure to be sheathed on the periphery in roller main body portion after metal parts expands, but also metal can be made
It can be closely set on the periphery in roller main body portion after component is cooling.
The beneficial effects of the present invention are: the light-type roller, using carbon fiber-reinforced resin as the main body material in roller main body portion
Material, then metal parts is set on the periphery in carbon fiber-reinforced resin roller main body portion, make the lighter weight of roller, to make turning for roller
Dynamic inertia is smaller, easily turns round, improves production efficiency, and elasticity is good for the light-type roller, is unlikely to deform, and is more favorable for raw in business
Reference is promoted in production.
And the method that light-type roller is manufactured in the present invention, it is easy to operate, and metal parts can be closely bonded to setting
In on the periphery in roller main body portion.
The above description is only an overview of the technical scheme of the present invention, in order to better understand the technical means of the present invention,
And can be implemented in accordance with the contents of the specification, the following is a detailed description of the preferred embodiments of the present invention and the accompanying drawings.
Detailed description of the invention
Fig. 1 is the front view of light-type roller of the invention.
Specific embodiment
With reference to the accompanying drawings and examples, specific embodiments of the present invention will be described in further detail.Implement below
Example is not intended to limit the scope of the invention for illustrating the present invention.
Embodiment one
A kind of light-type roller as shown in Fig. 1, including columnar roller main body portion 1 coat on the periphery in roller main body portion 1
There is stainless steel metal component 2, chrome plating 3, the main body material in roller main body portion 1 are provided in the peripheral surface of stainless steel metal component 2
Material is carbon fiber-reinforced resin, and carbon fiber-reinforced resin is current material.Using carbon fiber-reinforced resin as the master in roller main body portion 1
Body material, then on the periphery in roller main body portion 1 be arranged metal parts 2, make the lighter weight of roller, thus make the rotary inertia of roller compared with
It is small, it easily turns round, improves production efficiency, and elasticity is good for the light-type roller, is unlikely to deform, and is more favorable for applying in production.
In the above-described embodiments, stainless steel metal component 2 with a thickness of 0.5mm, to make the lighter weight of roller, and reduce
Cost.
In the above-described embodiments, chrome plating 3 with a thickness of 50 μm, chrome plating 3 can make any surface finish of roller, and make roller corrosion resistant
Erosion and scratch resistant.
In the above-described embodiments, the peripheral surface in roller main body portion 1 polishes smooth setting, roller main body portion with a thickness of 8mm, benefit
It is set on the periphery in roller main body portion 1 in the even closer fitting of metal parts 2.
The manufacturing method of the light-type roller, comprising the following steps:
A, metal parts 2 being heated by electric heater unit, heating temperature is 120 DEG C, heating time 30min,
The metal parts 2 expanded；
B, the metal parts 2 of obtained expansion is sheathed on the periphery in roller main body portion 1, after cooling, obtains being provided with gold
Belong to the roller main body portion 1 of component 2；
C, coating 3 is plated in the peripheral surface of the metal parts 2 in the roller main body portion 1 for being provided with metal parts 2.
The manufacturing method of the light-type roller, it is easy to operate, and metal parts 2 can be closely bonded and be set to roller main body portion
On 1 periphery.
In the above-described embodiments, before heating to metal parts 2, the internal diameter of metal parts 2 is less than the outer diameter in roller main body portion 1
0.05mm not only may insure to be sheathed on the periphery in roller main body portion 1 after metal parts 2 expands, but also can make metal parts 2
It can be closely bonded on the periphery for being set to roller main body portion 1 after cooling.
Embodiment two
It can be only that with reference also to Fig. 1 in first embodiment, the difference of this second embodiment and first embodiment: roller
Be coated with aluminum metal component 2 on the periphery of main part 1, aluminum metal component 2 with a thickness of 1.5mm, chrome plating 3 with a thickness of 80 μ
M, roller main body portion with a thickness of 30mm.In the manufacturing method of the light-type roller, heating temperature is 170 DEG C, and heating time is
60min, before heating to metal parts 2, the internal diameter of metal parts 2 is less than the outer diameter 0.15mm in roller main body portion 1.
Embodiment three
It can be only that with reference also to Fig. 1 in first embodiment, the difference of this third embodiment and first embodiment: no
Become rusty steel metal component 2 with a thickness of 1.0mm, chrome plating 3 with a thickness of 65 μm, roller main body portion with a thickness of 20mm.The light-type
In the manufacturing method of roller, heating temperature is 150 DEG C, heating time 45min, before being heated to metal parts 2, metal parts 2
Internal diameter is less than the outer diameter 0.10mm in roller main body portion 1.
Each technical characteristic of embodiment described above can be combined arbitrarily, for simplicity of description, not to above-mentioned reality
It applies all possible combination of each technical characteristic in example to be all described, as long as however, the combination of these technical characteristics is not deposited
In contradiction, all should be considered as described in this specification.
The embodiments described above only express several embodiments of the present invention, and the description thereof is more specific and detailed, but simultaneously
It cannot therefore be construed as limiting the scope of the patent.It should be pointed out that coming for those of ordinary skill in the art
It says, without departing from the inventive concept of the premise, various modifications and improvements can be made, these belong to protection of the invention
Range.Therefore, the scope of protection of the patent of the invention shall be subject to the appended claims.
Claims (9)
1. a kind of light-type roller, which is characterized in that including columnar roller main body portion, be provided on the periphery in the roller main body portion
Metal parts, coating is provided in the peripheral surface of the metal parts, and the roller main body portion is carbon fiber-reinforced resin roller master
Body portion.
2. a kind of light-type roller as described in claim 1, which is characterized in that the metal parts with a thickness of 0.5-1.5mm.
3. a kind of light-type roller as described in claim 1, which is characterized in that the coating is chrome plating, the chrome plating
With a thickness of 50-80 μm.
4. a kind of light-type roller as described in claim 1, which is characterized in that the metal parts be stainless steel metal component or
Aluminum metal component.
5. a kind of light-type roller as described in claim 1, which is characterized in that the peripheral surface in the roller main body portion polishes smooth
Setting.
6. a kind of light-type roller as described in claim 1, which is characterized in that the roller main body portion with a thickness of 8-30mm.
7. such as a kind of manufacturing method of light-type roller of any of claims 1-6, which is characterized in that including following step
It is rapid:
A, the metal parts is heated by heating device, the metal parts expanded；
B, the metal parts of obtained expansion is sheathed on the periphery in the roller main body portion, obtains the roller for being provided with metal parts
Main part；
C, coating is plated in the peripheral surface of the metal parts in the obtained roller main body portion for being provided with metal parts.
8. a kind of manufacturing method of light-type roller as claimed in claim 7, which is characterized in that the heating temperature of the heating device
Degree is 120-170 DEG C, and the heating time of the heating device is 30-60min.
9. a kind of manufacturing method of light-type roller as claimed in claim 7, which is characterized in that heated to the metal parts
Before, the internal diameter of the metal parts is less than the outer diameter 0.05-0.15mm in the roller main body portion.